Abstract
Herein, kinetic modelling and kinetic parameters were used to study methanol dehydration to dimethyl ether reaction and revealed that the best model to fit the experimental data was the Bercic model. The dehydration reaction undergoes dissociative adsorption Langmuir–Hinshelwood mechanism of methanol on the alumina catalyst surface, with the calculated value of the activation energy was 136.7 kJ mol−1. Moreover, the effect of different kinetic parameters such as the catalyst weight and methanol concentration or water in the feed on the catalytic performance of η-Al2O3 was examined in a fixed bed reactor under the reaction conditions where the temperature ranged from 180 to 350 °C with a WHSV = 12.1 h−1.
Graphical Abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Energy consumption throughout the world has been continuously increased especially for industrialized cities. The carbon-based non-renewable sources, mainly crude oil, are unsustainable because of the production of the significant amount of greenhouse gases in which is the main cause of the global warming. To meet the energy demand and decrease the air pollution an alternative renewable energy should be developed. The production of clean biofuel such as dimethyl ether (DME) is an attractive alternative for pollution mitigation. DME is an environmentally friendly fuel with clean-burning and smoke-free emissions [1]. The attractive combustion properties are due to it containing neither sulphur nor nitrogen, with very low SOx or NOx emissions. The lack of direct carbon-to-carbon bonds means it does not generate particulate matter emissions. DME can be produced by two main routes; either from syngas using a bi-functional catalyst (Eq. 1) or via the dehydration of methanol over solid catalysts such as Al2O3 (Eq. 2), according to the following reactions [1,2,3,4,5,6]:
The synthesis of efficient and commercially attractive, robust catalysts has become increasingly challenging due to the both increased demand for DME production and the catalytic process required for methanol to DME process (MTD). Alumina is a cost-efficient material that can be tailored to unique textural properties including high surface area and high porosity. Moreover, alumina can be used as a catalyst support in different oxidation reactions [7, 8]. Therefore, optimizing Al2O3 as a catalyst or a support for such processes remains a topic of great importance [9]. Extensive studies were performed on γ-Al2O3 for MTD reaction. In our previous publication [10]; we showed that γ-Al2O3 and η-Al2O3 catalysts can be prepared from different precursors of aluminium chloride and nitrates, respectively. The produced catalysts showed different surface morphology and acidity with η-Al2O3 showed similar surface characteristics of the commercial zeolite [HZSM-5(80)]. Moreover, η-Al2O3 showed higher catalytic activity during the MTD process than that of the commercial zeolite at reaction temperatures above 275 °C. Thus, η-Al2O3 is considered as a promising catalyst for the commercial production of DME from methanol. Accordingly, kinetic investigation of η-Al2O3 catalyst for the MTD process is needed. To the extent of the authors’ knowledge, there has been no detailed kinetic study of η-Al2O3 in MTD reaction along with studying the surface hydrophilicity and acidity, therefore, this area requires further examination.
The dehydration reaction occurs over a solid acid catalyst where its acidity plays a big role in the product distribution. Over very strong acidic sites, further dehydration will take place producing olefins. In order to suppress the dehydration to olefins reaction and increase the selectivity towards the DME, weak or moderate acidity catalysts are desirable as in the Al2O3. Methanol dehydration is known to take place on Lewis acid-pair sites and its rate increases as the surface Lewis acidity increases [11]. It was well reported that γ-Al2O3, a typical Lewis acid catalyst and also the η-Al2O3 used in the study, can catalyse dehydration of MTD [10]. Several reaction mechanisms have been presented for methanol dehydration on acid catalysts [11, 12]. Either Brønsted acid sites or Lewis acid–base pair sites are believed to play a role in such reaction and, generally, the stronger the acid sites the more active the catalysts, however, it should be remembered that as far as Brønsted sites are concerned, their strength and the reaction temperature should be controlled to avoid hydrocarbons formations [10]. The mechanism based on the Lewis acidity, on the other hand, requires adjacent acid–base pair sites to provide the reaction between the adsorbed alcohol molecule on an acidic site and an adsorbed alkoxide anion on a basic site [11].
