Abstract
In this paper, a general low-cost and substrate-independent chemical etching strategy is demonstrated for the synthesis of ZnO nanotubes array. During the chemical etching, the nanotubes array inherits many features from the preformed nanorods array, such as the diameter, size distribution, and alignment. The preferential etching along c axis and the surfactant protection to the lateral surfaces are considered responsible for the formation of ZnO nanotubes. This surfactant-assisted chemical etching strategy is highly expected to advance the research in the ZnO nanotube-based technology.
Avoid common mistakes on your manuscript.
Introduction
One-dimensional (1D) nanostructures are of particularly interest due to their unique properties different from that of bulk and nanoparticles [1–5]. It is well known that the hollow nanostructures have more prominent advantages (such as the enhanced confinement effect and larger area–volume ratios) over the other 1D nanostructures, such as nanowires and nanorods, and thus are promising candidates in catalysts, gas sensors, phosphors, and solar cells [6–9]. Zinc oxide (ZnO), with a direct band gap of 3.37 eV and a high exciton binding energy of 60 meV at room temperature, is an important technological semiconductor due to its distinguished optical, electrical, and piezoelectrical properties [10, 11]. Various kinds of 1D ZnO nanostructures array, such as nanorods, nanobelts, nanoneedles, and nanotips, have recently been synthesized by a good number of techniques [10, 11]. In contrast, only limited studies have been reported on the fabrication of ZnO nanotubes array, which is probably because the tubular form is generally available in layered materials such as carbon nanotubes. Current synthesis of ZnO nanotubes array is mainly based either on the chemical vapor deposition or the electrochemical approach [12–17], which generally requires economically prohibitive temperatures and complex processes, and is unfavorable for mass production. Additionally, despite the good controllability realized by the electrochemical method, the growth of ZnO nanotubes array can only be achieved on the conductive substrates, which greatly confines the wide applications of the resulted nanotubes in many other fields (such as gas sensing, which generally utilize nonconductive quartz substrates). Exploring strategy for a general low-cost and substrate-independent fabrication of ZnO nanotubes array is thus highly desirable.
Recently, a controllable synthesis of 1D novel nanostructures with different morphologies has been realized in our group by using various chemical etching methods [18–20], in which the preferential etching along c axis was found to be an important etching behavior for ZnO polar crystal. In this paper, by using the surfactant as the protection layer to the nonpolar surfaces of ZnO nanorod, we demonstrate a surfactant-assisted chemical etching approach to synthesize the ZnO nanotubes array. This chemical etching strategy is substrate independent and facile in manipulation, thus provides an avenue of a general and low-cost fabrication of the ZnO nanotubes array, which is highly expected to advance the ZnO nanotube-based technology.
Experimental
Typically, ZnO nanocrystals were spin coated onto silicon wafer to form a seed layer according to the literature [21], and hydrothermal growth was carried out by suspending the silicon wafer upside down in an autoclave filled with an aqueous solution of 6 ml ammonia (25 wt%) and 80 ml zinc chloride solution (0.1 M) at 95°C for 70 min (growth step). After growth, the wafer was thoroughly rinsed with de-ionized water and suspended once again into a 90 ml solution containing ammonia (0.5 wt%) and cetyltrimethyl ammonium bromide (CTAB; 0.5 wt%) at room temperature for 3.5 h (etching step) and then washed with de-ionized water again. The as-synthesized samples were characterized by X-ray diffraction (XRD, Philips X’pert PRO), field emission scanning electron microscopy (FE-SEM, Sirion 200), and transmission electron microscopy (TEM, JEOL 2010, 200 kV). A He–Cd laser system with the excitation wavelength of 325 nm was used to investigate the photoluminescence properties of the final products.
