Abstract
L10-ordered FePt/Fe thin bi-layers were grown using a molecular beam epitaxy onto (100)-MgO substrates changing the soft Fe layer thickness. The study of the intermixing phenomena occurring at the hard/soft interfaces was carried out using surface Mössbauer spectroscopy. The magnetic properties of the samples were analyzed with a magneto-optical Kerr effect magnetometer. The surface morphology and the magnetic domains were analyzed with an UHV atomic and magnetic force microscopy in tapping and lift mode respectively.The present work clearly demonstrates that the degree of interface intermixing and reactions is the responsible for the coercivity behavior in exchange-spring magnets.
Similar content being viewed by others
References
Carbucicchio, M., Ciprian, R., Palombarini, G., Magn, J.: Magn. Mater. 322, 1307 (2010)
Kneller, E.F., Hawig, R.: IEEE Trans. Magn. 27, 3588 (1991)
Leineweber, T., Kronmüller, H.: Phys. Status Solidi B 201, 291 (1997)
Casoli, F., Albertini, F., Fabbrici, S., Bocchi, C., Nasi, L., Ciprian, R., Pareti, L.: IEEE Trans. Magn. 41, 3877 (2005)
Carbucicchio, M., Ciprian, R.: Solid State Commun. 152, 189 (2012)
Christodoulides, J.A., Bonder, M.J., Huang, Y., Stoyanov, S., Hadjipanayis, G.C., Simopoulos, A., Weller, D.: Phys. Rev. B 68, 054428–1–7 (2003)
Tilbrook, M.: Mössbauer and Magnetisation Measurements of FePt Nanoparticles for Magnetic Recording Media. Department of Physics, Thesis University of Western Australia (2000)
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is part of the Topical Collection on Proceedings of the International Symposium on the Industrial Applications of the Mössbauer Effect (ISIAME 2016), Cape Town, South-Africa, 4-8 September 2016
Edited by Frans Waanders
Rights and permissions
About this article
Cite this article
Carbucicchio, M. Influence of the phenomena occurring at the interface between L10-ordered-FePt and Fe on the coercivity behavior. Hyperfine Interact 237, 153 (2016). https://doi.org/10.1007/s10751-016-1366-6
Published:
DOI: https://doi.org/10.1007/s10751-016-1366-6