Abstract
The effect of hot isostatic pressing treatment on the fatigue crack growth behavior of Ti–6Al–4V alloy fabricated by electron beam melting was investigated. The results indicate that the fatigue crack growth rate of the HIPed samples is higher than that of the as-fabricated one under certain stress intensity factor (ΔK < 18 MPa m1/2). With further increase in ΔK, the fatigue crack growth rates of the studied two samples become similar. The variation of α lamella thickness and the pore defects distribution have an effect on the fatigue crack growth rates in the studied samples, and the latter plays the dominant role.
Similar content being viewed by others
References
H. Galarraga, R.J. Warren, D.A. Lados, R.R. Dehoff, M.M. Kirka, P. Nandwana, Mater. Sci. Eng. A 685, 417 (2017)
L.E. Murr, S.A. Quinones, S.M. Gaytan, M.I. Lopez, A. Rodela, E.Y. Martinez, D.H. Hernandez, E. Martinez, F. Medina, R.B. Wicker, J. Mech. Behav. Biomed. Mater. 2, 20 (2009)
Y.J. Liu, S.J. Li, W.T. Hou, S.G. Wang, Y.L. Hao, R. Yang, T. Sercombe, L.C. Zhang, J. Mater. Sci. Technol. 32, 505 (2016)
Y.J. Liu, H.L. Wang, S.J. Li, S.G. Wang, W.J. Wang, W.T. Hou, Y.L. Hao, R. Yang, L.C. Zhang, Acta Mater. 126, 58 (2017)
Y.J. Liu, S.J. Li, H.L. Wang, W.T. Hou, Y.L. Hao, R. Yang, T.B. Sercombe, L.C. Zhang, Acta Mater. 113, 56 (2016)
S.S. Al-Bermani, M.L. Blackmore, W. Zhang, I. Todd, Metall. Mater. Trans. A 41, 3422 (2010)
N. Hrabe, T. Quinn, Mater. Sci. Eng. A 573, 271 (2013)
Z. Wang, J. Zhang, S.J. Li, W.T. Hou, Y.L. Hao, R. Yang, Rare Metal Mater. Eng. 43, 161 (2014). (in Chinese)
B.V. Hooreweder, D. Moens, R. Boonen, J.P. Kruth, P. Sas, Adv. Eng. Mater. 14, 92 (2012)
X.L. Zhao, S.J. Li, M. Zhang, Y.D. Liu, T.B. Sercombe, S.G. Wang, Y.L. Hao, R. Yang, L.E. Murr, Mater. Des. 95, 21 (2016)
Y. Bai, X. Gai, S.J. Li, L.C. Zhang, Y.J. Liu, Y.L. Hao, X. Zhang, R. Yang, Y.B. Gao, Corros. Sci. 123, 289 (2017)
N.W. Dai, L.C. Zhang, J.X. Zhang, Q.M. Chen, M.L. Wu, Corros. Sci. 102, 484 (2016)
N.W. Dai, L.C. Zhang, J.X. Zhang, X. Zhang, Q.Z. Ni, Y. Chen, M.L. Wu, C. Yang, Corros. Sci. 111, 703 (2016)
N.W. Dai, J.X. Zhang, Y. Chen, L.C. Zhang, J. Electrochem. Soc. 164, C428 (2017)
L.E. Murr, S.M. Gaytan, D.A. Ramirez, E.Y. Martinez, J. Hernandez, K.N. Amato, P.W. Shinndo, F.R. Medina, R.B. Wicker, J. Mater. Sci. Technol. 28, 1 (2012)
R.P. Guo, L. Xu, Y.P. Zong, R. Yang, Acta Metall. Sin. (Engl. Lett.) 30, 735 (2017)
H.B. Suo, Z.Y. Chen, J.W. Li, Aerosp. Manuf. Technol. 12, 18 (2009)
A. Safdar, L.Y. Wei, A. Snis, Z. Lai, Mater. Charact. 65, 8 (2012)
S.L. Lu, H.P. Tang, Y.P. Ning, N. Liu, D.H. Stjohn, M. Qian, Metall. Mater. Trans. A 46, 3824 (2015)
L.E. Murr, E.V. Esquivel, S.A. Quinones, S.M. Gaytan, M.I. Lopez, E.Y. Martinez, F. Medina, D.H. Hernandez, E. Martinez, J.L. Martinez, S.W. Stafford, D.K. Brown, T. Hoppe, W. Meyers, U. Lindhe, R.B. Wicker, Mater. Charact. 60, 96 (2009)
Z. Zhao, J. Chen, S. Guo, H. Tan, X. Lin, W.D. Huang, J. Mater. Sci. Technol. 33, 675 (2017)
X. Feng, S. Peng, Y.J. Ma, J.F. Lei, X.H. Wu, Y.Y. Cui, R. Yang, Chin. J. Nonferrous Met. 23, s462 (2013)
S.R. Dey, A. Hazotte, E. Bouzy, S. Naka, Acta Mater. 53, 3783 (2005)
K.S. Ravichandran, Acta Metall. Mater. 39, 401 (1991)
K.S. Chan, C.C. Wojcik, D.A. Koss, Metall. Mater. Trans. A 12, 1899 (1981)
M.R. Bach, W.J. Evans, V. Randle, R.J. Wilson, Mater. Sci. Eng. A 257, 139 (1998)
Y. Takahashi, M. Tanaka, K. Higashida, K. Yamaguchi, H. Nonguchi, Acta Mater. 58, 1972 (2010)
K. Prasad, S.V. Kamat, J. Alloys Compd. 491, 237 (2010)
M. Toyosada, K. Gotoh, Int. J. Fatigue 26, 983 (2004)
Y. Xiong, X.X. Hu, Int. J. Fatigue 30, 67 (2008)
J. Pokluda, R. Pippan, Mater. Sci. Eng. A 462, 355 (2007)
Y.J. Ma, J.R. Liu, J.F. Lei, Y.Y. Liu, R. Yang, Chin. J. Nonferrous Met. 10, 1789 (2009)
Y.J. Ma, J.W. Li, J.F. Lei, Z.Y. Tang, Y.Y. Liu, R. Yang, Acta Metall. Sin. 46, 1086 (2010). (in Chinese)
H.P. Tang, J. Wang, C.N. Song, N. Liu, L. Jia, J. Elambasseril, M. Qian, JOM 69, 466 (2017)
Acknowledgements
This work was supported partially by MoST project (2017YFC1104900, 2016YFC1102601), National Natural Science Foundation of China (51271182, 51631007).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Liu, Y., Zhang, J., Li, SJ. et al. Effect of HIP Treatment on Fatigue Crack Growth Behavior of Ti–6Al–4V Alloy Fabricated by Electron Beam Melting. Acta Metall. Sin. (Engl. Lett.) 30, 1163–1168 (2017). https://doi.org/10.1007/s40195-017-0665-5
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-017-0665-5