Results and Discussion
Figure 1a shows the FESEM image of the ZnO nanorods obtained in the growth step, in which the nanorods with an average size of about 200 nm and flat termination can be clearly seen (inset in Fig. 1a). After the surfactant-assisted in situ chemical etching (etching step), tubular structures were formed, as shown in Fig. 1c. One can see that the nanotubes array inherits many features from the nanorods array, such as the diameter, size distribution, and alignment. The corresponding XRD pattern shown in Fig. 1b and d all indicate that the ZnO nanorods and nanotubes have a wurtzite (hexagonal) ZnO structure. It is interesting to note that the intensity of the (0002) diffraction peak at 2θ = 34.4° for the nanotubes array decreases substantially when compared with that for the nanorods array.
The typical TEM image of a single ZnO nanotube is shown in Fig. 2a, in which an obvious contrast between the tube wall and the inner part can be clearly observed, providing a direct evidence of the tubular structure. The selected area electron diffraction pattern shown in Fig. 2b demonstrates the single crystalline feature of the ZnO nanotube. Figure 2c shows the corresponding HRTEM image of the ZnO nanotube, in which the measured interplane spacing (0.52 nm) matches well with the literature reported value of the (0001) plane in wurtzite ZnO, indicating that the nanotube grows along the (0001) direction.
To investigate the formation mechanism of the ZnO nanotubes array, experiments with different etching time were performed (keeping other experimental conditions unchanged). Figure 3 shows the FESEM image of the product after etching for 0, 0.5, 1, and 1.5 h, respectively. Before etching, as shown in Fig. 3a, each nanorod obtained in the growth step has a flat termination. After etching for 0.5 h, the central part of the flat termination was firstly etched away, as shown in Fig. 3b, forming a very shallow pit at the top end of the nanorod. As the etching continued, a deeper and wider pit was formed on the top of the ZnO nanorod (see Fig. 3c, 3d). Prolonging the etching time leads to the further deepening of the hollow part and the final formation of the tubular structure.
It was found that the using of the surfactant in the etching step is much critical for the formation of the tubular nanostructure. If CTAB is not used in the etching process, the ZnO nanorods will become shorter and shorter (always with shallow pits at the top end) and finally be etched into the broken pieces (Figure S1). Too much CTAB used in the etching step (over 2 wt%) will lead to the formation of a thin surfactant coat on the surface of ZnO nanorods array, and thus block the subsequent etching (Figure S2). In addition, the amount of ammonia used in the etching step is also important for the controllable fabrication of ZnO nanotubes array. In the etching step, too much (larger than 5 wt%) or too little (lower than 0.1 wt%) amount of ammonia will result in the fast dissolution of ZnO nanorods array or no effect on the morphology change of ZnO nanorods.
From the above discussion, one can see that the formation of the nanotubes array undergoes two steps, the growth and the surfactant-assisted etching of the ZnO nanorods array, which can be described by reaction (1). In the growth step, the precursor Zn(NH3)4 2+ reacts with OH− to form ZnO, and the equilibrium in Eq. (1) moves to the right side, corresponding to the deposition of ZnO, which only happens at temperatures higher than 75°C. In the etching step, because the reaction proceeds at room temperature, the equilibrium in Eq. (1) will shift to the left side, leading to the etching of ZnO [22].
As is well known, ZnO is a polar crystal, and c axis is the most active direction both for the crystal growth and for the etching. In addition, the etching for ZnO also demonstrates a curvature dependency [18]. NH3 is a polar molecule, and there exists a lone pair of electrons in its electronic structure. Because ZnO surface is also negatively/positively charged, the polar molecules of NH3 can be easily attached on. For the location with higher curvature, the area density of the surface charges is higher, therefore, the electrostatic adhesion of NH3 on ZnO nanorod is stronger, leading to a faster etching rate in this area. For free etching (without the surfactant), as shown in Fig. 4a, the etching is preferentially along the c axis, and that is why a shallow pit firstly forms. Then, the preferential etching location is replaced by the edge area of the shallow pit due to the much higher curvature. After the etching away of the top area, etching along c axis becomes dominant. Therefore, the alternatively dominant etchings result in the shorter and shorter of the ZnO nanorod, and always with a shallow pit on the top end, as shown in Fig. 4a. It has been reported that some surfactants such as SDS and CTAB can be used as effective agents to control the diameter of ZnO nanorod because these molecules can be firmly bonded by the lateral surfaces [23, 24]. Therefore, we speculate that the preferential etching along c axis and the surfactant protection to the lateral surfaces are responsible for the formation of ZnO nanotubes, as schematically illustrated in Fig. 4b, in which the CTAB protection to lateral surface of the top end of ZnO nanorod prevents the further etching of shallow pit edge, thus provides an obstacle for the curvature-dependent etching at the top end of ZnO nanorod and facilitates the etching along c axis.
