Abstract
We report observation of catalyst-free hydride vapor phase epitaxy growth of InN nanorods. Characterization of the nanorods with transmission electron microscopy, and X-ray diffraction show that the nanorods are stoichiometric 2H–InN single crystals growing in the [0001] orientation. The InN rods are uniform, showing very little variation in both diameter and length. Surprisingly, the rods show clear epitaxial relations with thec-plane sapphire substrate, despite about 29% of lattice mismatch. Comparing catalyst-free with Ni-catalyzed growth, the only difference observed is in the density of nucleation sites, suggesting that Ni does not work like the typical vapor–liquid–solid catalyst, but rather functions as a nucleation promoter by catalyzing the decomposition of ammonia. No conclusive photoluminescence was observed from single nanorods, while integrating over a large area showed weak wide emissions centered at 0.78 and at 1.9 eV.
Avoid common mistakes on your manuscript.
Introduction
InN marks the lower bandgap limit achievable within the group III-nitride semiconductor family. To date, it has also been the most difficult-to-grow among that family, mainly because at its growth temperature, InN decomposes almost as readily as ammonia. Incorporation of In into GaN has also been difficult, especially at high In percentage, due to the large difference in growth temperature between InN and GaN [1]. An even more challenging scenario is encountered when one attempts a catalytic growth of InN nanowires. Catalytic growth is commonly preferred, for it allows control of size and position of the wires. A catalyst of choice is one that is inert and can liquefy, if not as a pure element, at least by eutectic reaction with another element, below the growth temperature. The most common choice is Au. Au can melt eutectically in reaction with Si but not as well on sapphire, the more common substrate for nitrides. Furthermore, nitrogen is claimed to be poorly soluble in Au [2]. Growth with Au catalyst has been reported [3], but due to its relatively low efficiency, it typically requires large flow of ammonia. In many studies, catalyzed nitride nanowires are grown with Ni [4, 5]. In this paper, we report an observation of catalyst-free epitaxial growth of remarkably size-uniform and vertically-aligned InN nanorods on c-plane sapphire. We compare this growth to Ni catalyzed growth under the same conditions and suggest that a growth mechanism other than vapor–liquid–solid (VLS) may be responsible for the observed uniformity.
Experimental Details
Growth of InN onc-plane sapphire was carried out in a custom designed HVPE reactor. The reactor consists of 75 mm quartz tube, placed in a three-zone Mellen horizontal furnace. Quartz insert with a rectangular cross-section is employed to produce laminar flow in the growth zone and to suppress turbulence (Fig. 1). Two of the heating zones are used for hydride reactions of column-III-metals with HCl gas. In this work, only indium was used as the source metal and the InCl was formed in a direct reaction between molten In and HCl gas diluted with N2. The resulting Indium chloride is formed in an internal quartz tube (10 mm cross section) at 500 °C and is carried in its dedicated tube into the rectangular part. The third zone is the growth zone that was kept at 550 °C during the process. Ammonia is delivered to the growth zone via separate 10 mm diameter quartz tube, and the InCl gas reacts with ammonia to form InN. The growth was carried out either with 1.5 nm of thermally deposited Ni as catalyst or without catalyst.
Process gasses were exhausted through a Lab Guard wet scrubbing system. The growth was carried out at atmospheric pressure. Ultra high purity Ar was used as a carrier gas. Typical carrier flow was 3000 sccm, HCl and NH3 flows were 1–10 and 50–200 sccm, respectively. The efficiency of ammonia decomposition drops with temperature, and is rather low at the InN growth temperatures. For this reason, the growth of InN requires a relatively high flow of ammonia [6]. The growth was estimated to be at a rate of ∼45 nm/min and was carried out for 30 min.
Scanning electron microscopy was carried out in a LEO (Zeiss) 982 FEG-SEM Field Emission Gun Scanning Electron Microscope with a Noran thin-window electron-dispersive spectroscopy (EDS) detector. Tunneling electron microscopy (TEM) was performed using a JEOL 2010-FEG-TEM/STEM operated at 200 keV with attached EDAX thin-window detector. Photoluminescence (PL) was excited at room temperature using a HeCd laser (325 nm, 8 mW). The emitted luminescence was dispersed by a monochromator, filtered, and sensed using a Si CCD camera.
