Abstract
Background
Due to various environmental problems, biodegradable polymers such as poly (3-hydroxybutyrate) (PHB) have gained much attention in recent years. Purple non-sulfur (PNS) bacteria have various attractive characteristics useful for environmentally harmless PHB production. However, production of PHB by PNS bacteria using genetic engineering has never been reported. This study is the first report of a genetically engineered PNS bacterial strain with a high PHB production.
Results
We constructed a poly (3-hydroxyalkanoate) depolymerase (phaZ) gene-disrupted Rhodobacter sphaeroides HJ strain. This R. sphaeroides HJΔphaZ (pLP-1.2) strain showed about 2.9-fold higher volumetric PHB production than that of the parent HJ (pLP-1.2) strain after 5 days of culture. The HJΔphaZ strain was further improved for PHB production by constructing strains overexpressing each of the eight genes including those newly found and annotated as PHB biosynthesis genes in the KEGG GENES Database. Among these constructed strains, all of gene products exhibited annotated enzyme activities in the recombinant strain cells, and HJΔphaZ (phaA3), HJΔphaZ (phaB2), and HJΔphaZ (phaC1) showed about 1.1-, 1.1-, and 1.2-fold higher volumetric PHB production than that of the parent HJΔphaZ (pLP-1.2) strain. Furthermore, we constructed a strain that simultaneously overexpresses all three phaA3, phaB2, and phaC1 genes; this HJΔphaZ (phaA3/phaB2/phaC1) strain showed about 1.7- to 3.9-fold higher volumetric PHB production (without ammonium sulfate; 1.88 ± 0.08 g l−1 and with 100 mM ammonium sulfate; 0.99 ± 0.05 g l−1) than those of the parent HJ (pLP-1.2) strain grown under nitrogen limited and rich conditions, respectively.
Conclusion
In this study, we identified eight different genes involved in PHB biosynthesis in the genome of R. sphaeroides 2.4.1, and revealed that their overexpression increased PHB accumulation in an R. sphaeroides HJ strain. In addition, we demonstrated the effectiveness of a phaZ disruption for high PHB accumulation, especially under nitrogen rich conditions. Furthermore, we showed that PNS bacteria may have some unidentified genes involved in poly (3-hydroxyalkanoates) (PHA) biosynthesis. Our findings could lead to further improvement of environmentally harmless PHA production techniques using PNS bacteria.
Similar content being viewed by others
Background
Poly (3-hydroxyalkanoates) (PHA) are biodegradable polymers produced and accumulated in various kinds of microorganisms as a carbon and energy storage material. PHA have physical properties similar to those from conventional fossil fuel-based thermoplastics [1]. Therefore, PHA are more attractive as environmentally harmless polymers than conventional oil-based ones. Furthermore, because of existing problems with microplastic, a ban on oil-based and single-used plastics was recently approved in the European Union. From this background, the demand for PHA is expected to increase in the future.
A lot of studies on PHA production by various kinds of microorganisms have been reported so far [2,3,4,5,6]. Among these microorganisms, purple non-sulfur (PNS) bacteria may be one of the most attractive candidates for PHA production improvements due to their unique characteristics. PNS bacteria have diverse growth modes such as aerobic respiratory, anaerobic photoheterotrophic, and photolithoautotrophic growth, and can assimilate various kinds of carbon sources including sugars and organic acids. Therefore, PNS bacteria may be able to respond to various types of growth requests depending on the situation. In addition, PNS bacteria can utilize light energy for potent adenosine triphosphate synthesis, and thus can efficiently produce various materials such as hydrogen, 5-aminolevulinic acid, and PHA at high yields. Many useful chemicals, such as hydrogen, PHA, and carotenoids, can be produced simultaneously by PNS bacteria [7, 8]. Therefore, PNS bacteria is occasionally chosen as a host microorganism for PHA production [9,10,11,12,13,14]. Suzuki et al. [9] reported that when the Rhodobacter sphaeroides RV strain was grown under anaerobic, photoheterotrophic, and pH–stat conditions, the RV strain grown at weak alkaline pH (8.0 or 8.5) produced more PHB than those grown at neutral pH (7.0 or 7.5). Previously, various other growth factors were also examined such as types of substrates and light intensity [10], and this study revealed that R. sphaeroides ATCC 17023 strain preferred a carbon source of about 100 mM acetate for PHB production and more than 30 μE m−2 s−1 of light intensity for anaerobic photoheterotrophic growth. Similarly, acetate was often reported as a preferred carbon source for PHB production by other PNS bacteria [12,13,14]. Hassan et al. [11] evaluated the two-stage PHA production from palm oil mill effluent using palm oil sludge and R. sphaeroides IFO 12203 strain. Formic acid is released when palm oil is treated using sludge in the first stage, which drastically inhibits PHA production by R. sphaeroides IFO 12203 in the second stage. Sangkharak et al. isolated halotolerant R. sphaeroides E16 strain from a marine source and created its mutant strains, N20 and U7, by using mutation inducing treatments [13, 14]. The obtained N20 strain finally produced about 2.5-fold higher PHB (7.8 g l−1) than the wild type strain through growth optimization. However, genetic differences between the wild type strain and each of the mutant strains were not analyzed.
However, despite the attractive characteristics of PNS bacteria as a host microorganism for bioproduction, only a few studies about PHA including poly (3-hydroxybutyrate) (PHB) biosynthesis using genetic engineering techniques have been reported so far [15,16,17,18]. Furthermore, these studies did not focus on improving PHA production, but on describing the genetic function and PHA biosynthesis in PNS bacteria. In other words, studies aimed at improving PHA production by PNS bacteria using genetic engineering have not been reported yet.
Generally, PHA biosynthesis is promoted in carbon rich and other nutrient efficient condition [19]. Therefore, when PHA is produced from wastes containing various kinds of nutrients such as nitrogen, this nutrient rich environment may lead to a poor PHA yield. Hence, to efficiently produce PHA from wastes, purification procedures such as denitrification are needed. However, these procedures are often troublesome and costly. To overcome this problem, the development of genetic engineering approaches for the biosynthesis of PHA is important.
