Low-temperature solution process for preparing flexible transparent carbon nanotube film for use in flexible supercapacitors

  • Research Article
  • Published:
Nano Research Aims and scope Submit manuscript

Abstract

Single-walled carbon nanotubes (SWNTs) possess high conductivity, mechanical strength, transparency, and flexibility, and are thus suitable for use in flexible electronics, transparent electrodes, and energy-storage and energy-harvesting applications. However, to exploit these properties, SWNTs must be de-bundled in a surfactant solution to permit processing and use. We report a new method to prepare a SWNT-based transparent conducting film (TCF) using the diazo dye 3,3′-([1,1′-biphenyl]-4,4′-diyl)bis(4-amino naphthalene-1-sulfonic acid), commonly known as Congo red (CR), as a dispersant. Uniform 20-nm-thick TCFs were prepared on rigid glass and flexible polyethylene terephthalate (PET) substrates. The CR-SWNT dispersion and the CR-SWNT TCFs were characterized via UV-Vis-NIR, Raman spectroscopy, FT-IR spectroscopy, transmission electron microscopy (TEM), field-emission scanning electron microscopy (FE-SEM) and dynamic light scattering (DLS) measurements. The sheet resistivity of the CRSWNT TCF was ~34 ± 6.6 Ω/□ with a transmittance of 81% at 550 nm, comparable to that of indium tin oxide-based films. Unlike SWNT dispersions prepared in common surfactants, such as sodium dodecyl sulfate (SDS), sodium cholate (SC), and Triton X-100, the CR-SWNT dispersion was amenable to forming TCF by drop coating. The CR-SWNT TCF was also very stable, maintaining a very low sheet resistivity even after 1,000 consecutive bending cycles of 8 mm bending radius. Further, manganese dioxide (MnO2) was electrochemically deposited on the CR-SWNT-PET film (MnO2-CR-SWNT-PET). The as-prepared MnO2-CR-SWNT-PET electrode exhibited high specific capacitance and bendability, demonstrating promise as a candidate electrode material for flexible supercapacitors.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Ellmer, K. Past achievements and future challenges in the development of optically transparent electrodes. Nat. Photonics 2012, 6, 809–817.

    Article  Google Scholar 

  2. Angmo, D.; Krebs, F. C. Flexible ITO-free polymer solar cells. J. Appl. Polym. Sci. 2013, 129, 1–14.

    Article  Google Scholar 

  3. Lewis, J. Material challenge for flexible organic devices. Mater. Today 2006, 9, 38–45.

    Article  Google Scholar 

  4. Ghaffarzadeh, K.; Das, R. Transparent Conductive Films (TCF) 2014–2024: Forecasts, Markets, Technologies; DTechEx: London, 2014.

    Google Scholar 

  5. Hecht, D. S.; Hu, L. B.; Irvin, G. Emerging transparent electrodes based on thin films of carbon nanotubes, graphene, and metallic nanostructures. Adv. Mater. 2011, 23, 1482–1513.

    Article  Google Scholar 

  6. Xia, Y. J.; Sun, K.; Ouyang, J. Y. Solution-processed metallic conducting polymer films as transparent electrode of optoelectronic devices. Adv. Mater. 2012, 24, 2436–2440.

    Article  Google Scholar 

  7. Kiruthika, S.; Gupta, R.; Rao, K. D. M.; Chakraborty, S.; Padmavathy, N.; Kulkarni, G. U. Large area solution processed transparent conducting electrode based on highly interconnected Cu wire network. J. Mater. Chem. C 2014, 2, 2089–2094.

    Article  Google Scholar 

  8. Guo, C. F.; Sun, T. Y.; Liu, Q. H.; Suo, Z. G.; Ren, Z. F. Highly stretchable and transparent nanomesh electrodes made by grain boundary lithography. Nat. Commun. 2014, 5, 3121.

    Google Scholar 

  9. Hsu, P.-C.; Wu, H.; Carney, T. J.; McDowell, M. T.; Yang, Y.; Garnett, E. C.; Li, M.; Hu, L. B.; Cui, Y. Passivation coating on electrospun copper nanofibers for stable transparent electrodes. ACS Nano 2012, 6, 5150–5156.

    Article  Google Scholar 

  10. Liu, Q. F.; Fujigaya, T.; Cheng, H. M.; Nakashima, N. Freestanding highly conductive transparent ultrathin single-walled carbon nanotube films. J. Am. Chem. Soc. 2010, 132, 16581–16586.

