Abstract
MXenes have recently been recognized as potential materials based on their unique physical and chemical characteristics. The widely growing family of MXenes is rapidly expanding their application domains since their first usage as energy materials was reported in 2011. The inherent chemical nature, high hydrophilicity, and robust electrochemistry regard MXenes as a promising avenue for environment-remediation technologies such as adsorption, membrane separation, photocatalysis and the electrocatalytic sensor designed for pollutant detection. As the performance of MXenes in these technologies is on a continuous path to improvement, this review intends to cumulatively discuss the diversity and chemical abilities of MXenes and their hybrid composites in the fields mentioned above with a focus on MXenes improving surface-characteristics. The review is expected to promote the diversity of MXenes and their hybrid configuration for advanced technologies widely applied for environmental remediation.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.1 Introduction
The rapid advancement in global industrialization has raised severe environmental concerns [1, 2]. Here, the release of industrial waste effluent without proper treatment is one of the primary causes of environmental pollution. The large volume of contaminated effluent contains a mixture of toxic azo dyes, pesticides, and heavy metals from various industries related to coloring, printing, plastics, leather, food, and pharmaceuticals [3, 4]. In general, environmental pollutants could be classified as organic and inorganic, where toxic heavy metals and dyes are the primary sources of water contamination. The pharmaceutical residues and chemical toxins are another emerging class of environmental pollutants, which have shown deteriorating behaviour towards human life. Thus, removing such contaminants using a safe, chemically practical, and environmentally friendly approach is a priority. Among the prominent technologies, adsorption [5], membrane separation [6], photocatalysis [7], and the electrocatalytic sensor systems [8], designed mainly for capturing, isolating, degrading, and detecting the environmental pollutants/toxins, are considered as practical and economically viable remediation technologies.
To date, a variety of materials such as polymers, carbon-based materials, metals, and metal oxides have been considered for developing robust adsorbent, photocatalyst, or sensing platform for the technologies mentioned above [9, 10]. In this context, MXenes, a new family of transition metal carbides/nitrides, have gained significant scientific attention based on their unique 2D surface characteristics, high hydrophilicity, and surface-functionalization ability. Since the first report on MXenes, i.e., Naguib et al., more than 30 different MXene members have been successfully synthesized and reported for their intrinsic characteristics [11, 12]. In general, MXenes have a representative formula of Mn+1XnTx, where "M" denotes a transition metal, "X" can be a carbon (C) or nitride (N), n = 1∼3, and Tx represents the associated surface functionality (like –OH, –F, –O) [13,14,15]. These surface functionalities have strong relevance to the physical and chemical properties of MXene materials, which further influence their potential in surface-interactive applications such as adsorption or membrane separation. Unlike graphene with low hydrophilicity, MXenes offer high hydrophilicity and activity towards ion-exchange and redox process due to their surface functionalities. Furthermore, the 2D structure, coupled with robust redox ability, have recognized MXenes’ potential in engineering photocatalyst and electrocatalytic sensors for the degradation and the detection of environmental contaminants [16,17,18]. The rapid development of MXenes in the environmental remediation and detection technologies calls for an objective understanding of the influence of their surface-related properties on the final performance of MXene-based hybrids.
This review discusses the growing fame of MXenes and their hybrids in environmental remediation application, starting with adsorption and membrane separation extending to photocatalysis, with the last section attributed to MXene-based electrocatalytic sensors designed particularly for the identification and quantification of toxins. Figure 1 shows a doughnut chart generalizing the wide-spectrum application of MXenes in these technologies. The discussion is based on the MXenes’ decisive surface characteristics as pristine or in a composite configuration, with the last section dedicated to the conclusion and future-perspective of MXenes in environmental remediation technologies.
2 MXenes in chemical adsorption of pollutants
2.1 Chemical adsorbents of dyes
Dyes, which are essential components in textile, paper, and printing industries, despite their practical usage, poses a severe threat to the ecosystem and causes water contamination. Thus, the removal of these dyes is an essential and urgent demand when it comes to environmental remediation. To date, numerous methods have been developed to remove such dyes, and among them, adsorption is the most promising route based on its low cost and preparative applicability. The high specific surface area, negatively charged surface, layered structure, high hydrophilicity have recognized MXenes as ideal adsorbent materials to remove dyes.
The efficient adsorption cationic dyes, such as methylene blue (MB), by multilayered MXene, i.e., ML-Ti3C2Tx, were first reported by Mashtalir’s group [19]. The report described the adsorptive properties of ML-Ti3C2Tx MXene against a cationic and an anionic dye, i.e., MB and acid blue 80 (AB80), respectively. The results revealed that MB could irreversibly be bonded to Ti3C2Tx (with an adsorption capacity of ∼39 mg g−1), while AB80 showed negligible adsorption capability towards MXene. The preferential adsorption of the cationic dye over anionic dye was attributed to the electrostatic interactions between the positively charged dye and the negatively charged MXene surface. The adsorption behaviour of dyes over alkali-treated MXenes was later studied by Wei et al. [20]. The authors utilized a facile approach to expand the interlayer spacing and tune the surface functional groups of Ti3C2Tx using hot alkaline solution treatment. The interlayer spacing of Ti3C2Tx MXene was expanded 29%, and all the –F surface functional groups were transformed to –OH. The alkali treatment enhanced the adsorption capability and accelerated the removal rate of MB dye. Among the treated MXenes, LiOH-Ti3C2Tx and NaOH-Ti3C2Tx demonstrated the fastest absorption of MB with NaOH-Ti3C2Tx achieving the highest adsorption capacity of 189 mg g−1. The high adsorption capability was ascribed to the synergism of surface functionalization and enlarged inter-layer adsorption with Langmuir as the standard adsorption model. Moreover, Li et al. [21] reported the chemical modification of MXene with polymers for dye adsorption. Here, MXene-based core–shell composite denoted as MXene-COOH@(PEI/PAA)n, was prepared from chemically-modified MXene using a layer-by-layer (LbL) self-assembly approach, as shown in Fig. 2a. The pristine MXene was firstly treated with ClCH2COOH to form carboxyl-modified MXene material (MXene-COOH). Then, the MXene-COOH was subjected to polyethene polyimide (PEI) and poly(acrylic acid) (PAA) in a stepwise manner to create a bilayer polymer overcoat around the MXene-COOH via a self-assembly process under electrostatic interactions. The SEM and TEM images presented in Fig. 2b–g indicate the formation of an overcoat-like layer on MXene after polymer’s coupling. The MXene-COOH@(PEI/PAA)n with abundant chemical moieties and hierarchical core-cell structure allowed efficient adsorption of three kinds of dyes, i.e., safranine T (ST, 33.76 mg g−1), neutral red (NR, 42.50 mg g−1), and MB (36.69 mg g−1) (Fig. 2h–m).
a Schematic illustration of the fabrication of the MXene-COOH@(PEI/PAA)n composite. b–g SEM and TEM images of MXene, MXene-COOH, and the composite. h–m Adsorption capacities and rate constants for MXene, MXene-COOH, and the composite for MB, ST, and NR dyes at 298 K respectively. Reprint with permission[21]:
In another study, Peng et al. [22] developed a new approach to synthesize 2D MXenes, including Ti3C2 and Nb2C, via the solvothermal treatment of sodium tetrafluoroborate (NaBF4) and hydrochloric acid. Here, NaBF4 reacted with HCl, resulting in an in-situ production of HF, which enabled etching of the MAX phase precursors, i.e., Ti3AlC2 and Nb2AlC. The produced MXenes (h-Ti3C2 and h-Nb2C) possessed superior specific surface area to those prepared using the traditional HF etching method. The h-Ti3C2 achieved a high MB adsorption capacity of 189 mg g−1, whereas h-Nb2C showed relatively weaker adsorption towards MB and no adsorption capacity towards methylene orange (MO). It could be explained based on Nb larger atomic mass (92.9) compared to Ti (47.8). Cai et al. [23] transformed 2D Ti3C2Tx-MXene into the rod-like architecture by modifying the pristine MXene with phytic acid (PA) under hydrothermal conditions. In this case, PA was coupled with the MXene to improve the overall amphiphilicity based on its surface interactive groups, and the hydrothermal reaction time defined the rod-like morphology of the MXene. The PA-MXene composite exhibited enhanced adsorption properties for MB and Rhodamine B (RhB) dyes, with an adsorption capacity of 42 and 22 mg. g−1 with 85 and 84% capacity retention after continuous 12 cycles of adsorption, respectively. The use of MXenes in the removal of colored dyes is an area of growing interest. However, there is still room to explore, particularly in the selective removal of pigments based on the surface charge engineering of MXenes.
