Abstract
The influence of C insertion on Dzyaloshinskii–Moriya interaction (DMI) as well as current-induced domain wall (DW) motion (CIDWM) and tilting in Pt/Co/Ta racetracks is investigated via a magneto-optical Kerr microscope. The similar DMI strength for Pt/Co/Ta and Pt/Co/C/Ta samples reveals that DMI mainly comes from the Pt/Co interface. Fast DW velocity around tens of m/s with current density around several MA/cm2 is observed in Pt/Co/Ta. However, it needs double times larger current density to reach the same magnitude in Pt/Co/C/Ta, indicating DW velocity is related to the spin-orbit torque efficiency and pinning potential barrier. Moreover, in CIDWM, DW velocity is around 103 times larger than that in field-induced DW motion (FIDWM) with current-generated effective field keeping the same magnitude as applied magnetic field, revealing that the current-generated Joule heating has an influence on DW motion. Interestingly, current-induced DW tilting phenomenon is observed, while this phenomenon is absent in FIDWM, demonstrating that the current-generated Oersted field may also play an essential role in DW tilting. These findings could provide some designing prospects to drive DW motion in SOT-based racetrack memories.
Avoid common mistakes on your manuscript.
Background
Current-induced magnetic domain wall motion (CIDWM) in racetracks has revealed a newly developing magnetic racetrack memory device [1, 2]. Owing to this promising prospect, lots of work have been carried out during the last few decades. CIDWM was firstly investigated in ferromagnets (FMs) with in-plane magnetic anisotropy and the spin-polarized current-generated spin transfer torque (STT) acts as the driving force [3, 4]. Afterwards, CIDWM was also realized in FMs with perpendicular magnetic anisotropy (PMA) [5, 6]. However, in some PMA materials, domain wall (DW) motion direction is opposite to the direction of the electron flow, which is contradictory to the prediction of STT [7, 8]. And much more works are found that DW motion is along the current direction in heavy metal (HM)/FM bilayer structures with PMA. It was demonstrated that HM-generated spin-orbit torques (SOTs) by spin Hall effect and/or Rashba effect together with the interfacial Dzyaloshinskii–Moriya interaction (DMI) due to the structural inversion asymmetry of FM are considered to drive a chiral DW motion along the current direction [9, 10]. Therefore, in order to enhance the efficiency of CIDWM, it requires the HM with large spin Hall angle (θSH) to generate a larger torque to drive DW motion. Many efforts have been devoted to obtain a large θSH of HMs by varying the thickness of HM [11, 12], decorating the interface between HM and FM [13, 14], changing the crystallinity of HM [15], and even involving oxygen in HM [16]. Besides, some reports also achieve large effective θSH based on HM/FM/HM structures, in which two HM layers have opposite sign of θSH [17,18,19]. When a current passing through the two HM layers, the generated spin currents from two kinds of HM layers will work in concert to improve the SOT efficiency for decreasing the current density to switch the magnetization or drive the DW motion. Meanwhile, the DMI strength in this kind of trilayers may be different from the bilayers, since there are two interfacial interactions on both sides of the FM layer. It was found that DMI strength has a large influence on DW velocity when an extended collective coordinate model was proposed to explain the DW tilting behavior [20]. In addition, the DW tilting was also reported in GaMnAs micro-wires [20,21,22].
