Abstract
The sintering behavior of cBN powder with various particle sizes from 0.5 to 12 µm was investigated when sintered at temperatures from 1500 to 2500 °C and pressure of 7.7 GPa without additives. Above 2000 °C, translucent sintered bodies were obtained. Microstructure observation indicated that the optimum sintering temperature was near 2350 °C for fine powders of 0.5 to 1.2 µm and 2 to 4 µm, and slightly higher than 2350 °C for powders from 8 to 12 µm. The fracture toughness of the well-sintered bodies decreased with grain growth above the optimum sintering temperature.
Similar content being viewed by others
References
R. H. Wentorf, Jr., A. C. DeVries, and F. P. Bundy, Science 208, 873–880 (1980).
G. Rai, in New Diamond Science and Technology, edited by R. Messier, J. T. Glass, J. E. Butler, and R. Roy (Mater. Res. Soc. Symp. Int. Proc. NDST2, Pittsburgh, PA, 1991), pp. 1069–1079.
Y. Utsumi, S. Yamata, H. Hara, N. Kaneki, and K. Shimada in New Diamond Science and Technology, edited by R. Messier, J. T. Glass, J. E. Butler, and R. Roy (Mater. Res. Soc. Int. Symp. Proc. NDST2, Pittsburgh, PA, 1991), pp. 1081–1086.
M. Wakatsuki, K. Ichinose, and T. Aoki, Mater Res. Bull. 7, 999–1003 (1972).
F. R. Corrigan and F. P. Bundy, J. Chem. Phys. 63, 3812–3817 (1975).
N. V. Novikov, Y. V. Sirota, V. I. Mal’nec, and I.A. Petrusha, Diamond Relat. Mater. 2, 1253–1256 (1993).
M. Akaishi, T. Sato, M. Ishii, T. Taniguchi, and S. Yamaoka, J. Mater. Sci. Lett. 12, 1883–1885 (1993).
T. Taniguchi, M. Akaishi, S. Yamaoka, J. Am. Ceram. Soc. 79, 547–549 (1996).
S. Yamaoka, M. Akaishi, and F. Ueda, New Diamond (in Japanese) 7 (3), 28–29 (1991).
T. Taniguchi, M. Akaishi, and S. Yamaoka, in Advanced Materials ‘96, The 3rd NIRIM International Symposium on Advanced Materials (ISAM ‘96) Proceedings. (NIRIM, Tsukuba, Japan, 1996), pp. 275–280.
M. Akaishi, H. Kanda, and S. Yamaoka, J. Hard Mater. 3, 75 (1992).
C. A. Brooks, Inst. Phys. Conf. Ser. 75, 207–220 (1986).
A. G. Evans and E. A. Charles J. Am. Ceram. Soc. 59, 371 (1976).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Taniguchi, T., Akaishi, M. & Yamaoka, S. Sintering of cubic boron nitride without additives at 7.7 GPa and above 2000 °C. Journal of Materials Research 14, 162–169 (1999). https://doi.org/10.1557/JMR.1999.0024
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1999.0024