Abstract
In hybrid organic–inorganic and all-inorganic metal halide perovskite nanomaterials, two-dimensional (2D) Ruddlesden–Popper (RP) perovskites have become one of the most interesting materials because of tunable bandgaps varied with the layer thickness, effective modulation of the electron-hole confinement, and high stability. Here, we report a one-pot synthesis of 2D RP perovskite (BA)2(MA)n − 1PbnX3n + 1 (BA = 1-butylammonium, MA = methylammonium, X = Br or I) quantum dots (QDs) with an average size of 10 nm at room temperature. The (BA)2(MA)n − 1PbnBr3n + 1 (Br series) QDs and (BA)2(MA)n − 1PbnI3n + 1 (I series) QDs exhibited tunable emitting spectrum in the range of 410–523 nm and 527–761 nm, respectively, with full width at half maximum (FWHM) of 12–75 nm. The emission color was tuned by the ratio of MA and halide. The photoluminescence quantum yield of 2D perovskite QDs reached 48.6% with more thermodynamic stability in comparison with 3D MAPbX3 QDs. Overall results indicated that developing a solution synthesis for 2D RP perovskite QDs with great optical properties paves the way toward future optoelectronic devices and perovskite quantum dot photovoltaics.
Avoid common mistakes on your manuscript.
Background
Development of new fluorescent materials with the narrow emissive band and color adjustment is a key technology for the lighting and display technologies with high color performance [1,2,3,4,5]. Colloidal quantum dots (QDs) have been considered as promising candidates because of their unique intrinsic properties, such as tunable color light and higher photoluminescence quantum yields (PLQYs) [2, 4]. Instead of traditional II–VI or III–V semiconductors, new 3D organic–inorganic perovskite [6,7,8,9,10] or inorganic halide perovskite QDs [11,12,13,14,15,16,17] with unit cell formula AMX3 (A is small organic or inorganic cation ((such as CH3NH3+ or Cs+), X is a halogen (Cl−, Br− or I−), M is a metal (Pb or Sn) that can coordinate to six halides) have been developed. These 3D perovskites exhibited excellent performance in the light-emitting diode and solar energy conversion because of the tunability of wavelength (from 400 nm to 800 nm) and sharp emission (full width at half maximum, FWHM ∼ 20 nm) [14, 18,19,20]. However, one obstacle to 3D perovskite as active materials in photoelectronic applications is the nonradiative pathways through sub-band defect states, resulting in lower PLQYs and less EL emission [21, 22]. Recently, Ruddlesden–Popper perovskites materials with reduced dimensionality have been discovered to be two-dimensional (2D) perovskite structure which was formed by inserting different large organic cations (R) in the A-site of AMX3 slices along the crystallographic planes. These 2D layer perovskite materials have a general chemical formula of (RNH3)2(CH3NH3)n − 1AnX3n + 1 and exhibit beneficial layer edge states with no typical trap states, resulting in long PL lifetime, relevant photo-stability, and chemical stability for better optoelectronic devices performance [23,24,25,26].
Recently, the 2D and 3D perovskite materials are found to be thick and grain size controllable for a higher exciton binding energy with higher electron-hole capture rate for radiative recombination [26, 27]. Besides, 2D-layered perovskites also possess an optical property of the quantum confinement effect wherein the band gap of the perovskites can be adjusted by the different thickness of the perovskite layer [25]. Several reports indicated that 2D-layered perovskite thin films demonstrated good performance in photovoltaic or light-emitting diode because of long-lived free carriers provided by lower energy states at the edges of the layered perovskites and tunable emission wavelength controlled by the thickness of perovskite [23, 25, 28,29,30]. Because of the unique properties of the 2D perovskite materials, the corresponding colloidal nanocrystal is attractive to be developed and investigated to understand their optical properties for future highly luminescent and stable colloidal perovskite nanocrystals. For example, a series of quasi-2D lead(II) bromide perovskites with submicron size would exhibit different quantum size confinement effects by using different length organic cation which can tune emission from bright green to blue [31, 32]. Up to date, the study of the optical property of 2D perovskite QDs with the size smaller than 10 nm is few. Therefore, size control of 2D perovskite QDs remains an important issue for further photophysical and optoelectronic properties investigation.
