Abstract
The present study is concerned with evaluating the influence of various concentrations of Ag within Cu:Ag bimetallic nanoparticles developed for use as a promising anti-bacterial agent against antibiotic-resistant bacteria. Here, Cu:Ag bimetallic nanoparticles with various concentration ratios (2.5, 5.0, 7.5, and 10 wt%) of Ag in fixed amount of Cu labeled as 1:0.025, 1:0.050, 1:0.075, and 1:0.1 were synthesized using co-precipitation method with ammonium hydroxide and deionized water as solvent, polyvinyl pyrrolidone as a capping agent, and sodium borohydride and ascorbic acid as reducing agents. These formulated products were characterized through a variety of techniques. XRD confirmed phase purity and detected the presence of distinct fcc structures belonging to Cu and Ag phases. FTIR spectroscopy confirmed the presence of vibrational modes corresponding to various functional groups and recorded characteristic peak emanating from the bimetallic. UV–visible spectroscopy revealed reduction in band gap with increasing Ag content. SEM and HR-TEM micrographs revealed spherical morphology of Ag-doped Cu bimetallic with small and large scale agglomerations. The samples exhibited varying dimensions and interlayer spacing. Bactericidal action of synthesized Cu:Ag bimetallic NPs depicted statistically significant (P < 0.05) inhibition zones recorded for various concentrations of Ag dopant against Staphylococcus aureus (S. aureus), Escherichia coli (E. coli), and Acinetobacter baumannii (A. baumannii) ranging from (0.85–2.8 mm), (0.55–1.95 mm) and (0.65–1.85 mm), respectively. Broadly, Cu:Ag bimetallic NPs were found to be more potent against gram-positive compared with gram-negative. Molecular docking study of Ag–Cu bimetallic NPs was performed against β-lactamase which is a key enzyme of cell wall biosynthetic pathway from both S. aureus (Binding score: − 4.981 kcal/mol) and A. bauminnii (Binding score: − 4.013 kcal/mol). Similarly, binding interaction analysis against FabI belonging to fatty acid biosynthetic pathway from A. bauminnii (Binding score: − 3.385 kcal/mol) and S. aureus (Binding score: − 3.012 kcal/mol) along with FabH from E. coli (Binding score: − 4.372 kcal/mol) was undertaken. These theoretical computations indicate Cu-Ag bimetallic NPs as possible inhibitor of selected enzymes. It is suggested that exploring in vitro inhibition potential of these materials may open new avenues for antibiotic discovery.
Avoid common mistakes on your manuscript.
Introduction
A variety of micro-organisms composed of bacteria, fungi, viruses, and parasites are present within the earth and its environment. These species cause complications in the production and use of medical equipment, healthcare merchandise, processed foods, water purification systems, and domestic sanitation products [1, 2]. Antibiotics are routinely employed by physicians to kill bacteria that cause illness in humans and animals. The disadvantage of frequent use of antibiotics is that it makes bacteria drug-resistant with time. Antibiotics also serve to reduce the number of ‘good’ bacteria present in the body, which fight against infections. Illnesses resulting from infections caused by antibiotic-resistant bacteria have become a major cause for concern in the field of medicine today. In this respect, many germs have been identified to be drug-resistant [3,4,5,6,7]. Novel efforts are under way to address the issue of drug-resistant bacteria and substitute current antimicrobial agents with more efficient and complementary therapies. In this regard, nanotechnology has rendered a substantial contribution to the production of nanomaterials such as metallic and metal oxide NPs (i.e., Ag, Cu, CuO, TiO2, SiO2, MgO, and ZnO) to fight an ever-increasing number of antimicrobial-resistant microorganisms. Among these, Cu and Ag NPs have shown encouraging antimicrobial properties [8,9,10,11,12].
In recent years, bimetallic NPs have been developed and used for various applications in the fields of chemistry, material science, biotechnology, and environmental protection. Bimetallic NPs containing copper (Cu) and silver (Ag) with a high fraction of surface atoms and large specific surface area have been widely studied [13]. These bimetallic NPs are of great interest due to their enhanced chemical, optical, catalytic, biological, plasmonic, and especially antimicrobial properties [14,15,16,17,18,19,20]. Ag ions can be reduced by ethanol under atmospheric conditions at 800 to 1000 °C to obtain silver NPs [21, 22]. Silver NPs possess good antimicrobial efficacy, therefore, it is used in the production of sunscreen creams and water treatment [23]. Cu NPs are fabricated by the reduction of copper sulfate with hydrazine in ethylene glycol under microwave irradiation, and can also be used as an antibacterial agent [24,25,26].
Metals such as Cu and Ag individually do not have promising optical, catalytic, and structural properties and cannot be converted into bimetallics. On the other hand, combining both metals (Cu:Ag) offers new opportunities to tune the structure and morphology of the resulting product for desired applications. Based upon its final structure, e.g., core–shell, dumb-bell structure, two-interface structure, randomly-mixed structure, or flower-shape structure, bimetallic NPs can exhibit a range of antimicrobial activity [27,28,29,30,31]. Various methods are available for the synthesis of bimetallic NPs including co-precipitation, sol–gel, hydrothermal, reduction, micro-emulsion, and polyol method [32,33,34,35,36,37].