Therefore, we aimed to produce PHB by genetic engineering using R. sphaeroides as a host microorganism. PHB was synthesized from acetyl coenzyme A (acetyl-CoA) via catalytic reactions of three kinds of enzymes (Fig. 1). First, acetyl coenzyme A acetyltransferase (enzyme: ACAT, gene: phaA) transfers an acetyl group from one molecule of acetyl-CoA to the acetyl group of a second acetyl-CoA and produces acetoacetyl coenzyme A (acetoacetyl-CoA) and coenzyme A (CoASH). Second, acetoacetyl coenzyme A reductase (enzyme: AACR, gene: phaB) reduces the acetoacetyl group of acetoacetyl-CoA and produces (R)-3-hydroxybutanoyl coenzyme A ((R)-3-hydroxybutanoyl-CoA) using nicotinamide adenine dinucleotide phosphate (NADPH) as a cofactor. Finally, poly (3-hydroxyalkanoate) polymerase (enzyme: PHAP, gene: phaC) polymerizes several (R)-3-hydroxybutanoyl groups from (R)-3-hydroxybutanoyl-CoA molecules and produces PHB and CoASH. Synthesized PHB is degraded by poly (3-hydroxyalkanoate) depolymerase (enzyme: PHADP; gene: phaZ) as necessary, and used as a carbon source.
PHB biosynthetic pathway. First, ACAT transfers an acetyl group from one molecule of acetyl-CoA to the acetyl group of a second acetyl-CoA and produces acetoacetyl-CoA and CoASH. Second, AACR reduces the acetoacetyl group of acetoacetyl-CoA and produces (R)-3-hydroxybutanoyl-CoA. Finally, PHAP polymerizes several (R)-3-hydroxybutanoyl groups from (R)-3-hydroxybutanoyl-CoA molecules and produces PHB and CoASH. Synthesized PHB is degraded by PHADP to form (R)-3-((R)-3-hydroxybutanoyloxy) butanoate
First, we searched for the PHB biosynthetic genes in R. sphaeroides 2.4.1 genome database and found that it harbors four genes annotated as phaA (KEGG ID: RSP_0745, RSP_1354, RSP_2197, and RSP_3184); two as phaB (KEGG ID: RSP_0747 and RSP_3963), and two more as phaC (KEGG ID: RSP_0382 and RSP_1257). The function of most of these genes has not been characterized yet.
In this study, to improve PHB yield in R. sphaeroides, we constructed a phaZ (KEGG ID: RSP_0383)-disrupted strain and several strains overexpressing PHB biosynthetic genes to evaluate their effect in the synthesis of the polymer by R. sphaeroides cells.
Results
PHB production of R. sphaeroides HJ (pLP-1.2) and HJΔphaZ (pLP-1.2) strains
The volumetric PHB production of R. sphaeroides HJ (pLP-1.2) (R. sphaeroides HJ harboring intact pLP-1.2) and HJΔphaZ (pLP-1.2) (phaZ disrupted R. sphaeroides HJ harboring intact pLP-1.2) strains was measured. The PHB production of the HJΔphaZ (pLP-1.2) strain was greatly improved compared to that of its parental strain HJ (pLP-1.2), because PHB was not degraded in the mutant strain after 3 days of incubation, while the polymer was degraded in the HJ (pLP-1.2) strain cells (Fig. 2a). In addition, PHB production until 2 days was higher in the HJΔphaZ (pLP-1.2) strain than in the HJ (pLP-1.2) strain. Overall, the HJΔphaZ (pLP-1.2) strain showed about 2.9-fold higher volumetric PHB production (1.10 ± 0.03 g l−1) than that of the HJ (pLP-1.2) strain (0.38 ± 0.03 g l−1) after 5 days of incubation by losing its PHB degrading ability. Interestingly, the dry cell weight (DCW) of the HJΔphaZ (pLP-1.2) strain showed only a slight increase (2.02 ± 0.01 g l−1), when compared to the HJ (pLP-1.2) strain (1.76 ± 0.04 g l−1), whereas the percentage of PHB content was much higher in the HJΔphaZ (pLP-1.2) strain (54.2 ± 3.6%) than in its parent strain HJ (pLP-1.2) (21.8 ± 3.6%) after 5 days of incubation.
Volumetric PHB production, DCW, and PHB content of the HJ (pLP-1.2) and HJΔphaZ (pLP-1.2) strains. a Volumetric PHB production during a 5 day culturing time; b DCW after 5 days of incubation; c PHB content after 5 days of incubation. Cells were grown anaerobically at 30 °C under illumination at 8.2 W m−2 for 5 days. Three independent fermentation experiments were done. Data are presented as the mean ± standard deviation (n = 3)
PHB production of recombinant R. sphaeroides HJΔphaZ strains overexpressing PHB biosynthetic genes
The R. sphaeroides HJΔphaZ strain was used as the host strain for further improvement of PHB production by overexpressing PHB biosynthetic genes. Crude extracts of the eight recombinant strains showed higher ACAT, AACR, and PHAP activities than those of the parent strain, indicating successful expression of these genes and production of their corresponding products in the bacterial cells (Table 1).
Then, we compared the PHB production of the four recombinant HJΔphaZ strains overexpressing each one of the phaA genes with that of the parental strain HJΔphaZ (pLP-1.2). We found that after 5 days of incubation, the HJΔphaZ (phaA1) (R. sphaeroides HJΔphaZ overexpressing phaA1) strain had produced PHB at a slightly higher concentration (1.16 ± 0.01 g l−1) than the parental strain (1.10 ± 0.03 g l−1), while both the HJΔphaZ (phaA3) (R. sphaeroides HJΔphaZ overexpressing phaA3) and HJΔphaZ (phaA4) (R. sphaeroides HJΔphaZ overexpressing phaA4) strains had apparently produced more PHB (1.25 ± 0.01 and 1.22 ± 0.01 g l−1, respectively) than the HJΔphaZ (pLP-1.2) strain (Fig. 3). However, the HJΔphaZ (phaA2) (R. sphaeroides HJΔphaZ overexpressing phaA2) strain showed almost the same PHB production profile (1.13 ± 0.02 g l−1 at 5 days of incubation) compared to the HJΔphaZ (pLP-1.2) strain at each one of the time points evaluated; whereas the crude extract from the HJΔphaZ (phaA2) strain cells exhibited a higher ACAT activity than that from the HJΔphaZ (pLP-1.2) strain cells, as previously mentioned (Table 1).
Interestingly, these strains showed somewhat different results in DCW and PHB content compared to the volumetric PHB production. The HJΔphaZ (phaA3) strain showed a slightly higher DCW (2.18 ± 0.01 g l−1) than the HJΔphaZ (pLP-1.2) strain (2.02 ± 0.01 g l−1) after 5 days of incubation (Fig. 4a), while the HJΔphaZ (phaA1), HJΔphaZ (phaA2), and HJΔphaZ (phaA4) strains showed almost the same or even a slightly decreased DCW (2.02 ± 0.01, 1.96 ± 0.04, and 2.06 ± 0.06 g l−1, respectively) compared to the HJΔphaZ (pLP-1.2) strain; whereas the HJΔphaZ (phaA4) stain apparently produced a higher volumetric PHB than that of the HJΔphaZ (pLP-1.2) strain. In contrast, the PHB content of the HJΔphaZ (phaA1), HJΔphaZ (phaA2), HJΔphaZ (phaA3) and HJΔphaZ (phaA4) strains was higher (56.5 ± 0.2, 57.8 ± 0.7, 57.2 ± 0.9, and 59.4 ± 1.8% after 5 days of incubation, respectively) than that of the HJΔphaZ (pLP-1.2) strain (54.2 ± 3.6%) (Fig. 4b).
