Abstract
The sustained transportation of particles in a suspension commonly results in particle attrition leading to grain size reduction and shape modification. Particle attrition is a well-studied phenomenon that has mainly focussed on sediments produced in aeolian or fluvial environments. Here, we present analogue experiments designed to explore processes of attrition in the kimberlite system; we focus on olivine as it is the most abundant constituent of kimberlite. The attrition experiments on olivine use separate experimental set-ups to approximate two natural environments relevant to kimberlites. Tumbling mill experiments feature a low energy system supporting near continual particle-particle contact and are relevant to re-sedimentation and dispersal processes. Experiments performed in a fluidized particle bed constitute a substantially higher energy environment pertinent to kimberlite ascent and eruption. The run-products of each experiment are analysed for grain size reduction and shape modification and these data are used to elucidate the rates and extents of olivine attrition as a function of time and energy. Lastly, we model the two experimental datasets with an empirical rate equation that describes the production of daughter products (fines) with time. Both datasets approach a fines production limit, or plateau, at long particle residence times; the fluidized system is much more efficient producing a substantially higher fines content and reaches the plateau faster. Our experimental results and models provide a way to forensically examine a wide range of processes relevant to kimberlite on the basis of olivine size and shape properties.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Attrition, driven by particle-particle interactions, results in the size reduction and shape modification of particles and operates in a wide variety of geological environments. From the Engineering Sciences, we identify two modes of attrition that can operate within a gas/liquid suspension (Bemrose and Bridgwater 1987; Xiao et al. 2014; Jones et al. 2017): (1) fragmentation and (2) abrasion. Fragmentation involves complete fracturing of the original particles (i.e. parent particles) to form a group of smaller, daughter particles. ‘Critical’ collisions causing fragmentation typically occur through direct high-energy impact with other particles or with a hard surface at, or above, a threshold velocity (e.g. Dufek et al. 2012). Abrasion is a less energetic process wherein the rough edges or asperities of the parent (and daughter) particles are rounded off to produce particles with smoother surfaces and morphologies. A consequence of abrasion processes is parent grain size reduction by the production of very fine particles, often measuring ≤10 μm.
There are several factors that control the rates of attrition and they can be broadly divided into two groups: particle properties and environmental factors (Bemrose and Bridgwater 1987). Particle properties include, but are not limited to size, shape, surface texture, size distribution, hardness, and the presence (or absence) of internal defects. Environmental factors affecting rates of attrition include particle residence times, particle concentrations, temperature, pressure, and differential velocities between colliding particles or between particles and a confining wall. Attrition is most successful when differential velocities are high, particle concentrations are high, parent particle shapes are irregular, residence times are long and particle size distributions are poorly sorted (e.g. Forsythe and Hertwig 1949; Bemrose and Bridgwater 1987; Ray et al. 1987; Xiao et al. 2011; Knight et al. 2014; Xiao et al. 2014; Jones et al. 2017).
Particle attrition affecting kimberlitic minerals operates in several different environments between the lithospheric mantle and the site of kimberlite extraction on the Earth’s surface (Fig. 1). Mantle-derived olivine is the dominant constituent of kimberlite (Mitchell 1986; Mitchell 1995) and commonly shows strong evidence for reshaping during transport, eruption and re-sedimentation (Reid et al. 1975; McCandless 1990; Arndt et al. 2006; Afanas’ev et al. 2008; Holden et al. 2009; Jerram et al. 2009; Arndt et al. 2010; Moss et al. 2010; Moss and Russell 2011; Jones et al. 2014; Brett et al. 2015). On that basis, our study focusses on olivine attrition. Olivine has poor cleavage and often displays brittle conchoidal fracture. Attrition of olivine occurs in many parts of the “kimberlite system” (Fig. 1) and has import for (1) tracing of indicator minerals in reworked and transported kimberlite materials, (2) interpretation of volcaniclastic deposits of kimberlite based on grain size and shape analysis, (3) understanding diamond grade distributions in volcaniclastic kimberlite deposits (Harvey et al. 2013), and (4) establishing the conditions (transport regime and duration) attending kimberlite transport during ascent through the lithosphere.