In this study, Cu:Ag bimetallic NPs were synthesized through co-precipitation method using ammonium hydroxide and deionized water as solvent, polyvinyl pyrrolidone as a capping agent, and sodium borohydride and ascorbic acid as reducing agents. Four samples with various concentrations were prepared. With increasing concentrations of Ag in prepared bimetallic NPs, samples showed enhanced activity against bacteria acinetobacter baumannii that causes fever and nausea. The synthesized material assumed red appearance during rapid growth suggesting that antimicrobial activity was enhanced with increasing concentrations of Ag in bimetallic NPs. Furthermore, In silico predictions using molecular docking study were performed to identify the interaction pattern of Cu:Ag bimetallic NPs against β-lactamase enzyme of cell wall biosynthetic pathway alongside FabI and FabH enzymes of fatty acid biosynthetic pathway.
Methods
The current study was aimed to synthesize various concentrations of Ag within Cu:Ag bimetallic nanoparticles through hydrothermal route to investigate the efficacy of antibacterial agent against antibiotic-resistant bacteria.
Materials
Copper (II) chloride (CuCl2 0.2H2O, 98.9%), and silver nitrate (AgNO3) as precursors, polyvinyl pyrrolidone (PVP, an average molecular weight of 40,000) as capping agent, sodium borohydride (NaBH4, 99.9%) and L-Ascorbic acid (C6H8O6, 99.0%) as reducing agents and ammonium hydroxide (NH4OH) were used in the present study after acquiring them from Sigma Aldrich, USA.
Synthesis of bimetallic Cu:Ag NPs
Bimetallic Cu:Ag NPs were prepared using co-precipitation method as portrayed in Fig. 1. In deionized water, 1.25 g of PVP and 0.5 g of ascorbic acid were added and stirred vigorously at 100 °C. Two solutions of 40 mL of ammonium hydroxide were prepared individually; in one solution, 1.7 g copper chloride and in the other solution 1.7 g silver nitrate were added. These two solutions are then poured one after the other into the initially prepared solution with the addition of 0.5 g of NaBH4. Afterwards, the final solution was stirred at 100 °C for 4 h to make it homogeneous and later centrifuged at 6000 rpm for complete extraction of NPs. The obtained bimetallic NPs were dried at 100 °C for complete elimination of moisture and impurities, to make sure that the prepared bimetallic products were in pure form [12]. Similarly, four samples with various Ag concentrations (mol 2.5%, 5%, 7.5%, and 10%) were prepared with fixed Cu ratios.
Antimicrobial activity
In vitro bactericidal potential of Cu:Ag bimetallic NPs was evaluated against pathogenic bacteria S. aureus, E. coli and A. baumannii isolates obtained from bovine mastitic milk using well diffusion method. Mannitol salt agar, MacConkey agar and Lauria Bertani agar were swabbed with isolated bacteria activated growth 1.5 × 108 CFU/ml. After media solidification, five wells were prepared using yellow pipette possessing dimensions of 15 mm diameter and ten microliter (5 µg/mL). Freshly prepared Cu:Ag bimetallic NPs were loaded into wells with different ratios in comparison with ten microliters of amoxicillin (5 µg/mL) as positive control and 50 μl of DIW as negative control. The bactericidal activity of synthesized Cu:Ag bimetallic NPs was determined by measuring inhibition zones (in mm) formed after incubation for 15 h at 37 °C.
Statistical analysis
The bactericidal activity of synthesized NPs with inhibition zone (mm) measurements was considered statistically significant using SPSS 20.0, one-way analysis of variance (ANOVA) [57].
Molecular docking study
Antibiotics decrease bacterial growth and cause death of bacteria through cell wall damage, disrupting biochemical processes, cell membrane damage, and penetration through biofilm [38]. In recent decades, plenty of nanoparticles with potential bactericidal activity have been reported, which kill bacteria either through cell wall disruption or by blocking the food source by a mechanism similar to known antibiotics [39,40,41]. Hence, enzymes belonging to these biochemical pathways are thought to be an important and attractive target for antibiotic discovery [12]. Here, key enzymes from cell wall biosynthetic pathway (i.e. β-lactamase) and fatty acid biosynthetic pathway (i.e. FabH and FabI) were selected as possible targets to evaluate the mechanism of interaction of Cu:Ag bimetallic NPs with their active pocket as inhibitors (see Fig. 2).
3D structural parameters of selected enzymes were fetched from protein data bank with PDB code: 4U0X (2.03 Å Resolution) for β-lactamase [42] and 6AH9; Resolution 1.74 Å [43] for Enoyl-[acyl-carrier-protein] reductase (FabI) from A. bauminnii. The β-lactamase (3D structure) with PDB ID: 1MWU; Resolution 2.6 Å [44] and FabI with PDB code: 4CV1; Resolution 1.95 [45] from S. aureus while for FabH from E. coli has PDB code: 4Z8D; Resolution 2.0 Å [46].