Dry cell weight and PHB content of recombinant HJΔphaZ strains. a DCW of each recombinant HJΔphaZ strain after 5 days of incubation. b PHB content of each recombinant HJΔphaZ strain after 5 days of incubation. Three independent fermentation experiments were done. Data are presented as the mean ± standard deviation (n = 3)
On the other hand, both of the HJΔphaZ (phaB1) (R. sphaeroides HJΔphaZ overexpressing phaB1) and HJΔphaZ (phaB2) (R. sphaeroides HJΔphaZ overexpressing phaB2) stains produced more PHB (1.18 ± 0.01 and 1.20 ± 0.06 g l−1) than the control HJΔphaZ (pLP-1.2) strain after 5 days of incubation (Fig. 3). These two strains showed almost the same DCW (2.08 ± 0.02 and 2.02 ± 0.02 g l−1) (Fig. 4a) and a higher PHB content (56.9 ± 0.4 and 59.6 ± 3.6%) (Fig. 4b) than those of the HJΔphaZ (pLP-1.2) strain after incubation of 5 days.
Overexpression of the phaC gene also improved PHB production, more efficiently than the overexpression of either phaA or phaB genes. Both the HJΔphaZ (phaC1) (R. sphaeroides HJΔphaZ overexpressing phaC1) and HJΔphaZ (phaC2) (R. sphaeroides HJΔphaZ overexpressing phaC2) strains produced more PHB (1.32 ± 0.02 and 1.29 ± 0.02 g l−1) (Fig. 3), and showed a higher DCW (2.12 ± 0.04 and 2.19 ± 0.09 g l−1) (Fig. 4a) and PHB content (62.2 ± 1.9 and 56.3 ± 3.5%) than the parental strain (Fig. 4b), after 5 days of incubation.
PHB production of R. sphaeroides HJΔphaZ (phaA3/phaB2/phaC1) strain at different concentrations of ammonium sulfate
From our results regarding PHB production of the recombinant HJΔphaZ strains overexpressing the predicted PHB biosynthetic genes, and because volumetric PHB production is the most important parameter for industrial mass production of PHB, we decided to overexpress phaA3, phaB2, and phaC1 genes simultaneously in the HJΔphaZ strain. The HJΔphaZ (phaA3/phaB2/phaC1) (R. sphaeroides HJΔphaZ overexpressing phaA1, phaB2, and phaC1) strain and the control HJ (pLP-1.2) and HJΔphaZ (pLP-1.2) strains were grown in AAY medium containing various concentration of ammonium sulfate (AS) as nitrogen source.
In AAY medium without AS, the HJ (pLP-1.2) strain continuously accumulated PHB (1.13 ± 0.19 g l−1 after 5 days of incubation) (Fig. 5a). In contrast, when the HJ (pLP-1.2) strain was grown in AAY medium containing AS, intracellular PHB was degraded after 3 days of incubation; PHB degradation tended to increase at higher concentration of AS (10 mM AS: 0.38 ± 0.03, 50 mM AS: 0.31 ± 0.04, and 100 mM AS: 0.26 ± 0.03 g l−1 after 5 days of incubation, respectively) (Fig. 5a). The DCW and associated PHB content of the HJ (pLP-1.2) strain were also affected by AS concentration (DCW; without AS: 2.37 ± 0.19, 10 mM AS: 1.76 ± 0.04, 50 mM AS: 1.91 ± 0.07, and 100 mM AS: 2.05 ± 0.13 g l−1 after 5 days of incubation, respectively; PHB content; without AS: 48.0 ± 2.9, 10 mM AS: 21.8 ± 2.1, 50 mM AS: 16.6 ± 2.7, and 100 mM AS: 12.8 ± 2.0% after 5 days of incubation, respectively) (Fig. 6a, b).
Volumetric PHB production of the recombinant HJ and HJΔphaZ strains at different AS concentrations. a HJ (pLP-1.2) strain grown in AAY medium with various concentrations of AS. b HJΔphaZ (pLP-1.2) strain grown in AAY medium with various concentrations of AS. c HJΔphaZ (phaA3/phaB2/phaC1) strain grown in AAY medium with various concentrations of AS. Cells were grown anaerobically at 30 °C under illumination at 8.2 W m−2 for 5 days. Three independent fermentation experiments were done. Data are presented as the mean ± standard deviation (n = 3)
DCW and PHB content of the recombinant HJ and HJΔphaZ strains at different AS concentrations. a DCW of each of the recombinant HJ and HJΔphaZ strains grown in AAY medium with various concentrations of AS after 5 days of incubation. b PHB content of each of the recombinant HJ and HJΔphaZ strains grown in AAY medium with various concentrations of AS after 5 days of incubation. Cells were grown anaerobically at 30 °C under illumination at 8.2 W m−2 for 5 days. Three independent fermentation experiments were done. Data are presented as the mean ± standard deviation (n = 3)
On the other hand, the HJΔphaZ (pLP-1.2) strain continuously accumulated PHB even when the strain was grown in AAY medium containing high concentration of AS (Fig. 5b). Though the volumetric PHB production of the HJΔphaZ (pLP-1.2) strain was apparently affected by the concentration of AS, the volumetric PHB production after 5 days of incubation was similar in each AS concentration (without AS: 1.13 ± 0.05, 10 mM AS: 1.10 ± 0.03, 50 mM AS: 1.04 ± 0.05 and 100 mM AS: 0.98 ± 0.02 g l−1 after 5 days of incubation, respectively). These different PHB accumulation profiles during the 5 days of cultivation may be caused by cell growth. DCW of the HJΔphaZ (pLP-1.2) strain grown at different AS concentration decreased as concentration increased (without AS: 2.18 ± 0.05, 10 mM AS: 2.02 ± 0.01, 50 mM AS: 1.95 ± 0.08 and 100 mM AS: 1.84 ± 0.01 g l−1 after 5 days of incubation, respectively) (Fig. 6a), whereas PHB content of the HJΔphaZ (pLP-1.2) strain was not changed by AS concentration (without AS: 51.9 ± 2.5, 10 mM AS: 53.6 ± 2.1, 50 mM AS: 53.3 ± 2.7 and 100 mM AS: 53.2 ± 0.6% after 5 days of incubation, respectively) (Fig. 6b). Therefore, PHB accumulation of the HJΔphaZ (pLP-1.2) strain was not affected by AS concentration, however the cell growth of the strain decreased by the presence of AS, and, consequently, its volumetric PHB production also decreased.