The ascent of kimberlite magma is considered to be fast relative to most other terrestrial magmas with estimates varying between ~1 to 10’s m s−1, corresponding to total average transit times of <10 h to ~2 days (McGetchin et al. 1973; Eggler 1989; Sparks et al. 2006; Wilson and Head 2007). There is strong evidence and general acceptance that the buoyancy supporting rapid ascent derives from the presence of an exsolved fluid (e.g. Russell et al. 2012; Sparks 2013; Stone and Luth 2016). The exsolution of a low-density volatile phase reduces the magma’s bulk density, provides buoyancy, and promotes accelerated ascent creating fast-moving, potentially-turbulent, suspensions of melt, fluid and mantle cargo (e.g. Sparks et al. 2006; Wilson and Head 2007; Arndt et al. 2010; Russell et al. 2012). As advanced by Jones et al. (2014) and Brett et al. (2015), this environment, attending the transport of kimberlite magma, is ideal for efficient attrition of the abundant mineral grains liberated by mantle xenolith breakup. They suggested that the rounded shapes and abraded surfaces of mantle-derived xenocrystic minerals are a strong indicator of turbulent ascent of kimberlite magmas through the lithospheric mantle and within subsurface feeder dykes. However, the exact depths at which CO2 saturation occurs in the mantle lithosphere remains a matter of debate and is highly dependent on many intrinsic variables such as the melt composition, temperature and original CO2 content (e.g. Eggler 1989; Wilson and Head 2007; Russell et al. 2012; Brett et al. 2015; Stone and Luth 2016; Stamm and Schmidt 2017).
Rapid turbulent transport of kimberlite through the mantle lithosphere represents an important environment for physical modification of xenocryst shapes, sizes and surfaces. However, xenocryst properties will continue to be modified during emplacement and eruption and during and after kimberlite deposition. Pipe forming and pipe filling phases of eruption produce a wide range of volcaniclastic lithofacies including primary pyroclastic vent-proximal deposits to significantly reworked kimberlite-rich sediments (e.g. Stiefenhofer and Farrow 2004; Brown et al. 2009; Porritt and Cas 2009; Buse et al. 2011; Porritt and Cas 2011; Sparks 2013).
The explosive phase of kimberlite eruption can result in olivine fragmentation and, in fact, the shapes of olivine (e.g. fractured) can be critical elements to identifying pyroclastic deposits (Moss et al. 2008; Buse et al. 2011; van Straaten et al. 2011). High energy explosive eruption environments occur during: i) the onset of the eruption (e.g., brecciation of near-surface crustal rock), ii) the pipe excavation phase of eruption (e.g. Brown et al. 2008; Barnett 2008), iii) rapid decompression and continued volatile expansion in the conduit (e.g., sustained eruption), iv) the generation of dilute surge currents (e.g., phreatomagmatic explosive events; Porritt et al. 2013), and v) during the fluidization of pyroclastic infill (e.g., massive volcaniclastic kimberlite) (Sparks et al. 2006; Walters et al. 2006; Gernon et al. 2009b). Volatile expansion in the conduit creates a rapidly rising, turbulent, fluid-particle suspension that supports entrainment of juvenile pyroclasts, mantle crystal cargo and accessory lithic fragments into the eruption plume. This represents another, environment for particle attrition (Dufek et al. 2012; Jones and Russell 2017). More importantly, collapse of the eruption plume can generate pyroclastic density currents and/or surges (Moss et al. 2008; Porritt et al. 2008; Gernon et al. 2009a; Porritt and Cas 2011; Sparks 2013) which are high-energy environments capable of particle reshaping and resizing. Previous studies of attrition processes in silicic pyroclastic density currents (PDCs) have documented the effects of attrition on pumice during transport (Manga et al. 2011; Kueppers et al. 2012), and the abrasive stripping of glass from crystal surfaces (Meyer 1971; Jones et al. 2016). Logically, these studies have shown attrition rate to decrease with distance from the vent, reflecting the dissipation of energy with transport distance (Dufek and Manga 2008).
Kimberlite deposits and the components within the deposits are all susceptible to post-eruption processes (e.g. re-sedimentation). Attrition of kimberlite indicator minerals during transport within glacial and fluvial systems is of interest to diamond exploration because of its capacity to inform on distances to the source kimberlite pipe (McCandless 1990; Afanas’ev et al. 2008; Afanasiev et al. 2011; Afanasiev and Pokhilenko 2013). Several experimental studies have established the relative attrition susceptibility of different kimberlite indicator minerals (e.g., garnet, ilmenite, pyroxene) by using experimental duration as a proxy for transport distance. Using an ultrasonic dispenser Afanas’ev et al. (2008) were able to quantify the relative abrasion stability of different mineral phases. In decreasing stability, they report the following order: diamond, pyrope, olivine, picroilmenite, apatite, kimberlite (rock fragments). Cummings et al. (2014), experimentally abraded pyrope, chrome diopside and ilmenite grains in a tumbling mill and found that the pyrope grains abraded the easiest and in two stages. Firstly, by the removal of a kelyphite rim by surface abrasion and then, secondly, by grain breakage (fragmentation) along internal defects. Furthermore, the concept of grain size modification and the inherent particle size distribution evolution accompanying fluvial transport has been used to evaluate the diamond grade in placer-style deposits (e.g. Sutherland 1982). Lastly, we note that, grain size reduction by attrition can occur during mining and extraction processes and often contributes a significant economic loss via the breakage of diamonds (Armstrong 2017).