In this report, monodisperse 2D Ruddlesden–Popper perovskite (BA)2(MA)n − 1PbnX3n + 1 (BA = 1-butylammonium, MA = methylammonium, X = Br or I) QDs with an average size of 10 nm have been successfully prepared via a facile method. (BA)2(MA)n − 1PbnBr3n + 1 (Br series) and (BA)2(MA)n − 1PbnI3n + 1 (I series) QDs exhibited tunable emitting spectrum in the range of 410–523 nm and 527–761 nm, respectively. The layered structure of 2D perovskite QDs was confirmed by X-ray diffraction (XRD). Photoluminescence (PL) of 2D perovskite QDs was characterized with a sharp emission (FWHM) of 12–42 nm, high quantum yields of 6.8–48.6%, and short radiative lifetimes of 1.6–75.9 ns.
Results and discussion
2D (BA)2(MA)n − 1PbnX3n + 1 perovskite QDs were fabricated by a facile one-pot synthesis method, as shown in Fig. 1a. First, a precursor solution was prepared by dissolving PbX2 (X = Br or I), methylammonium halogen (MAX), butylammonium halogen (BAX), octylamine (OLA), and oleic acid (OA) with proper ratios in the dimethylformamide (DMF) solution. The resulting solution was added drop by drop into a quenching solvent chlorobenzene to form 2D perovskite QDs at ambient conditions. By adjusting the ratio of MAX and PbX2 in a precursor solution (in Table 1), 2D perovskite QDs with different n values will be performed. The OA and OLA played a role in the co-surfactants to stabilize the growth of QDs. The as-prepared 2D Br series and I series perovskite QDs were found to be dispersed well and the corresponding photo-images (Fig. 1b, c) of the QDs with increases of “n” value showed the changes of emission color from blue to greenish and greenish to bright red under ultraviolet light irradiation, respectively. Especially, 3D lead (II) iodide perovskite QDs (n = ∞) exhibited the weakest emission 2D I series perovskite QDs with other n values. The result also showed that the 2D perovskite QDs exhibited more structural and optical stability than 3D perovskite QDs after formation of QDs.
To investigate the optical properties of 2D Br series and I series perovskite QDs with different emission color, the PL spectra of these 2D perovskite QDs in chlorobenzene (CB) solvent were measured as shown in Fig. 2. The PL spectra of 2D perovskite QDs for Br series and I series exhibit emission wavelength across the visible region from 410 to 523 nm and 527–761 nm, respectively. Both PL spectra for two series QDs show a red shift upon increase of n value and low FWHM values of each emission around ~ 11–21 nm, suggesting the formation of highly pure 2D perovskite QDs. Br series with n = 4 and 5 and I series with n = 3 and 4 exhibited a main peak along with a small shoulder attributed to a mixture of 2D perovskite QDs with different n values in the same solution. Especially, the emission peak of (BA)2(MA)n − 1PbnI3n + 1 with n = 1 at 527 nm is observed, indicating a larger band gap in comparison with previous reports. High PLQYs of 2D Br series and I series perovskite QDs (Fig. 2c, d) were obtained from 6.8 to 48.6% and 1.1 to 24.8%, respectively. Overall results indicated that the 2D perovskite QDs exhibited an obviously quantum confinement effect due to the formation of quantum well by separating different thicknesses of the inorganic layers from the BA molecules as spacers.
Figure 3 shows that the representative transmission electron microscopy (TEM) images of well-dispersed 2D Br series and I series perovskite QDs with n = 1 and 2 exhibited spherical shape with a small size distribution. The average size of these QDs is around 10 nm. The results indicate that the crystal growth of the QDs is controlled by co-surfactants (OA and OLA). Besides, other 2D perovskite QDs with different n values are shown in (Additional file 1: Figure S1). The representative high-resolution TEM (HRTEM) images (the inset of Fig. 3a–d) show clear lattice structures of the QDs with high crystallinity. The results showed that the d-spacing of both 2D perovskite QDs with n = 1 was estimated to be 0.27 nm, which matches to the (0100) phase. The d-spacing of 2D Br series and I series perovskite QDs with n = 2 was calculated to be ~ 0.29 nm and ∼0.69 nm, which is related to the (200) and (111) plane of 2D perovskite QDs, respectively.
