Abstract
The effects of a rare-earth element on the microstructure, mechanical properties, and whisker growth of Sn-58Bi alloys and solder joints in ball grid array (BGA) packages with Ag/Cu pads have been investigated. Mechanical testing indicated that the elongation of Sn-58Bi alloys doped with Ce increased significantly, and the tensile strength decreased slightly, in compar- ison with undoped Sn-58Bi. In addition, the growth of both fiber- and hillock-shaped tin whiskers on the surface of Sn-58Bi-0.5Ce was retarded in the case of Sn-3Ag-0.5Cu-0.5Ce alloys. The growth of interfacial intermetallic compounds (IMC) in Sn-58Bi-0.5Ce solder joints was slower than that in Sn-58Bi because the activity of Ce atoms at the interface of the Cu6Sn5 IMC/solder was reduced. The reflowed Sn-58Bi and Sn-58Bi-0.5Ce BGA packages with Ag/Cu pads had a ball shear strength of 7.91 N and 7.64 N, which decreased to about 7.13 N and 6.87 N after aging at 100°C for 1000 h, respectively. The reflowed and aged solder joints fractured across the solder balls with ductile characteristics after ball shear tests.
Similar content being viewed by others
References
W.J. Tomlinson and I. Collier, J. Mater. Sci. 22, 1835 (1987).
J. Zhou, D. Huang, Y.L. Fang, and F. Xue, J. Alloys. Compd. 480, 903 (2009).
G.D. Li, Y.W. Shi, H. Hao, Z.D. Xia, Y.P. Lei, and X.Y. Li, J. Mater. Sci.: Mater. Electron. 20, 186 (2009).
D.Q. Yu, J. Zhao, and L. Wang, J. Alloys. Compd. 376, 170 (2004).
L. Wang, D.Q. Yu, J. Zhao, and M.L. Huang, Mater. Lett. 56, 1039 (2002).
C.M.L. Wu, D.Q. Yu, C.M.T. Law, and L. Wang, J. Electron. Mater. 31, 921 (2002).
C.M.L. Wu, D.Q. Yu, C.M.T. Law, and L. Wang, J. Electron. Mater. 31, 928 (2002).
W.M. Xiao, Y.W. Shi, G.C. Xu, R. Ren, F. Guo, Z.D. Xia, and Y.P. Lei, J. Alloys. Compd. 472, 198 (2009).
Y.W. Shi, J. Tian, H. Hao, Z.D. Xia, Y.P. Lei, and F. Guo, J. Alloys. Compd. 453, 180 (2008).
M.A. Dudek, R.S. Sidhu, N. Chawla, and M. Renavikar, J. Electron. Mater. 35, 2088 (2006).
M.A. Dudek and N. Chawla, Metall. Mater. Trans. 41A, 610 (2010).
T.H. Chuang and S.F. Yen, J. Electron. Mater. 35, 1621 (2006).
T.H. Chuang, Metall. Mater. Trans. 38A, 1048 (2007).
T.H. Chuang and H.J. Lin, Metall. Mater. Trans. 39A, 2862 (2008).
T.H. Chuang and H.J. Lin, J. Electron. Mater. 38, 420 (2009).
C.M.L. Wu, D.Q. Yu, C.M.T. Law, and L. Wang, Mater. Sci. Eng. R 44, 1 (2004).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chuang, TH., Wu, HF. Effects of Ce Addition on the Microstructure and Mechanical Properties of Sn-58Bi Solder Joints. J. Electron. Mater. 40, 71–77 (2011). https://doi.org/10.1007/s11664-010-1385-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-010-1385-z