It is easily understood that another possibility in producing ZnO nanotubes array is to combine the growth and etching into one step, i.e. after the growth of the ZnO nanorods array, directly decreasing the temperature from 95 to below 75°C, without taking out the silicon wafer. However, it was found that the resulted product was nanorods array with the similar feature obtained in the above-mentioned growth step, which might be due to the low NH3 concentration dissolved in the reaction solution.
The room temperature photoluminescence spectra of the ZnO nanotubes array shown in Fig. 5 (the red curve) exhibits the typical near-band-gap ultraviolet emission centered at 396 nm and a broad visible emission band, which is usually attributed to deep-level emission caused by defects of oxygen vacancies. It is observable that the etching of the nanorod array in diluted etching solution does not influence the band edge emission intensity but causes a 8-nm red shift from 387 to 395 nm. Such a red shift might be related to the lattice strain due to the heterogeneous etching at the surface of the nanorod [7, 25], which can be evidenced by the enhanced intensity of the defects related emission (see Fig. 5). In addition, the changing of the dielectric environment and consequent renormalization of ZnO band structure induced by screening of the surfactant molecules might also contribute to the red shift.
The surfactant-assisted in situ chemical etching strategy presented in this study is general, and other substrates (polymers, ITO glasses, ceramic tubes/plates, etc.) also can be used to fabricate the ZnO nanotubes array via the same chemical etching process, which allows for the applications of ZnO nanotubes array in many fields, such as electronics, photocatalysis, and gas sensing. Additionally, the easy mediation in the diameter of the preformed nanorod array [23, 24] in the growth step makes it possible to produce the ZnO nanotubes with different diameters.
Conclusions
In summary, a general low-cost and substrate-independent synthesis of ZnO nanotubes array via a surfactant-assisted chemical etching strategy is demonstrated. The as-obtained ZnO nanotubes array shows an intensive ultraviolet photoluminescence emission, indicating the nanotubes array is promising for application in future nanoscale optoelectronic devices. The preferential etching along c axis and the surfactant protection to the lateral surfaces are considered responsible for the formation of ZnO nanotubes. This surfactant-assisted chemical etching strategy is highly expected to advance the research in the ZnO nanotube-based technology.
References
Fang XS, Bando Y, Liao MY, Gautam UK, Zhi CY, Dierre B, Liu BD, Zhai TY, Sekiguchi T, Koide Y, Golberg D: Adv. Mater.. 2009, 21: 2034. COI number [1:CAS:528:DC%2BD1MXmsVSns78%3D] COI number [1:CAS:528:DC%2BD1MXmsVSns78%3D] 10.1002/adma.200802441
Zeng HB, Xu XJ, Bando Y, Gautam UK, Zhai TY, Fang XS, Liu BD, Golberg D: Adv. Funct. Mater.. 2009, 19: 3165. COI number [1:CAS:528:DC%2BD1MXht1KisrvP] COI number [1:CAS:528:DC%2BD1MXht1KisrvP] 10.1002/adfm.200900714
Cao BQ, Teng XM, Heo SH, Li Y, Cho SO, Li GH, Cai WP: J. Phys. Chem. C. 2007, 111: 2470. COI number [1:CAS:528:DC%2BD2sXot1aluw%3D%3D] COI number [1:CAS:528:DC%2BD2sXot1aluw%3D%3D] 10.1021/jp066661l