The above discussion highlights the importance of studying the reaction kinetics of methanol dehydration over η-Al2O3 catalyst along with studying the different kinetic parameters. Herein, we studied the effect of different operating conditions such as the effect of catalyst weight, % methanol concentration and % water in the reaction feed along the fitted kinetic modelling and correlate the results with the surface hydrophilicity and morphology of η-Al2O3 during the MTD reaction.
2 Experimental
2.1 Materials and Methods
The chemicals used in the present study were all of analytical grade and supplied by Aldrich, UK. The chemicals included aluminium nitrate nonahydrate [Al(NO3)3⋅9H2O] and ammonia solution (35%). The He and air gases were purchased from BOC with purity 99.99%.
2.2 Catalyst Preparation
The preparation of alumina has been described elsewhere [10]. It was prepared from aluminium nitrate nonahydrate that was then precipitated by ammonia solution giving a precipitate which dried at 120 °C and designated as AN120, followed by calcination at 550 °C and designated as η-Al2O3.
2.3 Catalyst Characterisation
Powder X-ray diffraction (XRD) was carried out using a PANalytical X’Pert Pro X-ray diffractometer. This diffractometer was equipped with a Cu Kα X-ray source with a wavelength of 1.5405 Å. The diffractograms were collected up to 2θ = 80°. The X-ray tube was set at 40 kV and 40 mA. Peaks were selected and compared to diffraction patterns in the software library.
Brunauer–Emmett–Teller (BET) analysis was performed using a Micromeritics ASAP 2020 system. BET surface area and pore volume were measured by N2 adsorption and desorption isotherms at liquid nitrogen temperature (− 196 °C).
TPD-pyridine was used to determine the total surface acidity of the catalyst using the adsorption of pyridine as a probe molecule. Small portions (50 mg) of each sample were pre-heated to 250 °C for 2 h in the air before exposure to the probe molecule (pyridine) in a sealed desiccator for 2 weeks. The pyridine-covered samples were subjected to thermogravimetric or differential scanning calorimetry (DSC) analyses on heating up to 600 °C at a heating rate of 10°C min−1 in dry N2 (flow rate = 40 ml min− ). The weight loss due to desorption of pyridine from the acidic sites was determined as a function of total surface acidity as sites \({\text{g}}_{{{\text{cat}}}}^{{ - 1}}\) [10].
Scanning electron microscopy (SEM) was carried out on a FEI Quanta 250 FEG MKII with a high-resolution environmental microscope (ESEM) using XT Microscope Control software and linked to an EDX detector. The EDX used was a 10 mm2 SDD Detector-x-act from Oxford Instruments which utilizes Aztec® EDS analysis software. Both systems used the same chamber.
The static contact angle (CA) of the catalyst pellets with water was measured in order to determine the hydrophilicity of the alumina using a CA meter equipped with a CCD camera (FTA1000 Drop Shape Instrument-B Frame system).
2.4 Catalyst Activity
Catalyst activity tests were conducted in an isothermal fixed-bed reactor made of stainless steel (6 mm OD). The catalyst bed consisted of 50–200 mg (250–425 µm) of a catalyst placed between two plugs of quartz wool. Aera mass flow controllers were used to control the flow of gases to the reactor. The liquid methanol and/or water were injected via a Cheminert® M Series liquid handling pump. A stable flow of methanol vapour to the reactor was established by passing the combined flow of He and methanol through a saturator system, with the evaporation chamber maintained at 150 °C. To prevent condensation, all lines were heated to ~ 150 °C. This mixture was then fed to the fixed bed reactor. The reaction conditions used were different % MeOH in the kinetic experiments under atmospheric pressure over a temperature range from 180 to 350 °C. The total flow rate was 100 cm3 min−1. Before the reaction, the catalyst was activated in a stream of pure He at 325 °C for 0.5 h under atmospheric pressure stream at a total flow rate of 50 cm3 min−1. Then, the methanol and He mixture were fed to the reactor and samples analysed by on-line gas chromatography (Perkin-Elmer 500) equipped with a thermal conductivity detector and a flame ionisation detector. A Hayesep DB column was used for the separation of CO, CO2, DME, MeOH, CH4, C2H4, C2H6, ethanol, propanol, and butanol. Each data point was repeated five times to determine the reproducibility of the data for the products.
