Abstract
Self-matt coating of waterborne polyurethane (WBPU) was synthesized by combining prepolymer and self-emulsification methods. The emulsion was fabricated from both hydroxy carboxylic acid and aminosulfonic acid types of hydrophilic chain-extending agents, in which the 2-[(2-aminoethyl) amino] ethane sulphonate sodium (AAS salt) was produced in laboratory. This emulsion demonstrated an excellent matt performance without the addition of extra matting agents after filming. Four different kinds of surface properties were measured on the film: the specular gloss (60° gloss meter), the contact angle (CA), the surface roughness degree (3D Surface Profilometer), and the topography of the coatings surface (SEM). The results showed that tons of spherical particles with diameter in a few micrometers were aggregated on the film surface. The effect of the roughness parameters (R a and R q ) and the average particle size of the emulsions on the specular gloss degree were probed. The research indicated that the emulsion with average particle size in the range of 2.5–3.0 µm and, meanwhile, the film with roughness parameters R a and R q both greater than 1 µm could attain the best matt effect. The WBPU emulsions showed good physical and mechanical properties, and were introduced into wood varnish for matting purpose.
Similar content being viewed by others
References
Huang YH, Chen MH, Lee B et al (2014) Evenly distributed thin-film Ag coating on stainless plate by tricomponent Ag/Silicate/PU with antimicrobial and biocompatible properties. ACS Appl Mater Interfaces 6:20324–20333. doi:10.1021/am5057213
Gurunathan T, Rao CRK, Narayan R, Raju KVSN (2013) Polyurethane conductive blends and composites: synthesis and applications perspective. J Mater Sci 48:67–80. doi:10.1007/s10853-012-6658-x
Wynne JH, Fulmer PA, McCluskey DM et al (2011) Synthesis and development of a multifunctional self-decontaminating polyurethane coating. ACS Appl Mater Interfaces 3:2005–2011. doi:10.1021/am200250d
Wu CI, Huang JW, Wen YL et al (2009) Preparation of antibacterial waterborne polyurethane/silver nanocomposite. J Chin Chem Soc 56:1231–1235. doi:10.1002/jccs.200900177
Allen KJ, Eastman JJ, Best KE, Eastman JJ (2010) Cleanable waterborne polyurethane coatings. US Patent Number 20100233431A1
Nsib F, Ayed N, Chevalier Y (2008) Matting agent concentration and its effect on the colour and the rheology of matted coatings. J Appl Sci 8:1527–1533. doi:10.3923/jas.2008.1527.1533
Kitaike Y, Hatakeyama H, Tayama S, Nakagawa K (1996) Mat thermoplastic resin composition and laminate therefrom, matting agent therefore, and method for matting thermoplastic resin. US Patent Number 5563227
Gunde M, Kunaver M, Cekada M (2007) Surface analysis of matt powder coatings. Dye Pigment 74:202–207. doi:10.1016/j.dyepig.2006.01.049
Bauer F, Decker U, Czihal K et al (2009) UV curing and matting of acrylate nanocomposite coatings by 172 nm excimer irradiation. Prog Org Coat 64:474–481. doi:10.1016/j.porgcoat.2008.08.009
LaFleur EE, Nungesser EH (2014) Clear matte coating. US Patent Number 8900669B2
Urs BR (2005) Matte-finish polyurethane coating composition. US Patent Number 6878771B2
Ou J, Zhang M, Liu H et al (2015) Matting films prepared from waterborne acrylic/micro-SiO2 blends. J Appl Polym Sci 132:41707. doi:10.1002/app.41707
Kumar V, Misra N, Paul J et al (2013) Organic/inorganic nanocomposite coating of bisphenol A diglycidyl ether diacrylate containing silica nanoparticles via electron beam curing process. Prog Org Coat 76:1119–1126. doi:10.1016/j.porgcoat.2013.03.010
Fletcher TE (2002) A simple model to describe relationships between gloss behaviour, matting agent concentration and the rheology of matted paints and coatings. Prog Org Coat 44:25–36. doi:10.1016/S0300-9440(01)00206-5
Yokoyama A, Saliya RG, Ma SH (2013) Matting agent composition containing polytrimethylene ether diol and use thereof. US Patent Number 8415015B2
Yong Q, Nian F, Liao B et al (2015) Synthesis and characterization of solvent-free waterborne polyurethane dispersion with both sulfonic and carboxylic hydrophilic chain-extending agents for matt coating applications. RSC Adv 5:107413–107420. doi:10.1039/C5RA21471H