Molecular docking study of Cu:Ag bimetallic NPs was performed using ICM Molsoft v3.8–4a or above (Molsoft L.L.C., La Jolla, CA) software to identify binding interactions with key residues of active site [47]. The protein/receptor preparation tool of ICM was used for optimization and structure preparation of selected enzyme targets. Steps involved were addition of polar H-atoms, deletion of water molecules, and energy minimization using default parameters. The co-crystallized ligand molecule was removed to provide room for docking of NPs. The binding pocket was defined using grid box specifying position of crystallized ligand. The conformation with lowest binding energy out of top 10 docked conformations was selected in each case to analyze interaction pattern and binding tendency of Ag–Cu bimetallic NPs inside active pocket. Pymol and discovery studio visualizer software were employed for analysis and 3D-view depiction of binding interactions [48]. The structure of Cu:Ag bimetallic NPs was retrieved from PubChem in.sdf format.
Characterization
Structural analysis and phase purity were observed by engaging XRD (PAN analytical X’pert pro XRD) with Cu-Kα radiation (λ = 0.154 nm, 20° to 80°). The presence of vibrational modes corresponding to various functional groups was evaluated using Fourier transform infrared spectroscopy-FTIR with Perkin Elmer spectrometer. Absorption spectra were acquired using a UV–visible-Genesys 10S spectrophotometer. FESEM coupled with EDS spectrometer (JSM-6610LV) and HR-TEM (JEOL JEM 2100F) were employed to visualize surface morphologies. The ICM v3.8-4a or above (Molsoft L.L.C., La Jolla, CA) software was used for molecular docking analysis.
Results and Discussion
XRD analysis was undertaken to assess the constitution of phases and crystal structure of formulated products. Figure 3a reveals the XRD pattern plotted between 20° and 80°. In bimetallic Cu:Ag, observed reflections around ~ 38.2°, 46°, 64.4°, and 77.1° are attributed to (111), (200), (220), and (311) facets of fcc Ag phase according to JCPDS No. 04-0783 [32, 49,50,51,52]. Whereas, in the case of Cu, diffractions appearing at 32.6°, 44.2°, and 51° denoted (110), (111), and (200) lattice planes that confirmed the presence of fcc structured CuO and metallic Cu, respectively, and well-matched with JCPDS No. 04-0836 [32, 53,54,55,56]. In extracted pattern, both Ag and Cu peaks were observed which signifies the presence of NPs constituting both Ag and Cu phases. Moreover, the existence of CuO in samples with lower Ag content (e.g., 1:0.025, 1:0.050, and 1:0.075) reveals that Cu NPs were oxidized and exhibited non-protective behavior at high-temperature due to lower Ag concentrations [52]. Conversely, in the sample with the highest Ag content (1:0.1), CuO peak exhibits low intensity which indicates the formation of partially oxide-free product [57]. This suggests that improved oxidation resistance of bimetallic NPs will occur due to the addition of Ag [52]. No additional peak of impurity was detected within the instrument detection limits while each crystallographic plane comprises energetically distinct sites based on atom density. Both Cu and Ag NPs have high atom density facets at (111) that served to expose the maximum orientation of planes [51, 58]. Using Bragg’s law, d-spacing of Ag and Cu were found to be 0.24 and 0.21 nm, respectively which corresponds to distinct plane (111) of both elements and was in line with HR-TEM findings (Fig. 6) [51, 59,60,61,62]. Corresponding SAED rings (Fig. 3b–d) obtained from prepared bimetallic products display distinct ring patterns that demonstrate well-crystallized products and accord well with XRD patterns.
FTIR spectra were recorded between 500 and 4000 cm−1 as presented in Fig. 3e; the transmitted band positioned between 600 and 900 cm−1 is caused by the formation of Cu:Ag bonding [63]. The observed band around ~ 1200 and 1400 cm−1 is attributed to C–O and C–H, respectively; peaks appearing at ~ 1800 and 2100 cm−1 corresponds to C=O and N–H bonding due to PVP and NH4OH [64]. Transmittances observed around ~ 2800 cm−1 and 3400 cm−1 are ascribed to the presence of C≡N and hydroxyl group (O–H) [64].
Figure 4a shows the absorption spectra of Ag–Cu bimetallic NPs with clear absorption bands sited at 340, 410, and 500 nm, which are ascribed to surface plasmonic resonance absorption of metallic Ag and Cu [52]. The band appearing at 410 nm typically arises due to the presence of Ag NPs, and latter peak positioned at 510 nm is attributed to the existence of Cu NPs [52, 57,58,59, 65,66,67]. It may be suggested that bimetallic NPs are developed with distinct Ag and Cu phases, instead of bimetallic development that was also affirmed by XRD results as discussed earlier [52]. Slight redshift in absorption band at 410 nm and an increase in maximum absorption with increasing Ag content was observed [58]. Using the Tauc equation,
where α is considered as coefficient of absorption [2.303 log(T/d), T is transmitted light and d shows thickness of sample cell], h symbolizes Planck’s constant (6.62607015 × 10−34 Js), \(\nu\) is frequency of light, K shows absorption index, and Eg is equal to band gap energy in eV. The value of “n” is related to electronic transition type of band gap [13, 26, 68, 69]. The band gap of prepared bimetallic products was calculated and found to be 3.2, 2.9, 2.7, and 2.6 eV, as demonstrated in Fig. 4b–e.