To investigate the layered crystalline structures of these 2D Br series and I series perovskite QDs, XRD patterns were performed as shown in Fig. 4. The results indicate that additional low angle peaks found for each 2D perovskite QDs are attributed to the incremental expansion of unit cell of perovskite with increases of the thickness of the 2D perovskite layers in the crystal structure. All the 2D perovskite QDs with n ≥ 2 compositions show diffraction peaks at 15.1° and 14.1° for Br series and I series, respectively, which are the same as the (100) diffraction patterns of the 3D perovskite materials [33, 34]. The peak in the two series is more broadened with increases of n value, indicating that the grain size of 2D perovskite QDs become smaller than that of 3D MAPbBr3 [35]. Also, the angle of (100) phase in Br series is lower than that of I series, which can be attributed to the smaller ionic radius of the Br series compared with I—that the lattice parameter. Besides, a series of Bragg reflections peaks at lower angles (2θ < 14.1°) are observed for 2D I series perovskites QDs (Fig. 4b). This indicates that the large BA group is incorporated into the perovskite crystal structure, resulting in enlarging the size of unit cells in comparison with 3D perovskite [36, 37]. We also found a series of reflections peak appeared at low angles (2θ < 14°) for these 2D RP perovskite QDs. In Br series of 2D RP perovskite QDs, the diffraction peaks (2θ < 14°) are attributed to the n = 1, n = 2, and n = 3 phases, but no diffraction patterns from n ≥ 4 phases are observed, which is similar to 3D perovskite NCs. For I series, there are n = 1, n = 2, n = 3, and n = 4 phases found in the diffraction peaks. In both series, only 2D RP perovskite QDs with n = 1 value has a single phase that exists. For other n value compositions, there are usually two phases presented in the synthesized sample. All phases for different n values have been pointed out in both XRD spectra. According to the Scherrer equation, the estimated diameter of the QDs is similar to the obtained result from TEM images.
To investigate the photophysical property of these 2D Br series and I series perovskite QDs, time-resolved PL spectroscopy (TRPL) was performed as shown in Fig. 5. The results show non-exponential decay traces with average lifetimes of τ = 1 ~ 9 ns and 48 ~ 75 ns for Br series and I series, respectively. It is found that I series QDs with red emission show higher PL decay time than Br series QDs due to the smaller band gap of I series. Moreover, our 2D I series QDs demonstrate a relatively longer lifetime in comparison with exfoliated (BA)2(MA)n − 1PbnI3n + 1 crystal (τ < 10 ns) reported in the literature [11, 38]. Overall results indicate that 2D perovskite QDs exhibit a fewer trap state resulting in less nonradiative decay mechanisms such as electron–phonon coupling and long PL lifetime.
Conclusions
A facile synthesis method of highly luminescent 2D RP perovskite QDs with Br series and I series has been illustrated. The band gap of the QDs for Br series and I series can be adjusted by the ratio of MA and halide, expressing tunable emission light across the visible region 410 to 523 nm and 527 to 761 nm, respectively. A remarkably high quantum yield of up to 48.6% was obtained. Also, we found that 2D perovskite QDs exhibited more optical stability in comparison with 3D perovskite QDs, which resulted in less nonradiative decay from electron–phonon coupling. It is believed that the brightly luminescent 2D perovskite QDs will be the trigger for developing much more stable solution-processed perovskite materials in optoelectronic applications.