2.2 Chemical adsorbent of toxic ions
Heavy metal ions are the most dangerous environmental pollutants due to their non-degradable and persistent nature. The long-lasting toxicities of heavy metal ions are effective even at low concentrations, making them high-risk pollutants that require immediate attention. The presently employed techniques that are considered efficient in removing such metal ions include chemical precipitation, filtration, adsorption, and electro-dialysis [24]. In comparison to dyes, whose concentration is relatively high in aquatic systems, removing metal ions is challenging due to their low concentrations (ppm to ppb). However, the methods based on biological processes or chemical reactions are usually ineffective at low concentrations. Thus, the engineered adsorbent needs to be cost-effective and efficient enough to capture toxic metal ions at the ppb level.
MXenes and their derivatives with abundant surface functionalities and large surface areas are considered as potential adsorbents for heavy metal cations. Several reports indicate MXenes have strong adsorption towards various heavy metal ions. Peng et al. [25] developed a functional 2D Ti3C2Tx-MXene material by an exfoliation and alkalization-intercalation method for Pb ions adsorption. The obtained MXene exhibited a preferential Pb (II) sorption behaviour in the presence of competing cations such as Ca (II)/Mg (II) at high concentrations. The kinetics data confirmed that the sorption equilibrium was achieved in a short duration of 120 s. The MXene could achieve an efficient Pb (II) uptake with a sorption capacity of 4500 kg water per alk-MXene. The experimental and computational modelling confirmed the sorption behaviour to primarily rely on the -OH groups and the activated Ti sites in the MXene, which facilitated the Pb (II) ion-exchange.
In regard to water contaminants, the chromium ion Cr (VI) is another toxic and carcinogenic ion. Ying et al. [26] utilized 2D Ti3C2Tx nanosheets to remove toxic Cr(VI) from water. The complete exfoliation with suitable sheet morphology of the MXene was achieved with 10% HF etchant (Fig. 3a, b). In this case, the Ti3C2Tx nanosheets were efficient in removing Cr (VI) with an adsorption capacity of 250 mg g–1. Figure 3c, d shows that the Cr (VI) removal efficiency relied directly on the content of MXene and pH of the system, whereas the adsorption was based on the charge-interactions between the positively charge chromium and MXene, as depicted in Fig. 3e. The Cr (VI) residual concentration in the treated water effluent was less than 5 ppb, which was relatively low compared to the standard value of 0.05 ppm.
a SEM, b TEM, c dosage effect of the Ti3C2Tx on Cr (VI) removal with insert showing corresponding photo with change in color visible in in the case of 0.4 g; d Influence of pH on the Cr (VI) removal efficiency of MXenes; e schematic of the charge-interaction based mechanism for the removal of Cr(VI) using Ti3C2Tx nanosheets. Reprint with permission [26]:
MXene derivatives can also be used as an adsorbent to the Zou et al. [27] reported an MXene-derived urchin-like rutile TiO2-C (u-RTC) composite for Cr(VI) removal. In this case, in situ phase transformation of MXene was carried under FeCl3 conditions. First, a layered anatase TiO2–C (l-ATC) nanocomposite with dense (001) facets forms, which then transforms to u-RTC subsequent to Fe (III) ion induction. The MXene-derived u-RTC achieved a high Cr (VI) adsorption capacity of ∼225 mg g−1, which was much greater than the pristine MXene (∼62 mg g−1) and its l-ATC precursor (∼11 mg g−1). The first-principles calculations revealed that the bridging oxo-groups within the hybrid system could effectively inhibit the adsorption of H2O molecules, thus leading to a high Cr (VI) adsorption capacity. Fard et al. [28] reported the use of MXene for the adsorption of barium ions. In this case, pristine MXene nanosheets demonstrated extraordinary efficiency in removing barium ions with a capacity of 9.3 mg g−1 with a removal efficiency reaching up to 100% under the optimum conditions.
The performance of 2D Ti3C2Tx MXene nanosheets for the adsorptive removal of copper ions from aqueous media was also investigated [29]. The delaminated-Ti3C2Tx showed a high capability to adsorb Cu2+ based on its 2D-layer configuration, large specific surface area, and hydrophilicity. Here, the oxygenated moieties on MXenes were responsible for the reductive adsorption of Cu2+. Moreover, the Ti3C2Tx exhibited a higher and faster Cu2+ uptake than the multilayer-Ti3C2Tx, reflecting the importance of layer thickness. The maximum adsorption capacity, in this case, was 78.45 mg g–1, where 80% of the total Cu ions were adsorbed within 1 min. In terms of commercial competitiveness, the adsorption capacity of the delaminated-Ti3C2Tx was 2.7 times higher than activated carbon. Shahzad et al. [30] used a Fe2O3/MXene nanocomposite for the adsorption of mercuric ions (Hg(II)). The nanocomposite removed the Hg (II) in a wide pH range with an exceptional uptake capacity of 1128.41 mg g−1. The adsorption behaviour was well-fitted to Redlich-Peterson adsorption isotherm, with adsorption behaviour following pseudo-second-order kinetics.
MXenes, based on their surface-active groups, have also been considered effective against other toxic ions. Among many, the excessive discharge of phosphates into the aqueous system could result in eutrophication. In this context, Zhang et al. [31] prepared a sandwiched structural MXene-iron oxide (MXI) composite by the intercalation of magnetic ferric oxide into MXene. The MXI composite exhibited remarkable applicability for trace phosphate sequestration. Compared to the commercial adsorbents, the MXI composite showed a fast separation of 120 s, together with the superior treatment capacities of 2100 and 2400 kg g−1 in simulated and real phosphate wastewater, respectively. The efficient sequestration was ascribed to the formation of a unique nano-ferric oxide morphology, where ultrafine nano-Fe2O3 particles could intercalate into the interior layers of MXene, enlarging the interlayer distance and stimulating the available overlapping activated layers. Pandey et al. [32] utilized Ti3C2Tx MXene in chemical reduction and removal of bromate ions (BrO3−), which are toxic if present in drinking water. Its Ti–C active layer could reduce bromate to bromide while transforming to TiO2 nanocrystals. The reduction performance of the Ti3C2Tx nanosheets was affected by the concentration of MXene, contact time, pH, and temperature of the system. This system allowed excellent bromate uptake (∼321.8 mg g−1) within 50 min at pH 7 and 25 °C.
The specific uptake capacities of MXenes and MXene-based composites and derivatives towards dyes and ionic pollutants are listed in Table 1. Although the MXene-based materials are promising candidates for removing the toxic ions, there are still major challenges, such as the restacking of MXene layers and selective adsorption of toxic ions from a complex matrix require immediate attention before such material could be anticipated as commercial sorbents.
2.3 Chemical adsorbent of radioactive ions
The radioactive ions are produced after the radioactive nuclides are consumed at the nuclear power plant or other nuclear-related technologies such as mining or medical research [33]. As the leakage of the radioactive ions to the surrounding soil and groundwater becomes a serious hazard, the efficient nuclear waste treatment and environmental management are necessary. Here, MXenes, based on their surface redox-ability and tunable adsorption properties, have proven to be relatively advantageous for adsorbing radioactive heavy metal ions [34]. Wang et al. [35] demonstrated the capability of multilayered V2CTx MXene towards efficient adsorption of uranium ions U(VI) from aqueous solutions. The V2CTx exhibited an outstanding adsorption capability with U(VI) uptake capacity of 174 mg g–1, fast sorption kinetics, and desirable selectivity. The DFT calculation suggested that the uranyl ions prefer to coordinate with the –OH groups bonded to the V-sites in the MXene nanosheets via bidentate inner-sphere complexes, reflecting the importance of the surface functionalization. In another attempt, Wang et al. [36] synthesized a series of hydrated and dry Ti3C2Tx for the fast removal of U(VI) from aqueous solutions. In comparison to the dry counterpart, the hydrated MXene showed the efficient removal of U(VI) with an adsorption capacity of 214 mg g−1, mainly due to its more flexible nature and much larger interlayer spacing. This study identified Ti3C2Tx as a promising candidate for U(VI) capture and encapsulation. In similar content, Wang et al. [37] showed the capability of 2D Ti2CTx MXene to remove uranium via a sorption-reduction strategy. The batch experiments demonstrated that the Ti2CTx could exhibit excellent U(VI) removal over a wide pH range, with an uptake capacity of 470 mg g–1 at pH 3.0. The study suggested that the Ti2CTx material could also be a potential candidate to develop permeable reactive barriers with potential applications in treating wastewaters affected by uranium mining.
