Bismuth-based glass powders with different quantities of Li2O were directly prepared by high-temperature spray pyrolysis. The bismuth-based glass powders were completely spherical and submicron in size irrespective of the quantities of the Li2O additive. The high optical transmittances of the dielectric layers formed from the glass powders obtained by spray pyrolysis were due to the decrease in the glass-transition temperatures of the glass powders with the addition of Li2O. The ‘yellowing phenomenon’ was not observed in the dielectric layers formed from the glass powders obtained by spray pyrolysis, whereas it occurred in the dielectric layers formed from the glass powders obtained through the conventional melting process.
Similar content being viewed by others
References
J.Y. Song, S.Y. Choi, Displays 27, 112 (2002)
S.K. Hong, H.Y. Koo, D.S. Jung, Y.C. Kang, Appl. Phys. A 85, 63 (2006)
J.S. Jeon, M.R. Cha, N.S. Kim, H.S. Choi, Mater. Sci. Forum 510–511, 506 (2006)
D. Jembrih-Simburger, C. Neelmeijer, O. Schalm, P. Fredrickx, M. Schreiner, K. De Vis, M. Mader, D. Schryvers, J. Caen, J. Anal. At. Spectrom. 17, 321 (2002)
M. Yamane, S. Shibata, A. Yasumori, T. Yano, H. Takada, J. Non-Cryst. Solids 203, 268 (1996)
Y.C. Kang, I.W. Lenggoro, K. Okuyama, S.B. Park, J. Electrochem. Soc. 146, 1227 (1999)
A. Gurav, T. Kodas, T. Pluym, Y. Xiong, Aerosol Sci. Technol. 19, 411 (1993)
G.L. Messing, S.C. Zhang, G.V. Jayanthi, J. Am. Ceram. Soc. 76, 2709 (1993)
S.E. Platsinis, S. Vemury, Powder Technol. 88, 267 (1996)
A.Y. Zhang, T. Suetsugu, K. Kadono, J. Non-Cryst. Solids 353, 44 (2007)
Author information
Authors and Affiliations
Corresponding author
Additional information
PACS
42.70.Ce; 85.60.Pg; 71.55.Jv
Rights and permissions
About this article
Cite this article
Hong, S., Jung, D., Cho, J. et al. Effect of alkali metal on the properties of Bi-based glass powders prepared by spray pyrolysis. Appl. Phys. A 90, 733–737 (2008). https://doi.org/10.1007/s00339-007-4346-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00339-007-4346-5