    Article  Google Scholar 

  11. Ho, X. N.; Wei, J. Films of carbon nanomaterials for transparent conductors. Materials 2013, 6, 2155–2181.

    Article  Google Scholar 

  12. De Volder, M. F. L.; Tawfick, S. H.; Baughman, R. H.; Hart, A. J. Carbon nanotubes: Present and future commercial applications. Science 2013, 339, 535–539.

    Article  Google Scholar 

  13. Rösner, B.; Guldi, D. M.; Chen, J.; Minett, A. I.; Fink, R. H. Dispersion and characterization of arc discharge single-walled carbon nanotubes - Towards conducting transparent films. Nanoscale 2014, 6, 3695–3703.

    Article  Google Scholar 

  14. Mistry, K. S.; Larsen, B. A.; Bergeson, J. D.; Barnes, T. M.; Teeter, G.; Engtrakul, C.; Blackburn, J. L. n-Type transparent conducting films of small molecule and polymer amine doped single-walled carbon nanotubes. ACS Nano 2011, 5, 3714–3723.

    Article  Google Scholar 

  15. Wang, J.; Zhang, J. T.; Sundramoorthy, A. K.; Chen, P.; Chan-Park, M. B. Solution-processed flexible transparent conductors based on carbon nanotubes and silver grid hybrid films. Nanoscale 2014, 6, 4560–4565.

    Article  Google Scholar 

  16. Yang, S. B.; Kong, B. S.; Jung, D. H.; Baek, Y. K.; Han, C. S.; Oh, S. K.; Jung, H. T. Recent advances in hybrids of carbon nanotube network films and nanomaterials for their potential applications as transparent conducting films. Nanoscale 2011, 3, 1361–1373.

    Article  Google Scholar 

  17. Park, S.; Vosguerichian, M.; Bao, Z. A. A review of fabrication and applications of carbon nanotube film-based flexible electronics. Nanoscale 2013, 5, 1727–1752.

    Article  Google Scholar 

  18. Wang, X. H.; Tao, L.; Hao, Y. F.; Liu, Z. H.; Chou, H.; Kholmanov, I.; Chen, S. S.; Tan, C.; Jayant, N.; Yu, Q. K. et al. Direct delamination of graphene for high-performance plastic electronics. Small 2014, 10, 694–698.

    Article  Google Scholar 

  19. Wang, P.-C.; Liu, L.-H.; Alemu Mengistie, D.; Li, K.-H.; Wen, B.-J.; Liu, T.-S.; Chu, C.-W. Transparent electrodes based on conducting polymers for display applications. Displays 2013, 34, 301–314.

    Article  Google Scholar 

  20. Hu, L. B.; Kim, H. S.; Lee, J.-Y.; Peumans, P.; Cui, Y. Scalable coating and properties of transparent, flexible, silver nanowire electrodes. ACS Nano 2010, 4, 2955–2963.

    Article  Google Scholar 

  21. Dürkop, T.; Getty, S. A.; Cobas, E.; Fuhrer, M. S. Extraordinary mobility in semiconducting carbon nanotubes. Nano Lett. 2003, 4, 35–39.

    Article  Google Scholar 

  22. Yao, Z.; Kane, C. L.; Dekker, C. High-field electrical transport in single-wall carbon nanotubes. Phys. Rev. Lett. 2000, 84, 2941–2944.

    Article  Google Scholar 

  23. Zhang, D. H.; Ryu, K.; Liu, X. L.; Polikarpov, E.; Ly, J.; Tompson, M. E.; Zhou, C. W. Transparent, conductive, and flexible carbon nanotube films and their application in organic light-emitting diodes. Nano Lett. 2006, 6, 1880–1886.

    Article  Google Scholar 

  24. Yim, J. H.; Kim, Y. S.; Koh, K. H.; Lee, S. Fabrication of transparent single wall carbon nanotube films with low sheet resistance. J. Vac. Sci. Technol. B 2008, 26, 851–855.

    Article  Google Scholar 

  25. Tyler, T. P.; Brock, R. E.; Karmel, H. J.; Marks, T. J.; Hersam, M. C. Electronically monodisperse single-walled carbon nanotube thin films as transparent conducting anodes in organic photovoltaic devices. Adv. Energy Mater. 2011, 1, 785–791.

    Article  Google Scholar 

  26. Tenent, R. C.; Barnes, T. M.; Bergeson, J. D.; Ferguson, A. J.; To, B.; Gedvilas, L. M.; Heben, M. J.; Blackburn, J. L. Ultrasmooth, large-area, high-uniformity, conductive transparent single-walled-carbon-nanotube films for photovoltaics produced by ultrasonic spraying. Adv. Mater. 2009, 21, 3210–3216.

