Abstract
Effect of current stressing on whisker growth in Cu/Sn–58Bi/Cu solder joints was investigated with current densities of 5 × 103 and 104 A/cm2 in oven at different temperatures. Two types of whiskers, columnar-type and filament-type, were observed on the solder film propagating along the surface of the Cu substrate and at the cathode interface, respectively, accompanied with many hillocks formation. Typically, these whiskers were 5–15 μm in length and 0.06–2 μm in diameter. EDX revealed that these whiskers and hillocks were mixtures of Sn and Bi rather than single crystal. It should be noted that the sprouted whiskers would not grow any more even if the current-stressing time increased again when the solder joint was stressed under lower current density. Nevertheless, when the current density was up to 104 A/cm2, the whiskers would melt along with the increasing current-stressing time. Results indicated that the compressive stress generated by precipitation of Cu6Sn5 intermetallics provides a driving force for whisker growth on the solder film, and the Joule heating accumulation should be responsible for whisker growth at the cathode interface.
Similar content being viewed by others
References
Nah JW, Paik KW, Suh JO, Tu KN (2003) J Appl Phys 94:7560
Lin YC, Zhong J (2008) J Mater Sci 43(9):3072. doi:https://doi.org/10.1007/s10853-007-2320-4
Lin YH, Hu YC, Tsai CM, Kao CR, Tu KN (2005) Acta Mater 53:2029
Lin YW, Lai YS, Lin YL, Tu C-T, Kao CR (2007) J Electron Mater 37:17
Kakeshita T, Kawanaka R, Hasegawa T (1982) J Mater Sci 17:2560. doi:https://doi.org/10.1007/BF00543888
Lin YW, Lai YS (2008) J Electron Mater 37(1):17
Yuki F, Michael O, Michael P (2007) Microelectron Reliab 47:88
Hu C-C, Tsai Y-D, Lin C-C, Lee G-L, Chen S-W, Lee T-C, Wen T-C (2008) J Alloy Compd 472:121. doi:https://doi.org/10.1016/j.jallcom.2008.04.094
He HW, Xu GC, Guo F (2009) J Mater Sci 44(8):2089. doi:https://doi.org/10.1007/s10853-009-3276-3
Chen C-M, Huang C-C (2008) J Mater Res 23(4):1051
Chen ZG (2002) J Electron Mater 31(10):1122
Chen ZG (2003) Ph.D. Thesis, Beijing University of Technology
Guo F, Xu GC, He HW (2009) J Mater Sci 44(20):5595. doi:https://doi.org/10.1007/s10853-009-3787-y
Hongwen HE, Guangchen XU, Hu HAO et al (2007) ICEPT, Shanghai, China, pp 225–229
Boettinger WJ, Johnson CE, Bendersky LA, Moon KW, Williams ME, Stafford GR (2005) Acta Mater 53:5033
Choi WJ, Lee TY, Tu KN (2003) Acta Mater 51:6253
Tu KN, Chen C, Wu AT (2007) J Mater Sci: Mater Electron 18:269
Jung K, Conrad H (2004) J Mater Sci 39:1803. doi:https://doi.org/10.1023/B:JMSC.0000016189.01285.35
Gu X, Chan YC (2008) J Electron Mater 37:1721
Galyon GT, Palmer L (2005) IEEE Trans Electron Packag Manuf 28(1):17
Ma HT (2009) J Mater Sci 44(14):3841. doi:https://doi.org/10.1007/s10853-009-3521-9
Cheng F, Nishikawa H, Takemoto T (2008) J Mater Sci 43(10):3643. doi:https://doi.org/10.1007/s10853-008-2580-7
Acknowledgements
The authors acknowledge the financial support of this work from the New Century Talent Support Program, Ministry of Education, and the Funding Project PHR (IHLB).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
He, H., Xu, G. & Guo, F. Electromigration-induced Bi-rich whisker growth in Cu/Sn–58Bi/Cu solder joints. J Mater Sci 45, 334–340 (2010). https://doi.org/10.1007/s10853-009-3939-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-009-3939-0