Other than uranium, MXenes have also shown promising adsorption capability towards heavy-metal ions in nuclear waste such as Re (IV), Th (IV), and Eu (III). The MXene adsorption efficiency towards Re (IV) was evaluated by Wang et al. [38]. The study utilized a three-dimensional (3D) MXene-polyelectrolyte nanocomposite for the enhanced removal of perrhenate ion (ReO4−). The introduction of poly (diallyl dimethylammonium chloride) (PDDA) into Ti2CTx-MXene regulated the surface charge and improved the stability. The Ti2CTx/PDDA composite achieved a removal capacity of up to 363 mg g–1 for Re (VII) with fast sorption kinetics and good selectivity in the presence of competing anions such as Cl– and SO42– with a concentration 1800 times higher than Re (VII). Li et al. [39] investigated the performance of 2D Ti2CTx MXene for Th(IV) removal and demonstrated that the hydrated MXene had a superior adsorption capability compared to the dry-counterpart. In this case, the sorption equilibrium was achieved within 720 min, with a maximum sorption capacity of 213.2 mg g−1. The hydrated Ti2CTx exhibited an excellent selectivity over a range of competing ions, and the sorption process was highly pH-dependent with no influence from the overall ionic strength. The thorium (Th (IV)) sorption mechanism was determined to be an inner-sphere complexation originating from the strong binding affinity of Ti–OH towards Th (IV). In another study, hierarchical titanate nanostructures (HTNs) were derived from in situ chemical conversion of 2D Ti3C2Tx-MXene crystal [40]. The formed HTNs were highly stable with a sorption capacity of 200 mg g−1 for Eu (III), owing to the well-maintained layered structure and abundant exchangeable guest cations. The sequestration of Eu (III) was realized by forming inner-sphere surface complexes in the nano-confined space, as evidenced by the decrease of Eu–O distances and coordination numbers. The finding of the inner-sphere complexation induced by Ti − O/Ti − OH coordination and confinement effect provided new insights into the interaction mechanism between radionuclides and titanates.
2.4 MXenes in membrane separation of pollutants
Membrane separation technology is a practical route for desalination and wastewater treatment. The ideal desalination and water treatment membranes should have high flux, high selectivity, stability, and resistance against fouling and chlorine-like chemicals [41]. The membrane should also be thin enough with sufficient mechanical stability to maximize water permeability with a constant salt rejection rate. At present, 2D carbon nanomaterials, such as graphene and graphene oxide (GO), are promising materials with molecular and ionic sieving capability. Although suitable for many applications, the flux of GO membranes is relatively small due to the reduced interlayer spacing under pressure. Here, MXenes, with the tunable surface chemistry and manageable interlayer spacing, have been proven to be highly practical.
The MXene-based water treatment membrane was firstly reported by Ren et al. [42]. The membrane was produced using a vacuum-assisted filtration method, where 2D Ti3C2Tx MXene nanosheets were assembled into a freestanding membrane. Unlike graphene or GO, the high hydrophilicity of Ti3C2Tx allows the presence of interlayer H2O, which promotes ultrafast water flux. The produced membrane was nonpermeable to cations with hydration radii larger than the MXene interlayer spacing (∼6 Å), and had good selectivity toward positively charged metal cations (like Li+, Na+, K+, Mg2+, Ca2+, Ni2+, and Al3+), and methylthioninium+ (MB+) dye cations. The proposed micrometer-thick membrane could reach 37.4 L m−2 h−1 bar−1 water flux with different sieving capabilities based on the target ions' hydration radius and charge.
Ding et al. [43] reported the use of porous MXene membrane, prepared using vacuum filtration with Fe(OH)3 nanoparticles as template (Fig. 4a). The obtained MXene membrane supported on anodic aluminum oxide substrate showed excellent water permeance of more than 1000 L m−2 h−1 bar−1 with a rejection rate of over 90% for molecules with sizes larger than 2.5 nm (Fig. 4b, c). The performance of the MXene-based membrane was superior to other membranes with a similar rejection rate.
a Schematic diagram depicting the assembly of porous MXene membrane with Fe (OH)3 nanoparticles as template. b analytical comparison of M1, M2, and MXene membranes projected for EB molecules; c separation efficiency of MXene membranes estimated for various molecules of different sizes. Reprint with permission [43].
GO-based membranes have proven their potential in gas and liquid separations. Improved performance could be achieved by coupling GO with MXene nanosheets. Kang et al. [44] attempted to integrate GO and MXene to prepare a 90 nm thick Ti3C2Tx–GO composite membrane. After swelling, the prepared membrane’s lattice period was 14.28 Å, which corresponds to the interlayer spacing of around 5 Å, capable of allowing two layers of water molecules. The composite membrane effectively rejected the dye molecules with hydrated radii above 5 Å and the positively charged dye molecules during pressure-driven filtration at 5 bar. The layer configuration enabled the assembled membrane to achieve an excellent rejection rate of 68% for methyl red, 99.5% for MB, 93.5% for rose Bengal, and 100% for brilliant blue (hydrated radii of 4.87, 5.04, 5.88, and 7.98 Å, respectively). This study paved a new pathway to produce efficient separation membranes based on composite interlayer engineering. In this context, Han et al.[45] prepared an MXene-coated polyether sulfone (PES) ultrafiltration membrane with 0.2 MPa for dye desalination and wastewater treatment. The configured composite membrane had rough and dense surface layers and uniform element distribution. Interestingly, the rejection rates of dyes and inorganic salts relied on the integrated content of MXene. At optimum conditions, high rejection rates to Congo red dye (CR) (92.3%) and gentian violet (80.3%) were obtained, respectively, with a high flux of 115 L m−2 h−1 at 0.1 MPa. However, the rejection rate of the inorganic salts was lower than 23% with flux above 432 L m−2 h−1 at 0.1 MPa due to the loose lamellar structure of the composite membranes.
In another attempt to further improve the antifouling properties and increase the water flux of the MXene membrane, Pandey et al. [46] reported Ag nanoparticles-modified 2D Ti3C2Tx MXene (Ag@MXene) as an ultrafast water purification membrane. The Ag@MXene composite membranes with variable Ag loadings (0 ~ 35%) were prepared using self-reduction of silver nitrate on MXene sheets. The optimum performance of the Ag@MXene membrane was achieved when the thickness and average pore size was about 470 and 2.1 nm, respectively. The membrane exhibited an outstanding water flux of ∼420 L m−2 h−1 bar−1, which was relatively higher compared to its pristine counterpart. Also, the Ag@MXene membrane achieved favourable rejection to organic foulants like bovine serum albumin (100%), methyl green (92.3%) and RhB (79.9%), indicating its suitability for practical application.
MXene-based membranes have also been explored for air filtration. Gao et al. [47] reported a 2D MXene nanosheet-modified PAN fiber membrane for air purification. The introduction of Ti3C2 MXene nanosheets in PAN fiber enhanced the PM2.5 removal efficiency to ∼99.7% with a low-pressure drop of ∼42 Pa, together with the antibacterial activity. The high PM 2.5 removal efficiency can be ascribed to the large surface and accessible terminations of the MXene nanosheets, allowing fast and abundant adsorption of PM2.5 particles based on the strong interactive forces.
Table 2 summarizes the water purification performances of the MXene-based membranes. Although there are promising outcomes, specific challenges are still needed to overcome before MXenes could reach their full-potential in water and air filtration. The most crucial concern is the swelling of MXene, similar to any other 2D material, which is a limiting factor for the filtration of multiple-ions with diverse sizes at the same time. Moreover, this further influences the stability and recyclability of MXene-based films. Interlayer engineering is an efficient approach to overcome this issue where the adjustment of channel size by controlling the d-spacing of MXenes can allow the control of swelling and avoid structural collapse. This could promote the development of MXene-based membranes with high selectivity, extreme cyclability, and good capability to filter-out a wide range of pollutants.
2.5 MXenes in photocatalytic degradation of pollutants
Photocatalytic degradation of organic pollutants is a promising environmental remediation technology. To date, several photoactive semiconductors, such as TiO2 [48], g-C3N4 [49], and CdS [50], have shown promising activity towards photodegradation of various organic pollutants. Although efficient, the photoexcited charge carrier’s fast recombination in these single semiconductor photocatalysts limits their practical application. Here, MXenes can serve as unique substrates to assemble advanced co-catalysts to effectively alleviate the charge-carrier recombination while enhancing the photocatalysts dispersibility and adsorption capability.