Hu JQ, Bando Y, Golberg D: J. Mater. Chem.. 2009, 19: 330. COI number [1:CAS:528:DC%2BD1cXhsFCisr3N] COI number [1:CAS:528:DC%2BD1cXhsFCisr3N] 10.1039/b808320g
Wang HQ, Wang GZ, Jia LC, Tang CJ, Li GH: J. Phys. Chem. C. 2007, 111: 14307. COI number [1:CAS:528:DC%2BD2sXhtVWrsb7M] COI number [1:CAS:528:DC%2BD2sXhtVWrsb7M] 10.1021/jp074783n
Liu JP, Li YY, Fan HJ, Zhu ZH, Jiang J, Ding RM, Hu YY, Huang XT: Chem. Mater.. 2010, 22: 212. COI number [1:CAS:528:DC%2BD1MXhsVSmu7zO] COI number [1:CAS:528:DC%2BD1MXhsVSmu7zO] 10.1021/cm903099w
Wang HQ, Wang GZ, Jia LC, Tang CJ, Li GH: J. Phys. D Appl. Phys.. 2007, 40: 6549. COI number [1:CAS:528:DC%2BD2sXhtlGht7jN]; Bibcode number [2007JPhD...40.6549W] COI number [1:CAS:528:DC%2BD2sXhtlGht7jN]; Bibcode number [2007JPhD...40.6549W] 10.1088/0022-3727/40/21/014
Banerjee S, Mohapatra SK, Misra M: Chem. Commun.. 2009, 7137.
Kawano T, Chiamori HC, Suter M, Zhou Q, Sosnowchik BD, Lin LW: Nano Lett.. 2007, 7: 3686. COI number [1:CAS:528:DC%2BD2sXht12ms7vK]; Bibcode number [2007NanoL...7.3686K] COI number [1:CAS:528:DC%2BD2sXht12ms7vK]; Bibcode number [2007NanoL...7.3686K] 10.1021/nl071964s
Norton DP, Heo YW, Ivill MP, Ip K, Pearton SJ, Chisholm MF, Steiner T: Mater. Today. 2004, 7: 34. COI number [1:CAS:528:DC%2BD2cXlt1WrsLc%3D] COI number [1:CAS:528:DC%2BD2cXlt1WrsLc%3D] 10.1016/S1369-7021(04)00287-1
Wang ZL: J. Phys. Condens. Matter. 2004, 16: R829. COI number [1:CAS:528:DC%2BD2cXmtVyhtLY%3D]; Bibcode number [2004JPCM...16R.829W] COI number [1:CAS:528:DC%2BD2cXmtVyhtLY%3D]; Bibcode number [2004JPCM...16R.829W] 10.1088/0953-8984/16/25/R01
Li L, Pan SS, Dou XC, Zhu YG, Huang XH, Yang YW, Li GH, Zhang LD: J. Phys. Chem. C. 2007, 111: 7288. COI number [1:CAS:528:DC%2BD2sXks12ms7g%3D] COI number [1:CAS:528:DC%2BD2sXks12ms7g%3D] 10.1021/jp0711242
Xi Y, Song J, Xu S, Yang R, Gao Z, Hu C, Wang ZL: J. Mater. Chem.. 2009, 19: 9260. COI number [1:CAS:528:DC%2BD1MXhsFSgtrnJ] COI number [1:CAS:528:DC%2BD1MXhsFSgtrnJ] 10.1039/b917525c
Wu CC, Wuu DS, Lin PR, Chen TN, Horng RH: Crys. Growth Des.. 2009, 9: 4555. COI number [1:CAS:528:DC%2BD1MXhtVens73F] COI number [1:CAS:528:DC%2BD1MXhtVens73F] 10.1021/cg900557n
Yu H, Zhang Z, Han M, Hao X, Zhu F: J. Am. Chem. Soc.. 2005, 127: 2378. COI number [1:CAS:528:DC%2BD2MXovFSqsQ%3D%3D] COI number [1:CAS:528:DC%2BD2MXovFSqsQ%3D%3D] 10.1021/ja043121y
She GW, Zhang XH, Shi WS, Fan X, Chang JC, Lee CS, Lee ST, Liu CH: Appl. Phys. Lett.. 2008, 92: 053111. Bibcode number [2008ApPhL..92e3111S] Bibcode number [2008ApPhL..92e3111S] 10.1063/1.2842386
Xu L, Liao Q, Zhang J, Ai X, Xu D: J. Phys. Chem. C. 2007, 111: 4549. COI number [1:CAS:528:DC%2BD2sXisVSiu7Y%3D] COI number [1:CAS:528:DC%2BD2sXisVSiu7Y%3D] 10.1021/jp068485m
Wang HQ, Li GH, Jia LC, Wang GZ, Li L: Appl. Phys. Lett.. 2008, 93: 153110. Bibcode number [2008ApPhL..93o3110W] Bibcode number [2008ApPhL..93o3110W] 10.1063/1.2951609
Wang HQ, Li GH, Jia LC, Wang GZ, Tang CJ: J. Phys. Chem. C. 2008, 112: 11738. COI number [1:CAS:528:DC%2BD1cXosF2gt74%3D] COI number [1:CAS:528:DC%2BD1cXosF2gt74%3D] 10.1021/jp803059k
Wang HQ, Li GH, Jia LC, Li L, Wang GZ: Chem. Commun.. 2009, 3786.