The HJΔphaZ (phaA3/phaB2/phaC1) strain produced more PHB than the HJ (pLP-1.2) and the HJΔphaZ (pLP-1.2) strains (Fig. 5c). When the HJΔphaZ (phaA3/phaB2/phaC1) strain was grown in AAY medium without AS, the strain showed a significantly high PHB accumulation (1.88 ± 0.08 g l−1 after 5 days of incubation). However, this significant PHB accumulation was suppressed in presence of AS, even when only 10 mM AS was added to AAY media (10 mM AS: 1.45 ± 0.03, 50 mM AS: 1.20 ± 0.01, 100 mM AS: 0.99 ± 0.05 g l−1 after 5 days of incubation). When the HJΔphaZ (phaA3/phaB2/phaC1) strain was grown in AAY medium containing 100 mM AS, PHB accumulation by simultaneous overexpression of phaA3, phaB2 and phaC1 was almost completely inhibited, because the volumetric PHB production profiles in AAY media containing 100 mM AS of the HJΔphaZ (phaA3/phaB2/phaC1) and HJΔphaZ (pLP-1.2) strains were almost the same. Unlike the PHB content of the HJΔphaZ (pLP-1.2), the HJΔphaZ (phaA3/phaB2/phaC1) showed decreased PHB content depending on AS concentration (without AS: 79.8 ± 6.0, 10 mM AS: 67.0 ± 1.9, 50 mM AS: 58.4 ± 0.5, and 100 mM AS: 51.7 ± 2.7% after 5 days of incubation, respectively) (Fig. 5c). These results also indicate that the presence of AS in AAY medium suppresses PHB biosynthesis. DCW of the HJΔphaZ (phaA3/phaB2/phaC1) strain also showed a growth inhibition induced by high concentrations of AS (without AS: 2.37 ± 0.08, 10 mM AS: 2.16 ± 0.06, 50 mM AS: 2.06 ± 0.03 and 100 mM AS: 1.92 ± 0.01 g l−1 after 5 days of incubation, respectively) (Fig. 6a).
Residual acetate concentrations in AAY medium may also provide worthwhile information. When recombinant strains were grown in AAY media without AS, the cells continuously consumed acetate through the 5 days of culture (Fig. 7a–c). In contrast, addition of AS to AAY medium lead to decreased acetate consumptions. Furthermore, two phaZ disrupted strains showed slightly increased acetate consumptions compared to the HJ (pLP-1.2) strain in AAY media without AS, whereas these two strains showed decreased acetate consumption compared to the parent strain in AAY medium containing AS. The PHB production profiles of the HJΔphaZ (pLP-1.2) and HJΔphaZ (phaA3/phaB2/phaC1) strains were much different, especially when cells were grown in AAY media without AS. However, the acetate consumption profiles of these two strains were very similar.
Residual acetate concentration in the media during PHB production of recombinant HJ and HJΔphaZ strains at different AS concentrations. a HJ (pLP-1.2) strain grown in AAY medium with various concentrations of AS. b HJΔphaZ (pLP-1.2) strain grown in AAY medium with various concentrations of AS. c HJΔphaZ (phaA3/phaB2/phaC1) strain grown in AAY medium with various concentrations of AS. Cells were anaerobically grown at 30 °C under illumination at 8.2 W m−2 for 5 days. Three independent fermentation experiments were done. Data are presented as the mean ± standard deviation (n = 3)
Discussion
In this study, we found eight genes presumed to be involved in PHB biosynthesis in the genome of R. sphaeroides 2.4.1, and showed that all of their gene products exhibited annotated enzyme activities (Table 1). Also, we demonstrated that many of them enhance PHB production when overexpressed (Fig. 3). Furthermore, we revealed that the disruption of phaZ also improved PHB production (Fig. 2a), especially under nitrogen rich condition (Fig. 5) due to the loss of its PHB degrading ability. This fact shows that the gene product of phaZ has PHADP activity as annotated. Generally, PHB degradation in the presence of nitrogen is observed in various other organisms, and therefore many studies on PHB production have been carried out in nitrogen limited conditions [9,10,11,12,13,14, 21, 24,25,26]. However, when phaZ is disrupted, the recombinant strain is considered to be not able to degrade PHB due to the lack of PHADP activity, even when the medium contains nitrogen, and consequently, PHB continues to be accumulated in cells. Deletion or disruption of phaZ have often employed for improving PHA production in other microorganisms [21, 24,25,26], and all of these attempts have resulted in improved PHA production. However, these studies were carried out under nitrogen limited conditions. Therefore, we have first demonstrated the effectiveness of phaZ gene disruption for enhancing PHB production under nitrogen rich conditions.
In this study, we further improved PHB production in R. sphaeroides HJ by the simultaneous overexpression of phaA3, phaB2, and phaC1 genes (Fig. 5). However, the PHB yield achieved in this study is lower than those from other PHB producing microorganisms such as Cupriavidus necator [6, 20, 21]. These microorganisms are often grown aerobically in sugars and oils as carbon sources. In contrast, in this study, R. sphaeroides strains were anaerobically and photoheterotrophically grown in a medium with an organic acid of acetate as the carbon source. Therefore, comparisons between other PHB producing microorganisms and R. sphaeroides are difficult. Indeed, R. sphaeroides grown in anaerobic and photoheterotrophic conditions apparently showed decreased DCW and PHB content compared to the cells grown in aerobic conditions [14]. In addition, optimization of growth condition such as examination of growth temperature and medium composition may further improve cell proliferation and its associated PHB production in R. sphaeroides. Indeed, some growth optimization studies practically improved the PHB yields by PNS bacteria [10, 14]. Furthermore, the characteristics of PNS bacteria mentioned above may enable us to produce PHB from wastes containing various kinds of organic compounds as nutrients, in warm outdoor conditions, and with a lot of sunlight. Our findings may lead to the development of an efficient and environmentally friendly PHB production protocol.
Unfortunately, PHB production by overexpression of genes encoding PHB synthetic enzymes was highly suppressed by the presence of nitrogen in the medium (Fig. 5c). Kranz et al. previously reported that genes involved in PHB biosynthesis in R. capsulatus were constantly expressed even when cells were grown in the presence of nitrogen [15]. Therefore, the cause of the suppression of PHB biosynthesis by nitrogen may be a posttranscriptional process. The gene expression vector pLP-1.2 used in this study has a puf promoter containing part of the bacteriochlorophyll biosynthetic and light harvesting machinery genes [22] and therefore, can highly express the gene of interest not only during anaerobic photosynthesis but also during aerobic respiration [23]. Indeed, successful production of each gene product was confirmed by assaying its activity (Table 1) even when the recombinant strains used for the enzyme assays were grown in AAY medium containing 10 mM AS. The fact that nitrogen may regulate PHB production post transcriptionally, together with the results showing that gene products activities can be detected even when the recombinant strains were grown under nitrogen rich conditions suggest that improvement of PHB yield under nitrogen rich conditions by genetic engineering may be a hard problem.