Mashtalir et al. [19] reported the first use of MXenes for the degradation of MB and AB80 dyes under ultraviolet (UV) light. In the absence of light, MXenes could adsorb 18% of MB and no AB80 up to 20 h, while under 5 h of irradiation, 62, and 81% degradation was achieved, respectively. The photo-activity, in this case, was the direct consequence of TiO2 produced after partial surface oxidation of the Ti3C2Tx MXene. The TiO2 provided the photocatalytic activity, whereas the under layered Ti3C2 served as an adsorbent bed, contributing to fast charge transport. Subsequently, the TiO2/Ti3C2 composites have been widely studied for photocatalytic application. Gao et al. [51] fabricated a TiO2/Ti3C2 composite for the photocatalytic degradation of MO dye. The composite exhibited an excellent photodegradation capability, where 98% of MO was completely mineralized in 30 min. Also, Peng et al. [52] prepared an MXene/TiO2 composite, in which TiO2 (001) facets were obtained via partial oxidation of Ti3C2 assisted by NaBF4. Here, Ti3C2 acted as a precursor to TiO2 and an active component to construct Schottky-junction with the (001) surface of the n-type semiconductor (TiO2). Under illumination, the heterojunction realized an ultra-low work function with spatial separation of photogenerated charge-carrier, achieving a photocatalytic degradation rate of 18.8 min−1 g−1 for MO dye. The same group [53] later reported a (111) TiO2-x/Ti3C2 nanocomposite, in which Ti3+-doped rutile TiO2 octahedrons with exposed active (111) facets were derived from 2D Ti3C2 sheets using hydrothermal oxidation followed by reduction via hydrazine hydrate (Fig. 5a, b). The 2D Ti3C2 served as a pathway for transferring photogenerated holes to promote the charge separation efficiency (Fig. 5c, d), whereas the exposed TiO2 (111) maximized the photocatalytic ability of the TiO2/Ti3C2 composite. The hybrid achieved enhanced MB dye degradation under visible light (75% of MB in 150 min). The TiO2/MXene composite has also been utilized for the photocatalytic degradation of pharmaceutical pollutant known as carbamazepine (CBZ) [54], which achieved a 98.67% degradation efficiency in 4 h. The kinetics of the photocatalytic reaction was determined to follow Langmuir–Hinshelwood kinetic model with a Kapp value of 0.0304 min−1 at pH 3.0.
a Schematic of the formation of (111) TiO2-x/Ti3C2 nanocomposite with b the crystallographic orientations of rod-like and octahedral rutile. c Photogenerated charge carrier transfer mechanism and d the corresponding band alignments. Reprint with permission [53].
The charge carrier recombination is a major limitation in semiconductor-based photocatalyst, restricting their long-term use in the photocatalytic degradation process. Here, the construction of heterojunction of semiconductor photocatalyst with other co-catalyst in a cascade-type configuration can readily minimize this charge-carrier recombination while improving the production efficiency of free radicals (˙O2− and ˙OH), that are responsible for the mineralization of the target pollutant. In regard to CuO based photocatalyst, Lu et al.[55] proposed coupling of CuO with Ti3C2/TiO2 system to construct an efficient Ti3C2/TiO2/CuO heterojunction. The composite was prepared by decomposing a mixture of Ti3C2 MXene and cupric nitrate under an argon atmosphere, which later realized 99% degradation efficiency for MO dye in 80 min. Similarly, Wojciechowski et al. [56] studied the photocatalytic degradation of salicylic acid (SA) using the composites that were prepared using a combination of Ti2C MXene and metal oxide (such as TiO2, Ag2O, and PdO) and metal (like Ag, Pd, and Au) nanoparticles. Unexpectedly, the modification of MXene with noble metal nanoparticles did not bring any significant improvement besides serving as metal centers to accept electrons from the conductive band of TiO2 particles that were previously embedded in MXenes to produce Ti2C/TiO2/Ag2O composites. The highest SA degradation (95.8%) was achieved after 180 min of irradiation in the configuration of Ti2C/3%TiO2/1%Ag2O.
The complete conversion of Ti-based MXenes into TiO2@C composites has also been reported for the photocatalytic activity. Li et al. [57] fabricated TiO2@C nanosheets by high-energy ball milling of 2D Ti2CTx. In this case, Ti2CTx served as a titanium and carbon source, and the formed TiO2 nanoparticles were uniformly distributed on the single- or few-layered carbon sheets. Unlike the pristine TiO2 and photocatalytic standard (P25), the TiO2@C nanosheets exhibited enhanced photocatalytic degradation of MB dye with a degradation efficiency of 85.7% in 360 min.
Metal sulfides are another major group of abundant and cheap minerals that have been coupled with MXenes to curb the charge-carrier recombination and achieve the high photocatalytic activity. Wang et al. [58] constructed a quasi-core–shell In2S3/TiO2@Ti3C2Tx heterostructure hybrid. The hybrid with a Ti3C2Tx content of 16 mg achieved an improved visible-light photocatalytic activity towards MO dye (92.1% MO in 60 min) with a degradation rate of 0.04977 min−1, which was 3.2 and 6.2 fold higher compared to pure In2S3 and pristine Ti3C2Tx, respectively. Also, Liu et al. [59] developed a 2D CdS@Ti3C2@TiO2 nanohybrid using a facile hydrothermal process, which exhibited significantly enhanced visible-light-driven (λ ≥ 420 nm) degradation of sulfachlorpyridazine (SCP), and several dye contaminants (100% for RhB, MB, SCP, and phenol in 60, 88, 88, and 150 min, respectively).
Besides TiO2 derived from Ti-based MXenes, other photocatalysts have also been used to combine with MXenes to fabricate advanced co-catalyst materials. CeO2 is a widely studied photocatalyst with limited solar spectrum utilization. In this context, Zhou et al. [60] synthesized a CeO2/Ti3C2 nanocomposite by coupling well-dispersed CeO2 nanorods with Ti3C2 sheets under a hydrothermal process. Compared to its pristine counterparts, the composite exhibited an enhanced photocatalytic activity for the photodegradation of RhB under UV-light irradiation, where 75% of RhB was degraded within 90 min.
Hematite (α-Fe2O3) is an attractive photocatalyst due to its accessibility, magnetic properties, corrosion resistance, low cost, and visible light absorption ability. Zhang et al. [61] prepared an α-Fe2O3/Ti3C2 MXene composite using an ultrasonic-assisted self-assembly approach. In this case, 2D α-Fe2O3 nanosheets were anchored to the Ti3C2 MXene, constructing a heterostructure with high visible absorption capability and ultrahigh degradation efficiency of 98% in 120 min for MB dye.
The ferrite-based materials are a promising family of photocatalyst, but their inherent narrow-bandgap limits their light absorption and photocatalytic ability. In this regard, Tariq et al. [62] doped Gd3+ and Sn4+ within BiFeO3 (Bi1–xGdxFe1–y Sny; BGFSO), and then combined with 2D Ti3C2Tx-MXene to improve the overall surface area and construct a charge-transfer network. The BGFO-20Sn/MXene nanohybrid demonstrated 100% photocatalytic degradation ability towards CR dye in 120 min with minimum charge-carrier recombination. Similarly, Iqbal et al. [63] hybridized a La, Mn-codoped BiFeO3 with Ti3C2Tx using a sol–gel method. The constructed composite delivered 92% degradation of CR dye just within 10 min under visible light irradiation. The spinel ferrites (such as CuFe2O4) are another type of photocatalyst known for their high plasticity and excellent chemical stability. However, the fast aggregation of the spinel ferrites based on their strong magnetic nature results in a diminished active site ratio. To overcome this issue, Cao et al. [64] anchored CuFe2O4 nanoparticles onto Ti3C2 MXene nanosheets using an in situ sol-hydrothermal method. The CuFe2O4/MXene photocatalyst was used for the photocatalytic degradation of pharmaceutical pollutants such as sulfamethazine (SMZ) under visible light, which achieved a degradation rate of 59.4%, with increased charge-carrier lifetime and photostability.