Within any geological environment, the nature of particle-particle interactions can be highly variable. However, to a first-order, attrition operates as two contrasting styles: (1) lower energy sustained abrasive contacts and (2) high velocity, transient particle-particle or particle-wall interactions. Here, we use experiments on olivine in a tumbling mill and a fluidized bed, respectively, to investigate and compare these two styles of attrition. Our experiments focus on the attrition of olivine, the dominant mantle phase in kimberlite, however, the fundamental principles we address here are pertinent to the attrition of all mantle-derived phases.
Methods
Pre-experiment sample characterization
Commercially-produced olivine sands, extracted from the mining of dunite, were purchased from the United Western Supply Company, Seattle (Uniwest), and from Luossavaara-Kiirunavaara Aktiebolag (LKAB) minerals (see Tables 1 and 2). Prior to experimentation, the olivine sand was washed to remove any adhering fine fragments left over from production and dry-sieved to two different restricted ranges of grain size: 1–2 mm (Uniwest olivine) and 250–500 μm (LKAB olivine). After this initial preparation, an aliquot of olivine grains from these size fractions was measured for density. We used a Micrometrics Accupyc II 1340 Helium Pycnometer to measure the sample volume and an analytical balance to measure the mass. Using this technique, we report olivine grain density values of 3256.9 kg m−3 and 3304.9 kg m−3 for the Uniwest and LKAB olivine, respectively. We also used the chemical compositions determined by X-Ray florescence (ALS Chemex; Table 1) and mass balance calculations to estimate the optimal olivine content (wt%) and olivine composition (Fo; mol%) of the washed olivine sands (Table 2).
Attrition experiments
In this study, two types of attrition experiments were performed providing two distinct types of particle-particle interaction. Firstly, experiments were performed in a tumbling mill (Fig. 2a), where all of the input particles (feed) remain in near continual contact. In each of these experiments 120 g of Uniwest olivine was loaded into the drum of the tumbling mill and sealed to ensure no particles could escape. The drum was then placed on the roller bars and left for a prescribed amount of time rotating at 32 revolutions per minute (rpm). We conducted experiments in the tumbling mill for durations of 0.25, 0.5, 1, 2 4, 5.28, 7.22, 10, 21 and 29.83 days.
Secondly, experiments were performed in a fluidized bed (Fig. 2b), wherein the particles were turbulently suspended in a gas jet. This apparatus consists of a feeding compressed air gas supply passed through a calibrated FMA5526 Omega gas flow meter into the base of the vertical attrition tube. At the tube base (inset; Fig. 2b), there is a distributor plate containing ~ 40 evenly spaced holes to break-up the gas and provide an even flux suspending the particles above. The particle-particle interactions occur in the 120 cm long vertical transparent plastic attrition tube situated above the distributor plate; the vertical attrition tube is connected to an elbow joint with a downward return to a water reservoir designed to ensure that no fines escape the system. In this study, 70 g of (LKAB) olivine grains were loaded onto the distributor plate and, then, subjected to a gas feed of 85.5 L min−1 for times of 0.5, 1, 2, 4.5, 6.3, 12.5, 24 and 32 h.
Post-experiment sample characterization
At the end of each experiment all the experimental run products were carefully collected and sieved using a standard stack of Tyler sieves. After each experiment, the apparatuses were flushed with deionised water over a 63 μm sieve to ensure that all of the fine particles were captured. The grain size distributions of all particles <63 μm, suspended in the wash water, were measured using a Malvern Mastersizer 2000 with the Hydro 2000Mu water dispersion module attached. In order to convert the volumetric measurement made by the Mastersizer to mass values (g), a known amount of 63–125 μm olivine was added to the sample. Using a pump speed of 1900 rpm, a refractive index of 1.7 and an absorption coefficient of 0.1, an aliquot of the attrition sample was added to the dispersion module and measured three times. An ultrasonic pulse was applied to the sample for 2 s before the measurement to prevent particles from aggregating in the water suspension. For each experimental product, three separate aliquots were taken, each measured three times.
