Abstract
The effect of rare-earth element (cerium salt) and organic acid (citric acid) on the anodic oxide film obtained in phosphoric acid and their synergistic mechanism in the anodizing process were studied. The results show that the synergistic effect of cerium salt and citric acid in anodization of phosphoric acid can reduce surface defects, improve its microstructure and properties of the anodic oxide film. With the analysis of EDAX and XPS, the hydroxide of cerium salt was deposited on the film surface. It is deduced that cerium salt takes part in the formation of oxide film directly on the synergistic effect of citric acid.
Similar content being viewed by others
References
Thompson GE, Wood GC (1981) Nature 290:230
Chou SM, Leidheiser H Jr (1986) Ind Eng Chem Prod Res 25:473
Kobayashl K, Shimizu K (1988) J Electrochem Soc 135:908
Patermerakis G, Moussoutzanis K (1995) J Electrochem Soc 142:737
Rigbyetal WR (1990) Trans Inst Metal Finish 68:95
All-Mawlawi D, Lin CZ, Moskovits M (1994) J Mater Res 9:1014
All-Mawlawi D, Douketis C, Bigioni T, Moskovits M, Routkevitch D, Ryan L, Haslett T, Williams A, Xu JM (1995) J Electrochem Soc 95:262
Wang Y (1993) Surf Eng 9:151
Hinton BR, Amott OR, Ryan NE (1986) Mater Forum 9:162
Mansfeld F, Kim L, Shih H (1987) Corros Sci 27:997
Mansfeld F, Calif V, Shih H et al (1993) US5194138, Mar 1993
Ruagta (1994) Rare earth. US Patent, 5362335, Nov 8, 1994
Wang B (1991) Rare Earth 12:24
Yang ZL (1998) Mat Pro 7:6
The School of Chemistry of Wuhan University (1981) Science Publishing Company, p 44
Hinton BRW, Arnott DR (1984) Metals Forum 7:211
Acknowledgements
This work was supported by the Nano-Tech Special Foundation of Shanghai Scientific and Technical Committee under Grant number 0352nm034.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, H., Wang, HW. Synergistic effect of rare earth salt and organic acid in the anodization of aluminum in phosphoric acid. J Mater Sci 41, 4759–4763 (2006). https://doi.org/10.1007/s10853-006-0046-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0046-3