In our previous work, we have investigated the effect of inserting a C interlayer between Co and Ta on the anisotropy field, switching field, and SOT effective fields in Pt/Co/Ta structures with PMA [23]. The obtained magnetization switching current density is in the order of 106 A/cm2 in both Pt/Co/Ta and Pt/Co/C/Ta devices. In this work, we investigate the current-induced DW motion and tilting behavior in these two samples and the influence of C insertion on DMI strength and DW velocity in micro-sized Pt/Co/Ta racetracks. We found a little change of the calculated DMI exchange constant (|D|), indicating that the DMI strength mainly comes from the contribution of the Pt/Co interface in Pt/Co/Ta and Pt/Co/C/Ta stacks. In field-induced DW motion, the measured DW velocity in Pt/Co/C/Ta is smaller than that in Pt/Co/Ta even under a large magnetic field, revealing that the pinning potential barrier has a great influence on DW motion. Besides, in CIDWM, a larger DW velocity is observed compared to that in field-induced motion with the same magnitude between the current generated effective field and applied magnetic field. It reveals that the current-generated Joule heating also affects the DW motion. More importantly, current-induced DW tilting phenomenon is observed in Pt/Co/Ta and Pt/Co/C/Ta stacks, which can be well explained by the current-generated Oersted field combined with spin Hall effective field.
Methods
Two film stacks Ta(3)/Pt(5)/Co(0.6)/Ta(5) and Ta(3)/Pt(5)/Co(0.6)/C(2)/Ta(5) (thickness in nm) were deposited on corning glass substrates at room temperature by direct current magnetron sputtering with a base pressure below 4.0 × 10−5 Pa. The bottom 3 nm Ta is used as the seed layer, and the top Ta layer has an around 1.5 nm TaOx capping layer due to the air exposure [17, 24]. Afterwards, the film stacks were patterned into 8.5-μm and 3.0-μm wide racetracks for Pt/Co/Ta and Pt/Co/C/Ta, respectively, using standard lithography and Ar-ion milling techniques to investigate CIDWM. Moreover, the 8.5-μm wide Hall bars patterned using the same techniques were used to measure the out-of-plane field (Hz)-dependent anomalous Hall resistance (RHall) at different in-plane bias fields (Hx) along the current direction to achieve the spin Hall effective field (HSHE) and estimate the DMI strength as reported by Pai et al. [25]. In their report, the shift of RHall-Hz loops at Hx can be well explained by a chiral Néel DW model. The shift was defined as HSHE, which can be used to quantify the SOT efficiency χ ≡ HSHE/J (J is the charge current density). The method was used to characterize the DMI strength and SOT efficiency in this work. Moreover, a magneto-optical Kerr microscope with polar Kerr effect was used to monitor the DW motion under the applied field or current pulse at room temperature.
Results and Discussion
Based on the chiral Néel DW model, we firstly investigated the anomalous Hall loops under the in-plane bias field Hx to obtain DMI strength and SOT efficiency (see the Additional file 1). The obtained DMI effective field (HDMI) for Pt/Co/Ta and Pt/Co/C/Ta is around 1370 and 1055 Oe, respectively. The saturated χ (χsat) standing for the largest SOT efficiency is around 10.0 and 8.3 Oe/(106 A/cm2) for Pt/Co/Ta and Pt/Co/C/Ta, respectively. The decreased χsat for Pt/Co/C/Ta may be in that some interdiffusion and chemical reaction from the interface between Co and C as well as the interface between C and Ta increase the spin flipping probability and reduce the effective injection of spin current from the top Ta. In addition, the strength of the DMI exchange constant |D| can be also calculated from the measured |HDMI| using |D| = μ0Ms∆|HDMI| [26], where ∆ is the DW width and it relates to exchange stiffness constant A and effective PMA energy density Keff through ∆ = (A/Keff)1/2. Using Ms (respectively around 1.213×106 and 1.288×106 A/m for Pt/Co/Ta and Pt/Co/C/Ta) and Keff (respectively around 4.1×105 and 2.1×105 J/m3 for Pt/Co/Ta and Pt/Co/C/Ta) as reported in the previous work and assuming A ≈ 1.5 × 10−11 J/m [27], we estimate |D| = 1.01 ± 