As shown in Eq. 3, the methanol conversion (XMeOH) was calculated on the basis of the molar flow rate of methanol in the feed (FMeOH,in) and in the outlet stream (FMeOH,out):
DME formation rate (rDME) was determined using Eq. 4, which represents the actual moles of the product, DME, that are present in the reactor outlet stream per gram of the catalyst:
The selectivity for DME (SDME) was determined using Eq. 5 as the ratio (expressed in mol%) between the content of carbon in the product DME and the sum of carbon content corresponding to all observed organic products which are present in the reactor outlet stream:
Here, FDME, \({F_{{\text{C}}{{\text{O}}_2}}}\) and FCO are the molar flow rates of DME, CO2 and CO, respectively in the outlet stream, n Ci is the number of carbon atoms for each of the hydrocarbons (byproducts) and F i is the molar flow rate of these hydrocarbons [13].
3 Results and Discussion
3.1 Catalyst Characterisation
Figure 1 shows the XRD diffractograms of Al(NO3)3⋅9H2O (precursor), AN120 (as-dried precipitate) and η-Al2O3. The precipitation of aluminium nitrate nonahydrate produced AN120 which showed a mixture of diffractograms of Bayerite (JCPDS 20-11) and Gibbsite (JCPDS 33-18) as shown in diffractograms (b). Interestingly, among all Al(OH)3 structures, Bayerite has the highest symmetry and thermodynamically is the most stable phase and characterised by its crystalline phase [14, 15]. η-Al2O3 diffraction lines (JCDD 04-0875) are shown in diffractograms (c) as a result of the thermal decomposition of Bayerite and Gibbsite at 550 °C.
The pyridine-DSC analysis was used to investigate the surface acidity of the η-Al2O3 catalyst as shown in Fig. 2a which showed mainly two endothermic peaks. The first broad endothermic peak at 80 °C is attributed to the removal of physisorbed water and pyridine along with pyridine desorption from the weak Lewis acidic sites. The small sharp endothermic peak at 235 °C is characterised to the removal of pyridine from moderate Lewis acidic sites [16]. Alumina catalyst, in general, is characterised by its weak acidic sites. From a previous work, η-Al2O3 catalyst showed mainly Lewis acidic sites, thus the DSC results confirmed the presence of weak and medium Lewis acidic sites over the surface of η-Al2O3 catalyst [10].
The surface hydrophilicity was determined according to the water CA as seen in Fig. 2b. The wettability of the catalyst surface, demonstrated by CA (θ) of a droplet of water, is assumed by Young’s equation (Eq. 6)
where \({\gamma }_{\text{SV}}\), \({\gamma }_{\text{SL}}\) and \({\gamma }_{\text{LV}}\) stand for the interfacial surface tension of solid (S), liquid (L) and gas vapour (V). This equation is derived from the thermodynamic equilibrium of the free energy at the S–L–V interphase. The surface wettability is measured according to the CA and may be divided into four different categories; super-hydrophilic (θ < 10°), hydrophilic (10 < θ < 90°), hydrophobic (90 < θ < 150°) and super-hydrophobic (θ > 150°). It is well known that pure alumina in general and η-Al2O3 specifically is super-hydrophilic with CA approximately θ = 1.7° as seen in Fig. 2b.
The surface morphology of η-Al2O3 was investigated using SEM technique which showed a smaller particle size distribution as shown in Fig. 3. XRD analysis calculation using Scherrer equation showed a crystallite size of 5.5 nm as shown in Table S1. The nitrogen adsorption–desorption isotherms of η-Al2O3 catalyst showed type IV isotherm of mesoporous structures as shown in Fig. S1 with a surface area of 223 m2 g−1.
