Abstract
Surface enhancement of engineering materials is necessary for preventing service failure and corrosion attacks industrially. The surface modification, strengthening effect and electrochemical comparative study of Zn-Al2O3-CeO3 and Zn-TiO2-CeO3 coating on mild steel was investigated. Deposition was performed to obtain a better surface adherent coating using the electrodeposition technique. Co-deposition of mild steel resulted into surface modification attributes to the complex alloys that were developed. Films of mild steel were electrodeposited on zinc electrodes using the chloride bath solutions. The effect of deposition potentials was systematically studied using a focus ion beam scanning electron microscope (FIB-SEM) and an atomic force microscope (AFM) to observe the surface morphology, topography and the surface adherent properties of the coatings. The elemental composition and the phases evolved in composite coatings were measured by means of the energy dispersed spectrometer (EDS). The microhardness measurements and corrosion behaviours of the deposits were investigated. Weight loss measurement was conducted on the plated samples to observe the rate of corrosion and it was observed that there was severe corrosion on the controlled sample in comparison to the plated samples and that Zn-TiO2-CeO3 resisted more corrosion attacks.
Similar content being viewed by others
References
Praveen BM, Venkatesh TV (2008) Electrodeposition and properties of Zn-nanosized TiO2 composite coatings. J Appl Surf Sci 254:2418–2424
Popoola API, Fayomi OSI (2011) Effect of some process variables on zinc coated low carbon steel substrate. J Corros Sci 20:4264–4272
Durodola BM, Olugbuyiro JAO (2011) Effect of some plating variables on zinc coated low carbon steel substrates. J Corros Sci 10:1255–1262
Naik YA, Venkatesha TV, Nayak PV (2002) Electrodeposition of zinc from chloride solution. J Appl Surf Sci 26:725–733
Zhu XB, Cai C, Zheng GQ, Zhang Z, Li JF (2011) Electrodeposition and corrosion behaviour of nanostructured Ni-Tin composite films. J Trans Non-Ferrous Metals Soc China 21:2216–2224
Lou HH, Huang Y (2006) Electroplating. J Corros Sci 9:1081–1089
Wan Nik WB, Zulkifli F, Rahman MM, Rosliza R (2011) Corrosion behaviour of mild steel in seawater from two different sites of Kuala Terengganu coastal area. Int J Basic Appl Sci 11:75–80
Berner T, Dreyer MS, Flowers L, Selgrade MJ (2009) Toxicological review of cerium oxide and cerium compounds. J Corros Sci 27:18–28
Popoola API, Fayomi OSI, Popoola OM (2012) Comparative studies of microstructural, tribological and corrosion properties of plated Zn and Zn-alloy coatings. Int J Electrochem Sci 7:4860–4870
Vlasa A, Varvara S, Pop A, Bulea C, Muresan LM (2010) Electrodeposited Zn-Tio2 nanocomposite coatings and their corrosion behaviour. Int J Electrochem Sci 40:1519–1527
Sadiku-Agboola O, Sadiku ER, Biotidara OF (2012) The properties and the effect of operating parameters on nickel plating (review). Int J Phys Sci 7:349–360
Dong D, Cheng XH, Xiao WT, Yang GB, Zhang PY (2009) Preparation and properties of electroless Ni-P-Sio2 composite coatings. J Appl Sci 255:7051–7055
Choi Y, Barik NI, Hong SI (2001) Microstructural observation and wear properties of thin chrome layers prepared by pulse plating. J Thin Solid Films 397:24–29
Meenu S, Balaraju JN, Ravishankar B, RAJAM KS (2010) Improvement in the properties of nickel by nano-Cr2O3 incorporation. J Surf Coat Technol 206:66–75
Li, J.; Sun, Y.; Sun, X. & Qiao, J, (2005) Mechanical and corrosion-resistance performance of electrodeposited titania-nickel nanocomposite coatings. Surf Coat Technol,;192(2-3):331– 335, ISSN 2578972
Aruna, S. T.; William Grips, V. K. & Rajam, K. S. (2009) Ni-based electrodeposited composite coating exhibiting improved microhardness, corrosion and wear resistance properties. J Alloys Comp;468(1-2):546–552, ISSN 09258388
Erler, F.; Jakob, C.; Romanus, H.; Spiess, L.; Wielage, B.; Lampke, T. & Steinhouser, S. (2003) Interface behaviour in nickel composite coatings with nano-particles of oxidic ceramic. Electrochimica Acta;48(20-22):3063-3070, ISSN 00134686
Szczygieł, Bogdan & Kołodziej, Małgorzata (2005) Composite Ni/Al2O3 coatings and their corrosion resistance. Electrochimica Acta;50:4188-4195, ISSN 00134686
Aruna, S. T.; Ezhil Selvi, V. ; William Grips, V. K. & Rajam, K. S. 2011. corrosion- and wear-resistant properties of ni–al2o3 composite coatings containing various forms of alumina. J Appl Electrochem ;41:461-468, ISSN 15728838
Wang Y, Kovacevic R, Liu J (1998) Mechanism of surface modification of CeO2 in laser remelted alloy spray coatings. Wear 221:47–53
Schem M, Schmidt T, Gerwann J, Wittmar M, Veith M, Thompson GE, Zheludkevich ML (2009) Ceo2-filled Sol–Gel coatings for corrosion protection of AA2024-T3 aluminium alloy. Corros Sci 51(10):2304–2315
Shibli SMA, Archana SR, Muhamed Ashraf P (2008) Development of nano cerium oxide incorporated aluminium alloy sacrificial anode for marine applications. Corros Sci 50(8):2232–2238
Hamlaoui Y, Rémazeilles C, Bordes M, Tifouti L, Pedraza F (2010) Electrodeposition of ceria-based layers on zinc electroplated steel. Corros Sci 52(3):1020–1025. doi:10.1016/J.Corsci.2009.11.027
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Popoola, A.P..., Fayomi, O.S.I., Aigbodion, V.S. et al. Surface modification, strengthening effect and electrochemical comparative study of Zn-Al2O3-CeO3 and Zn-TiO2-CeO3 coating on mild steel. Int J Adv Manuf Technol 85, 1419–1427 (2016). https://doi.org/10.1007/s00170-015-8063-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-015-8063-5