In the HJΔphaZ (pLP-1.2) strain cells, PHAP activity in crude extract was much lower than that of ACAT and AACR (Table 1). At first glance, this result indicates that PHAP, encoded by phaC, is the limiting step for PHB biosynthesis in R. sphaeroides HJ cells. However, not only the overexpression of phaC genes, but also the overexpression of phaA and phaB genes improved PHB accumulation in the R. sphaeroides HJΔphaZ (pLP-1.2) strain (Fig. 3). If PHAP were the limiting step in PHB biosynthesis in R. sphaeroides HJ cells, the overexpression of phaA and phaB genes should not improve PHB yield. In other organisms, there are several reports that phaB may be the limiting step for PHB biosynthesis [27]; results obtained in this study do not agree with these reports. Generally, enzyme activities are easily changed by various factors such as substrate supply and the presence of inhibitors. Therefore, the limiting step for PHB biosynthesis in R. sphaeroides HJ cells may also change by these various factors. Our results showing that overexpression of phaA, phaB, and phaC genes increased PHB production in R. sphaeroides HJ cells may be due to changes in the substrate supply by the overexpression of these genes themselves. Clarifying these molecular biological mechanisms may be very difficult. However, in this study, the fact that overexpression of phaA, phaB, and phaC genes is one of the effective strategies to improve PHB yield in R. sphaeroides was revealed.
We observed interesting results regarding the DCW and PHB concentrations when each strain was cultured under various concentrations of AS (Fig. 6a, b). Although the DCW from the HJΔphaZ (pLP-1.2) and HJΔphaZ (phaA3/phaB2/phaC1) strains were decreased in the presence of high concentrations of AS, HJ (pLP-1.2) showed a different profile. Similar to HJΔphaZ (pLP-1.2) and HJΔphaZ (phaA3/phaB2/phaC1) strains, the HJ (pLP-1.2) strain achieved the highest DCW level when the strain was cultured in AAY medium without AS. However, when 10 mM of AS was present in the AAY medium, the DCW of the HJ (pLP-1.2) initially decreased considerably, following which the levels increased with increasing AS concentration. The PHB content of the HJ (pLP-1.2) strain grown in 100 mM AS was very low (12.8 ± 2.0%), therefore, it was considered that most of the DCW production in the HJ (pLP-1.2) strain in the presence of 100 mM AS was caused by the bacterium itself, not including PHB. This fact implies that AS in the medium promoted bacterial growth. Generally, the growth and PHA production of bacteria are significantly affected by C/N ratio (mole of carbon per mole of nitrogen) in the growth medium [28]. Therefore, it is considered that the HJ (pLP-1.2) strain degraded PHB and used it as a carbon source in combination with high concentrations of AS as a nitrogen source. On the other hand, the HJΔphaZ (pLP-1.2) and HJΔphaZ (phaA3/phaB2/phaC1) could not use PHB as carbon source as the phaZ genes of these strains were disrupted. Therefore, added AS led to impairment of the C/N ratio in the cells of the strains with disrupted phaZ and this impaired C/N ratio may cause poor cell growth in these strains.
Generally, two different loci involved in PHB biosynthesis in bacterial genomes are known [29]. Indeed, phaA1 and phaB1, and phaC1 and phaZ are located on two loci in the R. sphaeroides genome. However, other PHB biosynthetic genes in PNS bacteria except for phaA1, phaB1, and phaC1 have not been focused so far. Searching for previous PHB biosynthesis studies on genetically engineered PNS bacteria, we found an interesting fact: R. capsulatus SB1003 did not lose its PHB biosynthesis ability even after the deletion of the phaA1 and phaB1 genes [15]. At first, we suspected that R. capsulatus SB1003 could harbor genes corresponding to phaA2, phaA3, phaA4, and phaB2. Therefore, we searched for the eight PHB biosynthetic genes of R. sphaeroides 2.4.1, overexpressed in this study, in the R. capsulatus SB1003 strain genome and found that there are no genes corresponding to phaB2 nor phaC2 (Additional file 1: Table S3). Furthermore, no genes annotated as AACR were found except for the phaB1 corresponding gene. These facts strongly imply that there must be unidentified isozymes of AACR or an alternative PHB biosynthesis pathway in R. capsulatus SB1003, like the PHB biosynthesis from fatty acids via the beta-oxidation pathway found in Pseudomonas sp. [30]. Thus, unidentified genes encoding PHB biosynthetic enzymes or alternative PHB biosynthesis pathway may also exist in other PNS bacteria.
Conclusions
In this study, we found eight genes involved in PHB biosynthesis in the genome of R. sphaeroides 2.4.1, and revealed that overexpression of these genes increased PHB accumulation in a R. sphaeroides HJ strain. In addition, we demonstrated the effectiveness of a phaZ disruption to achieve a high PHB accumulation, especially under nitrogen rich conditions. Furthermore, we showed that there is a possibility that PNS bacteria may have other still unidentified genes involved in PHB biosynthesis. Our findings could lead to further improvements of environmentally harmless PHA production methods using PNS bacteria.
Methods
Strains and media
R. sphaeroides HJ, which was isolated in a previous study [31], and R. sphaeroides 2.4.1 were used as a host strain and a source of genes, respectively. R. sphaeroides strains were routinely grown at 30 °C in ASY medium consisting of a basal medium (20 mM potassium phosphate buffer (pH 7.0), 1% (v/v) inorganic solution, 1% (v/v) vitamin solution, 0.1 g l−1 CaCl2·2H2O, 0.2 g l−1 MgSO4·7H2O), 10 g l−1 disodium succinate, 1.0 g l−1 yeast extract, and 1.25 g l−1 AS. The composition of both inorganic and vitamin solutions have been previously described [31]. For PHB production, R. sphaeroides HJ derivative strains were grown in AAY medium consisting basal medium, 100 mM sodium acetate, 1.0 g l−1 yeast extract, and 10 mM AS. Escherichia coli NovaBlue (Novagen, Darmstadt, Germany) and S17-1 strains were used for DNA manipulation and conjugation transfer, respectively. E. coli strains were aerobically grown at 37 °C in Luria-Bertani (LB) medium (10 g l−1 tryptone, 5 g l−1 yeast extract, and 10 g l−1 sodium chloride). Kanamycin (Km; 20 mg l−1), streptomycin (Sm; 20 mg l−1), spectinomycin (Spc; 20 mg l−1) and sucrose (200 g l−1) were added when necessary.