0.16 mJ/m2 for Pt/Co/Ta and |D| = 1.15 ± 0.14 mJ/m2 for Pt/Co/C/Ta. The difference of |D| value seems to be weak in these two samples. This may be explained by that the total DMI strength results from the two contributions of bottom Pt/Co interfaces and top Co/Ta or Co/C interfaces. Since the bottom Pt/Co interfaces are very similar, they contribute equally to |D|. Whereas, for the contribution from the top Co/Ta or Co/C interface, Ma et al. [28] reported that |D| induced by Ta is much weaker than that by Pt. Hence, top Co/Ta interface is weak for the contribution of the total |D|. And the contribution from the top Co/C interface is also negligible due to the very weak spin-orbit coupling of C. It is also noted that both the bottom Pt/Co and top Co/Ta interfaces contribute to the DMI but may partially cancel each other [28], leading to the slightly decreased |D| for Pt/Co/Ta samples compared to Pt/Co/C/Ta samples. As a consequence, the similar |D| for Pt/Co/Ta and Pt/Co/C/Ta samples reveals that the DMI strength mainly comes from the contribution of the Pt/Co interface. Additionally, for these two samples, HDMI/HK (respectively around 0.2 and 0.3 for Pt/Co/Ta and Pt/Co/C/Ta) is smaller than 2/π. While HDMI is not beyond the theoretical threshold required to stabilize Néel DWs [25, 26], the chiral Néel DW in these two samples is demonstrated by observing the CIDWM behavior which will be discussed below. Meanwhile, the anomalous Hall loops under the in-plane bias field (Hy) orthogonal the current direction are also investigated. Even though a large Hy is applied, the shift of RHall-Hz loops is quite small (see the Additional file 1). It could be due to that Hy gradually transforms the chiral Néel-type DWs to Bloch-type DWs, and the effective field HSHE is nearly zero for a Bloch-type DW according to the formula [10, 29, 30]:
where, θSHE, Ms, tF, Jx, \( \widehat{m} \) and \( \widehat{j} \) represent the effective spin Hall angle, saturation magnetization of FM layer, thickness of FM layer, current density along x direction, unit vector of the magnetization and unit vector of the current density, respectively.
Next, the DW velocity (v) under the out-of-plane magnetic field and in-plane current pulse were measured using the Kerr microscope to investigate the DW motion behavior. A pre-prepared DW was formed using a magnetic field pulse just above the nucleation field after the racetrack saturated at an opposite large magnetic field. Velocity under Hz pulse is shown in Fig. 1a, b for two samples. For Pt/Co/C/Ta, v is still smaller than that of Pt/Co/Ta sample even under a large driving magnetic field. It is possibly due to the much more defects formation after C decoration, which increases the pinning fields [23]. It also can be seen that lgv is proportional to Hz-1/4, indicating a creep regime of DW motion according to the creep law [31]:
where UC is a characteristic energy related to the disorder-induced pinning potential, kB is the Boltzmann constant, T is the temperature, and Hdep is the depinning field at which the Zeeman energy is equal to the DW pinning energy. The fitting slope gives a measurement of \( \frac{U_c}{k_BT}{H_{dep}}^{1/4}=s \), s is around 37.4 and 76.5 Oe1/4 for Pt/Co/Ta and Pt/Co/C/Ta, respectively. Since the Hdep for Pt/Co/C/Ta is two times larger than that for Pt/Co/Ta [23], the difference of Hdep1/4 between them is smaller than 1.5. However, the difference of s between them is larger than 2. It indicates that the Pt/Co/C/Ta sample has a larger pinning potential, which is consistent with the above discussion. Moreover, the insets in Fig. 1a, b also show the snapshots of domain images under different magnetic fields. One can see that the DW shape shows larger distribution for Pt/Co/C/Ta than that for Pt/Co/Ta. It also indicates that the pinning potential is not quite homogeneous in Pt/Co/C/Ta due to C decoration inducing randomly distributed pinning sites. Whereas, the regular DW tilting under the magnetic field is not observed for these two samples, which is different from the theoretical collective coordinate model [20].