Methods
Chemicals used
Lead (II) bromide (98 + %, Acros), lead (II) iodide (99%, Acros), methylamine solution (33 wt% in absolute ethanol, Acros), n-butylamine (99.5%, Acros), hydrobromic acid (48%, Fisher), hydroiodic acid (57 wt% aqueous, Acros), octylamine (99 + %, Acros), oleic acid (SLR grade, Alfa Aesar), N,N-dimethylformamide (99.8%, Macron), and toluene (HPLC quality, Acros). All reagents and solvents were used as received without further purification.
Synthesis of alkylammonium halide
Butylammonium bromide (BABr), methylammonium bromide (MABr), butylammonium iodide (BAI), and methylammonium iodide (MAI) were prepared by addition of HBr (48%) or HI (57%) to butylamine (99.5%) or to a solution of methylamine (33 wt%) in absolute ethanol, respectively. The molar ratio of the acid and the amine was 1.1:1.0. The resulting mixture was stirred for 2 h and maintained at 0 °C using an ice water bath. Then, the solvent was removed by a rotary evaporator. The precipitate was washed with diethyl ether by stirring the solution for 30 min several times. After filtration, the white solid was dried at 60 °C in a vacuum oven. After drying overnight, the alkylammonium halide crystals were all sealed under argon and transferred into a glove box for further use.
2D-layered nanocrystals (NCs) synthesis
All syntheses were carried out at room temperature under ambient conditions. For different layered 2D NCs, BAX, MAX, and PbX2 (X = Br or I) were mixed in different molar ratios (2: n − 1: 3n + 1, n = 1, 2, 3, …, ∞) and were dissolved in DMF forming 0.04 mM PbX2 solution. 0.5 mL OA and 0.05 mL octylamine were added into 5 mL of the solution. Next, 100 μL of this mixture was injected into 10 ml toluene under vigorous stirring to form 2D NCs. Detailed synthesis compositions were presented in Fig. 1b.
Characterizations
The morphology and structure of 2D perovskites QDs were revealed by transmission electron microscope (TEM) and high-resolution TEM, respectively. TEM images were conducted in a 200 kV transmission electron microscope (JEOL, 2100F) and 120 kV transmission electron microscope (HITACHI, HT7700). The crystal structures and qualities of 2D perovskites QDs were determined from the XRD θ–2θ scan data by using powder X-ray diffractometer (Rigaku Miniflex 600). Photoluminescence spectra were obtained from fluorescence spectrophotometer (HITACHI F-4500). The PLQY of 2D RP perovskite (BA)2(MA)n − 1PbnX3n + 1 QDs were measured in the toluene, using C-102 and DCJTB compounds as the standards. The QY of C-102 and DCJTB are 0.76 and 0.78, respectively [39, 40]. Time-resolved photoluminescence (TRPL) spectroscopy was acquired using a time-correlated single photon counting (TCSPC) spectrometer set-up (FluoTime 300, PicoQuant GmbH). Samples were photo-excited using a 375 nm and 466 nm laser head (LDH-P-C-470, PicoQuant GmbH) with a pulse duration of 70 ps, fluence of 90 μW and a repetition rate of 4 MHz.