    Article  Google Scholar 

  27. Jung, H.; Yu, J. S.; Lee, H. P.; Kim, J. M.; Park, J. Y.; Kim, D. Ascalable fabrication of highly transparent and conductive thin films using fluorosurfactant-assisted single-walled carbon nanotube dispersions. Carbon 2013, 52, 259–266.

    Article  Google Scholar 

  28. Yang, S. B.; Kong, B. S.; Jung, H. T. Multistep deposition of gold nanoparticles on single-walled carbon nanotubes for high-performance transparent conducting films. J. Phys. Chem. C 2012, 116, 25581–25587.

    Article  Google Scholar 

  29. Tkalya, E. E.; Ghislandi, M.; de With, G.; Koning, C. E. The use of surfactants for dispersing carbon nanotubes and graphene to make conductive nanocomposites. Curr. Opin. Colloid Interface Sci. 2012, 17, 225–231.

    Article  Google Scholar 

  30. Kymakis, E.; Amaratunga, G. A. J. Electrical properties of single-wall carbon nanotube-polymer composite films. J. Appl. Phys. 2006, 99, 084302.

    Article  Google Scholar 

  31. Rahman, R.; Servati, P. Effects of inter-tube distance and alignment on tunnelling resistance and strain sensitivity of nanotube/polymer composite films. Nanotechnology 2012, 23, 055703.

    Article  Google Scholar 

  32. Geng, H.-Z.; Kim, K. K.; So, K. P.; Lee, Y. S.; Chang, Y.; Lee, Y. H. Effect of acid treatment on carbon nanotubebased flexible transparent conducting films. J. Am. Chem. Soc. 2007, 129, 7758–7759.

    Article  Google Scholar 

  33. Jin, R.; Zhou, Z. X.; Mandrus, D.; Ivanov, I. N.; Eres, G.; Howe, J. Y.; Puretzky, A. A.; Geohegan, D. B. The effect of annealing on the electrical and thermal transport properties of macroscopic bundles of long multi-wall carbon nanotubes. Phys. B 2007, 388, 326–330.

    Article  Google Scholar 

  34. Zhang, Q. H.; Vichchulada, P.; Shivareddy, S. B.; Lay, M. D. Reducing electrical resistance in single-walled carbon nanotube networks: Effect of the location of metal contacts and low-temperature annealing. J. Mater. Sci. 2012, 47, 3233–3240.

    Article  Google Scholar 

  35. Guo, H.-L.; Wang, X.-F.; Qian, Q.-Y.; Wang, F.-B.; Xia, X.-H. A green approach to the synthesis of graphene nanosheets. ACS Nano 2009, 3, 2653–2659.

    Article  Google Scholar 

  36. Dumitrescu, I.; Wilson, N. R.; Macpherson, J. V. Functionalizing single-walled carbon nanotube networks: Effect on electrical and electrochemical properties. J. Phys. Chem. C 2007, 111, 12944–12953.

    Article  Google Scholar 

  37. Lobez, J. M.; Han, S.-J.; Afzali, A.; Hannon, J. B. Surface selective one-step fabrication of carbon nanotube thin films with high density. ACS Nano 2014, 8, 4954–4960.

    Article  Google Scholar 

  38. Nirmalraj, P. P. N.; Lyons, P. E.; De, S.; Coleman, J. N.; Boland, J. J. Electrical connectivity in single-walled carbon nanotube networks. Nano Lett. 2009, 9, 3890–3895.

    Article  Google Scholar 

  39. Hu, C. G.; Chen, Z. L.; Shen, A. G.; Shen, X. C.; Li, J.; Hu, S. S. Water-soluble single-walled carbon nanotubes via noncovalent functionalization, by arigid, planar and conjugated diazo dye. Carbon 2006, 44, 428–434.

    Article  Google Scholar 

  40. Lu, X. H.; Yu, M. H.; Wang, G. M.; Tong, Y. X.; Li, Y. Flexible solid-state supercapacitors: Design, fabrication and applications. Energy Environ. Sci. 2014, 7, 2160–2181.

    Article  Google Scholar 

  41. Fei, H. J.; Yang, C. Y.; Bao, H.; Wang, G. C. Flexible allsolid- state supercapacitors based on graphene/carbon black nanoparticle film electrodes and cross-linked poly(vinyl alcohol)–H2SO4 porous gel electrolytes. J. Power Sources 2014, 266, 488–495.

    Article  Google Scholar 

  42. Peng, L. L.; Peng, X.; Liu, B. R.; Wu, C. Z.; Xie, Y.; Yu, G. H. Ultrathin two-dimensional MnO2/graphene hybrid nanostructures for high-performance, flexible planar supercapacitors. Nano Lett. 2013, 13, 2151–2157.