Afterwards, the CIDWM behavior was also investigated to make a comparison with field-induced DW motion. A up-to-down (U-D) or down-to-up (D-U) domain was firstly nucleated by a pulse magnetic field from a saturated state, and then, a pulse current was applied to push the DW motion using a pulse generator with pulse width in the range of 5–100 ns. Figure 2a, b shows the CIDWM velocity without any applied magnetic fields. The positive or negative velocity means the DW motion along or against the current direction. It implies the formation of a chiral Néel DW with the existence of DMI in these two samples [10, 30]. The increased velocity at the higher current density is due to the increased HSHE acting on the chiral Néel DW. However, it needs double times larger current density to reach the same DW velocity in Pt/Co/C/Ta compared to that in Pt/Co/Ta structures. It may be ascribed to the decreased SOT efficiency and increased pinning potential barrier by C interfacial decoration. Moreover, the DW velocity by current driving is around 103 times larger than that by magnetic field driving with the current generated effective field keeping the same value as magnetic field. It reveals that other mechanisms such as Joule heating and/or Oersted field generated from the current may also play a significant role in CIDWM. It should be noted, in Fig. 2b as well as Fig. 3c, that the decreases of DW velocity and DW tilt angle are observed in Pt/Co/C/Ta sample when the current density is at ± 19.2 MA/cm2. Meanwhile, one can see more nucleation area like white or black dots in the inset of Figs. 2b and 3c at higher current densities. This could be ascribed to that the thermal activates some random nucleation sites at large current densities due to the large Joule heating existing and the pinning potential barrier landscape could also be redistributed, which can exert an influence on the motion velocity and tilting angle.
During the current-induced DW motion, DW tilting phenomenon is clearly observed in these two samples and the tilting is gradually formed in a time-dependent observation with a sufficient short pulse as the driving force. In order to gain an insight into the current-induced DW tilting, we measure DW tilt angle (ψ) which is defined in Fig. 3a at different current densities. It should also be noted that the tilt angle may slightly change during the motion due to the wide depinning distribution along the racetracks, which will result in a large measuring error at a specific current density. From Fig. 3b, c one can see a roughly linear dependence of the tilt angle on the current density for both samples. It agrees with the previous theoretical work [20], in which approximately linear dependences of the tilt angle and DW velocity on the lower current density can be observed. However, a large DW tilt angle happens with at least one order larger current density in their simulation. This is not consistent with our observation and the tilting behavior is also not observed during the field-induced DW motion in our experiment. Therefore, the influence of the DMI or graded distribution of the pinning potential barrier on the current-induced DW tilting can be weak. Besides, the anomalous Hall effect may also lead to the DW tilting, but the contribution is expected to be small in a nanometer-thick racetrack [20]. One possible explanation is that the applied current not only generates spin Hall effective field HSHE, but also the Oersted field (HOersted) which also can lead to DW motion. Both HSHE and HOersted could have an influence on the DW tilting. In Fig. 4, we plot the sketch of these effective fields to clarify the DW tilting behavior. The domain arrangement is shown as U-D-U-D sketches, and the magnetization in the DW with a left-handed chirality is shown