Abbreviations
- (BA)2(MA)n − 1PbnBr3n + 1 :
-
Br series
- (BA)2(MA)n − 1PbnI3n + 1 :
-
I series
- 2D:
-
Two-dimensional
- 3D:
-
Three-dimensional
- BA:
-
1-Butylammonium
- BAX:
-
Butylammonium halogen
- CB:
-
Chlorobenzene
- DMF:
-
Dimethylformamide
- FWHM:
-
Full width at half maximum
- HRTEM:
-
High-resolution TEM
- MA:
-
Methylammonium
- MAX:
-
Methylammonium halogen
- OA:
-
Oleic acid
- OLA:
-
Octylamine
- PL:
-
Photoluminescence
- PLQYs:
-
Photoluminescence quantum yields
- QDs:
-
Quantum dots
- RP:
-
Ruddlesden–Popper
- TEM:
-
Transmission electron microscopy
- TRPL:
-
Time-resolved PL spectroscopy
- XRD:
-
X-ray diffraction
References
Dai X et al (2014) Solution-processed, high-performance light-emitting diodes based on quantum dots. Nature 515(7525):96
Shirasaki Y, Supran GJ, Bawendi MG, Bulović V (2013) Emergence of colloidal quantum-dot light-emitting technologies. Nat. Photonics 7(1):13
Yoffe A (2001) Semiconductor quantum dots and related systems: electronic, optical, luminescence and related properties of low dimensional systems. Adv Phys 50(1):1–208
Shields AJ (2007) Semiconductor quantum light sources. Nat. photonics 1(4):215
Kulkarni AP, Tonzola CJ, Babel A, Jenekhe SA (2004) Electron transport materials for organic light-emitting diodes. Chem Mater 16(23):4556–4573
Cha M et al (2016) Enhancing perovskite solar cell performance by interface engineering using CH3NH3PbBr0. 9I2. 1 quantum dots. J Am Chem Soc 138(27):8581–8587
Gong X et al (2016) Highly efficient quantum dot near-infrared light-emitting diodes. Nat. Photonics 10(4):253
Kim Y et al (2015) Efficient luminescence from perovskite quantum dot solids. ACS Appl Mater Interfaces 7(45):25007–25013
Im J-H, Chung J, Kim S-J, Park N-G (2012) Synthesis, structure, and photovoltaic property of a nanocrystalline 2H perovskite-type novel sensitizer (CH 3 CH 2 NH 3) PbI 3. Nanoscale Res Lett 7(1):353
Ahmadian-Yazdi M-R, Eslamian M (2018) Fabrication of semiconducting methylammonium lead halide perovskite particles by spray technology. Nanoscale Res Lett 13(1):6
Protesescu L et al (2015) Nanocrystals of cesium lead halide perovskites (CsPbX3, X= Cl, Br, and I): novel optoelectronic materials showing bright emission with wide color gamut. Nano Lett 15(6):3692–3696
Sutton RJ et al (2016) Bandgap-tunable cesium lead halide perovskites with high thermal stability for efficient solar cells. Adv Energy Mater 6(8):1502458
Bekenstein Y, Koscher BA, Eaton SW, Yang P, Alivisatos AP (2015) Highly luminescent colloidal nanoplates of perovskite cesium lead halide and their oriented assemblies. J Am Chem Soc 137(51):16008–16011
Song J et al (2015) Quantum dot light-emitting diodes based on inorganic perovskite cesium lead halides (CsPbX3). Adv Mater 27(44):7162–7167
Jellicoe TC et al (2016) Synthesis and optical properties of lead-free cesium tin halide perovskite nanocrystals. J Am Chem Soc 138(9):2941–2944
Weidman MC, Seitz M, Stranks SD, Tisdale WA (2016) Highly tunable colloidal perovskite nanoplatelets through variable cation, metal, and halide composition. ACS Nano 10(8):7830–7839
Chen MY et al (2018) Strongly coupled tin-halide perovskites to modulate light emission: tunable 550–640 nm light emission (FWHM 36–80 nm) with a quantum yield of up to 6.4%. Adv. Mater 30(20):1706592
Jeon NJ et al (2014) Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nat Mater 13(9):897
Noh JH, Im SH, Heo JH, Mandal TN, Seok SI (2013) Chemical management for colorful, efficient, and stable inorganic–organic hybrid nanostructured solar cells. Nano Lett 13(4):1764–1769
Noel NK et al (2014) Lead-free organic–inorganic tin halide perovskites for photovoltaic applications. Energy Environ Sci 7(9):3061–3068
Deschler F et al (2014) High photoluminescence efficiency and optically pumped lasing in solution-processed mixed halide perovskite semiconductors. J Phys Chem Lett 5(8):1421–1426
Stranks SD et al (2014) Recombination kinetics in organic-inorganic perovskites: excitons, free charge, and subgap states. Phys Rev Appl 2(3):034007