To document the morphology of the olivine grains and how they change during attrition we analyzed the largest grain size fraction from both the tumbling mill (1–2 mm) and the fluidized bed (250–500 μm) experiments. For each controlled experiment (i.e. time and condition; Table 3) between 10 and 20 grains were selected from each run product and mounted for study of grain shapes and surfaces. Using a Hitachi SU-70 scanning electron microscope (SEM) and a 5 kV accelerating voltage, scanning electron images were taken at a range of magnifications.
For the tumbling mill experiments we used images of grains >1 mm to track the change in grain shape as a function of residence time. Specifically, 150 grains from the feeding size class (1–2 mm) were randomly selected and individually photographed under a binocular microscope with an intense backlight. Then, using the software, ImageJ (http://rsbweb.nih.gov/ij/) a threshold was applied to the images to separate the grain from the image background. The images were then converted to binary masks. This 2-D projection of the grain was quantified for circularity which serves as a metric for extent of abrasion:
where A [mm2] is the projected area and P [mm] is the grain perimeter. This shape factor is bounded such that values of 1 represent a perfect circle.
Results
Tumbling mill experiments
Grain size distribution changes within the tumbling mill run-products are shown in Fig. 3. The parent feed abundance (1 to 2 mm) is systematically reduced with increased residence time in the tumbling mill (black triangles; Fig. 3a). However, this reduction is non-linear with respect to time; the grains experience a rapid period of attrition within the first ~5 days and thereafter attrition appears to slow once the input grains have been reduced by ~2.5 wt%. The mass of daughter products (fragments <1 mm in diameter) increases systematically, also in a non-linear manner, with increased attrition time (grey circles; Fig. 3a). After long residence times (>5 h) the mass of daughter products does not increase and reaches a stable value of ~ 3.2 g. In some cases, the parent mass decay and subsequent increase in daughter abundance is not systematic (e.g. data at 504 h; 21 days), this may result from small olivine fragments adhering to these larger grains. By comparing the restricted 1–2 mm grain size range of the input (parent) material to the experimental run products after 30 days (the longest duration investigated), it can be seen that grains 500 μm to 1 mm in diameter contribute most of the daughter product mass (Fig. 3b). Furthermore, a secondary mode is observed at grain diameters <7.88 μm.
The original olivine grains have an angular morphology and most external surfaces show conchoidal fracture (Fig. 4a). These initial features are inherited from the mining process wherein the dunite rocks are crushed and sieved to a range of industrial size classes. The starting material properties are similar to, although not identical, to the mantle material liberated at the crack-tip of the ascending dyke (e.g. Jones et al. 2014; Brett et al. 2015). In the tumbling mill experiments these sharp exterior edges become increasingly rounded with time and small olivine chips/fragments are observed to adhere to the grain surface. The surfaces of the grains become rough at the micron scale (~10’s of μm) and feature multiple hemi-spherical chips and pits (Fig. 4b). We used image analysis to quantify the changes in morphology as a function of attrition time (Fig. 4c). The original grains have a starting circularity value of 0.681 and, as they become rounded, their circularity increases with residence time. Similar to the grain size data (Fig. 3), the shape modification is exponential with respect to time. In the first ~7 days grains rapidly round to reach a circularity of 0.726, after which the rate of rounding decreases and after a further 23 days of tumbling circularity values are only marginally increased (0.733). We note that the anomalous data point at 240 h (10 days) can be correlated with a small (0.2 g) loss of material during the experiment.
Fluidized bed experiments
The grain size data from the fluidized bed experiments are presented in the same way as the tumbling mill datasets (Fig. 5). Again, the parent feed abundance (initially 70 g of 500 μm to 1 mm) is systematically reduced in an exponential manner with increased residence time (black triangles; Fig. 5a). The period of rapid, initial attrition occurs within the first 4.5 h and reduces the feed abundance to ~90%. Also, the mass of daughter fragments produced (grey circles; Fig. 5a) rapidly increases to 7.4 g within the first 4.5 h and thereafter reaches a stable value of ~8.0 g. Again, to observe how the grain size distribution changes with attrition, the grain size distribution of the run products from the longest duration experiment (32 h) is plotted with reference to the initial feed (Fig. 5b). Grains with diameters between 500 and 250 μm constitute most of the daughter mass (~10 wt%) and like with the tumbling mill data a second mode is observed at <7.88 μm.