Pacholski C, Kornowski A, Weller H: Angew. Chem. Int. Ed.. 2002, 41: 1188. COI number [1:CAS:528:DC%2BD38XivVyktL0%3D] COI number [1:CAS:528:DC%2BD38XivVyktL0%3D] 10.1002/1521-3773(20020402)41:7<1188::AID-ANIE1188>3.0.CO;2-5
Wei A, Sun XW, Xu CX, Dong ZL, Yang Y, Tan ST, Huang W: Nanotechnology. 2006, 17: 1740. COI number [1:CAS:528:DC%2BD28XkslOksb8%3D]; Bibcode number [2006Nanot..17.1740W] COI number [1:CAS:528:DC%2BD28XkslOksb8%3D]; Bibcode number [2006Nanot..17.1740W] 10.1088/0957-4484/17/6/033
De la Rosa E, Sepulveda-Guzman S, Reeja-Jayan B, Torres A, Salas P, Elizondo N, Yacaman MJ: J. Phys. Chem. C. 2007, 111: 8489. 10.1021/jp071846t
Dev A, Panda SK, Kar S, Chakrabarti S, Chaudhuri S: J. Phys. Chem. B. 2006, 110: 14266. COI number [1:CAS:528:DC%2BD28XmsV2jsb8%3D] COI number [1:CAS:528:DC%2BD28XmsV2jsb8%3D] 10.1021/jp062729l
Hsu CL, Chang SJ, Lin YR, Tsai SY, Chen IC: Chem. Commun.. 2005, 3571.
Acknowledgments
This work was supported by the National Natural Science Foundation of China (No: 10904145 and No: 10704074), and the Anhui Natural Science Foundation (No: 090414188).
Open Access
This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
11671_2010_9608_MOESM1_ESM.jpg
Figure S1: Figure S1 SEM images of products obtained by etching the preformed ZnO nanorods array in ammonia solution (0.5 wt%) with different etching time: (a) 0 hr, (b) 1 hr, (c) 2 hrs, and (d) 3.5 hrs. From this result, we can see that without using the surfactant of CTAB, the ZnO nanorods become shorter and shorter in the etching process, always with shallow pits at the top end, and finally etch into broken pieces (JPG 458 KB)
11671_2010_9608_MOESM2_ESM.jpg
Figure S2: Figure S1 SEM image of the product obtained by the surfactant-assisted in situ chemical etching, in which the amount of CTAB used in the etching process is 5 wt%. From this result, we can see that the using of too much amount of CTAB will lead to the coating of the surface of ZnO nanorods array by a surfactant film, thus preventing the subsequent etching. (JPG 354 KB)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Wang, H., Li, M., Jia, L. et al. Surfactant-Assisted in situ Chemical Etching for the General Synthesis of ZnO Nanotubes Array. Nanoscale Res Lett 5, 1102 (2010). https://doi.org/10.1007/s11671-010-9608-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11671-010-9608-z