MXenes have also been used as promising support materials to increase light harvesting characteristics of the tungsten-based photocatalysts. Fang et al. [65] proposed an Ag2WO4/Ti3C2 composite, where the integration of the conductive Ti3C2 allowed the heterogeneous distribution of the Ag2WO4 catalyst. The Ti3C2 promptly enhanced the catalytic activity and raised the corrosion resistance ability of Ag2WO4, besides acting as a conductive substrate to improve the photoinduced charge transportation charge-carrier lifetime (34.5 μs). The Ag2WO4/Ti3C2 composite exhibited robust photocatalytic activity toward tetracycline hydrochloride (TC) and sulfadimidine (SFE) with 62.9% and 88.6% degradation efficiency, respectively. Also, Cuia et al. [66] synthesized a 2D/2D Bi2WO6/Nb2CTx hybrid photocatalyst using a simple hydrothermal process, which exhibited promising photocatalytic activity against RhB, MB, and tetracycline hydrochloride (TC-HCl). In this case, the 2D/2D interfacial configuration led to the improved separation of photogenerated carriers and degradation efficiency of 99.8, 92.7, 83.1% for RhB, MB, TC-HCl, respectively. In another case, Cai et al. [67] fabricated an Ag3PO4/Ti3C2 Schottky catalyst using a self-assembly strategy. The composite achieved a high photocatalytic rate for the degradation of 2,4-dinitrophenol, which was 2.5-fold higher than the Ag3PO4/graphene and 10 times higher than the pristine Ag3PO4. The superior photocatalytic activity, in this case, was attributed to the intimate contact between the hybrid components, and the constructed Schottky barrier was responsible for limiting the charge-carrier recombination.
Among the widely used photocatalyst, graphitic carbon nitride (g-C3N4) is a well-known metal-free catalyst with high stability and adequate bandgap. However, g-C3N4 suffers from a short charge-carrier lifetime, which leads to the gradual diminishing photocatalytic activity. In this regard, Liu et al. [68] developed a visible-light photocatalyst composed of g-C3N4 and Ti3C2 using an evaporation-induced self-assembly method. The g-C3N4/Ti3C2 composite exhibited an excellent photocatalytic activity towards pharmaceutical pollutant know as ciprofloxacin (CIP) with 100% degradation within 150 min. The degradation profile followed a pseudo-first-order kinetic, where the CIP decomposition was 2.2 folds faster than the pristine g-C3N4 under visible-light irradiation. To further improve the performance of g-C3N4/Ti3C2 composite, Ding et al. [69] suggested the integration of plasmonic particles, e.g. Ag. In this case, the layered Ti3C2 MXene acted as a supporter and reductant to produce Ag nanoparticles, which later contributed to the photogenerated electrons transportation. The constructed Schottky junction in synergism with Ag nanoparticles improved the optical absorption and electron-donating ability, making the Ag-integrated g-C3N4/Ti3C2 composite realize 81.8% degradation ability for aniline. The photodegradation performance was 4 and 8 times higher than the pristine g-C3N4 and Ti3C2, respectively.
The transformation of 2D layered MXenes into 3D macroscopic hydrogel has recently shown tremendous photocatalysis potential [70, 71]. When MXenes are assembled into hydrogel systems, they offer exciting and versatile platforms to design MXene-based soft materials with tunable properties [72]. In this regard, Chen et al. [73] reported an organics-free and straightforward strategy to construct a 3D Ti3C2Tx-based hydrogel (RTiC) using a GO-assisted self-convergence process, as shown in Fig. 6a. The hydrogel was then integrated with Eosin Y (photosensitizer) thereby allowing the composite gel to demonstrate enhanced photoactivity towards Cr(VI) and 4-Nitrophenol (4-NA), with 99.3 and 97% degradation efficiencies in 10 and 5 min, respectively (Fig. 6a–d). In addition, bismuth oxyhalides have also been coupled with MXene for improved photocatalytic performance. Cui et al. [74] used Ti3C2Tx MXene material to construct a BiOBr0.5I0.5/MXene heterostructure photocatalyst, which realized 100% and 50% degradation for RhB and phenol, respectively. Table 3 summarizes all the MXene-based photocatalysts reported for the photodegradation of the environmental pollutants.
a Fabrication process of the RTiC with photocatalytic reduction of b Cr(VI) and c 4-NA using RTiC/EY hydrogel and the powdered counterpart with d corresponding transient photocurrent spectra and e Nyquist plots from the electrochemical impedance spectroscopy. Reprint with permission [73]: copyright, 2018, American Chemical Society
The use of MXenes has also been realized in the catalytic removal/degradation of environmental pollutants without irradiation. In this case, the catalytic system is configured to improve the oxidants overall performance or reductant to achieve complete degradation or mineralization of the pollutant. In this context, Li et al. [75] proposed MXene–COOH@(PEI/PAA)n@Au composite with hierarchical core–shell structure, which exhibited high catalytic activity towards nitro compounds, such as 2-nitrophenol (2-NP) and 4-nitrophenol (4-NP), in the presence of NaBH4 (reductant). In this case, the complete degradation of 2-NP and 4-NP was achieved in 36 and 30 min, respectively. Moreover, the catalyst was highly stable with maintained catalytic ability even after 8 continuous catalytic cycles. Xie et al. [76] prepared Pd/Ti3C2Tx graphene hydrogels with a 3D interconnected porous structure using a facile two-step process. The as-prepared Pd/Ti3C2Tx graphene hydrogels had a prominent porous structure, which could easily buffer the swelling of Ti3C2Tx during the catalytic process. Therefore, the mechanically robust Pd/Ti3C2Tx graphene hydrogels exhibited high activity, easy separability, and good cyclability. In another case, Lu et al. [77] synthesized a Co3O4/Ti3C2 MXene nanocomposite using a simple solvothermal method. The Co3O4/Ti3C2 nanocomposite exhibited an outstanding degradation efficiency for MB and RhB dyes (128.91 mg g−1 of MB in 300 min, 47.076 mg g−1 of RhB in 100 min) with maintained catalytic capability for 8 consecutive catalytic cycles. Besides, Liu et al. [78] prepared a sandwich-like Co3O4/Ti3C2Tx composite via a one-pot approach, which exhibited an outstanding catalytic degradation ability towards bisphenol A (BPA) in the presence of peroxymonosulfate (PMS, oxidant). Among the optimum content, the Co3O4/MXene-20% exhibited the highest removal capability, with 95% BPA degradation within 7 min. Additionally, Yin et al. [79] proposed a Pd/Ti3C2Tx composite for the reductive degradation of nitro compounds and morin. Figure 7a shows the scheme for the self-reductive formation of Pd nanoparticles on MXene, where the growth of the Pd particles was controlled by adjusting the reaction time. The Pd/MXene composite demonstrated excellent catalytic degradation ability against 4-nitrophenol (4-NP), and nitroaniline (2-NA) in the presence of NaBH4 with the reaction rate of 0.180 and 0.089 s−1, respectively (Fig. 7b–g). The catalyst maintained its robust activity even after 8 consecutive cycles, with a conversion rate of more than 94 and 91.8% for 4-NP and 2-NA, respectively. The Pd/MXene catalyst was capable of degrading mulberry pigment (morin) (Fig. 7h–j), but in this case, the degradation efficiency was relatively low compared to that achieved for 4-NP and 2-NA. Table 4 summarizes the MXene-based catalysts without irradiation along with their analytical parameters and efficiencies.
a Scheme showing the self-reduction formation of Pd nanoparticles on MXene sheets. UV-spectra and the corresponding rate kinetic plots obtained using the Pd/MXene composite catalysts of b–d 4-nitrophenol (4-NP), e–g and nitroaniline (2-NA) and h–j morin. Reprint with permission [79].
2.6 MXenes in electrocatalytic sensors designed for pollutant detection
The detection of toxins/pollutants is the first step to environmental remediation. The electrocatalytic platform is an attractive technique for direct/indirect analysis of various contaminants based on its simplicity, university, and selectivity. The sensitivity of the electrocatalytic sensor directly relies on the catalytic component of the devised sensor. Thus, an electrocatalytic material with a robust active surface, sufficient conductivity, and high redox activity could significantly enhance the sensor's sensitivity and selectivity towards a particular toxin. Recently, MXenes have gathered substantial attention from the sensor's community based on their tunable surface chemistry, hydrophilicity, and active functionalization [80]. Additionally, MXene could comfortably be decorated/hybridized with other active components such as metal nanoparticles and carbon-based materials to achieve enhanced sensitivity and selectivity. In regard to toxic ions, Rasheed et al. [81] realized the application of 2D MXene sheets in redox-based catalytic detection of bromate ions. The spectroscopic analysis revealed that the adsorption of bromate ions over MXene sheets resulted in the simultaneous reduction of bromate and partial oxidation of MXenes. The constructed sensor exhibited robust sensitivity, with a detection limit of 41 nM for the working window of 50 nM-5 μM. The study provided evidence that MXene sheets could be directly used in redox-based sensor systems. In another case of detecting toxic metals, Cheng et al. [82] demonstrated the use of PANI-modified Ti3C2 slices for the electrochemical determination of mercury ions. The PANI-Ti3C2 composite with their co-coupling realized a linear detection range between 0.1 and 20 μgL−1 with a low detection limit of 0.017 μgL−1.
