Magneto-crystalline properties of BaFe_12−2x M _x Sn _x O₁₉ (M = Sn, Ni, Zn) ferrite powders

Abstract

BaFe_12−2x M _x Sn _x O₁₉ compounds, where M = Sn²⁺, Ni²⁺ or Zn²⁺ ions, were synthesized by mechanical milling and partially by citrate precursor methods. Analysis of magneto-crystalline structure has been carried out by Mössbauer spectroscopy. The Sn⁴⁺ ions replace Fe³⁺ ions on 2b and slightly on 2a + 4f₁ sites, Zn²⁺ ions strongly prefer 4f₁ sites, Sn²⁺ ions prefer 4f₁ sites too and Ni²⁺ ions occupy 4f₂ and 12k or 2a sites. The magnetic properties were evaluated by the vibrating sample magnetometry and the thermomagnetic analysis. A large variation of the intrinsic coercivity H _c (330 to 78 kA/m) and of temperature coefficient of coercivity of ΔH _c /Δϑ (0.39 to 0.22 kA/m°C) were achieved as a function of the (Zn–Sn) and (Sn–Sn) substitutions, respectively. The Curie temperature T _c decreased with the (Ni–Sn) substitution from 447 to 399°C.