Abstract
Sulfur (S) is introduced as an additive in the growth atmosphere of carbon nanotubes (CNTs) in the range of 940-1020°C. CNT products with distorted sidewalls can be obtained by S-assisted growth. Moreover, many fascinating CNT structures can also be found in samples grown with S addition, such as bamboo-like CNTs, twisted CNTs, arborization-like CNTs, and bead-like CNTs. Compared with CNTs grown without S, more nitrogen-doping content is achieved in CNTs with S addition, which is beneficial for the properties and applications of nitrogen-doped CNTs. In addition, S can also enhance the encapsulation of ferromagnetic materials and thus improve the soft magnetic properties of CNTs, which is favorable to the applications of CNTs in the electromagnetic wave-absorbing and magnetic data storage areas.
Avoid common mistakes on your manuscript.
Introduction
Sulfur (S) is an important additive for controlling the structures and properties of carbon nanotubes (CNTs). Many interesting carbon nanostructures, such as Y-junction CNTs [1], sea-urchin-like CNTs [2], long single-walled CNT (SWCNT) strands [3], double-walled CNT films [4], amorphous CNTs [5], large-diameter SWCNTs [6], ultra-short CNTs [7], and small-diameter multi-walled CNTs [8] can be obtained by S-assisted growth. Meanwhile, enhanced mechanical properties [3], water-solubility [6], catalyst support performance [6], electrochemical properties [7], and photovoltaic performance [9] can all be achieved by CNT products with S-assisted growth. Therefore, the introduction of S into growth atmosphere of CNTs has attracted much research interest because of their promotional effect on synthesis of carbon nanostructures with novel morphologies and properties.
Nitrogen-doping (N-doping) is an effective way to modify the properties of CNTs. Nitrogen-doped (N-doped) CNTs demonstrate negative differential resistance behavior [10], high electrocatalytic activity for oxygen reduction [11], and can also be used as suitable support for uniform distribution of Pt catalyst [12, 13]. In addition, N-doping has a significant effect on controlling chirality and crystallinity of CNTs [14], leading to n-type CNTs [15], and improving the field emission performance of CNTs [16–18]. The effective doping of nitrogen into CNTs is mainly achieved in situ during CNT growth [12–16, 19], and N-doping content is usually controlled by adjusting the ratio of carbon source to nitrogen source [16, 19], which is disadvantageous for increasing the doping content of CNTs produced with liquid carbon source. For example, N-doped CNTs can be synthesized by mixture of xylene and pyridine, and CNTs with different N-doping contents are obtained from different xylene/pyridine ratios, but their doping contents cannot be larger than that with pure pyridine [19]. Therefore, it is crucial to develop an efficient way to improve the N-doping content in CNTs from the view of both theoretical and applied research.
In this study, S was introduced as an additive in the growth of CNTs. CNTs with distorted walls were obtained, which might be good supports for catalyst nanoparticles. Many other fascinating CNT structures were also obtained in this study's samples, such as bamboo-like CNTs, twisted CNTs, arborization-like CNTs, and bead-like CNTs. When S was used as growth promoter, the improved CNTs with high N-doping content could be achieved. In addition, the effect of S addition on enhanced soft magnetic properties of CNTs was also demonstrated.
Experimental
Experimental setup and procedure are similar to that described in the previous report by the authors about N-doped CNT arrays [18]. Ferrocene and pure S powders were dissolved in acetonitrile to form a solution (20 mg/ml), and fed into chemical vapor deposition (CVD) reactor by a syringe pump at a constant rate of 0.4 ml/min for 0.5-1 h. A mixture of Ar (2000 sccm) and H2 (300 sccm) acts as the carrier gas. In order to investigate the effect of S on CNT growth at a relatively low temperature, the temperature is set in the range of 940-1020°C. The S concentration in the catalyst (atomic ratio of S:Fe) is 1:10. CNTs without S additive are also prepared for comparison.
The resulting CNTs were characterized using scanning electron microscope (SEM, JOEL JSM-6460 LV SEM), transmission electron microscope (TEM, JEM-200 CX), microscopic confocal Raman spectrometer (Renishow RM 2000, using 632.8-nm laser excitation), Auger electron spectroscopy (AES, PHI-700), and X-ray diffractometer (XRD, Bruker D8 advence). The magnetization measurements were performed on a vibrating sample magnetometer (LakeShore VSM-7307) at room temperature. Thermogravimetric analysis (TGA) results were obtained using 6-mg samples in air flow at a heating rate of 20°C/min.