From SEM images (Fig. 5a–d) of as-synthesized Cu:Ag bimetallic nanocomposites, it was observed that small-sized particles were deposited on the surface of large particles. An increase in Ag content from 2.5 to 7.5% led to the formation of various particles with varying morphology which finally culminated into chunky Cu:Ag NPs. Further, accumulation of uneven and tiny Ag particles was augmented with increasing dopant concentration suggesting appearance of more scattered blocks on its surface. This signifies the major influence that Ag doping into Cu has on morphology, which was further confirmed with HR-TEM micrographs (see Fig. 5e–h).
To further elaborate on the morphology and d-spacing of prepared bimetallic, HR-TEM with 10 nm resolution was engaged. In Fig. 6a, d-spacing (0.21 nm) of Cu NPs corresponds to (111) facet of Cu, as also evident in XRD results (Fig. 3a). Figure 6b portrays a slight increase in layer spacing (0.21 to 0.22 nm) and shows Ag NPs with 0.24 nm interplanar distance that matched with (111) plane. Similarly, Fig. 6c, d shows calculated layer spacings and separate phases of bimetallic while Fig. 6e demonstrates particle shape of Ag and Cu NPs. The particles in HR-TEM images are seen to possess a core–shell structure. In Fig. 6d within a single particle, lattice fringes emanating from Cu and Ag were recorded. This strongly suggests the formation of core–shell bimetallic NPs with different Cu:Ag ratios yielding irregular quasi-spherical NPs. Furthermore, TEM image showed particles seem like as dark and bright region. This variation in contrast within a single particle may indicate the presence of two distinct constituent materials suggesting the creation of bimetallic Cu:Ag particles [70, 71].
The presence of distinct peak in EDS spectrum and elemental composition originating from bimetallic affirmed successful formation of Cu:Ag NPs. Figure 7a represents EDS spectrum obtained from 1:0.050 sample which shows clear peaks of Cu and Ag. Figure 7b is taken from 1:010 sample where peaks for C and O were detected in doped samples. These show up since carbon tabs are utilized to hold samples during SEM examination and/or due to background counts in SEM–EDS sensor.
In vitro bactericidal efficacy of Cu:Ag bimetallic NPs using agar well diffusion assay is presented in Table 1. The results demonstrate direct proportional relationship between synthesized NPs concentration and inhibition zones (mm). Statistically significant (P < 0.05) inhibition zones recorded for (2.5, 5, 7.5 and 10 wt%) Ag dopant against S. aureus, E. coli and A. baumannii ranged from 0.85–2.8 mm, 0.55–1.95 mm and 0.65–1.85 mm, respectively, see Table 1. All results were compared with DIW (0 mm) and amoxicillin (4 mm) as negative and positive control, respectively. Similarly, %age efficacy of doped NPs increased (21.2–70%), (13.7–48.7%) and (16.2–46.2%) against S. aureus, E. coli and A. baumannii, respectively. Overall Cu:Ag bimetallic NPs were found to be more potent against S. aureus (i.e. gram + ive) compared with E. coli and A. baumannii (i.e. gram −ive).
Size, concentration, and shape of NPs directly affect oxidative stress produced by nanostructures. Bactericidal efficacy in the form of inhibition zones (mm) improved due to greater wt% doping of Ag-doped Cu bimetallic NPs due to increased cations (++) availability. Bactericidal action in regard to size and concentration depicts an inverse relationship to size [58, 59]. Nano-sized structures produce reactive oxygen species (ROS) efficiently which reside in bacterial cell membranes leading to extrusion of cell organelles and ultimately death of bacteria [60]. Besides ROS production, cationic interaction of Ag+ and Cu++ with negatively charged parts of bacteria cell membrane results in improved bactericidal efficacy at increasing concentrations through cell lysis and bacteria collapse [58, 61].
Biological applications of various classes of nanoparticles have been extensively studied since the last few decades. Owing to unique characteristics of NPs, they have been widely utilized for their potential as bactericidal agent with the ability to substitute traditional antibiotics. NPs interact with bacterial cells, disrupt cell membrane permeation and destroy key metabolic pathways [72]. The specific mechanism of nanoparticle toxicity towards bacteria needs to be explored. It is believed that NPs interact with bacterial cell involving electrostatic forces, van der Waals forces or hydrophobic interactions that ultimately result in death of bacteria. Enzymes have been reported as main virulence factor involved in bacterial infection and targeting them to inhibit their activity aid in tackling the caused infection [73]. Here, molecular docking study of Cu:Ag NPs against enzyme targets of cell wall alongside fatty acid biosynthetic pathway identified binding interaction pattern of these NPs inside active pocket. Keeping in view in vitro antibacterial potential of these NPs against A. bauminnii, S. aureus and E. coli, the enzyme targets were selected from these microorganisms to get an insight into possible mechanism behind their bactericidal activity.