Results
Vertically aligned nanorods grew over the entire sample area at density varying roughly between 1 and 2 rods per μm2(Fig. 2, top-left panel). The rods are strikingly uniform in size, with thickness of 374 ± 21 nm (standard deviation 5.6 %) and length of 1725 ± 56 nm (standard deviation 3.2 %) (Fig. 2, top-right panel). We believe that the higher standard deviation in the width value is an artifact resulting from ill-defined diameter of hexagonal cross-section rod. Samples deposited with Ni catalyst produced the same size, length, and shape of rods, except for a much higher nucleation density of 6–8 rods per μm2(Fig. 2, bottom panel), effectively fusing the nanorods into a continuous layer.
Close examination of adjacent rods (Fig. 3) reveals that the rods are aligned to one another, i.e., no relative rotations observed around the growth axis, which suggests that the rods have epitaxial relations with the substrate. While the rods appear to possess sixfold symmetry, they actually show 12 facets that appear as two six-faceted rods grown into one another from the two ends of the wire toward the middle. However, selected area diffractions did not show any difference between adjacent facets. Electron dispersive spectroscopy shows that the main elements are In and N (Fig. 4). No other element could be conclusively identified. Specifically, we could not detect any Ni on the rod tip as in the classic case of VLS catalysis [7].
2Θ−ω symmetric X-ray diffraction (Fig. 5, top) main peaks are clearly identified as Al2O3(0006), InN(0002), and InN(0004), which confirms what is already suggested in the SEM image, that the rods adopt thec-orientation of their sapphire substrate. Zooming into the background of the diffraction spectrum (Fig. 5, bottom) reveals InN peak, diffracted by the sloped sides of the tip, as well as InN and InN and a peak of InN (and a weaker InN ) which are likely to originate from a small percentage of uprooted rods laying on their side. Neither free Ni nor its chlorides, nitrides, or oxides were detected.
Figure 6shows a single InN nanorod on a TEM grid and the corresponding selective area diffraction. The diffraction is from the zone axis, and provides another confirmation of the [0001] growth orientation. High-resolution imaging was not possible due to the thickness of the rods and the low decomposition temperature of InN, but electron diffraction from a larger selected area diffraction aperture confirms that the rods are single crystals. STEM/EDS was used to monitor Ni in Ni catalyzed rods. Ni signal was below the noise limit. This suggests that Ni is either etched away by the HCl product of the HVPE reaction or remains at the substrate interface.
Photoluminescence measurements were carried out at room temperature. Photoluminescence, integrating emissions from a wide area, is shown in Fig. 7. It combines the results of two measurements: one, with Ar laser pumping and InGaAs detector for the infrared range, and another using He–Cd laser pumping and Si detector for the visible range. It shows weak emission centered at 0.78 eV and even weaker emission peak centered at 1.9 eV. Both these emissions have been suggested to be InN band edge emission. The commonly suggested (though not conclusively established) explanation on these emissions today is for the 0.7–0.8 eV to be the band edge of pure InN [8], and for the 1.9 eV to result from some presence of oxygen compounds, pulling the band edge up towards that of the In2O3(∼3.7 eV) [9]. However, no evidence for oxygen was present in EDS of individual rods, or for oxides in XRD of the entire sample. In the case of nanowires, it is always more instructive to obtain luminescence from an individual wire, in order to exclude background that often includes various defective particles. However, in our case, emission from individual nanorods was consistently below the noise level.
To assess the material resistivity, we carried out standard four-point probe sheet resistance measurement on continuous layers of fused nanorods grown using Ni catalyst. The measured sheet resistance of 55.5 Ohm/square, multiplied by the film thickness of 1.8 mm, yields 0.01 Ohm cm.
Discussion
Weak radiative recombination is not uncommon in narrow gap III–V semiconductors, especially when nanostructured. Possibly, the increased surface-to-volume ratio gives rise to enhanced effect of surface recombination. Since surface states are typically below the bandgap energy, and since our InGaAs detector was limited to 0.6 eV, our experiment was practically blind to any emission below 0.6 eV. Surface deep levels usually mean surface depletion. However, narrow gap III–V semiconductors, especially In-based, such as InAs and InSb, are known to have their surface Fermi level pinned above the conduction band, giving rise to surface accumulation layer [10]. The high density of accumulated electrons at the surface is a known cause for non-radiative recombination through Auger processes. Auger recombination has been shown to be the main non-radiative recombination mechanism in InGaAs semiconductor devices, having band gap energy in the range of 0.6–0.8 eV [11]. While the effectiveness of Auger processes in InN is still under debate [12, 13], it is known to strongly depend on the doping. The resistivity of our material (0.01 Ohm cm) seems low enough to make this mechanism important.