Smith IC, Hoke ET, Solis-Ibarra D, McGehee MD, Karunadasa HI (2014) A layered hybrid perovskite solar-cell absorber with enhanced moisture stability. Angew Chem Int Ed 126(42):11414–11417
Cao DH, Stoumpos CC, Farha OK, Hupp JT, Kanatzidis MG (2015) 2D homologous perovskites as light-absorbing materials for solar cell applications. J Am Chem Soc 137(24):7843–7850
Tsai H et al (2016) High-efficiency two-dimensional Ruddlesden–Popper perovskite solar cells. Nature 536(7616):312
Blancon J-C et al (2017) Extremely efficient internal exciton dissociation through edge states in layered 2D perovskites. Science 355:1288–1292
Zhang F et al (2015) Brightly luminescent and color-tunable colloidal CH3NH3PbX3 (X= Br, I, Cl) quantum dots: potential alternatives for display technology. ACS Nano 9(4):4533–4542
Stoumpos CC et al (2016) Ruddlesden–Popper hybrid lead iodide perovskite 2D homologous semiconductors. Chem Mater 28(8):2852–2867
Yang S et al (2017) Ultrathin two-dimensional organic–inorganic hybrid perovskite nanosheets with bright, tunable photoluminescence and high stability. Angew Chem Int Ed 56(15):4252–4255
Milot RL et al (2016) Charge-carrier dynamics in 2D hybrid metal–halide perovskites. Nano Lett 16(11):7001–7007
Sichert JA et al (2015) Quantum size effect in organometal halide perovskite nanoplatelets. Nano Lett 15(10):6521–6527
Yuan Z, Shu Y, Xin Y, Ma B (2016) Highly luminescent nanoscale quasi-2D layered lead bromide perovskites with tunable emissions. Chem Comm 52(20):3887–3890
Levchuk I et al (2017) Brightly luminescent and color-tunable formamidinium lead halide perovskite FAPbX3 (X= Cl, Br, I) colloidal nanocrystals. Nano Lett 17(5):2765–2770
Meng L et al (2017) Pure formamidinium-based perovskite light-emitting diodes with high efficiency and low driving voltage. Adv Mater 29(4):1603826
Xiao Z et al (2017) Efficient perovskite light-emitting diodes featuring nanometre-sized crystallites. Nat. Photonics 11(2):108
Wang N et al (2016) Perovskite light-emitting diodes based on solution-processed self-organized multiple quantum wells. Nat. Photonics 10(11):699
Byun J et al (2016) Efficient visible quasi-2D perovskite light-emitting diodes. Adv Mater 28(34):7515–7520
Zhang M et al (2014) Composition-dependent photoluminescence intensity and prolonged recombination lifetime of perovskite CH 3 NH 3 PbBr 3− x cl x films. Chem. Comm. 50(79):11727–11730
Rurack K, Spieles M (2011) Fluorescence quantum yields of a series of red and near-infrared dyes emitting at 600–1000 nm. Anal Chem 83(4):1232–1242
Lee K-H, Kim S-M, Kim J-Y, Kim Y-K, Yoon S-S (2010) Red fluorescent organic light-emitting diodes using modified pyran-containing DCJTB derivatives. Bull Kor Chem Soc 31(10):2884–2888
Acknowledgements
We thank Miss Tzu-Pei Chen and Prof. Chun-Wei Chen in the Department of Materials Science and Engineering, National Taiwan University for assistance at TRPL measurement.
Funding
This work has been financially supported by the Ministry of Science and Technology of Taiwan (MOST 106-2113-M-029-006-MY2 and MOST 106-2632-M-029-001) and Tunghai University.
Availability of data and materials
The data sets supporting the conclusions of this article are included within the article.
Author information
Authors and Affiliations
Contributions
YHC, JCL, and YCC carried out the experiment under DYW’s guidance. TRK provided a useful suggestion. TRK and DYW co-write the paper. All authors contributed to the data analysis and scientific discussion. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
Additional TEM images and absorption spectra. (DOCX 2168 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Chang, YH., Lin, JC., Chen, YC. et al. Facile synthesis of two-dimensional Ruddlesden–Popper perovskite quantum dots with fine-tunable optical properties. Nanoscale Res Lett 13, 247 (2018). https://doi.org/10.1186/s11671-018-2664-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2664-5