The poor electron transfer is an issue of acetylcholinesterase (AChE)-based electrocatalytic sensors for low-concentration organophosphate pesticides (OPs) detection. Jiang et al. [83] utilized MXene to construct a multi-component system, which could potentially serve as both an immobilization matrix for AChE and a conductive bed to facilitate charge transfer at the electrode interface. The devised AChE-based electrocatalytic biosensor relied on the enzymatic inhibition pathway, whereas the combination of Ti3C2Tx nanosheets with Ag nanoparticles increased the active interfacial sites. Thus, the hybrid system showed a good affinity towards acetylthiocholine chloride (ATCl) with an apparent Michaelis–Menten constant (Kmapp) value of 257.67 μM. The catalytic sensor could detect malathion in a linear range from 10−14 to 10−8 M, with satisfactory selectivity, acceptable reproducibility, and excellent stability. The devised sensor was also applicable for detecting malathion in a real sample (tap water) with satisfactory recoveries.
In another study, Wu et al. [84] proposed the direct use of Ti3C2Tx nanosheets for the electrocatalytic detection of carbendazim (CBZ). The computational studies indicated the importance of -F termination of Ti3C2Tx in electrochemical sensing. The device could detect CBZ in a range of 50 nM to 100 µM with a low detection limit of 10.3 nM and high selectivity in the presence of fenamiphos (10 folds), ametryn (10 folds), and metal ions (50 folds). Xie et al. [85] also proposed an MXene/rGO composite for CBZ. The composite was prepared by coupling the MXene and GO in a solution system followed by the electrochemical reduction of GO to rGO (Fig. 8a). The conductive network of rGO packed with MXene layers constructed a platform with enhanced catalytic activity and improved signal production ability based on fast charge-transport pathways and increased active surface sites. Consequently, the MXene/rGO exhibited a sensitive signal response towards CBZ in a wide linear range of 2.0 nM-10.0 μM and a low detection limit of 0.67 nM (Fig. 8b–e). The configured electrocatalyst was also capable of working in the organic matrix, such as cucumber and orange juice samples.
a Schematic illustration showing the preparation steps for MXene/rGO composite and its deposition on GCE for electrocatalytic sensing of CBZ drug. b CV profiles of the composite with CBZ (5.0 μM) in 0.1 M phosphate buffered Saline (PBS) (pH 7.0) in reference to bare GCE and other compositional competitors; c the corresponding relationship of peak current and natural log of scan rate d The variation of CV scans with different scan rate in the range of 10 to 400 mVs−1 and. e DPV plots for CBZ at concentrations of 0.002, 0.007, 0.05, 0.07, 0.1, 0.3, 0.5, 0.7, 1.0, 3.0, 5.0, 7.0, 9.0 and 10.0 μM, respectively, with inset showing the corresponding linear fit calibration. Reprint with permission [85].
The MXene-based composite configurations have also been explored for detecting environmental pollutants. The high conductivity, 2D structure, large surface area, hydrophilicity and mechanical flexibility make MXenes to be a potential substrate to assemble hybrid composites [86]. In addition, the tunable surface chemistry and controlled layered structure of MXene (single or multi-layer) further allow MXene-based composites to show desirable characteristics, in favor of enhancing the sensitivity and selectivity of the sensors [87]. In this context, Huang et al. [88] utilized the MXene/MWCNT composite for the simultaneous detection of catechol (CT) and hydroquinone (HQ). The overlapping oxidation peaks of CT and HQ are a challenge when it comes to their precise detection. Here, the MXene, coupled with MWCNT, enabled separated signals for both toxins with an ultra-low detection limit of 6.6 and 3.9 nM for HQ and CT, respectively. The high conductivity and redox ability of the MXene in synergism with MWCNT enabled the selective oxidation of the CT and HQ with a significant potential difference. The devised sensor successfully detected HQ and CT in industrial wastewater with a recovery rate of 96.9 ~ 104.7% and 93.1 ~ 109.9%, respectively. Similarly, Wu et al. [89] used chitosan-modified MXene platform for the immobilization of tyrosinase, which was used to detect phenol. The 2D laminar structure and favourable functionality of the MXene enabled the chitosan molecules to be anchored easily, facilitating the immobilization of tyrosinase enzyme. The detection mechanism relied on the tyrosinase capability to oxidize phenol to o-quinone, which was later electrochemically reduced to polyhydric phenol on the electrode surface, thereby amplifying the electrocatalytic phenol signal. The fabricated MXene-based tyrosinase biosensor exhibited good analytical performance with a phenol detection range of 0.05 ~ 15.5 μmol L−1 and a detection limit of 12 nmol L−1.
Table 5 comprises the most recent reported MXene-based electrocatalytic sensors designed to detect various environmental pollutants. Although MXenes have shown promising potential in sensory devices, future investigations should be directed to anodic stabilization of MXene for the direct electrocatalytic determination of target pollutants.
3 Conclusions and perspective
Since their first discovery, MXenes, with their tunable surface chemistry, ease of functionalization, high hydrophilicity and excellent conductivity, have shown tremendous potential in multidisciplinary applications. In this review, we have outlined the recent progress of MXenes in environmental remediation applications, starting with adsorption and membrane separation, photocatalysis with their extension to electrocatalytic sensors designed particularly to detect toxins. The large surface area with the negatively charged surface has enabled MXene-based nanomaterials to exhibit promising adsorption abilities. MXene and related composites' sorption capabilities have been explored for diverse environmental applications ranging from adsorption and photocatalytic removal of toxic dyes, ions, and toxic compounds. Unlike conventional sorbents, e.g., carbon and graphene-based materials, MXenes offer ample advantages in tunable surface chemistry and high hydrophilicity, allowing easy surface-sorption of toxins.
Regarding adsorption and membrane separation, MXene sheets stability is yet a critical issue that directly influences the overall life-span of the MXene-based adsorbents. Moreover, the adsorption mechanism relies on the nature of the surface moieties. Thus, new synthetic routes and post-treatment methods could be anticipated to increase stability and induce selective sorption capability to MXene-based membranes. The use of MXenes in photocatalytic removal of pollutants requires efforts to engineer well-connected interfaces to improve photon adsorption and charge-carrier transportation. In this context, the engineered hybrids with improved interfacial arrangements and superior redox capability could produce efficient and broad-spectrum photocatalysts with robust degradation ability. The stability of MXenes is a bottle-neck issue for their application in environmental remediation technologies. The understanding of the oxidation pathways in different solvents and the subsequent lattice change of MXenes requires in-depth investigation. Moreover, the variation of the electronic structure of MXenes after doping with various metals and metal oxides to produce efficient photocatalysts should be focused on, for which the investigation approach on atomic level will be helpful.
In regards to the membrane, the control of water-flux is directly associated with MXenes flake size. Thus, both theoretical and experimental approaches should be adopted to realize an optimum flux rate with a high salt rejection rate besides revealing the underlying mechanism. The selective sorption/isolation of toxic species is another challenge for MXene-based adsorbents and membranes, which requires experimental procedures directed towards engineering MXene sheets with one type of uniform terminations. MXene-based membranes tend to swell, leading to the rejection of ions and low selectivity. Here, interlayer engineering to tune the d-spacing of MXene sheets can be a viable route to avoid swelling or structural collapse of MXene membranes.
Among the newly emerging applications, MXenes have gained progress in the area of electrocatalytic sensory systems. Unlike graphene, which offers good conductivity at the expense of low hydrophilicity, MXenes provide superior conductivity in addition to high dispersibility, recognizing them as an ideal platform for the electrocatalytic sensor. At present, the anodic stability of MXene is an issue that hinders the direct utilization of MXene for the electrocatalytic detection of pollutants. In this regard, the coupling of MXenes with electro-active polymer to construct composites have been proven effective in detecting toxins such as heavy metal ions. The use of MXenes has also been reported for enzyme-based sensors sensitive towards phenolic pollutants. Currently, the use of MXenes in the electrochemical sensor is still in infancy, requiring an in-depth understanding of its surface-related electrochemical behaviour. Although the integration of MXenes in electrocatalytic sensors has improved the signal sensitivity and the detection limit for various pollutants, the contribution of MXenes, in most cases, is merely limited to increase the conductivity.