While PL does not provide a conclusive identification of InN, both in general and specifically in our experiment, our X-ray and TEM/selective area diffraction data present a clear picture ofc-oriented material growth, with EDS clearly identifying the main elements as indium and nitrogen. The lack of Ni signal in EDS spectra does not exclude Ni incorporation within the InN rods, but conclusively confirms its absence at the rod tip, at the typical VLS catalyst placement, commonly observed in VLS growth.
Ni does not melt (not even by eutectic reaction with sapphire or aluminum) at the growth temperature range [14]. Therefore, it is quite clear that if the growth still takes place by vapor–liquid–solid mode, the only available liquid metal in the system is that of the group III metal, i.e., the growth is most likely self-catalyzed by the group III metal [15]. Nonetheless, we observe a clear increase in nucleation density in c-plane sapphire samples deposited with Ni compared with bare samples grown simultaneously at the same run (comparing the top and bottom panels of Fig. 2). We therefore suggest that Ni serves as a nucleation promoter possibly by virtue of its ability to catalyze ammonia decomposition [16–20]. This type of catalysis is less likely to yield diameter control, as does the common VLS-mode catalyst, but may easily explain the order of magnitude denser nucleation of rods we observe in the presence of Ni. Further structural studies, e.g., cross-sectional TEM of the nucleation phase of the growth, could shed more light on the details of the Ni role.
Self-VLS-catalysis, e.g., with In, as is possible in our case, is also unlikely to provide any control, as the metal vapor is being showered all over the sample continuously through the growth, unlike the case of VLS, where the size and placement of catalyst droplets is well-defined at the beginning of the growth and is relatively stable through the growth. Hence the outstanding diameter uniformity that we observe cannot be explained by the VLS model and does not seem to be related to the Ni catalyst either.
Another form of outstanding uniformity is the rotational alignment of the rods. Such alignment would only be possible under epitaxial relations. However, this is rather surprising considering a lattice mismatch of 29% between InN and sapphire, known to produce structural defects (misfit dislocations) in films. Typically in such cases, the wire structure shows a wider cone shaped base, where the strain is gradually relieved [21, 22]. No such effect, or any other effect of strain has been observed in our case. In a theoretical work, Ertekin et al. showed that nanowire heterostructures are more effective at relieving mismatch strain coherently compared with films. The critical diameter for coherent growth of nanowires on lattice-mismatched substrates was predicted to be up to one order of magnitude larger than that of thin film growth [23]. Yet, most of the published works on growth of InN nanorods on c-plane sapphire typically observe random orientations emanating from each nucleus with no clear expitaxial relation to the substrate [24–26].
Epitaxial growth of InN on c-plane sapphire has been explored [27, 28]. However, to date, an intermediate layer of AlN (often formed by nitridation of the sapphire substrate) or a bilayer AlN\GaN have always been used to bridge the mismatch and reduce the defect formation. In our case, we did not perform any intentional pretreatment. Nitridation is highly unlikely to have taken place at 550 °C. Unintentional In2O3 is also unlikely to be able to bridge between InN and sapphire, because In2O3 is of cubic symmetry. Hence, it seems highly likely that the epitaxial relations we observed were direct, although the details of the actual mechanism require further investigation.
Conclusion
Our observation suggests that InN may establish direct epitaxial relation withc-plane sapphire and may also form nanoscale fibers without extrinsic catalyst. Use of Ni as catalyst is only seen to increase the nucleation density and is therefore suggested to work as nucleation promoter by catalyzing ammonia decomposition.
References
Bhuiyan AG, Hashimoto A, Yamamoto A: J. Appl. Phys.. 2003, 94: 2779. COI number [1:CAS:528:DC%2BD3sXms1Cjtrw%3D]; Bibcode number [2003JAP....94.2779B] COI number [1:CAS:528:DC%2BD3sXms1Cjtrw%3D]; Bibcode number [2003JAP....94.2779B] 10.1063/1.1595135
Okamoto H, Massalski TB: J. Phase Equilib.. 1984, 5: 381.