as thin black arrow along the in-plane orientation. In a thin uniform racetrack, if the thickness (t) is much less than the width (w), the generated HOersted is concentrated on the two edges and its averaged component over the thickness can be calculated by HOersted = ±jt[3 + 2lnw/t]/4π [22]. The obtained HOersted are around 19.6 and 37.4 Oe for Pt/Co/Ta and Pt/Co/C/Ta using the maximum current density of 10.0 and 19.2 MA/cm2, respectively, which is comparable to the spin Hall effective field HSHE (around 100.0 and 159.4 Oe for Pt/Co/Ta and Pt/Co/C/Ta at the same current densities). Since HSHE and HOersted have the same direction at the positions marked as green stars, a larger effective field will act on the DW at the green star area, which results in a much larger velocity compared to that at the opposite area of the green stars in the racetrack. Therefore, a tilting DW with a specific trapezoid shape can be formed shown in the left lower panel of Fig. 4. The inset of Fig. 3b for Pt/Co/Ta also obviously shows the similar shape at some representative current densities. Moreover, the increased tilt angle at the higher current density may be explained by the large velocity difference in both edges of the racetrack due to the increased HOersted. Meanwhile, one can find that the domain shape will have a transformation once the domain arrangements and/or the current polarity changes according to the above analysis. All the sketched domain shape at a current pulse is consistent with the experimental observations. Moreover, the above explanation about DW tilting is also valid when an in-plane Hx or Hy is applied. When Hx is applied, it will change the magnetization orientation in DWs. Therefore, the HSHE will change a sign for the DW with its original horizontal magnetization opposite to Hx, which makes the trapezoid-shape domain expand or shrink (depending on the sign of Hx) as shown in the right middle panel of Fig. 4. When Hy is applied, a strong Hy will change a Néel-type DW to a Bloch one. HSHE will become zero according to Eq. (1), and only current generated Oersted field HOersted drives the DW motion. This will make the domain expand at one edge. One can also see that the change of the domain at the edge happens as Hy is around − 1400 Oe as shown in the right lower panel of Fig. 4. This is consistent with the analysis that HOersted as the only driving force is responsible for the DW motion. However, it cannot lead to a regular DW tilting behavior. Therefore, the current-induced DW tilting could be ascribed to the current-induced Oersted field combined with spin Hall effective field.
Conclusions
In summary, current-induced domain wall motion and tilting are observed in Pt/Co/Ta and Pt/Co/C/Ta structures. The DMI strength and SOT efficiency are obtained using a transport measurement method which can reach to 1.01 ± 0.16 (1.15 ± 0.14) mJ/m2 and 10.0 (8.3) Oe/MA/cm2 for Pt/Co/Ta (Pt/Co/C/Ta) samples, respectively. The similar DMI strength for Pt/Co/Ta and Pt/Co/C/Ta samples reveals that the DMI strength mainly comes from the contribution of the Pt/Co interface. The reduced DW velocity in field-induced DW motion for Pt/Co/C/Ta indicates the DW velocity is related to the pinning potential barrier. In addition, current-generated Joule heating and Oersted field play a significant role in the DW motion and tilting. For the racetrack memory application, the large current-generated Oersted field should be considered since it will dramatically change the recording bit shape and even shrink the area of the recording bits. This may be not beneficial to the practical application. Our findings could provide some designing prospects to drive DW motion in SOT-based racetrack memories.
Abbreviations
- CIDWM:
-
Current-induced domain wall motion
- DMI:
-