3.2 Kinetic Study of Pure Alumina
3.2.1 Effect of Different Kinetic Parameters
3.2.1.1 Effect of Catalyst Weight
The % methanol conversion was significantly increased with increasing the catalyst weight as seen in Fig. 4. In general, by increasing the catalyst weight from 50 to 200 mg at reaction temperature of 250 °C, the % methanol conversion increased four times. It is apparent that with low catalyst weight in the reactor, i.e., 50 mg, it was insufficient catalyst to facilitate the dehydration reaction below 200 °C with T50% of 275 °C. However, by increasing the catalyst weight to 200 mg, an increase in methanol conversion was observed as there are more active acidic sites species present to facilitate the MTD reaction with T50% of 222 °C.
3.2.1.2 Effect of Methanol Concentration
Figure 5 clearly shows that, in general, the % methanol conversion is inversely proportional to the % concentration of methanol in the reaction feed. The inhibition effect is minor at reaction temperature above 300 °C. In contrast, the inhibition effect of methanol concentrations at reaction temperature below 275 °C is obvious; for instance, at reaction temperature of 250 °C, the % conversion decreased by 20% upon increasing the % methanol concentration from 20 to 75% in the reaction feed. This inhibition effect is due to the crowded alcohol molecules, over the surface active sites, which retard the dehydration of CH3OH to produce DME. This is, consequently, reflected on the values of % conversion, where its values gradually reduced with increasing the alcohol concentration in the reaction feed.
3.2.1.3 Effect of Water in the Feed
Figure 6 shows the inhibition effect of water on the MTD process. During the methanol dehydration reaction, water is produced which also has a significant effect on catalyst deactivation [17,18,19,20] as η-Al2O3 is super-hydrophilic [21], and facilitates strong water adsorption. Both water and methanol compete for adsorbing on the active sites of η-Al2O3 with water being adsorbed more strongly [17]. Osman et al. [5] showed that is possible to increase the hydrophobicity of the support thereby reducing the deactivation by water. The catalytic activity dramatically decreased by five times upon adding of 5% water in the reaction feed at a reaction temperature of 250 °C and then slightly decreased by adding further water in the reaction feed (15%). The water inhibition effect is insignificant at a reaction temperature above 300 °C as the water adsorption on the active alumina site is not that strong.
Development of new and cheap catalysts for MTD process on a large scale is of great interest. Usually, methanol is converted over solid catalyst either as simply dehydration, yielding DME and water, or as deep dehydration, producing hydrocarbons [22]. At the reaction conditions used [240–300 °C]; hydrocarbons products were hardly detected as a side reaction product [10]. The kinetics of methanol dehydration on acidic catalysts has been studied extensively resulting in different kinetics equations. A list of kinetic models for MTD is given in Table 1 [23].
It is evident that some of the rate equations for dehydration where the reaction rate are proportional to the square root of the methanol concentration. This indicates that the MTD reaction undergoes dissociative adsorption of methanol on the catalyst surface [27].
It is stated in Froment and Bischoff [30] that the reaction rate for surface catalysed reactions with a mechanism is based on chemisorption and a single rate-determining step, which can be written as a combination of three groups. These are a kinetic group, a driving-force group, and an adsorption group. The rate is thus expressed as
where \(\text{kinetic factor}=k\), the Arrhenius equation is used to describe the variation of the rate constant with temperature
\({\text{driving}}\;{\text{force}}\;{\text{group}}=\Phi \left( {P,\;y_{j}^{0},\;{X_{{\text{CO}}}},\;{K_P}} \right)\)
\({K}_{P}\) is the equilibrium constant for MTD reaction (Eq. 2):
\({({\text{adsorption}}\;{\text{group}})^{\text{n}}}=~\Phi {\left( {P,\;y_{j}^{0},\;{X_{{\text{CO}}}},\;{K_{j,a}}} \right)^n},\) where \({K}_{j,a}\) is the adsorption equilibrium constants defined by the van’t Hoff equation
The kinetic data were obtained in an integral reactor where the methanol conversions greater than 10% are produced. For an integral plug-flow reactor, the reaction rate is calculated as:
The integration of the rate equation over the reactor bed leads to:
Here, the methanol conversion for Eq. 12 was performed by applying numerical integration using fourth order Runge–Kutta method, the MATLAB subroutine function ODE15s.