Construction of plasmids
For construction of the phaZ gene disruption vector, phaZ and Spc resistance genes (spcR) were amplified by PCR using chromosomal DNA from R. sphaeroides HJ and plasmid pHRP311 [32] as templates, with an appropriate set of primers each (Additional file 1: Table S4). The amplified DNA encoding phaZ gene was cloned between the SphI and the XbaI sites of pK18mobsacB [33] to obtain pK18ms-phaZ. Subsequently, the amplified DNA encoding spcR gene was cloned into the NotI site of phaZ gene in pK18ms-phaZ to obtain pK18ms-phaZ/spcR.
To construct gene expression vectors, phaA1, phaA2, phaA3, phaA4, phaB1, phaB2, phaC1 and phaC2 genes were amplified by PCR using chromosomal DNA of R. sphaeroides 2.4.1 as a template, with the appropriate primer sets (summarized in Additional file 1: Table S4). Each PCR product was cloned into the XbaI site of pLP-1.2 [34] using the In-Fusion® HD Cloning Kit (TaKaRa Bio, Otsu, Japan) to give pLP-1.2 derivatives. To express phaA3, phaB2 and phaC1 genes simultaneously in R. sphaeroides HJ cells, phaA3, phaB2 and phaC1 genes were amplified by PCR using primer sets: phaA3F and phaA3R2, phaB2F2 and phaB2R2, and phaC2F2 and phaC2R (Additional file 1: Table S4), using plasmids pLP-phaA3, pLP-phaB2 and pLP-phaC1 as templates, respectively. These three PCR products were cloned into the XbaI site of pLP-1.2 using In-Fusion® HD Cloning Kit (TaKaRa Bio) to give pLP-phaA3/phaB2/phaC1. All the overexpressed or disrupted genes used in this study are summarized in Table 2.
Construction of recombinant R. sphaeroides HJ strains
The pK18ms-phaZ/spcR was introduced into R. sphaeroides HJ cells using conjugative DNA transfer via E. coli S17-1 [34]. Transformants raised by homologous recombination with pK18ms-phaZ/spcR were selected using Km resistance and confirmed by PCR using the appropriate primer set. Transformants were aerobically grown in 5 ml of ASY liquid medium without antibiotics at 30 °C for 2 days. Grown cells were spread on ASY solid media containing Spc and sucrose, and aerobically grown at 30 °C for up to 3 days. The selected colony was confirmed as a phaZ disrupted strain (R. sphaeroides HJΔphaZ) by PCR using the appropriate primer set.
The different derivatives of pLP-1.2 were introduced into R. sphaeroides HJ and HJΔphaZ cells using conjugative DNA transfer via E. coli S17-1 [23]. Transformants harboring pLP-1.2 derivatives were selected using Km resistance. The E. coli and R. sphaeroides strains used in this study are summarized in Table 3.
PHB production
R. sphaeroides HJ derivative strains were aerobically grown on ASY solid media at 30 °C for 3 days. A single colony was inoculated into 5 ml of ASY liquid medium and aerobically grown at 30 °C for 3 days. Grown cells were inoculated into 20 ml of AAY liquid medium in 30 ml vials and incubated at 30 °C for 5 days. The vials, with a shell diameter of 33 mm were irradiated from the bottom with an 8.2 W/m2 of white light-emitting diode. The initial cell density (OD660) was adjusted to 0.25. The medium surface in the vial was covered with 10 ml of liquid paraffin to maintain anaerobic condition. More than three independent fermentation experiments were done for PHB production.
PHB determination
PHB accumulated in R. sphaeroides cells was determined as previously reported [35]. Cell culture samples of 100 μl were pelleted by centrifugation (16,000×g, 10 min). The cell pellets were then rinsed twice with ultrapure water and resuspended in 2 ml of a 5% hypochlorous acid solution for digestion. Resuspended cells were digested by incubation at 40 °C for 2 h. Digested cell solutions were pelleted by centrifugation (16,000 × g, 10 min), and the supernatants were removed. The PHB pellets were rinsed twice with ultrapure water and dried by incubation at 90 °C for 30 min. Thereafter, 1.5 ml of concentrated sulfuric acid was added to dried PHB pellets and incubated at 90 °C for 30 min to degrade PHB to crotonic acid. The formation of crotonic acid was determined by measuring absorbance at a wavelength of 208 nm and calculated from the molar extinction coefficient of crotonic acid at 208 nm (14,100 M−1 cm−1) [35].
The DCW of R. sphaeroides strains was determined using 10 ml of residual cell cultures after 5 days of incubation. Cells were collected by centrifugation (16,000×g, 10 min) and rinsed twice with ultrapure water. Cell pellets were dried at 80 °C overnight. Dry cell pellets were weighted using an electronic balance.
Enzyme assays
The activities of ACAT, AACR and PHAP in recombinant cells were determined by measuring the initial velocity of product formation. Recombinant R. sphaeroides strains grown for PHB production were sampled after 3 days of incubation; cells were collected by centrifugation (16,000×g, 1 min, 4 °C), and pellets were rinsed twice with ice-cold 20 mM potassium phosphate buffer. Cells were then resuspended in ice-cold 20 mM potassium phosphate buffer and disrupted by sonication. Disrupted cell mixtures were centrifuged (16,000×g, 10 min, 4 °C) to remove cellular debris, and the supernatants were used as crude extracts for enzyme assays.
To assay ACAT activity, we used a reaction mixture that contained 50 mM potassium phosphate buffer (pH 7.0), 0.1 mM acetyl-CoA, and 1 mM 5,5′-Dithiobis(2-nitrobenzoic acid) (DTNB). The reaction mixture (0.5 ml) was pre-incubated at 30 °C for 1 min in a quartz cell inserted into a V-670 spectrophotometer (JASCO, Tokyo, Japan) equipped with a MCB-100 thermostat (JASCO). After adding the enzyme and monitoring the absorbance of the solution at 412 nm, which arises from the formation of 5-thio-2-nitrobenzoic acid (TNB); the reaction was initiated at 30 °C. The concentration of TNB was determined using the molar extinction coefficient at 412 nm (13,600 M−1 cm−1).
To assay AACR activity, the reaction mixture contained 50 mM potassium phosphate buffer (pH 7.0), 0.1 mM acetoacetyl-CoA, and 0.1 mM NADPH. The reaction mixture was pre-incubated as described above. Addition of enzyme and monitoring the absorbance of the solution at 340 nm, which arises from NADPH, the reaction was initiated at 30 °C. The concentration of NADPH was determined using the molar extinction coefficient at 340 nm (62,200 M−1 cm−1).