Best docked conformation observed in case of Cu:Ag Bimetallic NPs with β-lactamase from A. bauminnii revealed hydrogen bonding interaction with Glu272 (2.8 Å) and Ser286 (3.2 Å) along with metal contact interaction with Val292 while the docking score was − 4.013 kcal/mol (Fig. 8a). Similarly, binding score of Ag–Cu bimetallic NPs observed against β-lactamase from S. aureus was − 4.981 kcal/mol possessing H-bonding interaction with Ser403 (3.2 Å), Tyr519 (3.6 Å), Gln521 (3.0 Å) and Asn464 (3.1 Å) as shown in Fig. 8b.
Second enzyme target selected in the current study FabI belong to fatty acid biosynthetic pathway and molecular docking predictions suggested Cu:Ag bimetallic NPs as potential inhibitor against this target. The Cu:Ag Bimetallic NPs showed good binding score (-3.385 kcal/mol) against FabI from A. bauminnii having H-bonding with Ser201 (2.7 Å), Ala199 (3.5 Å), and Leu198 (3.3 Å) as depicted in Fig. 8c. Similarly, best docked conformation of Ag–Cu NPs with active site of FabI from S. aureus showed H-bonding with Gly202 (2.5 Å)and Gln155 (2.5 Å) having binding score − 3.012 kcal/mol (Fig. 8d).
In addition, the binding capacity of Cu:Ag bimetallic NPs against FabH from E.coli was also evaluated and the binding score observed was − 4.372 kcal/mol having H-bonding interaction with Thr254 (3.5 Å), HIE244 (2.6 Å) and Glu302 (3.0 Å) shown in Fig. 8e.
Conclusion
Cu:Ag bimetallic nanoparticles were prepared through co-precipitation method for use in applications to combat bacteria-related ailments. XRD profiles confirmed the presence of fcc structured CuO and metallic Cu and Ag particles. Both Ag and Cu peaks were observed which signifies bimetallic NPs entailing Ag and Cu phases. Planes observed in XRD analysis correspond well to SAED rings. Attached chemical groups with formulated products and characteristic transmittance band between 600 and 900 cm−1 was caused by the formation of Cu:Ag bonding. The plotted spectra of UV–vis showed absorption at 410 nm which typically arises due to the presence of Ag NPs, and latter peak positioned at 510 nm was attributed to the existence of Cu NPs. The particles in HR-TEM images were seen to have a core–shell structure. Cu:Ag NPs clearly showed the formation of bimetallic NPs with different Cu:Ag ratios yielding irregular quasi-spherical NPs. Further, d-spacing of Cu NPs i.e., 0.21 nm corresponds to (111) facet of Cu detected in XRD results. A slight increase in layer spacing (from 0.21 to 0.22 nm) also shows that Ag NPs with 0.24 nm layer distance matched with (111) plane. Molecular docking study showed good agreement with in vitro bactericidal activity. The binding tendency of Cu:Ag bimetallic NPs against β-lactamase enzyme of cell wall biosynthetic pathway alongside FabI and FabH enzymes of fatty acid biosynthetic pathway demonstrated their inhibition potential that needs to be explored further through enzyme inhibition studies.
Availability of data and materials
All data are fully available on demand.
Abbreviations
- EDS:
-
Energy dispersive X-ray spectroscopy
- FTIR:
-
Fourier transform infrared spectroscopy
- G + ve:
-
Gram-positive
- G −ve:
-
Gram negative
- HR-TEM:
-
High resolution transmission electron microscopy
- JCPDS:
-
Joint committee on powder diffraction standards
- Ag:
-
Silver
- UV–Vis:
-
Ultra-violet visible spectroscopy
- XRD:
-
X-ray diffraction
References
Ma Z, Kim D, Adesogan AT, Ko S, Galvao K, Jeong KC (2016) Chitosan microparticles exert broad-spectrum antimicrobial activity against antibiotic-resistant micro-organisms without increasing resistance. ACS Appl Mater Interfaces 8(17):10700–10709
Niu J, Sun Y, Wang F, Zhao C, Ren J, Qu X (2018) Photomodulated nanozyme used for a gram-selective antimicrobial. Chem Mater 30(20):7027–7033
Gupta A, Mumtaz S, Li C-H, Hussain I, Rotello VMJCSR (2019) Combatting antibiotic-resistant bacteria using nanomaterials. Chem Soc Rev 48(2):415–427
Zhao X et al (2020) Smart Ti3C2Tx MXene fabric with fast humidity response and joule heating for healthcare and medical therapy applications. ACS Nano 17:8793–8805
Gu Z et al (2018) Exploring the nanotoxicology of MoS2: a study on the interaction of MoS2 nanoflakes and K+ channels. ACS Nano 12(1):705–717