The parameter estimation was based on minimization of the objective function using the sum of residual squares:
where n is the total number of experiments, \(X\) is the experimental methanol conversion, and \(\widehat{X}\) is the calculated methanol conversion.
3.2.2 Validation of the Kinetic Model
To determine the validity of the model, we applied F test (Eq. 14) and R2 a coefficient of determination (Eq. 15). It is stated that if \({R}^{2}\) > 0.9 and F > 10 ×F0.05, we can say that the model is reliable.
where n is number of the experiments, p a is number of parameters in the equation of model, and \(1-\alpha\) is the confidence level. If the calculated F value is higher than the tabulated ones, the regression is statistically meaningful. The highest calculated F value corresponds to the model that best fits the experimental data.
Statics results and values of activation energy and heat of adsorption of methanol and water for the fitted proposed models are tabulated in Table 2. It is clear that from the statistics values that the best model to fit the experimental data is Bercic model that the dehydration reaction undergoes dissociative adsorption Langmuir–Hinshelwood mechanism of methanol on the catalyst surface. The calculated value of the activation energy is 136.7 kJ mol−1 which is in agreement with the one estimated by Bercic and Levec [27] (143.7 kJ mol−1). For the heat of adsorption of methanol and water are 68.7 and 44.3 kJ mol−1, respectively, which are comparable with the values by Bercic and Levec [27] 70.5 and 41.1, respectively. Lu et al. [28] developed a detailed intrinsic mechanism containing seven elementary reactions, where Mollavali et al. [29] used Lu’s mechanism with different limiting step to derive kinetic global reaction equation.
The above values of heat of adsorption of water and methanol confirm that the inhibition effect of water is greater than that of methanol. For instance, at a reaction temperature of 250 °C, when water introduced in the reaction feed to the value of 5%, the % methanol conversion dramatically decreased by 63% from the initial conversion of the dry feed as seen in Fig. 6. On the other hand, by doubling the methanol concentration in the reaction feed from 20 to 40%, the methanol conversion slightly decreased by 5.4% as seen in Fig. 5. Moreover, the inhibition effect for both water and methanol decreased with increasing the reaction temperature, for instance in the case of water when the reaction temperature increased from 250 to 350 °C for 5% water in the feed, the % methanol conversion increased from 16 to 72%, respectively. In other words, at a reaction temperature of 350 °C, the % conversion of methanol for 5% water in the feed decreased by only 15% from the initial conversion of the dry feed. This can be explained by Eq. 10, as the reaction temperature increased, the desorption equilibrium value of water increased which means that water will be easily desorbed from the surface of the alumina catalyst at high reaction temperature, thus the inhibition effect of either water or methanol will be of minor significance at high reaction temperature. The fitted kinetic modelling results are in agreement with the surface morphology of η-Al2O3 which explained the strong water inhabitation effect that comes from the super-hydrophilicity nature of η-Al2O3 with CA approximately θ = 1.7° as seen in Fig. 2b which is in agreement with the kinetic model shown in Table 2. Moreover, during the reaction mechanism, water is produced which has a significant effect on the alumina catalyst deactivation, as water and methanol compete for adsorbing on the active sites of alumina catalyst with water being adsorbed more strongly [31]. It is worth noting that in our previous publication we showed that the prepared η-Al2O3 has similar morphology and surface acidity of zeolite [HZSM-5(80)] which is in line with the fitted kinetic modelling as our work matched with Lu model who studied the kinetic modelling of zeolite as shown in Table 2 [10].
The simulation and experimental results are given in the parity plot of Fig. 7, which compares the experimental conversions of methanol with those predicted by solving Bercic model and revealed that from the statistics values that the best model to fit the experimental data was Bercic model.