Results and discussion
Figure 1 shows the SEM images of as-grown CNTs at different temperatures with and without S. It can be seen from Figure 1a, b, c, d, e, f that aligned CNTs are obtained at all the three temperatures(940°C, 980°C, and 1020°C) with and without S. Aligned CNTs produced by acetonitrile without S have been reported in our previous study [18], and the results of this study demonstrate that the introduction of S is nondestructive to the alignment of CNTs.
The TEM images of the as-grown products are shown in Figure 2. Typical morphology of CNTs grown without S is shown in Figure 2a, and their sidewalls are straight as those shown in many previous reports [11, 18, 20]. However, in the case of products obtained by the S-assisted method, it can be clearly seen from Figure 2b, c, d that CNTs with distorted sidewalls can be obtained at different growth temperatures. Owing to the existence of abundant defect in surface, this kind of CNTs might supply more active positions for efficient immobilization of catalyst nanoparticles, and thus be useful for catalyst support applications [21]. Previous studies have demonstrated that S is favorable for the formation of pentagon and heptagon carbon rings, inducing curvature and further influencing the CNT morphology [1, 2]. Many pentagonal and heptagonal rings exist in the sp 2 carbon lattice, which are supposed to cause the distort-walled CNTs formation. Furthermore, many fascinating CNT structures can also be found in the CNT samples of this study with S, such as bamboo-like CNTs (Figure 2e), twisted CNTs (Figure 2f), arborization-like CNTs (Figure 2g), and bead-like CNTs (Figure 2h).
Raman spectroscopy has been proved to be a perfect tool to evaluate the crystallinity and defects in carbon structures [18, 20]. The Raman spectra of the CNTs grown at different temperatures with and without S are shown in Figure 3a, b. The strong bands around 1330, 1580, and 2650 cm-1 can be assigned to D-band, G-band, and 2D-band, respectively. Taking D- and G-bands into consideration, little difference is found between the CNTs with and without S. The obvious difference between their 2D-bands is shown in Figure 3. If S is introduced into the CVD reactor, then 2D-band downshifts approximately 30 cm-1. This might be attributed to the improved N-doping content [22]. The 2D-band of CNTs without S is almost symmetrical, but 2D-band is irregular with S. This may be due to the difference between their CNT walls, because 2D-band is sensitive to the stacking of graphene sheets [23].
The improvement of N-doping content is also confirmed by AES. Figure 3c shows the surface AES results of the two CNTs samples produced at 980°C with S and without S, respectively. Almost no signals of Fe were detected in both of the samples, indicating that Fe catalyst particles are fully covered by carbon layers. The CNTs produced with S consist of C (95.2 at.%), N (2.4 at.%), and O (2.4 at.%), while CNTs without S consist of C (96.9 at.%), N (1.2 at.%), and O (1.9 at.%). The presence of O can be attributed to the exposure of the CNTs in the air atmosphere [18, 24]. It can be seen that S has an effect on increasing N-doping content in CNTs. This might be because S induces pentagon and heptagon in sp 2 carbon lattice [1, 2], and these heterocyclic rings are supposed to be favorable to the enhancement of N-doping.
Hysteresis loops and the saturation magnetization (M s) of CNTs produced at different temperatures with and without S are shown in Figure 4 and Table 1, respectively. As shown in Table 1, the M s of CNTs with S is enhanced by 1.5-3.5 times compared with that without S. As proved in our previous study, the M s improvement of CNTs can be attributed to the increased encapsulation of ferromagnetic materials into their inner cavities [25]. Conversely, the enhanced M s also indicates that S can increase the encapsulation of ferromagnetic materials into CNTs.
In order to prove the enhanced encapsulation of ferromagnetic material, TGA was carried out, as shown in Figure 5. The residual weight percentage in the platform part of TGA curves at 600-900°C range can be used to determine the content of ferromagnetic material inside the CNTs [26]. It can be seen that the introduction of S can remarkably increase the encapsulation of ferromagnetic material compared with that without S.
The XRD analysis proved the existence of pure Fe and FeC3 in the CNTs grown with and without S, as shown in Figure 6a, b. Auger depth-resolved chemical analysis was carried out by sputtering the catalyst particle seeking with SEM using an in situ 1 keV Ar-ion gun, (sputtering speed: 13.5 nm/min, probe diameter 1.8 nm), and the resulting Auger depth profiles of CNTs grown at 980°C with and without S are shown in Figure 6c, d. The major difference between Figure 6c, d is that S peak exists in Figure 6c. This indicates the existence of iron S compound in CNTs produced with S, which is in accordance with the XRD result (Figure 6a). CNTs are good templates for housing metals or compounds, and these nanostructures combine the properties of metals/compounds and CNTs together [25]. S can enrich the categories and enhance the amount of encapsulation in CNTs, which is favorable to the applications of CNTs in the electromagnetic wave-absorbing [25], and magnetic data storage [27] areas.