Yin W et al (2016) Functionalized nano-MoS2 with peroxidase catalytic and near-infrared photothermal activities for safe and synergetic wound antibacterial applications. ACS Nano 10(12):11000–11011
Cao F et al (2017) An efficient and benign antimicrobial depot based on silver-infused MoS2. ACS Nano 11(5):4651–4659
Ruparelia JP, Chatterjee AK, Duttagupta SP, Mukherji SJAB (2008) Strain specificity in antimicrobial activity of silver and copper nanoparticles. Acta Biomater 4(3):707–716
Zain NM, Stapley A, Shama GJCP (2014) Green synthesis of silver and copper nanoparticles using ascorbic acid and chitosan for antimicrobial applications. Carbohydr Polym 112:195–202
Valodkar M, Modi S, Pal A, Thakore SJMRB (2011) Synthesis and anti-bacterial activity of Cu, Ag and Cu–Ag alloy nanoparticles: a green approach. Mater Res Bull 46(3):384–389
Chatterjee AK, Chakraborty R, Basu TJN (2014) Mechanism of antibacterial activity of copper nanoparticles. Nanotechnology 25(13):135101
Ikram M et al (2020) Bimetallic Ag/Cu incorporated into chemically exfoliated MoS2 nanosheets to enhance its antibacterial potential: in silico molecular docking studies. Nanotechnology 31(27):275704
Ikram M, Khan MI, Raza A, Imran M, Ul-Hamid A, Ali S (2020) Outstanding performance of silver-decorated MoS2 nanopetals used as nanocatalyst for synthetic dye degradation. Phys E Low-Dimens Syst Nanostruct 124:114246
Toshima N, Yonezawa TJNJOC (1998) Bimetallic nanoparticles—novel materials for chemical and physical applications. New J Chem 22(11):1179–1201
Toshima N (2008) Capped bimetallic and trimetallic nanoparticles for catalysis and information technology. Macromol Symp 270(1):27–39
Venkatesan P, Santhanalakshmi JJL (2010) Designed synthesis of Au/Ag/Pd trimetallic nanoparticle-based catalysts for Sonogashira coupling reactions. Langmuir 26(14):12225–12229
Perdikaki A et al (2016) Ag and Cu monometallic and Ag/Cu bimetallic nanoparticle-graphene composites with enhanced antibacterial performance. ACS Appl Mater Interfaces 8(41):27498–27510
Nazeruddin G, Prasad R, Shaikh Y, Shaikh AJDPL (2014) Synergetic effect of Ag-Cu bimetallic nanoparticles on antimicrobial activity. Front Chem 3:129–136
Rao KJ, Paria S (2015) Mixed phytochemicals mediated synthesis of multifunctional Ag–Au–Pd nanoparticles for glucose oxidation and antimicrobial applications. ACS Appl Mater Interfaces 7(25):14018–14025
Chen X et al (2017) Enhanced antimicrobial efficacy of bimetallic porous CuO microspheres decorated with Ag nanoparticles. ACS Appl Mater Interfaces 9(45):39165–39173
Das R, Nath S, Chakdar D, Gope G, Bhattacharjee RJJON (2009) Preparation of silver nanoparticles and their characterization. Int J Mol Sci 5:1–6
Das R, Nath SS, Chakdar D, Gope G, Bhattacharjee RJJOEN (2010) Synthesis of silver nanoparticles and their optical properties. Res Pharm Sci 5(4):357–362
Sánchez-López E et al (2020) Metal-based nanoparticles as antimicrobial agents: an overview. Nanomaterials (Basel) 10(2):292
Zhu H, Zhang C, Yin YJN (2005) Novel synthesis of copper nanoparticles: influence of the synthesis conditions on the particle size. Nanotechnology 16(12):3079
Raza A et al (2019) Enhanced industrial dye degradation using Co doped in chemically exfoliated MoS2 nanosheets. Appl Nanosci 10(5):1535–1544
Raza A et al (2020) A comparative study of dirac 2D materials, TMDCs and 2D insulators with regard to their structures and photocatalytic/sonophotocatalytic behavior. Appl Nanosci 10:3875–3899
Tahir K et al (2016) Visible light photo catalytic inactivation of bacteria and photo degradation of methylene blue with Ag/TiO2 nanocomposite prepared by a novel method. J Photochem Photobiol B Biol 162:189–198
Salari S, Mousavi SAA, Hadizadeh S, Izadi AJMP (2017) Epidemiology of dermatomycoses in Kerman province, southeast of Iran: a 10-years retrospective study (2004–2014). Microb Pathog 110:561–567
Thota S, Wang Y, Zhao J (2018) Colloidal Au–Cu alloy nanoparticles: synthesis, optical properties and applications. Mater Chem Front 2(6):1074–1089. https://doi.org/10.1039/C7QM00538E
Duan S, Wang R (2013) Bimetallic nanostructures with magnetic and noble metals and their physicochemical applications. Progress Nat Sci Mater Int 23(2):113–126
Ikram M et al (2020) 2D chemically exfoliated hexagonal boron nitride (hBN) nanosheets doped with Ni: synthesis, properties and catalytic application for the treatment of industrial wastewater. Appl Nanosci 10(9):3525–3528