4 Conclusions
Kinetic modeling studies were used to investigate the reaction mechanism of methanol dehydration over the pure η-Al2O3 catalyst and revealed that from the statistics values that the best model to fit the experimental data was Bercic model which was in agreement with literature that the dehydration reaction undergoes dissociative adsorption Langmuir–Hinshelwood mechanism of methanol on the catalyst surface. The calculated value of the activation energy is 136.7 kJ mol− 1, where, the heat of adsorption of methanol and water are 68.7 and 44.3 kJ mol− 1, respectively. The % methanol conversion was significantly increased with increasing the catalyst weight, while it was dramatically decreased with increasing either the % methanol or water in the reaction feed at the low reaction temperature (< 250 °C).
References
Khoshbin R, Haghighi M (2014) Direct conversion of syngas to dimethyl ether as a green fuel over ultrasound-assisted synthesized CuO–ZnO–Al2O3/HZSM-5 nanocatalyst: effect of active phase ratio on physicochemical and catalytic properties at different process conditions. Catal Sci Technol 4(6):1779–1792
Figoli NS, Hillar SA, Parera JM (1971) Poisoning and nature of alumina surface in the dehydration of methanol. J Catal 20(2):230–237
Asthana S, Samanta C, Bhaumik A, Banerjee B, Voolapalli RK, Saha B (2016) Direct synthesis of dimethyl ether from syngas over Cu-based catalysts: enhanced selectivity in the presence of MgO. J Catal 334:89–101
Cai M, Palčić A, Subramanian V, Moldovan S, Ersen O, Valtchev V et al (2016) Direct dimethyl ether synthesis from syngas on copper–zeolite hybrid catalysts with a wide range of zeolite particle sizes. J Catal 338:227–238
Osman AI, Abu-Dahrieh JK, McLaren M, Laffir F, Nockemann P, Rooney D (2017) A facile green synthetic route for the preparation of highly active γ-Al2O3 from aluminum foil waste. Sci Rep 7(1):3593
Osman AI, Abu-Dahrieh JK, Abdelkader A, Hassan NM, Laffir F, McLaren M et al (2017) Silver-modified η-Al2O3 catalyst for DME production. J Phys Chem C 121(45):25018–25032
Osman AI, Meudal J, Laffir F, Thompson J, Rooney D (2017) Enhanced catalytic activity of Ni on η-Al2O3 and ZSM-5 on addition of ceria zirconia for the partial oxidation of methane. Appl Catal B 212:68–79
Osman AI, Abu-Dahrieh JK, Laffir F, Curtin T, Thompson JM, Rooney DW (2016) A bimetallic catalyst on a dual component support for low temperature total methane oxidation. Appl Catal B 187:408–418
Royaee SJ, Falamaki C, Sohrabi M, Talesh ASS (2008) A new Langmuir–Hinshelwood mechanism for the methanol to dimethylether dehydration reaction over clinoptilolite–zeolite catalyst. Appl Catal A 338(1–2):114–120
Osman AI, Abu-Dahrieh JK, Rooney DW, Halawy SA, Mohamed MA, Abdelkader A (2012) Effect of precursor on the performance of alumina for the dehydration of methanol to dimethyl ether. Appl Catal B 127:307–315
Hosseininejad S, Afacan A, Hayes RE (2012) Catalytic and kinetic study of methanol dehydration to dimethyl ether. Chem Eng Res Des 90(6):825–833
Akarmazyan SS, Panagiotopoulou P, Kambolis A, Papadopoulou C, Kondarides DI (2014) Methanol dehydration to dimethylether over Al2O3 catalysts. Appl Catal B 145:136–148
Abu-Dahrieh J, Rooney D, Goguet A, Saih Y (2012) Activity and deactivation studies for direct dimethyl ether synthesis using CuO–ZnO–Al2O3 with NH4ZSM-5, HZSM-5 or γ-Al2O3. Chem Eng J 203(0):201–211
Jiao WQ, Yue MB, Wang YM, He MY (2012) Synthesis of morphology-controlled mesoporous transition aluminas derived from the decomposition of alumina hydrates. Microporous Mesoporous Mater 147(1):167–177