    Article  Google Scholar 

  43. Wu, C. Z.; Lu, X. L.; Peng, L. L.; Xu, K.; Peng, X.; Huang, J. L.; Yu, G. H.; Xie, Y. Two-dimensional vanadyl phosphate ultrathin nanosheets for high energy density and flexible pseudocapacitors. Nat. Commun. 2013, 4, 2431.

    Google Scholar 

  44. Liu, F.; Song, S. Y.; Xue, D. F.; Zhang, H. J. Folded structured graphene paper for high performance electrode materials. Adv. Mater. 2012, 24, 1089–1094.

    Article  Google Scholar 

  45. Nyholm, L.; Nyström, G.; Mihranyan, A.; Strømme, M. Toward flexible polymer and paper-based energy storage devices. Adv. Mater. 2011, 23, 3751–3769.

    Google Scholar 

  46. Li, H.; Zhao, Q.; Wang, W.; Dong, H.; Xu, D. S.; Zou, G. J.; Duan, H. L.; Yu, D. P. Novel planar-structure electrochemical devices for highly flexible semitransparent power generation/storage Sources. Nano Lett. 2013, 13, 1271–1277.

    Article  Google Scholar 

  47. Miller, J. R. Valuing reversible energy storage. Science 2012, 335, 1312–1313.

    Article  Google Scholar 

  48. Ge, J.; Cheng, G. H.; Chen, L. W. Transparent and flexible electrodes and supercapacitors using polyaniline/single-walled carbon nanotube composite thin films. Nanoscale 2011, 3, 3084–3088.

    Article  Google Scholar 

  49. He, S. J.; Chen, W. High performance supercapacitors based on three-dimensional ultralight flexible manganese oxide nanosheets/carbon foam composites. J. Power Sources 2014, 262, 391–400.

    Article  Google Scholar 

  50. Cai, W. H.; Lai, T.; Dai, W. L.; Ye, J. S. A facile approach to fabricate flexible all-solid-state supercapacitors based on MnFe2O4/graphene hybrids. J. Power Sources 2014, 255, 170–178.

    Article  Google Scholar 

  51. Shi, C. L.; Zhao, Q.; Li, H.; Liao, Z.-M.; Yu, D. P. Low cost and flexible mesh-based supercapacitors for promising large-area flexible/wearable energy storage. Nano Energy 2014, 6, 82–91.

    Article  Google Scholar 

  52. Li, W. Y.; Xu, K. B.; Li, B.; Sun, J. Q.; Jiang, F. R.; Yu, Z. S.; Zou, R. J.; Chen, Z. G.; Hu, J. Q. MnO2 nanoflower arrays with high rate capability for flexible supercapacitors. ChemElectroChem 2014, 1, 1003–1008.

    Article  Google Scholar 

  53. Cole, D. P.; Reddy, A. L. M.; Hahm, M. G.; McCotter, R.; Hart, A. H. C.; Vajtai, R.; Ajayan, P. M.; Karna, S. P.; Bundy, M. L. Electromechanical properties of polymer electrolytebased stretchable supercapacitors. Adv. Energy Mater. 2014, 4, 1300844.

    Article  Google Scholar 

  54. Seo, J. W. T.; Yoder, N. L.; Shastry, T. A.; Humes, J. J.; Johns, J. E.; Green, A. A.; Hersam, M. C. Diameter refinement of semiconducting arc discharge single-walled carbon nanotubes via density gradient ultracentrifugation. J. Phys. Chem. Lett. 2013, 4, 2805–2810.

    Article  Google Scholar 

  55. Sundramoorthy, A. K.; Mesgari, S.; Wang, J.; Kumar, R.; Sk, M. A.; Yeap, S. H.; Zhang, Q.; Sze, S. K.; Lim, K. H.; Chan-Park, M. B. Scalable and effective enrichment of semiconducting single-walled carbon nanotubes, by adual selective naphthalene-based azo dispersant. J. Am. Chem. Soc. 2013, 135, 5569–5581.

    Article  Google Scholar 

  56. Li, J. B.; Huang, Y. X.; Chen, P.; Chan-Park, M. B. In situ charge-transfer-induced transition from metallic to semiconducting single-walled carbon nanotubes. Chem. Mater. 2013, 25, 4464–4470.

    Article  Google Scholar 

  57. Mesgari, S.; Sundramoorthy, A. K.; Loo, L. S.; Chan-Park, M. B. Gel electrophoresis using a selective radical for the separation of single-walled carbon nanotubes. Faraday Discuss. 2014, 173, 351–363.