Morphological changes were documented via scanning electron microscopy for olivine grains measuring between 500 μm to 1 mm in diameter. The overall grain morphology (left panel; Fig. 6) progressively changes from an irregular shape with sharp edges to a sub-rounded grain with increased attrition time. The higher magnification images document the evolution of the olivine crystal surfaces (right panel; Fig. 6). In chronological order, the parent crystals have sharp, straight exterior edges and at higher magnification, their surfaces commonly feature river lines, hackle marks and evidence of conchoidal fracture (highlighted by white arrows). After 30 min, the exterior edges of the grain become more rounded and the surfaces begin to exhibit small adhering olivine fragments. After 12.5 h, the number of adhering fragments is dramatically increased and signs of surface fracture become abundant. An example of this is the central pit found in the 12.5 h olivine (Fig. 6). This fracture is interpreted to be recent as there are no adhering fine particles. Lastly, after 32 h the pits and chips also become smoothed and coated in small olivine fragments. These fine particles that commonly adhere to larger grains are thought to account for any non-systematic variations in grain size (Fig. 5).
Analysis and discussion
Rates of attrition
Both our datasets show that attrition is non-linear with respect to time. This is a well-known phenomenon and was first modelled by Gwyn (1969) as
where md is the mass of daughter particles, m0 the mass of parent feed, t is particle residence time and k and x are constants. Since this early model, workers have used comminution theory to shape three energy based models named after the proponents: the Rittinger (von Rittinger 1867), Kick (Kick 1885), and the Bond (Bond 1952) models. These three models have been used with variable success to describe attrition phenomena but generally underestimate the energy required for attrition (Rhodes 2008). Furthermore, the Gwyn (1969) model produces unrealistic infinite time limits. On that basis, we use the empirical model of Jones et al. (2017)
where a is the infinite-time attrition limit and b is the attrition rate constant [h−1]. Eq. 3 predicts attrition as a function of time for a model where the energy input into the system remains constant (e.g. the rotation rate of the tumbling mill remains constant).
The results of fitting the Jones et al. (2017) model to our new experimental data are shown in Fig. 7. These models show that the tumbling mill (Fig. 7a) is capable of producing a daughter to parent mass ratio of 0.025 at infinite times and has an attrition rate constant (b) of 0.075 h−1. Whereas the fluidized bed (Fig. 7b) has a and b constants that are one order of magnitude larger: 0.117 and 0.886 h−1 respectively. We interpret this difference to result from the different conditions that the olivine grains experience. It is known that the differential velocity between particles or objects (e.g. container walls) at impact is one of the main factors governing attrition (Bemrose and Bridgwater 1987). Higher differential velocities make attrition more successful. As a comparison, we can calculate the differential velocity an olivine grain may experience in each experimental set-up. For simplicity, in both cases we assume the differential velocity to be upon contact with a static part of the apparatus. In the case of the tumbling mill, the rotation speed was measured to be 32 rpm, this corresponds to an olivine grain velocity of 0.28 m s−1. For the fluidized bed, videos of an experiment were taken and subsequently used to track the evolution of the particle front during an experiment. Ten repeat measurements gave an average velocity of 0.86 m s−1. We hypothesize that, in this case, this variation in particle velocity explains the increased attrition efficiency within the fluidized bed. However, it is important to note that differential particle velocity is not the sole factor that effects attrition. In other situations, or systems, attrition rate can be controlled by other variables. Examples include: the feeding grain size distribution; temperature and the particle concentration.
Mechanisms of attrition
As previously stated, attrition takes two forms: fragmentation and abrasion. The grain size data from both experimental methods show that most of the size reduction occurs by rounding of the parental feed and the simultaneous of production of fines. We therefore interpret that abrasion is the main form of attrition in both the tumbling mill and the fluidized bed. This interpretation is further supported by the SEM imagery; the surfaces of the parent feed are found to have impact chips and pits that increase in abundance with increased time. Also, with increased residence time in the apparatus grains exhibit a greater number of adhering fine fragments. We interpret these fragments to be the products of abrasion. We suggest that under our experimental conditions most of the grain differential velocities are not above the “critical” velocity for fragmentation to occur (e.g. Dufek et al. 2012). Furthermore, if fragmentation dominated we would observe a sub-population of grains at an intermediate grain size – this is not observed.