Conclusions
CNTs with distorted sidewalls are synthesized by the S-assisted CVD method. S is favorable to the formation of pentagon and heptagon carbon rings, and these rings are supposed to result in the formation of CNTs with distorted sidewalls. This kind of CNTs might supply more active positions for catalyst nanoparticles and have potential usage in catalyst support area. It is also found that S addition can enhance the N-doping content of CNTs, resulting from heterocyclic rings, which are favorable for the enhancement of N-doping. The effect of S on enhancing the soft magnetic properties of CNTs is also demonstrated, and the enhanced saturation magnetization can be attributed to the enhanced encapsulation of ferromagnetic material. Enhanced soft magnetic properties of CNTs are favorable for the applications of CNTs in the electromagnetic wave-absorbing and magnetic data storage areas.
Abbreviations
- AES:
-
Auger electron spectroscopy
- CNTs:
-
carbon nanotubes
- CVD:
-
chemical vapor deposition
- N:
-
nitrogen
- S:
-
sulfur
- SEM:
-
scanning electron microscope
- SWCNT:
-
single-walled CNT
- TGA:
-
thermogravimetric analysis
- TEM:
-
transmission electron microscope
- XRD:
-
X-ray diffraction.
References
Romo-Herrera JM, Sumpter BG, Cullen DA, Terrones H, Cruz-Silva E, Smith DJ, Meunier V, Terrones M: An atomistic branching mechanism for carbon nanotubes: sulfur as the triggering agent. Angew Chem Int Ed 2008, 47: 2948. 10.1002/anie.200705053
Romo-Herrera JM, Cullen DA, Cruz-Silva E, Ramirez D, Sumpter BG, Meunier V, Terrones H, Smith DJ, Terrones M: The Role of Sulfur in the synthesis of novel carbon morphologies: from covalent Y-junctions to Sea-Urchin-Like structures. Adv Funct Mater 2009, 19: 1193. 10.1002/adfm.200800931
Zhu HW, Xu CL, Wu DH, Wei BQ, Vajtai R, Ajayan PM: Direct synthesis of long single-walled carbon nanotube strands. Science 2002, 296: 884. 10.1126/science.1066996
Wei JQ, Jiang B, Wu DH, Wei BQ: Large-scale synthesis of long double-walled carbon nanotubes. J Phys Chem B 2004, 108: 8844. 10.1021/jp049434x
Luo T, Chen LY, Bao KY, Yu WC, Qian YT: Solvothermal preparation of amorphous carbon nanotubes and Fe/C coaxial nanocables from sulfur, ferrocene, and benzene. Carbon 2006, 44: 2844. 10.1016/j.carbon.2006.03.020
Ma J, Wang JN, Wang XX: Large-diameter and water-dispersible single-walled carbon nanotubes: synthesis, characterization and applications. J Mater Chem 2009, 19: 3033. 10.1039/b820088b
Wang XX, Wang JN, Su LF: Preparation and electrochemical performance of ultra-short carbon nanotubes. J Power Sources 2009, 186: 194. 10.1016/j.jpowsour.2008.09.074
Huang JQ, Zhang Q, Wei F, Qian WZ, Wang DZ, Hu L: Liquefied petroleum gas containing sulfur as the carbon source for carbon nanotube forests. Carbon 2008, 46: 291. 10.1016/j.carbon.2007.11.044
Wei JQ, Jia Y, Shu QK, Gu ZY, Wang KL, Zhuang DM, Zhang G, Wang ZC, Luo JB, Cao AY, Wu DH: Double-walled carbon nanotube solar cells. Nano Lett 2007, 7: 2317. 10.1021/nl070961c
Lee SU, Belosludov RV, Mizuseki H, Kawazoe Y: Designing nanogadgetry for nanoelectronic devices with nitrogen-doped capped carbon nanotubes. Small 2009, 5: 1769. 10.1002/smll.200801938
Gong KP, Du F, Xia ZH, Durstock M, Dai LM: Nitrogen-doped carbon nanotube arrays with high electrocatalytic activity for oxygen reduction. Science 2009, 323: 760. 10.1126/science.1168049
Fang WC: High methanol oxidation activity of well-dispersed Pt nanoparticles on carbon nanotubes using nitrogen doping. Nanoscale Res Lett 2010, 5: 68. 10.1007/s11671-009-9444-1
Sun SH, Zhang GX, Zhong Y, Liu H, Li RY, Zhou XR, Sun XL: Ultrathin single crystal Pt nanowires grown on N-doped carbon nanotubes. Chem Commun 2009, 18: 7048. 10.1039/b916080a