Wefers K, Misra C (1987) Oxides and hydroxides of aluminum. Alcoa Technical Paper No. 19, revised
Dumitriu E, Hulea V (2003) Effects of channel structures and acid properties of large-pore zeolites in the liquid-phase tert-butylation of phenol. J Catal 218(2):249–257
Alamolhoda S, Kazemeini M, Zaherian A, Zakerinasab MR (2012) Reaction kinetics determination and neural networks modeling of methanol dehydration over nano γ-Al2O3 catalyst. J Ind Eng Chem 18:2059–2068
Xu M, Lunsford JH, Goodman DW, Bhattacharyya A (1997) Synthesis of dimethyl ether (DME) from methanol over solid-acid catalysts. Appl Catal A 149(2):289–301
Lertjiamratn K, Praserthdam P, Arai M, Panpranot J (2010) Modification of acid properties and catalytic properties of AlPO4 by hydrothermal pretreatment for methanol dehydration to dimethyl ether. Appl Catal A 378(1):119–123
Raoof F, Taghizadeh M, Eliassi A, Yaripour F (2008) Effects of temperature and feed composition on catalytic dehydration of methanol to dimethyl ether over alumina. Fuel 87(13–14):2967–2971
Kim SD, Baek SC, Lee Y-J, Jun K-W, Kim MJ, Yoo IS (2006) Effect of γ-alumina content on catalytic performance of modified ZSM-5 for dehydration of crude methanol to dimethyl ether. Appl Catal A 309(1):139–143
Ladera RM, Ojeda M, Fierro JLG, Rojas S (2015) TiO2-supported heteropoly acid catalysts for dehydration of methanol to dimethyl ether: relevance of dispersion and support interaction. Catal Sci Technol 5(1):484–491
Zhang L, Zhang H-T, Ying W-Y, Fang D-Y (2011) Intrinsic kinetics of methanol dehydration over Al2O3 catalyst. World Acad Sci Eng Technol 59:1538–1543
Kallo D, Knozinger H (1967) Dehydratisierung von alkoholen an aliminiumoksid. Chem Ing Tech 39:676–680
Figueras F, Nohl A, Mourgues L, Trambouze Y (1971) Dehydration of methanol and tert-butyl alcohol on silica-alumina. Trans Faraday Soc 67:1155–1163
Klusacek K, Schneider P (1982) Stationary catalytic kinetics via surface concentrations from transient data methanol dehydration. Chem Eng Sci 37:1523–1528
Bercic G, Levec J (1992) Intrinsic and global reaction rate of methanol dehydration over gamma-alumina pellets. Ind Eng Chem Res 31(4):1035–1040
Lu W-Z, Teng L-H, Xiao W-D (2004) Simulation and experiment study of dimethyl ether synthesis from syngas in a fluidized-bed reactor. Chem Eng Sci 59(22–23):5455–5464
Mollavali M, Yaripour F, Atashi H, Sahebdelfar S (2008) Intrinsic kinetics study of dimethyl ether synthesis from methanol on γ-Al2O3 catalysts. Ind Eng Chem Res 47(9):3265–3273
Hofmann H (1991) In: Von Froment GF, Bischoff KB (eds) Chemical reactor analysis and design. Wiley, New York 1990. 2. Aufl., XXXIV, 664 S., zahlr. Abb. u. Tab., Ln. Chem Ing Tech 63(2):103–103
Osman AI, Abu-Dahrieh JK, Rooney DW, Thompson J, Halawy SA, Mohamed MA (2017) Surface hydrophobicity and acidity effect on alumina catalyst in catalytic methanol dehydration reaction. J Chem Technol Biotechnol 92(12):2952–2962
Acknowledgements
The authors would like to acknowledge the support given to AO from South Valley University in Egypt and all the support given by Professor David Rooney at the School of Chemistry and Chemical Engineering, Queen’s University Belfast.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no conflict of interest.
Electronic Supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Osman, A.I., Abu-Dahrieh, J.K. Kinetic Investigation of η-Al2O3 Catalyst for Dimethyl Ether Production. Catal Lett 148, 1236–1245 (2018). https://doi.org/10.1007/s10562-018-2319-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-018-2319-2