In general, other MXene phases, i.e., V4C3Tx and Nb2CTx, should also be investigated for their versatility and potential in environmental remediation technologies. Moreover, research should be directed to MXene derived hybrid composites that can contribute to the advancement of environmental remediation technologies.
Availability of data and materials
Not applicable.
Abbreviations
- PEI/PAA:
-
Polyethylene polyimide /poly (acrylic acid)
- MB:
-
Methylene blue
- ST:
-
Safranine T
- NR:
-
Neutral red
- MO:
-
Methylene orange
- RhB:
-
Rhodamine B
- DL-MXene:
-
Delaminated MXene
- PDDA:
-
Poly (diallyl dimethylammonium chloride)
- HTNs:
-
Hierarchical titanate nanostructures
- PVDF:
-
Polyvinylidene difluoride
- AAO:
-
Anodic aluminum oxide
- PC:
-
Polycarbonate
- PES:
-
Polyethersulfone
- PAN:
-
Polyacrylonitrile
- BGFO-20Sn:
-
Gd and Sn co-doped bismuth ferrite BiFeO3 nanoparticles
- BLFMO:
-
La and Mn co-doped bismuth ferrite BiFeO3 nanoparticles
- CR:
-
Congo red
- MB:
-
Methyl blue
- AB80:
-
Acid blue 80
- MO:
-
Methyl orange
- CBZ:
-
Carbamazepine
- RhB:
-
Rhodamine B
- SCP:
-
Sulfachloropyridazine
- SA:
-
Salicylic acid
- 2,4-DNP:
-
2,4-Dinitrophenol
- TC-H:
-
Tetracycline hydrochloride
- TPL:
-
Thiamphenicol
- CPL:
-
Chloramphenicol
- SMZ:
-
Sulfamethazine
- SFE:
-
Sulfadimidine
- CIP:
-
Ciprofloxacin
- 4-NA:
-
4-Nitroaniline
- AChE:
-
Acetylcholinesterase
- ERGO:
-
Electrochemically reduced graphene oxide
- CT:
-
Catechol
- HQ:
-
Hydroquinone
- 2-NA:
-
Nitroaniline
- 4-NP:
-
4-Nitrophenol
References
L. Shao, G.Q. Chen, Environ. Sci. Technol. 47, 7787 (2013)
J.T. Jasper, Y. Yang, M.R. Hoffmann, Environ. Sci. Technol. 51, 7111 (2017)
T. Robinson, G. McMullan, R. Marchant, P. Nigam, Bioresour. Technol. 77, 247 (2001)
Y. Fu, T. Viraraghavan, Bioresour. Technol. 79, 251 (2001)
J. Qu, J. Environ. Sci. 20, 13 (2008)
M. Bagheri, S.A. Mirbagheri, Bioresour. Technol. 258, 318 (2018)
M.N. Chong, B. Jin, C.W. Chow, C. Saint, Water Res. 44, 2997 (2010)
S. Kempahanumakkagari, K. Vellingiri, A. Deep, E.E. Kwon, N. Bolan, K.-H. Kim, Coord. Chem. Rev. 357, 105 (2018)
Y. Zhu, S. Murali, W. Cai, X. Li, J.W. Suk, J.R. Potts, R.S. Ruoff, Adv. Mater. 22, 3906 (2010)
S.K. Fanourakis, J. Bahamonde, P.C. Bandara, D.F. Rodrigues, NPJ Clean Water 3, 1–15 (2020)
M. Naguib, O. Mashtalir, J. Carle, V.R. Presser, J. Lu, L. Hultman, Y. Gogotsi, M. Barsoum, ACS Nano 6, 1322 (2012)
M. Naguib, V.N. Mochalin, M.W. Barsoum, Y. Gogotsi, Adv. Mater. 26, 982 (2014)
B. Xu, Y. Gogotsi, Adv. Funct. Mater. 30, 2007011 (2020)
Q. Zhu, J. Li, P. Simon, B. Xu, Energy Storage Mater. 35, 630 (2021)
B. Xu, Y. Gogotsi, Chin. Chem. Lett. 31, 919 (2020)
T. Schultz, N.C. Frey, K. Hantanasirisakul, S. Park, S.J. May, V.B. Shenoy, Y. Gogotsi, N. Koch, Chem. Mater. 31, 6590 (2019)
Z. Li, Y. Wu, Small 15, 1804736 (2019)
J. Li, X. Li, B. Van der Bruggen, Environ. Sci. Nano 7, 1289 (2020)
O. Mashtalir, K.M. Cook, V.N. Mochalin, M. Crowe, M.W. Barsoum, Y. Gogotsi, J. Mater. Chem. A 2, 14334 (2014)
Z. Wei, Z. Peigen, T. Wubian, Q. Xia, Z. Yamei, S. Ming, Mater. Chem. Phys. 206, 270 (2018)
K. Li, G. Zou, T. Jiao, R. Xing, L. Zhang, J. Zhou, Q. Zhang, Q. Peng, Colloids Surf. A Physicochem. Eng. Asp. 553, 105 (2018)
C. Peng, P. Wei, X. Chen, Y. Zhang, F. Zhu, Y. Cao, H. Wang, H. Yu, F. Peng, Ceram. Int. 44, 18886 (2018)
C. Cai, R. Wang, S. Liu, X. Yan, L. Zhang, M. Wang, Q. Tong, T. Jiao, Colloids Surf. A Physicochem. Eng. Asp. 589, 124468 (2020)
C.F. Carolin, P.S. Kumar, A. Saravanan, G.J. Joshiba, M. Naushad, J. Environ. Chem. Eng. 5, 2782 (2017)
Q. Peng, J. Guo, Q. Zhang, J. Xiang, B. Liu, A. Zhou, R. Liu, Y. Tian, J. Am. Chem. Soc. 136, 4113 (2014)
Y. Ying, Y. Liu, X. Wang, Y. Mao, W. Cao, P. Hu, X. Peng, ACS Appl. Mater. Interfaces 7, 1795 (2015)
G. Zou, J. Guo, Q. Peng, A. Zhou, Q. Zhang, B. Liu, J. Mater. Chem. A 4, 489 (2016)
A.K. Fard, G. McKay, R. Chamoun, T. Rhadfi, H. Preud’Homme, M.A. Atieh, J. Chem. Eng. 317, 331 (2017)
A. Shahzad, K. Rasool, W. Miran, M. Nawaz, J. Jang, K.A. Mahmoud, D.S. Lee, ACS Sustain. Chem. Eng. 5, 11481 (2017)
A. Shahzad, K. Rasool, W. Miran, M. Nawaz, J. Jang, K.A. Mahmoud, D.S. Lee, J. Hazard. Mater. 344, 811 (2018)
Q. Zhang, J. Teng, G. Zou, Q. Peng, Q. Du, T. Jiao, J. Xiang, Nanoscale 8, 7085 (2016)
R.P. Pandey, K. Rasool, P. Abdul Rasheed, K.A. Mahmoud, ACS Sustain. Chem. Eng. 6, 7910 (2018)
R.O.A. Rahman, H.A. Ibrahium, Y.-T. Hung, Water 3, 551 (2011)
S.K. Hwang, S.-M. Kang, M. Rethinasabapathy, C. Roh, Y.S. Huh, Chem. Eng. J. 397, 125428 (2020)
L. Wang, L. Yuan, K. Chen, Y. Zhang, Q. Deng, S. Du, Q. Huang, L. Zheng, J. Zhang, Z. Chai, M.W. Barsoum, X. Wang, W. Shi, ACS Appl. Mater. Interfaces 8, 16396 (2016)
L. Wang, W. Tao, L. Yuan, Z. Liu, Q. Huang, Z. Chai, J.K. Gibson, W. Shi, Chem. Commun. 53, 12084 (2017)
L. Wang, H. Song, L. Yuan, Z. Li, Y. Zhang, J.K. Gibson, L. Zheng, Z. Chai, W. Shi, Environ. Sci. Technol. 52, 10748 (2018)
L. Wang, H. Song, L. Yuan, Z. Li, P. Zhang, J.K. Gibson, L. Zheng, H. Wang, Z. Chai, W. Shi, Environ. Sci. Technol. 53, 3739 (2019)
S. Li, L. Wang, J. Peng, M. Zhai, W. Shi, J. Chem. Eng. 366, 192 (2019)
P. Zhang, L. Wang, L.-Y. Yuan, J.-H. Lan, Z.-F. Chai, W.-Q. Shi, J. Chem. Eng. 370, 1200 (2019)