Liu X, Wu Y, Xie G, Wang Z, Li Y, Li QJIJES (2017) New green soft chemistry route to Ag-Cu bimetallic nanomaterials. Int J Electrochem Sci 12:3275–3282
McNamara K, Tofail SAJPCCP (2015) Nanosystems: the use of nanoalloys, metallic, bimetallic, and magnetic nanoparticles in biomedical applications. Phys Chem Chem Phys 17(42):27981–27995
Huang J, Lin L, Sun D, Chen H, Yang D, Li Q (2015) Bio-inspired synthesis of metal nanomaterials and applications. Chem Soc Rev 44(17):6330–6374. https://doi.org/10.1039/C5CS00133A
Rao CNR, Ramakrishna Matte HSS, Voggu R, Govindaraj A (2012) Recent progress in the synthesis of inorganic nanoparticles. Dalton Trans 41(17):5089–5120. https://doi.org/10.1039/C2DT12266A
Ikram M et al (2020) Photocatalytic and bactericidal properties and molecular docking analysis of TiO2 nanoparticles conjugated with Zr for environmental remediation. RSC Adv 10(50):30007–30024. https://doi.org/10.1039/D0RA05862A
Ikram M et al (2020) Dye degradation performance, bactericidal behavior and molecular docking analysis of Cu-doped TiO2 nanoparticles. RSC Adv 10(41):24215–24233
Dakal TC, Kumar A, Majumdar RS, Yadav V (2016) Mechanistic basis of antimicrobial actions of silver nanoparticles. Front Microbiol 7:1831
Rai M, Deshmukh S, Ingle A, Gade A (2012) Silver nanoparticles: the powerful nanoweapon against multidrug-resistant bacteria. J Appl Microbiol 112(5):841–852
White RJ, Cutting K, Kingsley A (2006) Topical antimicrobials in the control of wound bioburden. Ostomy Wound Manag 52(8):26–58
Lee N-Y, Hsueh P-R, Ko W-C (2019) Nanoparticles in the treatment of infections caused by multidrug-resistant organisms. Front Pharmacol 10:1153
Powers RA et al (2014) Biochemical and structural analysis of inhibitors targeting the ADC-7 cephalosporinase of Acinetobacter baumannii. Biochemistry 53(48):7670–7679
Crystal structure of enoyl-ACP reductase from Acinetobacter baumannii in complex with NAD and Triclosan. http://www.rcsb.org/structure/6AH9.
Lim D, Strynadka NC (2002) Structural basis for the β lactam resistance of PBP2a from methicillin-resistant Staphylococcus aureus. Nat Struct Biol 9(11):870–876
Schiebel J et al (2014) Rational design of broad spectrum antibacterial activity based on a clinically relevant enoyl-acyl carrier protein (ACP) reductase inhibitor. J Biol Chem 289(23):15987–16005
McKinney DC et al (2016) Antibacterial FabH inhibitors with mode of action validated in Haemophilus influenzae by in vitro resistance mutation mapping. ACS Infect Dis 2(7):456–464
Abagyan R, Totrov M (1994) Biased probability Monte Carlo conformational searches and electrostatic calculations for peptides and proteins. J Mol Biol 235(3):983–1002
Systemes D (2015) BIOVIA, discovery studio modeling environment. Release 4.5, Dassault Systemes: San Diego, CA
Li Y, Guo S, Yang H, Chao Y, Jiang S, Wang CJRA (2018) One-step synthesis of ultra-long silver nanowires of over 100 μm and their application in flexible transparent conductive films. RSC Adv 8(15):8057–8063
Lanje AS, Sharma SJ, Pode RBJJCPR (2010) Synthesis of silver nanoparticles: a safer alternative to conventional antimicrobial and antibacterial agents. Pharm Res 2(3):478–483
Khan Z, Obaid AYJRA (2016) Seedless, copper-induced synthesis of stable Ag/Cu bimetallic nanoparticles and their optical properties. RSC Adv 6(35):29116–29126
Chen Z, Mochizuki D, Maitani MM, Wada YJN (2013) Facile synthesis of bimetallic Cu–Ag nanoparticles under microwave irradiation and their oxidation resistance. Nanotechnology 24(26):265602
Ahamed M, Alhadlaq HA, Khan M, Karuppiah P, Al-Dhabi NAJJON (2014) Synthesis, characterization, and antimicrobial activity of copper oxide nanoparticles. J Nanomater 2014:637858
Sasmal AK, Dutta S, Pal TJDT (2016) A ternary Cu2O-Cu–CuO nanocomposite: a catalyst with intriguing activity. Dalton Trans 45(7):3139–3150
Betancourt-Galindo R et al (2014) Synthesis of copper nanoparticles by thermal decomposition and their antimicrobial properties. J Nanomater 2014:980545
Mardiansyah D et al (2018) Effect of temperature on the oxidation of Cu nanowires and development of an easy to produce, oxidation-resistant transparent conducting electrode using a PEDOT: PSS coating. Sci Rep 8(1):1–9