In the few instances where olivine surfaces are fresh enough to be observed in the rock record they also show evidence for abrasion to be the dominant attrition process (Jones et al. 2014; Brett et al. 2015). Specifically, Jones et al. (2014) present a series of SEM images from olivine grains originally located in within a lava flow. All the grains are highly rounded and their surfaces exhibit several hemi-spherical chips and numerous pits (as observed in Figs. 4 and 6). This further supports the hypothesis that mechanical particle-particle interactions modify the mantle crystal cargo during portions of the subsurface kimberlite ascent prior to effusive lava flow emplacement. However, the experimental products from both the tumbling mill (circularity of ~0.73) and the fluidized bed do not appear as rounded as those reported from the Igwisi Hills volcano (circularity of ~0.85; Jones et al. 2014). We therefore suggest that conditions attending parts of kimberlite ascent are likely to be of higher energy relative to the experiments described in this study.
Conclusions
In this study, we have performed a series of attrition experiments on the mineral, olivine. Our experiments have informed on the attrition potential within two different energy environments, which are both relevant to different parts of the kimberlite system (Fig. 1). The tumbling mill resembles relatively low energy environments where the interacting particles are kept in near-continual contact (e.g. sedimentary bed load transport in rivers), whereas the fluidized bed subjects particles to higher energy environments within a gas (e.g. the gas/fluid-rich head of an ascending dyke).
Grain size data and SEM imagery have allowed us to show that abrasion is the dominant form of attrition under our experimental conditions. Grain size reduction predominantly occurs through grain rounding and the simultaneous production of small surface-derived chips. In both environments, the mass of daughter products produced is non-linear with respect to time and can be modelled in the form md/m0 = a (1 – e–bt) where a and b are the infinite time limit and the attrition rate constant respectively. Due to greater differential particle velocities, these constants are an order of magnitude larger in the fluidized bed relative to the tumbling mill. Finally, we suggest that attrition rate models, like the ones presented here, could be used in the future to “forensically” assess the transport conditions of enigmatic kimberlite processes: e.g. what are the rates and durations of magma ascent?
References
Afanas’ev VP, Nikolenko EI, Tychkov NS et al (2008) Mechanical abrasion of kimberlite indicator minerals: experimental investigations. Russ Geol Geophys 49:91–97
Afanasiev VP, Pokhilenko NP (2013) Wear of diamond: an experimental study and field evidence. In: Proceedings of 10th International Kimberlite Conference. pp 317–321
Afanasiev VP, Pokhilenko NP, Lobanov SS (2011) Placer diamond potential of the Siberian craton: possible sources and ages. Geol Ore Depos 53:474–477
Armstrong J (2017) Karowe Diamond Mine: A world-class source of large exceptional diamonds. 11th Int Kimberl Conf Ext Abstr 3
Arndt NT, Boullier A-M, Clément J-P et al (2006) What olivine, the neglected mineral, tells us about kimberlite petrogenesis. eEarth Discuss 1:37–50
Arndt NT, Guitreau M, Boullier A-M, le Roex A, Tommasi A, Cordier P, Sobolev A (2010) Olivine, and the origin of kimberlite. J Petrol 51:573–602
Barnett W (2008) The rock mechanics of kimberlite volcanic pipe excavation. J Volcanol Geotherm Res 174:29–39
Bemrose CR, Bridgwater J (1987) A review of attrition and attrition test methods. Powder Technol 49:97–126
Bond FC (1952) The third theory of comminution. Trans AIME, Min Eng 193:484–494
Brett RC, Russell JK, Andrews GDM, Jones TJ (2015) The ascent of kimberlite: insights from olivine. Earth Planet Sc Lett 424:119–131
Brown RJ, Gernon T, Stiefenhofer J, Field M (2008) Geological constraints on the eruption of the Jwaneng Centre kimberlite pipe, Botswana. J Volcanol Geotherm Res 174:195–208
Brown RJ, Tait M, Field M, Sparks RSJ (2009) Geology of a complex kimberlite pipe (K2 pipe, Venetia mine, South Africa): insights into conduit processes during explosive ultrabasic eruptions. Bull Volcanol 71:95–112