Hsu CW, Ganguly A, Liang CH, Hung YT, Wu CT, Hsu GM, Chen YF, Chen CC, Chen KH, Chen LC: Adv. Funct. Mater.. 2008, 18: 938. COI number [1:CAS:528:DC%2BD1cXkslyhs7s%3D] COI number [1:CAS:528:DC%2BD1cXkslyhs7s%3D] 10.1002/adfm.200700739
Duan XF, Lieber CM: J. Am. Chem. Soc.. 2000, 122: 188. COI number [1:CAS:528:DyaK1MXnvF2qt7w%3D] COI number [1:CAS:528:DyaK1MXnvF2qt7w%3D] 10.1021/ja993713u
Zhang J, Zhang L, Vac J: Sci. Technol. B. 2003, 21: 2415. COI number [1:CAS:528:DC%2BD2cXptFGnsQ%3D%3D] COI number [1:CAS:528:DC%2BD2cXptFGnsQ%3D%3D] 10.1116/1.1625968
Cai XM, Yeb F, Jing SY, Zhang DP, Fan P, Xie EQ: Appl. Surf. Sci.. 2008, 255: 2153. COI number [1:CAS:528:DC%2BD1cXhsVChsL7K]; Bibcode number [2008ApSS..255.2153C] COI number [1:CAS:528:DC%2BD1cXhsVChsL7K]; Bibcode number [2008ApSS..255.2153C] 10.1016/j.apsusc.2008.07.051
Wagner RS, Ellis WC: Appl. Phys. Lett.. 1964, 4: 89. COI number [1:CAS:528:DyaF2cXls1yhug%3D%3D]; Bibcode number [1964ApPhL...4...89W] COI number [1:CAS:528:DyaF2cXls1yhug%3D%3D]; Bibcode number [1964ApPhL...4...89W] 10.1063/1.1753975
Chen HY, Shen CH, Lin HW, Chen CH, Wu CY, Gwo S, Davydov VY, Klochikhin AA: Thin Solid Films. 2006, 515: 961. COI number [1:CAS:528:DC%2BD28XhtFKktbvN]; Bibcode number [2006TSF...515..961C] COI number [1:CAS:528:DC%2BD28XhtFKktbvN]; Bibcode number [2006TSF...515..961C] 10.1016/j.tsf.2006.07.086
Butcher KSA, Tansley TL: Superlattice. Microst.. 2005, 38: 1. COI number [1:CAS:528:DC%2BD2MXlsVCksLw%3D]; Bibcode number [2005SuMi...38....1B] COI number [1:CAS:528:DC%2BD2MXlsVCksLw%3D]; Bibcode number [2005SuMi...38....1B] 10.1016/j.spmi.2005.03.004
Stoica T, Meijers RJ, Calarco R, Richter T, Sutter E, Lueth H: Nano Lett.. 2006, 6: 1541. COI number [1:CAS:528:DC%2BD28XmtF2qsLs%3D] COI number [1:CAS:528:DC%2BD28XmtF2qsLs%3D] 10.1021/nl060547x
Metzger WK, Wanlass MW, Ellingson RJ, Ahrenkiel RK, Carapella JJ: Appl. Phys. Lett.. 2001, 79: 3272. COI number [1:CAS:528:DC%2BD3MXot1Slsbs%3D]; Bibcode number [2001ApPhL..79.3272M] COI number [1:CAS:528:DC%2BD3MXot1Slsbs%3D]; Bibcode number [2001ApPhL..79.3272M] 10.1063/1.1418032
Ascazubi R, Wilke I, Cho S, Lu H, Schaff WJ: Appl. Phys. Lett.. 2006, 88: 112111. Bibcode number [2006ApPhL..88k2111A] Bibcode number [2006ApPhL..88k2111A] 10.1063/1.2185407
Tsai T-R, Chang C-F, Gwo S: Appl. Phys. Lett.. 2007, 90: 252111. Bibcode number [2007ApPhL..90y2111T] Bibcode number [2007ApPhL..90y2111T] 10.1063/1.2751110
Massalski TB: Binary Alloy Phase Diagrams. ASM International, Bilthoven; 1990.