Rout L, Kumar A, Dhaka RS, Dash PJRA (2016) Bimetallic Ag–Cu alloy nanoparticles as a highly active catalyst for the enamination of 1, 3-dicarbonyl compounds. RSC Adv 6(55):49923–49940
Rahman L-U et al (2015) Monitoring of 2-butanone using a Ag–Cu bimetallic alloy nanoscale electrochemical sensor. RSC Adv 5(55):44427–44434
Singh MK, Manda P, Singh A, Mandal RJAA (2015) Localized surface plasmon behavior of Ag-Cu alloy nanoparticles stabilized by rice-starch and gelatin. AIP Adv 5(10):107108
Zewail AH, Thomas JM (2010) 4D electron microscopy: imaging in space and time. World Scientific, Singapore
Edison TNJI, Baral ER, Lee YR, Kim SH (2016) Biogenic synthesis of silver nanoparticles using cnidium officinale extract and their catalytic reduction of 4-nitroaniline. J Clust Sci 27(1):285–298
Theivasanthi T, Alagar MJAPA (2011) Electrolytic synthesis and characterizations of silver nanopowder
Ismail M et al (2018) Green synthesis of antibacterial bimetallic Ag–Cu nanoparticles for catalytic reduction of persistent organic pollutants. J Mater Sci Mater Electron 29(24):20840–20855
Banik M, Patra M, Dutta D, Mukherjee R, Basu TJN (2018) A simple robust method of synthesis of copper–silver core–shell nano-particle: evaluation of its structural and chemical properties with anticancer potency. Nanotechnolgy 29(32):325102
Trinh DC, Dang TMD, Huynh KK, Fribourg-Blanc E, Dang MC (2015) Synthesis of Cu core Ag shell nanoparticles using chemical reduction method. Adv Nat Sci Nanosci Nanotechnol 6(2):025018
Tsuji M, Hikino S, Tanabe R, Sano YJCL (2009) Synthesis of bicompartmental Ag/Cu nanoparticles using a two-step polyol process. Chem Lett 38(8):860–861
Paszkiewicz M, Gołąbiewska A, Rajski Ł, Kowal E, Sajdak A, Zaleska-Medynska AJJON (2016) Synthesis and characterization of monometallic (Ag, Cu) and bimetallic Ag-Cu particles for antibacterial and antifungal applications. J Nanomater 2016:2187940
Hassan J, Ikram M, Ul-Hamid A, Imran M, Aqeel M, Ali S (2020) Application of chemically exfoliated boron nitride nanosheets doped with co to remove organic pollutants rapidly from textile water. Nanoscale Res Lett 15(1):2510
Ikram M, Raza A, Imran M, Ul-Hamid A, Shahbaz A, Ali S (2020) Hydrothermal synthesis of silver decorated reduced graphene oxide (rGO) nanoflakes with effective photocatalytic activity for wastewater treatment. Nanoscale Res Lett 15(1):95
Lee J-P et al (2013) Well-organized raspberry-like Ag@ Cu bimetal nanoparticles for highly reliable and reproducible surface-enhanced Raman scattering. Nanoscale 5(23):11620–11624
El-Yazeed WA, Ahmed AIJRA (2019) Monometallic and bimetallic Cu–Ag MOF/MCM-41 composites: structural characterization and catalytic activity. RSC Adv 9(33):18803–18813
Thill A et al (2006) Cytotoxicity of CeO2 nanoparticles for Escherichia coli. Physico-chemical insight of the cytotoxicity mechanism. Environ Sci Technol 40(19):6151–6156
Konieczna I et al (2012) Bacterial urease and its role in long-lasting human diseases. Curr Protein Pept Sci 13(8):789–806
Acknowledgements
Support provided by the Core Research Facilities at the King Fahd University of Petroleum & Minerals, Dhahran, Saudi Arabia is greatly appreciated.
Funding
Authors are thankful to 44ORIC/19 GCU Lahore and Higher Education Commission, HEC through start research grant project # 21-1669/SRGP/R&D/HEC/2017 Pakistan for financial support.
Author information
Authors and Affiliations
Contributions
SM and MI performed the whole experiments and AR wrote the manuscript. AG and RG provided the novel idea to carry out the experiment. AH performed antimicrobial and SA and JH participated in molecular docking study. participated in the data analysis of the results and discussion portion. M. Irshad and AS reviewed the manuscript, corrected the English. AUH carried out the FESEM and HRTEM analysis. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interest
Authors confirm that this manuscript has no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mureed, S., Naz, S., Haider, A. et al. Development of Multi-concentration Cu:Ag Bimetallic Nanoparticles as a Promising Bactericidal for Antibiotic-Resistant Bacteria as Evaluated with Molecular Docking Study. Nanoscale Res Lett 16, 91 (2021). https://doi.org/10.1186/s11671-021-03547-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-021-03547-6