Dzyaloshinskii–Moriya interaction
- D-U:
-
Down-to-up
- DW:
-
Domain wall
- FIDWM:
-
Field-induced domain wall motion
- FMs:
-
Ferromagnets
- HM:
-
Heavy metal
- PMA:
-
Perpendicular magnetic anisotropy
- SOT:
-
Spin-orbit torque
- STT:
-
Spin transfer torque
- U-D:
-
Up-to-down
References
Parkin SSP, Hayashi M, Thomas L (2008) Magnetic domain-wall racetrack memory. Science 320:190–194
Hayashi M, Thomas L, Moriya R, Rettner C, Parkin SSP (2008) Current-controlled magnetic domain-wall nanowire shift register. Science 320:209–211
Yamaguchi A, Ono T, Nasu S, Miyake K, Mibu K, Shinjo T (2004) Real-space observation of current-driven domain wall motion in submicron magnetic wires. Phys Rev Lett 92:077205
Berger L (1984) Exchange interaction between ferromagnetic domain wall and electric current in thin metallic films. J Appl Phys 55:1954–1957
Koyama T, Chiba D, Ueda K, Kondou K, Tanigawa H, Fukami S, Suzuki T, Ohshima N, Ishiwata N, Nakatani Y, Kobayashi K, Ono T (2011) Observation of the intrinsic pinning of a magnetic domain wall in a ferromagnetic nanowire. Nat Mater 10:194
Kim KJ, Hiramatsu R, Koyama T, Ueda K, Yoshimura Y, Chiba D, Kobayashi K, Nakatani Y, Fukami S, Yamanouchi M, Ohno H, Kohno H, Tatara G, Ono T (2013) Two-barrier stability that allows low-power operation in current-induced domain-wall motion. Nat Commun 4:2011
Moore TA, Miron IM, Gaudin G, Serret G, Auffret S, Rodmacq B, Schuhl A, Pizzini S, Vogel J, Bonfim M (2009) High domain wall velocities induced by current in ultrathin Pt/Co/AlOx wires with perpendicular magnetic anisotropy. Appl Phys Lett 95:179902
Ueda K, Kim KJ, Taniguchi T, Tono T, Moriyama T, Ono T (2015) In-plane field-driven crossover in the spin-torque mechanism acting on magnetic domain walls in Co/Ni. Phys Rev B 91:060405(R)
Ryu KS, Thomas L, Yang SH, Parkin S (2013) Chiral spin torque at magnetic domain walls. Nat Nanotechnol 8:527
Emori S, Bauer U, Ahn SM, Martinez E, Beach GSD (2013) Current-driven dynamics of chiral ferromagnetic domain walls. Nat Mater 12:611
Allen G, Manipatruni S, Nikonov DE, Doczy M, Young IA (2015) Experimental demonstration of the coexistence of spin Hall and Rashba effects in β-tantalum/ferromagnet Bilayers. Phys Rev B 91:144412
Behera N, Chaudhary S, Pandya DK (2016) Anomalous anti-damping in sputtered β-Ta/Py bilayer system. Sci Rep 6:19488
Zhang W, Han W, Jiang X, Yang SH, Parkin SSP (2015) Role of transparency of platinum-ferromagnet interfaces in determining the intrinsic magnitude of the spin Hall effect. Nat Phys 11:496
Huang KF, Wang DS, Lin HH, Lai CH (2015) Engineering spin-orbit torque in Co/Pt multilayers with perpendicular magnetic anisotropy. Appl Phys Lett 107:232407
Zhang W, Jungfleisch MB, Freimuth F, Jiang W, Sklenar J, Pearson JE, Ketterson JB, Mokrousov Y, Hoffmann A (2015) All-electrical manipulation of magnetization dynamics in a ferromagnet by antiferromagnets with anisotropic spin Hall effects. Phys Rev B 92:144405
Demasius KU, Phung T, Zhang W, Hughes BP, Yang SH, Kellock A, Han W, Pushp A, Parkin SSP (2016) Enhanced spin-orbit torques by oxygen incorporation in tungsten films. Nat Commun 7:10644
Woo S, Mann M, Tan AJ, Caretta L, Beach GSD (2014) Enhanced spin-orbit torques in Pt/Co/Ta heterostructures. Appl Phys Lett 105:212404
Yu JW, Qiu XP, Legrand W, Yang H (2016) Large spin-orbit torques in Pt/Co-Ni/W heterostructures. Appl Phys Lett 109:042403
Ueda K, Pai CF, Tan AJ, Mann M, Beacha GSD (2016) Effect of rare earth metal on the spin-orbit torque in magnetic heterostructures. Appl Phys Lett 108:232405
Boulle O, Rohart S, Buda-Prejbeanu LD, Jué E, Miron IM, Pizzini S, Vogel J, Gaudin G, Thiaville A (2013) Domain wall tilting in the presence of the Dzyaloshinskii-Moriya interaction in out-of-plane magnetized magnetic nanotracks. Phys Rev Lett 111:217203