Simpkins BS, Ericson LM, Stroud RM, Pettigrew KA, Pehrsson PE: J. Cryst. Growth. 2006, 290: 115. COI number [1:CAS:528:DC%2BD28XisFyju78%3D]; Bibcode number [2006JCrGr.290..115S] COI number [1:CAS:528:DC%2BD28XisFyju78%3D]; Bibcode number [2006JCrGr.290..115S] 10.1016/j.jcrysgro.2005.12.095
Grunze M, Golze M, Driscoll RK, Dowben PA: J. Vac. Sci. Technol.. 1981, 18: 611. COI number [1:CAS:528:DyaL3MXksV2qs7k%3D]; Bibcode number [1981JVST...18..611G] COI number [1:CAS:528:DyaL3MXksV2qs7k%3D]; Bibcode number [1981JVST...18..611G] 10.1116/1.570833
Grunze M, Dowben PA, Brundle CR: Surf. Sci.. 1983, 128: 311. COI number [1:CAS:528:DyaL3sXksF2ms74%3D]; Bibcode number [1983SurSc.128..311G] COI number [1:CAS:528:DyaL3sXksF2ms74%3D]; Bibcode number [1983SurSc.128..311G] 10.1016/S0039-6028(83)80034-X
Bassignana IC, Wagemann K, Kueppers J, Ertl G: Surf. Sci.. 1986, 175: 22. COI number [1:CAS:528:DyaL28XlsF2gsLg%3D]; Bibcode number [1986SurSc.175...22B] COI number [1:CAS:528:DyaL28XlsF2gsLg%3D]; Bibcode number [1986SurSc.175...22B] 10.1016/0039-6028(86)90081-6
Chrysostomou D, Flowers J, Zaera F: Surf Sci. 1999, 439: 34. COI number [1:CAS:528:DyaK1MXmslCgsLs%3D]; Bibcode number [1999SurSc.439...34C] COI number [1:CAS:528:DyaK1MXmslCgsLs%3D]; Bibcode number [1999SurSc.439...34C] 10.1016/S0039-6028(99)00458-6
Yina SF, Xub BQ, Zhouc XP, Au CT: Appl. Catal. A Gen.. 2004, 277: 1. 10.1016/j.apcata.2004.09.020
Martensson T, Patrik C, Svensson T, Wacaser BA, Larsson MW, Seifert W, Deppert K, Gustafsson A, Wallenberg LR, Samuelson L: Nano Lett.. 2004, 4: 1987. COI number [1:CAS:528:DC%2BD2cXnsleisbY%3D] COI number [1:CAS:528:DC%2BD2cXnsleisbY%3D] 10.1021/nl0487267
Kim H-M, Kim DS, Park YS, Kim DY, Kang TW, Chung KS: Adv. Mater.. 2004, 14: 991.
Ertekin E, Greaney PA, Chrzan DC, Sands TD: J. Appl. Phys.. 2005, 97: 114325. Bibcode number [2005JAP....97k4325E] Bibcode number [2005JAP....97k4325E] 10.1063/1.1903106
Syrkin A, Usikov A, Soukhoveev V, Kovalenkov O, Ivantsov V, Dmitriev V, Collins C, Readinger E, Shmidt N, Davydov V, Nikishin S, Kuryatkov V, Song D, Rosenbladt D, Holtz M: Phys. Status Solidi. 2006, 3: 1444. COI number [1:CAS:528:DC%2BD28XmvFOrsbY%3D] COI number [1:CAS:528:DC%2BD28XmvFOrsbY%3D] 10.1002/pssc.200565454
Kryliouk O, Park HJ, Won YS, Anderson T, Davydov A, Levin I, Kim JH, Freitas JA: Nanotechnology. 2007, 18: 135606. Bibcode number [2007Nanot..18m5606K] Bibcode number [2007Nanot..18m5606K] 10.1088/0957-4484/18/13/135606
Park HJ, Kryliouk O, Anderson T, Khokhlov D, Burbaev T: Physica E. 2007, 37: 142. COI number [1:CAS:528:DC%2BD2sXjtFKjtbY%3D]; Bibcode number [2007PhyE...37..142P] COI number [1:CAS:528:DC%2BD2sXjtFKjtbY%3D]; Bibcode number [2007PhyE...37..142P] 10.1016/j.physe.2006.06.022
Ohta J, Fujioka H, Honke T, Oshima M: Thin Solid Films. 2004, 457: 109. COI number [1:CAS:528:DC%2BD2cXktVajsrY%3D]; Bibcode number [2004TSF...457..109O] COI number [1:CAS:528:DC%2BD2cXktVajsrY%3D]; Bibcode number [2004TSF...457..109O] 10.1016/j.tsf.2003.12.003
Lua CJ, Duan XF, Lu H, Schaff WJ: J. Mater. Res.. 2006, 21: 1693. Bibcode number [2006JMatR..21.1693L] Bibcode number [2006JMatR..21.1693L] 10.1557/jmr.2006.0215
Acknowledgments
This work was supported by the National Science Foundation through grant # ECS-0322720. I.S. acknowledges a Converging Technologies personal grant from the Israeli Science Foundation - VATAT.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Shalish, I., Seryogin, G., Yi, W. et al. Epitaxial Catalyst-Free Growth of InN Nanorods onc-Plane Sapphire. Nanoscale Res Lett 4, 532 (2009). https://doi.org/10.1007/s11671-009-9276-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11671-009-9276-z