    Article  Google Scholar 

  58. Zhang, W.; Silva, S. R. P. Raman and FT-IR studies on dye-assisted dispersion and flocculation of single walled carbon nanotubes. Spectroc. Acta A 2010, 77, 175–178.

    Article  Google Scholar 

  59. Shin, H.-J.; Kim, S. M.; Yoon, S.-M.; Benayad, A.; Kim, K. K.; Kim, S. J.; Park, H. K.; Choi, J.-Y.; Lee, Y. H. Tailoring electronic structures of carbon nanotubes by solvent with electron-donating and -withdrawing groups. J. Am. Chem. Soc. 2008, 130, 2062–2066.

    Article  Google Scholar 

  60. Sa, V.; Kornev, K. G. Analysis of stability of nanotube dispersions using surface tension isotherms. Langmuir 2011, 27, 13451–13460.

    Article  Google Scholar 

  61. Matarredona, O.; Rhoads, H.; Li, Z. R.; Harwell, J. H.; Balzano, L.; Resasco, D. E. Dispersion of single-walled carbon nanotubes in aqueous solutions of the anionic surfactant NaDDBS. J. Phys. Chem. B 2003, 107, 13357–13367.

    Article  Google Scholar 

  62. Li, F. H.; Bao, Y.; Chai, J.; Zhang, Q. X.; Han, D. X.; Niu, L. Synthesis and application of widely soluble graphene sheets. Langmuir 2010, 26, 12314–12320.

  63. Frid, P.; Anisimov, S. V.; Popovic, N. Congo red and protein aggregation in neurodegenerative diseases. Brain Res. Rev. 2007, 53, 135–160.

    Article  Google Scholar 

  64. Mirri, F.; Ma, A. W. K.; Hsu, T. T.; Behabtu, N.; Eichmann, S. L.; Young, C. C.; Tsentalovich, D. E.; Pasquali, M. Highperformance carbon nanotube transparent conductive films by scalable dip coating. ACS Nano 2012, 6, 9737–9744.

    Article  Google Scholar 

  65. Gao, H. J.; Izquierdo, R.; Truong, V. V. Chemical vapor doping of transparent and conductive films of carbon nanotubes. Chem. Phys. Lett. 2012, 546, 109–114.

    Article  Google Scholar 

  66. Dupont, M. F.; Donne, S. W. Nucleation and growth of electrodeposited manganese dioxide for electrochemical capacitors. Electrochim. Acta 2014, 120, 219–225.

    Article  Google Scholar 

  67. Le, W.-Z.; Liu, Y.-Q.; Hu, G.-Q. Preparation of manganese dioxide modified glassy carbon electrode, by anovel film plating/cyclic voltammetry method for H2O2 detection. J. Chil. Chem. Soc. 2009, 54, 366–371.

    Google Scholar 

  68. Aboutalebi, S. H.; Chidembo, A. T.; Salari, M.; Konstantinov, K.; Wexler, D.; Liu, H. K.; Dou, S. X. Comparison of GO, GO/MWCNTs composite and MWCNTs as potential electrode materials for supercapacitors. Energy Environ. Sci. 2011, 4, 1855–1865.

    Article  Google Scholar 

  69. Feng, L.; Xuan, Z.; Zhao, H.; Bai, Y.; Guo, J.; Su, C.-W.; Chen, X. MnO2 prepared by hydrothermal method and electrochemical performance as anode for lithium-ion battery. Nanoscale Res. Lett. 2014, 9, 290.

    Article  Google Scholar 

  70. Xu, C. J.; Li, B. H.; Du, H. D.; Kang, F. Y.; Zeng, Y. Q. Electrochemical properties of nanosized hydrous manganese dioxide synthesized, by aself-reacting microemulsion method. J. Power Sources 2008, 180, 664–670.

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Biological Systems Engineering, University of Wisconsin-Madison, 460 Henry Mall, Madison, WI, 53706, USA

    Ashok K. Sundramoorthy, Yi-Cheng Wang & Sundaram Gunasekaran

Authors
  1. Ashok K. Sundramoorthy
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Yi-Cheng Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Sundaram Gunasekaran
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Sundaram Gunasekaran.

Electronic supplementary material

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sundramoorthy, A.K., Wang, YC. & Gunasekaran, S. Low-temperature solution process for preparing flexible transparent carbon nanotube film for use in flexible supercapacitors. Nano Res. 8, 3430–3445 (2015). https://doi.org/10.1007/s12274-015-0880-1

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12274-015-0880-1

Keywords

Search

Navigation