Abstract
A new family of electrochemical cells for decomposition of NO gas in the presence of excess O2, in which the cathode was covered with mixed oxide layer of NiO and YSZ (electro-catalytic electrode) were designed and investigated. The deNO x properties were increased by microstructural and compositional control of the electro-catalytic electrode. Nano-size Ni grains were self-assembled at NiO/YSZ interfaces by oxidation-reduction reaction of the NiO during the cell operation. In order to use the reduced Ni for NO decomposition reaction effectively, the authors investigated multilayering of the electro-catalytic electrode. Through this process, the adsorption of coexisting O2 was prevented and the deNO x properties of the electrochemical cell were improved.
Similar content being viewed by others
References
T. Hibino, Chem. Lett., 927 (1994).
J. Nakatani, Y. Ozeki, K. Sakamoto, and K. Iwayama, Chem. Lett., 315 (1996).
T. Hibino, T. Inoue, and M. Sano, Solid State Ionics, 130, 19 (2000).
T. Hibino, T. Inoue, and M. Sano, Solid State Ionics, 130, 31 (2000).
S. Bredikhin, K. Maeda, and M. Awano, Solid State Ionics, 144, 1 (2001).
S. Bredikhin, K. Maeda, and M. Awano, J. Electrochem. Soc., 148, D133 (2001).
S. Bredikhin, K. Matsuda, K. Maeda, and M. Awano, Solid State Ionics, 149, 327 (2002).
A. Aronin, G. Abroshimova, S. Bredikhin, K. Matsuda, K. Maeda, and M. Awano, J. Ceram. Soc. Jpn., 110, 722 (2002).
K. Matsuda, S. Bredikhin, K. Maeda, and M. Awano, Solid State Ionics, 156, 223 (2003).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hiramatsu, T., Bredikhin, S.I., Katayama, S. et al. High Selective deNO x Electrochemical Cell with Self-Assembled Electro-Catalytic Electrode. J Electroceram 13, 865–870 (2004). https://doi.org/10.1007/s10832-004-5205-9
Received:
Revised:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10832-004-5205-9