Jué E, Thiaville A, Pizzini S, Miltat J, Sampaio J, Buda-Prejbeanu LD, Rohart S, Vogel J, Bonfim M, Boulle O, Auffret S, Miron IM, Gaudin G (2016) Domain wall dynamics in ultrathin Pt/Co/AlOx microstrips under large combined magnetic fields. Phys Rev B 93:014403
Yamanouchi M, Chiba D, Matsukura F, Dietl T, Ohno H (2006) Velocity of domain-wall motion induced by electrical current in the ferromagnetic semiconductor (Ga, Mn)As. Phys Rev Lett 96:096601
Li D, Cui BS, Wang T, Yun JJ, Guo XB, Wu K, Zuo YL, Wang JB, Yang DZ, Xi L (2017) Effect of inserting a non-metal C layer on the spin-orbit torque induced magnetization switching in Pt/Co/Ta structures with perpendicular magnetic anisotropy. Appl Phys Lett 110:132407
Akyol M, Alzate JG, Yu GQ, Upadhyaya P, Wong KL, Ekicibil A, Amiri PK, Wang KL (2015) Effect of the oxide layer on current-induced spin-orbit torques in Hf|CoFeB|MgO and Hf|CoFeB|TaOx structures. Appl Phys Lett 106:032406
Pai CF, Mann M, Tan AJ, Beach GSD (2016) Determination of spin torque efficiencies in heterostructures with perpendicular magnetic anisotropy. Phys Rev B 93:144409
Thiaville A, Rohart S, Jue E, Cros V, Fert A (2012) Dynamics of Dzyaloshinskii domain walls in ultrathin magnetic films. Europhys Lett 100:57002
Metaxas PJ, Jamet JP, Mougin A, Cormier M, Ferré J, Baltz V, Rodmacq B, Dieny B, Stamps RL (2007) Creep and flow regimes of magnetic domain-wall motion in ultrathin Pt/Co/Pt films with perpendicular anisotropy. Phys Rev Lett 99:217208
Ma X, Yu GQ, Li X, Wang T, Wu D, Olsson KS, Chu ZD, An K, Xiao JQ, Wang KL, Li XQ (2016) Interfacial control of Dzyaloshinskii-Moriya interaction in heavy metal/ferromagnetic metal thin film heterostructures. Phys Rev B 94:180408 (R)
Khvalkovskiy AV, Cros V, Apalkov D, Nikitin V, Krounbi M, Zvezdin KA, Anane A, Grollier J, Fert A (2013) Matching domain-wall configuration and spin-orbit torques for efficient domain-wall motion. Phys Rev B 87:020402 (R)
Yu GQ, Upadhyaya P, Wong KL, Jiang WJ, Alzate JG, Tang JS, Amiri PK, Wang KL (2014) Magnetization switching through spin-Hall-effect-induced chiral domain wall propagation. Phys Rev B 89:104421
Emori S, Beach GSD (2012) Roles of the magnetic field and electric current in thermally activated domain wall motion in a submicrometer magnetic strip with perpendicular magnetic anisotropy. J Phys Condens Matter 24:024214
Acknowledgements
The authors thank prof. Li Xi for proofreading the manuscript.
The authors thank the Key Laboratory for Magnetism and Magnetic Materials of Ministry of Education for enabling the use of testing equipment.
Funding
This work was supported by the Program for Changjiang Scholars and Innovative Research Team in University PCSIRT (No. IRT16R35), the National Natural Science Foundation of China (Nos. 51671098), the Natural Science Foundation of Gansu Province (No. 17JR5RA210), and the Fundamental Research Funds for the Central Universities (lzujbky-2015-122).
Availability of Data and Materials
We confirm that all data and materials are authentic and available.
Author information
Authors and Affiliations
Contributions
DL and LX conceived the experiments. DL, JY, KW, XG, and BC fabricated the device. DL, MC, XZ, YW, and JM conducted the electrical measurements. DL, YZ, JW, and LX discussed the results. DL and LX wrote this manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
The estimation of the DMI effective fields and SOT efficiency as well as the influence of an in-plane bias field Hx or Hy on the anomalous Hall loops. (DOCX 529 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Li, D., Cui, B., Yun, J. et al. Current-Induced Domain Wall Motion and Tilting in Perpendicularly Magnetized Racetracks. Nanoscale Res Lett 13, 238 (2018). https://doi.org/10.1186/s11671-018-2655-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2655-6