Buse B, Sparks RSJ, Field M, Schumacher JC, Chisi K, Tlhaodi T (2011) Geology of the BK9 kimberlite (Damtshaa, Botswana): implications for the formation of dark volcaniclastic kimberlite. Bull Volcanol 73:1029–1045
Cummings DI, Kjarsgaard BA, Russell HAJ, Sharpe DR (2014) Comminution of indicator minerals in a tumbling mill: implications for mineral exploration. Geol Surv Canada Open File 18
Dufek J, Manga M (2008) In situ production of ash in pyroclastic flows. J Geophys Res Solid Earth 113:2156–2202
Dufek J, Manga M, Patel A (2012) Granular disruption during explosive volcanic eruptions. Nat Geosci 5:561–564
Eggler DH (1989) Kimberlites: how do they form. Kimberlites Relat rocks in: J. Ross (Editor), Kimberlites and Related Rocks. Geological Society of Australia Special Publication, pp 489–504
Forsythe WL, Hertwig WR (1949) Attrition characteristics of fluid cracking catalysts. Ind Eng Chem 41:1200–1206
Gernon TM, Fontana G, Field M, Sparks RSJ, Brown RJ, Mac Niocaill C (2009a) Pyroclastic flow deposits from a kimberlite eruption: the Orapa South Crater, Botswana. Lithos 112:566–578
Gernon TM, Gilbertson MA, Sparks RSJ, Field M (2009b) The role of gas-fluidisation in the formation of massive volcaniclastic kimberlite. Lithos 112:439–451
Gwyn JE (1969) On the particle size distribution function and the attrition of cracking catalysts. AIChE J 15:35–39
Harvey S, Read G, DesGagnes B, et al (2013) Utilization of olivine macrocryst grain size and abundance data as a proxy for diamond size and grade in pyroclastic deposits of the Orion South Kimberlite, Fort à La Corne, Saskatchewan, Canada. In: Proceedings of 10th International Kimberlite Conference. pp 79–95
Holden EJ, Moss S, Russell JK, Dentith MC (2009) An image analysis method to determine crystal size distributions of olivine in kimberlite. Comput Geosci 13:255–268
Jerram DA, Mock A, Davis GR, Field M, Brown RJ (2009) 3D crystal size distributions: a case study on quantifying olivine populations in kimberlites. Lithos 112:223–235
Jones TJ, Russell JK (2017) Ash production by attrition in volcanic conduits and plumes. Sci Rep–UK 7:5538
Jones TJ, Russell JK, Porritt LA, Brown RJ (2014) Morphology and surface features of olivine in kimberlite: implications for ascent processes. Solid Earth 5:313–326
Jones TJ, McNamara K, Eychenne J, Rust AC, Cashman KV, Scheu B, Edwards R (2016) Primary and secondary fragmentation of crystal-bearing intermediate magma. J Volcanol Geotherm Res 327:70–83
Jones TJ, Russell JK, Lim CJ, Ellis N, Grace JR (2017) Pumice attrition in an air-jet. Powder Technol 308:298–305
Kick F (1885) Das Gesetz der proportionalen Widerstande und seine Anwendungen. Reprinted 2010 by Kessinger Publishing, 130 pp
Knight A, Ellis N, Grace JR, Lim CJ (2014) CO2 sorbent attrition testing for fluidized bed systems. Powder Technol 266:412–423
Kueppers U, Putz C, Spieler O, Dingwell DB (2012) Abrasion in pyroclastic density currents: insights from tumbling experiments. Phys Chem Earth, Parts A/B/C 45:33–39
Manga M, Patel A, Dufek J (2011) Rounding of pumice clasts during transport: field measurements and laboratory studies. Bull Volcanol 73:321–333
McCandless TE (1990) Kimberlite xenocryst wear in high-energy fluvial systems: experimental studies. J Geochem Explor 37:323–331
McGetchin TR, Nikhanj YS, Chodos AA (1973) Carbonatite-kimberlite relations in the Cane Valley Diatreme, San Juan County, Utah. J Geophys Res 78:1854–1869
Meyer JD (1971) Glass crust on intratelluric phenocrysts in volcanic ash as a measure of eruptive violence. Bull Volcanol 35:358–368
Mitchell RH (1986) Kimberlites: petrology, mineralogy and geochemistry, 1st edn. Springer Science + Business Media, New York, XVIII, 442 pp
Mitchell RH (1995) Kimberlites and Orangeites. In: Mitchel RH, kimberlites, orangeites, and related rocks. Springer, pp 1–90
Moss S, Russell JK (2011) Fragmentation in kimberlite: products and intensity of explosive eruption. Bull Volcanol 73:983–1003
Moss S, Russell JK, Andrews GDM (2008) Progressive infilling of a kimberlite pipe at Diavik, Northwest Territories, Canada: insights from volcanic facies architecture, textures, and granulometry. J Volcanol Geotherm Res 174:103–116