Cawthorne JE, Joyce M, Fleming D (2003) Use of a chemically modified clay as a replacement for silica in matte coated ink-jet papers. J Coat Technol 75:75–81. doi:10.1007/BF02697916
Bauer F, Decker U, Naumov S, Riedel C (2014) Photoinitiator-free UV curing and matting of acrylate-based nanocomposite coatings: part 3. Prog Org Coatings 77:1085–1094. doi:10.1016/j.porgcoat.2014.03.013
Ou J, Yang Y, Gan J et al (2014) Preparation, properties, and applications of acrylic-polyurethane hybrid emulsions in extinction electrophoresis. J Appl Polym Sci 131:40078. doi:10.1002/app.40078
Nelson AM, Long TE (2014) Synthesis, properties, and applications of ion-containing polyurethane segmented copolymers. Macromol Chem Phys 215:2161–2174. doi:10.1002/macp.201400373
Bauer F, Flyunt R, Czihal K et al (2007) UV curing and matting of acrylate coatings reinforced by nano-silica and micro-corundum particles. Prog Org Coat 60:121–126. doi:10.1016/j.porgcoat.2007.07.005
Cakić SM, Špírková M, Ristić IS et al (2013) The waterborne polyurethane dispersions based on polycarbonate diol: effect of ionic content. Mater Chem Phys 138:277–285. doi:10.1016/j.matchemphys.2012.11.057
Pingping K, Wensheng S, Bingbing H, Shuangshuang X (2009) Synthesis and characterization of aliphatic diamine sulphonate. Chin J Org Chem 29:904–908
He Y, Zhang X, Zhang X et al (2012) Structural investigations of toluene diisocyanate (TDI) and trimethylolpropane (TMP)-based polyurethane prepolymer. J Ind Eng Chem 18:1620–1627. doi:10.1016/j.jiec.2012.02.023
Rahman MM, Kim H-D, Lee W-K (2009) Properties of waterborne polyurethane adhesives: effect of chain extender and polyol content. J Adhes Sci Technol 23:177–193. doi:10.1163/156856108X344667
Rahman MM, Hasneen A, Chung I et al (2013) Synthesis and properties of polyurethane coatings: the effect of different types of soft segments and their ratios. Compos Interfaces 20:15–26. doi:10.1080/15685543.2013.762890
Santos CC, Delpech MC, Coutinho FMB (2009) Thermal and mechanical profile of cast films from waterborne polyurethanes based on polyether block copolymers. J Mater Sci 44:1317–1323. doi:10.1007/s10853-009-3272-7
Zhang C, Wen X, Vyavahare NR, Boland T (2008) Synthesis and characterization of biodegradable elastomeric polyurethane scaffolds fabricated by the inkjet technique. Biomaterials 29:3781–3791. doi:10.1016/j.biomaterials.2008.06.009
Princi E, Vicini S, Castro K et al (2009) On the micro-phase separation in waterborne polyurethanes. Macromol Chem Phys 210:879–889. doi:10.1002/macp.200900013
Zhang S, Lv H, Zhang H et al (2006) Waterborne polyurethanes: spectroscopy and stability of emulsions. J Appl Polym Sci 101:597–602. doi:10.1002/app.23354
Król P, Król B, Stagraczyński R, Skrzypiec K (2013) Waterborne cationomer polyurethane coatings with improved hydrophobic properties. J Appl Polym Sci 127:2508–2519. doi:10.1002/app.37552
Davis A, Yeong YH, Steele A et al (2014) Superhydrophobic nanocomposite surface topography and ice adhesion. ACS Appl Mater Interfaces 6:9272–9279. doi:10.1021/am501640h
Keddie JL, Meredith P, Jones RAL, Donald AM (1995) Kinetics of film formation in acrylic latices studied with multiple-angle-of-incidence ellipsometry and environmental SEM. Macromolecules 28:2673–2682. doi:10.1021/ma00112a012
Vanderhoff JW, Bradford EB, Carrington WK (2007) The transport of water through latex films. J Polym Sci Polym Symp 41:155–174. doi:10.1002/polc.5070410116
Trezza TA, Krochta JM (2001) Specular reflection, gloss, roughness and surface heterogeneity of biopolymer coatings. J Appl Polym Sci 79:2221–2229. doi:10.1002/1097-4628(20010321)79:12<2221:AID-APP1029>3.0.CO;2-F
Maskery SE (1973) Development and applications for matting agents. Pigment Resin Technol 2:11–19. doi:10.1108/eb040916
Acknowledgments
The project was funded by the State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, Donghua University, China.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yong, Q., Nian, F., Liao, B. et al. Synthesis and surface analysis of self-matt coating based on waterborne polyurethane resin and study on the matt mechanism. Polym. Bull. 74, 1061–1076 (2017). https://doi.org/10.1007/s00289-016-1763-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00289-016-1763-7