Abstract
The fracture toughness of polycarbonate was obtained over the temperature range 20 to − 120° C. There is a strong thickness dependence which is described in terms of plane stress and plane strain values which are insensitive to temperatures above −40° C but the plane stress value increases below this temperature. This change is associated with theβ transition and stable crack growth was observed in this region with accompanying instabilities arising from adiabatic heating at the crack tip.
Similar content being viewed by others
References
J. P. Berry,J. Polymer Sci. A1 (1963) 993.
F. A. Johnson andJ. C. Radon,Eng. Fract. Mechs. 4 (1972) 555.
L. J. Broutman andF. J. Mcgarry,J. Appl. Polymer Sci. 9 (1965) 589.
G. P. Marshall, L. E. Culver andJ. G. Williams,Plastics and Polymers February (1969) 75.
G. P. Marshall, L. H. Coutts andJ. G. Williams,J. Mater. Sci. 9 (1974) 1409.
M. Parvin andJ. G. Williams,Int. J. Fract., in press.
N. G. Mccrum, B. E. Read andG. Williams, “Anelastic and Dielectric effects in polymeric solids” (Wiley, New York, 1967).
G. R. Irwin, J. A. Kies andH. L. Smith,Proc. ASTM 58 (1958) 640.
G. R. Irwin,J. Appl. Mechs. December29 (1962) 651.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Parvin, M., Williams, J.G. The effect of temperature on the fracture of polycarbonate. J Mater Sci 10, 1883–1888 (1975). https://doi.org/10.1007/BF00754478
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00754478