Terrones M: Controlling nanotube chirality and crystallinity by doping. Small 2005, 1: 1032. 10.1002/smll.200500238
Terrones M, Ajayan PM, Banhart F, Blase X, Carroll DL, Charlier JC, Czerw R, Foley B, Grobert N, Kamalakaran R, Kohler-Redlich P, Ruhle M, Seeger T, Terrones H: N-doping and coalescence of carbon nanotubes: synthesis and electronic properties. Appl Phys A 2002, 74: 355. 10.1007/s003390201278
Chun KY, Lee HS, Lee CJ: Nitrogen doping effects on the structure behavior and the field emission performance of double-walled carbon nanotubes. Carbon 2009, 47: 169. 10.1016/j.carbon.2008.09.047
Lai YH, Lian HB, Lee KY: Field emission of vertically aligned carbon nanotubes with various content of nitrogen. Diamond Relat Mater 2009, 18: 544. 10.1016/j.diamond.2008.10.011
Cui TX, Lv RT, Kang FY, Hu Q, Gu JL, Wang KL, Wu DH: Synthesis and enhanced field-emission of thin-walled, open-end, and well-aligned N-doped carbon nanotubes. Nanoscale Res Lett 2010, 5: 941. 10.1007/s11671-010-9586-1
Xu EY, Wei JQ, Wang KL, Li Z, Gui XC, Jia Y, Zhu HW, Wu DH: Doped carbon nanotube array with a gradient of nitrogen concentration. Carbon 2010, 48: 3097. 10.1016/j.carbon.2010.04.046
Yadav RM, Dobal PS, Shripathi T, Katiyar RS, Srivastava ON: Effect of growth temperature on bamboo-shaped carbon-nitrogen (C-N) nanotubes synthesized using ferrocene acetonitrile precursor. Nanoscale Res Lett 2009, 4: 197. 10.1007/s11671-008-9225-2
Centi G, Gangeri M, Fiorello M, Perathoner S, Amadou J, Begin D, Ledoux MJ, Pham-Huu C, Schuster ME, Su DS, Tessonnier JP, Schlogl R: The role of mechanically induced defects in carbon nanotubes to modify the properties of electrodes for PEM fuel cell. Catal Today 2009, 147: 287. 10.1016/j.cattod.2009.07.080
Ayala P, Arenal R, Loiseau A, Rubio A, Pichler T: The physical and chemical properties of heteronanotubes. Rev Mod Phys 2010, 82: 1843. 10.1103/RevModPhys.82.1843
Endo M, Kim YA, Fukai Y, Hayashi T, Terrones M, Terrones H, Dresselhaus MS: Comparison study of semi-crystalline and highly crystalline multiwalled carbon nanotubes. Appl Phys Lett 2001, 79: 1531. 10.1063/1.1400774
Lin YG, Hsu YK, Wu CT, Chen SY, Chen KH, Chen LC: Effects of nitrogen-doping on the microstructure, bonding and electrochemical activity of carbon nanotubes. Diamond Relat Mater 2009, 18: 433. 10.1016/j.diamond.2008.09.009
Lv RT, Kang FY, Gu JL, Gui XC, Wei JQ, Wang KL, Wu DH: Carbon nanotubes filled with ferromagnetic alloy nanowires: lightweight and wide-band microwave absorber. Appl Phys Lett 2008, 93: 223105. 10.1063/1.3042099
Lv RT, Kang FY, Wang WX, Wei JQ, Gu JL, Wang KL, Wu DH: Effect of using chlorine-containing precursors in the synthesis of FeNi-filled carbon nanotubes. Carbon 2007, 45: 1433. 10.1016/j.carbon.2007.03.032
Muller C, Elefant D, Leonhardt A, Buchner B: Incremental analysis of the magnetization behavior in iron-filled carbon nanotube arrays. J Appl Phys 2008, 103: 034302. 10.1063/1.2837037
Acknowledgements
The authors are grateful for the financial support received from China Postdoctoral Science Foundation (Grant No. 20090450021) and the National Natural Science Foundation of China (Grant No. 50902080, 50632040).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
TC carried out the most of experiments and drafted the manuscript. RL participated in the CNT synthesis and manuscript preparation. ZH participated in the analysis of Raman and XRD spectra. FK designed the experiments and revised the manuscript. KW and DW discussed and analyzed the experimental results. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Cui, T., Lv, R., Huang, Zh. et al. Effect of sulfur on enhancing nitrogen-doping and magnetic properties of carbon nanotubes. Nanoscale Res Lett 6, 77 (2011). https://doi.org/10.1186/1556-276X-6-77
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-6-77