PHAP activities were assayed as in the ACAT assay using a reaction mixture that contained 50 mM potassium phosphate buffer (pH 7.0), 0.1 mM (R)-3-hydroxybutanoyl-CoA, and 1 mM DTNB.
One unit was defined as the amount of enzyme that produces 1 μmol of the corresponding product per minute. Specific activities were determined from three independent experiments and are presented as the mean ± standard deviation. Protein concentrations were determined by the Bradford method.
Analytical methods
Cell and crotonic acid concentrations were measured using a UVmini-1240 Spectrometer (Shimadzu, Kyoto, Japan). Residual acetate concentration in AAY medium during PHB production was determined by HPLC (Shimadzu) equipped with Shim-pack SCR-102H columns (Shimadzu). Operating condition were: 50 °C and a mobile phase flow rate of 0.75 ml min−1. The mobile phase was linearly graduated using 50% 5 mM p-toluenesulfonic acid and 50% 20 mM 2,2-Bis(hydroxymethyl)-2,2′,2″-nitrilotriethanol containing 5 mM p-toluenesulfonic acid, and 0.1 mM di-sodium dihydrogen ethylenediaminetetraacetate dihydrate. Detection was performed with a conductivity detector CDD-10AVP (Shimadzu).
Abbreviations
- AACR:
-
acetoacetyl coenzyme A reductase
- ACAT:
-
acetyl coenzyme A acetyltransferase
- Acetoacetyl-CoA:
-
acetoacetyl coenzyme A
- Acetyl-CoA:
-
acetyl coenzyme A
- AS:
-
ammonium sulfate
- CoASH:
-
coenzyme A
- DCW:
-
dry cell weight
- DTNB:
-
5,5′-dithiobis(2-nitrobenzoic acid)
- HPLC:
-
high performance liquid chromatography
- Km:
-
kanamycin
- KmR :
-
kanamycin resistance
- LB:
-
Luria–Bertani
- NADPH:
-
nicotinamide adenine dinucleotide phosphate
- PCR:
-
polymerase chain reaction
- PHA:
-
poly (3-hydroxyalkanoates)
- PHADP:
-
poly (3-hydroxyalkanoate) depolymerase
- PHAP:
-
poly (3-hydroxyalkanoate) polymerase
- PHB:
-
poly (3-hydroxybutyrate)
- PNS:
-
purple non-sulfur
- (R)-3-hydroxybutanoyl-CoA:
-
(R)-3-hydroxybutanoyl coenzyme A
- Sm:
-
streptomycin
- SmR :
-
streptomycin resistance
- Spc:
-
spectinomycin
- SpcR :
-
spectinomycin resistance
- TNB:
-
5-thio-2-nitrobenzoic acid
References
Hazer DB, Kılıçay E, Hazer B. Poly(3-hydroxyalkanoate)s: diversification and biomedical applications: a state of the art review. Mater Sci Eng C. 2012;32:637–47.
Lin Z, Zhang Y, Yuan Q, Liu Q, Li Y, Wang Z, Ma H, Chen T, Zhao X. Metabolic engineering of Escherichia coli for poly(3-hydroxybutyrate) production via threonine bypass. Microb Cell Fact. 2015;14:185.
Preusting H, van Houten R, Hoefs A, van Langenberghe EK, Favre-Bulle O, Witholt B. High cell density cultivation of Pseudomonas oleovorans: growth and production of poly (3-hydroxyalkanoates) in two-liquid phase batch and fed-batch systems. Biotechnol Bioeng. 1993;41:550–6.
Gouda MK, Swellam AE, Omar SH. Production of PHB by a Bacillus megaterium strain using sugarcane molasses and corn steep liquor as sole carbon and nitrogen sources. Microbiol Res. 2001;156:201–7.
Poirier Y, Erard N, Petétot JM. Synthesis of polyhydroxyalkanoate in the peroxisome of Saccharomyces cerevisiae by using intermediates of fatty acid beta-oxidation. Appl Environ Microbiol. 2001;67:5254–60.
Arikawa H, Matsumoto K. Evaluation of gene expression cassettes and production of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a fine modulated monomer composition by using it in Cupriavidus necator. Microb Cell Fact. 2016;15:184.
Yigit DO, Gunduz U, Turker L, Yucel M, Eroglu I. Identification of by-products in hydrogen producing bacteria; Rhodobacter sphaeroides O.U. 001 grown in the waste water of a sugar refinery. J Biotechnol. 1999;70:125–31.
Luongo V, Ghimire A, Frunzo L, Fabbricino M, d’Antonio G, Pirozzi F, Esposito G. Photofermentative production of hydrogen and poly-β-hydroxybutyrate from dark fermentation products. Bioresour Technol. 2017;228:171–5.
Suzuki T, Tsygankov AA, Miyake J, Tokiwa Y, Asada Y. Accumulation of poly-(hydroxybutyrate) by a non-sulfur photosynthetic bacterium, Rhodobacter sphaeroides RV at different pH. Biotechnol Lett. 1995;17:395–400.
Brandl H, Gross RA, Lenz RW, Lloyd R, Fuller RC. The accumulation of poly(3-hydroxyalkanoates) in Rhodobacter sphaeroides. Arch Microbiol. 1991;155:337–40.
Hassan MA, Shirai Y, Kusubayashi N, Karim MIA, Nakanishi K, Hashimoto K. Effect of organic acid profiles during anaerobic treatment of palm oil mill effluent on the production of polyhydroxyalkanoates by Rhodobacter sphaeroides. J Ferment Bioeng. 1996;83:485–8.
Khatipov E, Miyakea M, Miyake J, Asada Y. Accumulation of poly-β-hydroxybutyrate by Rhodobacter sphaeroides on various carbon and nitrogen substrates. FEMS Microbiol Lett. 1998;162:39–45.
Sangkharak K, Prasertsan P. Optimization of polyhydroxybutyrate production from a wild type and two mutant strains of Rhodobacter sphaeroides using statistical method. J Biotechnol. 2007;132:331–40.
Kemavongse K, Prasertsan P, Upaichit A, Methacanon P. Poly-β-hydroxyalkanoate production by halotolerant Rhodobacter sphaeroides U7. World J Microbiol Biotechnol. 2008;24:2073–85.
Kranz RG, Gabbert KK, Locke TA, Madigan MT. Polyhydroxyalkanoate production in Rhodobacter capsulatus: genes, mutants, expression, and physiology. Appl Environ Microbiol. 1997;63:3003–9.