Moss S, Russell JK, Smith BHS, Brett RC (2010) Olivine crystal size distributions in kimberlite. Am Mineral 95:527–536
Porritt LA, Cas RAF (2009) Reconstruction of a kimberlite eruption, using an integrated volcanological, geochemical and numerical approach: a case study of the Fox Kimberlite, NWT, Canada. J Volcanol Geotherm Res 179:241–264
Porritt LA, Cas RAF (2011) The influence of complex intra-and extra-vent processes on facies characteristics of the Koala Kimberlite, NWT, Canada: volcanology, sedimentology and intrusive processes. Bull Volcanol 73:717–735
Porritt LA, Cas RAF, Crawford BB (2008) In-vent column collapse as an alternative model for massive volcaniclastic kimberlite emplacement: an example from the Fox kimberlite, Ekati Diamond Mine, NWT, Canada. J Volcanol Geotherm Res 174:90–102
Porritt LA, Russell JK, McLean H, et al (2013) A phreatomagmatic kimberlite: the A418 kimberlite pipe, Northwest Territories, Canada. In: Proceedings of 10th International Kimberlite Conference, pp 97–107
Ray Y-C, Jiang T-S, Wen CY (1987) Particle attrition phenomena in a fluidized bed. Powder Technol 49:193–206
Reid AM, Donaldson CH, Dawson JB, Brown RW, Ridley WI (1975) The Igwisi Hills extrusive kimberlites. Phys Chem Earth 9:199–218
Rhodes MJ (2008) Introduction to particle technology, 2nd edn. Wiley, West Sussex
Russell JK, Porritt LA, Lavallée Y, Dingwell DB (2012) Kimberlite ascent by assimilation-fuelled buoyancy. Nature 481:352–356
Sparks RSJ (2013) Kimberlite volcanism. Annu Rev Earth Planet Sci 41:497–528
Sparks RSJ, Baker L, Brown RJ, Field M, Schumacher J, Stripp G, Walters A (2006) Dynamical constraints on kimberlite volcanism. J Volcanol Geotherm Res 155:18–48
Stamm N, Schmidt MW (2017) Asthenospheric kimberlites: volatile contents and bulk compositions at 7 GPa. Earth Planet Sc Lett 474:309–321
Stiefenhofer J, Farrow DJ (2004) Geology of the Mwadui kimberlite, Shinyanga district, Tanzania. Lithos 76:139–160
Stone RS, Luth RW (2016) Orthopyroxene survival in deep carbonatite melts: implications for kimberlites. Contrib Mineral Petrol 171:1–9
Sutherland DG (1982) The transport and sorting of diamonds by fluvial and marine processes. Econ Geol 77:1613–1620
van Straaten BI, Kopylova MG, Russell JK, Smith BHS (2011) A rare occurrence of a crater-filling clastogenic extrusive coherent kimberlite, Victor Northwest (Ontario, Canada). Bull Volcanol 73:1047–1062
von Rittinger PR (1867) Taschenbuch der Aufbereitungskunde. Ernst & Korn
Walters AL, Phillips JC, Brown RJ, Field M, Gernon T, Stripp G, Sparks RSJ (2006) The role of fluidisation in the formation of volcaniclastic kimberlite: grain size observations and experimental investigation. J Volcanol Geotherm Res 155:119–137
Wilson L, Head JW (2007) An integrated model of kimberlite ascent and eruption. Nature 447:53–57
Xiao G, Grace JR, Lim CJ (2011) Attrition characteristics and mechanisms for limestone particles in an air-jet apparatus. Powder Technol 207:183–191
Xiao G, Grace JR, Lim CJ (2014) Evolution of limestone particle size distribution in an air-jet attrition apparatus. Ind Eng Chem Res 53:15845–15851
Acknowledgements
We thank Mila Huebsch, Camilo Romero, Alex Wilson, Amy Ryan and David Sasse for their assistance with the experiments and sample characterization. Constructive comments by Don I. Cummings, an anonymous expert and editor Bruce Kjarsgaard helped to improve the manuscript. T.J.J. was funded by Natural Environment Research Council, U.K., grant NE/L002590/1 and an International Kimberlite Conference grant. J.K.R. acknowledges funding from the Natural Sciences and Engineering Research Council of Canada Discovery Grants and Discovery Accelerator Supplements programs (15841).
Author information
Authors and Affiliations
Corresponding author
Additional information
Editorial handling: B. Kjarsgaard
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Jones, T.J., Russell, J.K. Attrition in the kimberlite system. Miner Petrol 112 (Suppl 2), 491–501 (2018). https://doi.org/10.1007/s00710-018-0580-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00710-018-0580-0