P.S. Goh, A.F. Ismail, Desalination 434, 60 (2018)
C.E. Ren, K.B. Hatzell, M. Alhabeb, Z. Ling, K.A. Mahmoud, Y. Gogotsi, J. Phys. Chem. Lett. 6, 4026 (2015)
L. Ding, Y. Wei, Y. Wang, H. Chen, J. Caro, H. Wang, Angew Chem. Int. Ed. 56, 1825 (2017)
K.M. Kang, D.W. Kim, C.E. Ren, K.M. Cho, S.J. Kim, J.H. Choi, Y.T. Nam, Y. Gogotsi, H.T. Jung, ACS Appl. Mater. Interfaces 9, 44687 (2017)
R. Han, X. Ma, Y. Xie, D. Teng, S. Zhang, RSC Adv. 7, 56204 (2017)
R.P. Pandey, K. Rasool, V.E. Madhavan, B. Aïssa, Y. Gogotsi, K.A. Mahmoud, J. Mater. Chem. A 6, 3522 (2018)
X. Gao, Z.-K. Li, J. Xue, Y. Qian, L.-Z. Zhang, J. Caro, H. Wang, J. Membr. Sci. 586, 162 (2019)
H. Tran Thi Thuong, C. Tran Thi Kim, L. Nguyen Quang, H. Kosslick, Pro. Nat. Sci.: Mater. Int. 29, 641 (2019)
B. Babu, B. Akkinepally, J. Shim, K. Yoo, Ceram. Int. 45, 15178 (2019)
S.N. Jamble, K.P. Ghoderao, R.B. Kale, Res. Chem. Intermed. 45, 1381 (2018)
Y. Gao, L. Wang, A. Zhou, Z. Li, J. Chen, H. Bala, Q. Hu, X. Cao, Mater. Lett. 150, 62 (2015)
C. Peng, X. Yang, Y. Li, H. Yu, H. Wang, F. Peng, A.C.S. Appl. Mater. Interfaces. 8, 6051 (2016)
C. Peng, H. Wang, H. Yu, F. Peng, Mater. Res. Bull. 89, 16 (2017)
A. Shahzad, K. Rasool, M. Nawaz, W. Miran, J. Jang, M. Moztahida, K.A. Mahmoud, D.S. Lee, J. Chem. Eng. 349, 748 (2018)
Y. Lu, M. Yao, A. Zhou, Q. Hu, L. Wang, J. Nanomater. 2017, 1 (2017)
T. Wojciechowski, A. Rozmyslowska-Wojciechowska, G. Matyszczak, M. Wrzecionek, A. Olszyna, A. Peter, A. Mihaly-Cozmuta, C. Nicula, L. Mihaly-Cozmuta, S. Podsiadlo, D. Basiak, W. Ziemkowska, A. Jastrzebska, Inorg. Chem. 58, 7602 (2019)
J. Li, S. Wang, Y. Du, W. Liao, Ceram. Int. 44, 7042 (2018)
H. Wang, Y. Wu, T. Xiao, X. Yuan, G. Zeng, W. Tu, S. Wu, H.Y. Lee, Y.Z. Tan, J.W. Chew, Appl. Catal. B Environ. 233, 213 (2018)
Q. Liu, X. Tan, S. Wang, F. Ma, H. Znad, Z. Shen, L. Liu, S. Liu, Environ. Sci. Nano 6, 3158 (2019)
W. Zhou, J. Zhu, F. Wang, M. Cao, T. Zhao, Mater. Lett. 206, 237 (2017)
H. Zhang, M. Li, J. Cao, Q. Tang, P. Kang, C. Zhu, M. Ma, Ceram. Int. 44, 19958 (2018)
A. Tariq, S.I. Ali, D. Akinwande, S. Rizwan, ACS omega 3, 13828 (2018)
M.A. Iqbal, S. Irfan Ali, A. Tariq, M.Z. Iqbal, S. Rizwan, Reprints 1, 0386 (2018)
Y. Cao, Y. Fang, X. Lei, B. Tan, X. Hu, B. Liu, Q. Chen, J. Hazard. Mater. 387, 122021 (2020)
Y. Fang, Y. Cao, Q. Chen, Ceram. Int. 45, 22298 (2019)
C. Cui, R. Guo, H. Xiao, E. Ren, Q. Song, C. Xiang, X. Lai, J. Lan, S. Jiang, Appl. Surf. Sci. 505, 144595 (2020)
T. Cai, L. Wang, Y. Liu, S. Zhang, W. Dong, H. Chen, X. Yi, J. Yuan, X. Xia, C. Liu, S. Luo, Appl. Catal. B Environ. 239, 545 (2018)
N. Liu, N. Lu, Y. Su, P. Wang, X. Quan, Sep. Purif. Technol. 211, 782 (2019)
X. Ding, C. Li, L. Wang, L. Feng, D. Han, W. Wang, Mater. Lett. 247, 174 (2019)
X. Xie, N. Zhang, Adv. Funct. Mater. 30, 2002528 (2020)
Y. Zhu, Z. Wu, X. Xie, N. Zhang, Pure Appl. Chem. 92, 1953 (2020)
F. Song, G. Li, Y. Zhu, Z. Wu, X. Xie, N. Zhang, J. Mater. Chem. A 8, 18538 (2020)
Y. Chen, X. Xie, X. Xin, Z.R. Tang, Y.J. Xu, ACS Nano 13, 295 (2019)
X. Shi, P. Wang, L. Lan, S. Jia, Z. Wei, J. Mater. Sci. Mater. Electron. 30, 19804 (2019)
K. Li, T. Jiao, R. Xing, G. Zou, Q. Zhao, J. Zhou, L. Zhang, Q. Peng, Green Energy Environ. 3, 147 (2018)
X. Xie, Z. Wu, N. Zhang, Chin. Chem. Lett. 31, 1014 (2020)
S. Luo, R. Wang, J. Yin, T. Jiao, K. Chen, G. Zou, L. Zhang, J. Zhou, L. Zhang, Q. Peng, ACS Omega 4, 3946 (2019)
Y. Liu, R. Luo, Y. Li, J. Qi, C. Wang, J. Li, X. Sun, L. Wang, J. Chem. Eng. 347, 731 (2018)
J. Yin, L. Zhang, T. Jiao, G. Zou, Z. Bai, Y. Chen, Q. Zhang, M. Xia, Q. Peng, Nanomaterials 9, 1009 (2019)
R.A. Soomro, S. Jawaid, Q. Zhu, Z. Abbas, B. Xu, Chin. Chem. Lett. 31, 922 (2020)
P.A. Rasheed, R.P. Pandey, K. Rasool, K.A. Mahmoud, Sens. Actuators B Chem. 265, 652 (2018)
H. Cheng, Int. J. Electrochem. Sci. 15, 2295 (2020)
Y. Jiang, X. Zhang, L. Pei, S. Yue, L. Ma, L. Zhou, Z. Huang, Y. He, J. Gao, J. Chem. Eng. 339, 547 (2018)
D. Wu, M. Wu, J. Yang, H. Zhang, K. Xie, C. Lin, A. Yu, J. Yu, L. Fu, Mater. Lett. 236, 412 (2018)
Y. Xie, F. Gao, X. Tu, X. Ma, Q. Xu, R. Dai, X. Huang, Y. Yu, A.L. Lu, J. Electrochem. Soc. 166, 1673 (2019)
R. Soomro, S. Jawaid, N. Kalawar, M. Tunesi, S. Karakus, A. Kilislioglu, M. Willander, Biosens. Bioelectron. 166, 112439 (2020)
P.K. Kalambate, N.S. Gadhari, X. Li, Z. Rao, S.T. Navale, Y. Shen, V.R. Patil, Y. Huang, Trends Anal. Chem. 120, 115643 (2019)
R. Huang, S. Chen, J. Yu, X. Jiang, Ecotoxicol. Environ. Saf. 184, 109619 (2019)
L. Wu, X. Lu, Dhanjai, Z.S. Wu, Y. Dong, X. Wang, S. Zheng, J. Chen, Biosens. Bioelectron. 107, 69 (2018)
Acknowledgements
Not applicable.
Funding
This work was financially supported by the National Natural Science Foundation of China (Grant U2004212).
Author information
Authors and Affiliations
Contributions
All authors have contributed to the writing of the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Tunesi, M.M., Soomro, R.A., Han, X. et al. Application of MXenes in environmental remediation technologies. Nano Convergence 8, 5 (2021). https://doi.org/10.1186/s40580-021-00255-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s40580-021-00255-w