Chou ME, Chang WT, Chang YC, Yang MK. Expression of four pha genes involved in poly-beta-hydroxybutyrate production and accumulation in Rhodobacter sphaeroides FJ1. Mol Genet Genomics. 2009;282:97–106.
Yang MK, Lin YC, Shen CH. Identification of two gene loci involved in poly-beta-hydroxybutyrate production in Rhodobacter sphaeroides FJ1. J Microbiol Immunol. 2006;39:18–27.
Chou ME, Yang MK. Analyses of binding sequences of the PhaR protein of Rhodobacter sphaeroides FJ1. FEMS Microbiol Lett. 2010;302:138–43.
García-Torreiro M, Lu-Chau TA, Lema JM. Effect of nitrogen and/or oxygen concentration on poly(3-hydroxybutyrate) accumulation by Halomonas boliviensis. Bioprocess Biosyst Eng. 2016;39:1365–74.
Arikawa H, Matsumoto K, Fujiki T. Polyhydroxyalkanoate production from sucrose by Cupriavidus necator strains harboring csc genes from Escherichia coli W. Appl Microbiol Biotechnol. 2017;101:7497–507.
Arikawa H, Sato S, Fujiki T, Matsumoto K. A study on the relation between poly(3-hydroxybutyrate) depolymerases or oligomer hydrolases and molecular weight of polyhydroxyalkanoates accumulating in Cupriavidus necator H16. J Biotechnol. 2016;227:94–102.
Vasilyeva L, Miyake M, Nakamura C, Nakada E, Tsygankov A, Asada Y, Miyake J. Expression of luciferase gene under control of the puf promoter from Rhodobacter sphaeroides. Biotechnol Appl Biochem. 1999;77:337–45.
Kumka JE, Schindel H, Fang M, Zappa S, Bauer CE. Transcriptomic analysis of aerobic respiratory and anaerobic photosynthetic states in Rhodobacter capsulatus and their modulation by global redox regulators RegA, FnrL and CrtJ. Microb Genom. 2017;3:e000125.
Poblete-Castro I, Binger D, Oehlert R, Rohde M. Comparison of mcl-Poly(3-hydroxyalkanoates) synthesis by different Pseudomonas putida strains from crude glycerol: citrate accumulates at high titer under PHA-producing conditions. BMC Biotechnol. 2014;14:962.
Arias S, Bassas-Galia M, Molinari G, Timmis KN. Tight coupling of polymerization and depolymerization of polyhydroxyalkanoates ensures efficient management of carbon resources in Pseudomonas putida. Microb Biotechnol. 2013;6:551–63.
Cai L, Yuan MQ, Liu F, Jian J, Chen GQ. Enhanced production of medium-chain-length polyhydroxyalkanoates (PHA) by PHA depolymerase knockout mutant of Pseudomonas putida KT2442. Bioresour Technol. 2009;100:2265–70.
Matsumoto K, Tobitani K, Aoki S, Song Y, Ooi T, Taguchi S. Improved production of poly(lactic acid)-like polyester based on metabolite analysis to address the rate-limiting step. AMB Express. 2014;4:83.
Sangkharak K, Prasertsan P. Nutrient optimization for production of polyhydroxybutyrate from halotolerant photosynthetic bacteria cultivated under aerobic-dark condition. Electron J Biotechnol. 2008;11:1–12.
Madison LL, Huisman GW. Metabolic engineering of poly(3-hydroxyalkanoates): from DNA to plastic. Microbiol Mol Biol Rev. 1999;63:21–53.
Chen GQ, Jiang XR. Engineering bacteria for enhanced polyhydroxyalkanoates (PHA) biosynthesis. Synth Syst Biotechnol. 2017;2:192–7.
Kobayashi J, Yoshimune K, Komoriya T, Kohno H. Efficient hydrogen production from acetate through isolated Rhodobacter sphaeroides. J Biosci Bioeng. 2011;112:602–5.
Parales RE, Harwood CS. Construction and use of a new broad-host-range lacZ transcriptional fusion vector, pHRP309, for Gram− bacteria. Gene. 1993;133:23–30.
Schäfer A, Tauch A, Jäger Kalinowski WJ, Thierbach G, Pühler A. Small mobilizable multi-purpose cloning vectors derived from the Escherichia coli plasmids pK18 and pK19: selection of defined deletions in the chromosome of Corynebacterium glutamicum. Gene. 1994;145:69–73.
Kobayashi J, Hasegawa S, Itou K, Yoshimune K, Komoriya T, Asada Y, Kohno H. Expression of aldehyde dehydrogenase gene increases hydrogen production from low concentration of acetate by Rhodobacter sphaeroides. Int J Hydrog Energy. 2012;37:9602–9.
Karr DB, Waters JK, Emerich DW. Analysis of poly-beta-hydroxybutyrate in Rhizobium japonicum bacteroids by ion-exclusion high-pressure liquid chromatography and UV detection. Appl Environ Microbiol. 1983;46:1339–44.
Authors’ contributions
JK planned the study, performed all the experiments, and wrote the manuscript. AK supervised the study. All authors read and approved the final manuscript.
Acknowledgements
Not applicable.
Competing interests
The authors declare that they have no competing interests.
Availability of data and materials
The figures and tables supporting the conclusions of this study are included in this article. The primer sequences are listed in the additional file.
Consent for publication
All authors consented to publish this paper.
Ethics approval and consent to participate
This article does not contain any studies with human participants or animals performed by any of the authors.
Funding
This work was supported by a Special Coordination Fund for Promoting Science and Technology, Creation of Innovative Centers for Advanced Interdisciplinary Research Areas (Innovative Bioproduction, Kobe) from the Ministry of Education, Culture, Sports, and Science and Technology (MEXT), Japan. This work was supported by JSPS KAKENHI Grant Number 18K14375.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Author information
Authors and Affiliations
Corresponding author
Additional file
Additional file 1: Table S1.
Volumetric PHB production, DCW, and PHB content of recombinant R. sphaeroides HJ strains. Table S2. Volumetric PHB production, DCW, and PHB content of recombinant R. sphaeroides HJ strains in various concentration of AS. Table S3 PHB synthetic genes in R. sphaeroides 2.4.1 and its corresponding genes in R. capsulatus SB 1003 strain. Table S4 Primers used in this study.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.
About this article
Cite this article
Kobayashi, J., Kondo, A. Disruption of poly (3-hydroxyalkanoate) depolymerase gene and overexpression of three poly (3-hydroxybutyrate) biosynthetic genes improve poly (3-hydroxybutyrate) production from nitrogen rich medium by Rhodobacter sphaeroides. Microb Cell Fact 18, 40 (2019). https://doi.org/10.1186/s12934-019-1088-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12934-019-1088-y