Abstract
TMC-incorporated carbon nitride (CN) with hexagonal and quadrangle honeycomb-like structure and having periodic lattice defects linked by –CONH– bond was synthesized through combining the high calcination with the chemical condensation of melamine and 1,3,5-benzenetricarbonyl trichloride. The obtained CN has a tri-s-triazine ring and benzene ring skeleton, which makes it have excellent mechanical and thermal stability. The BET specific surface area was enhanced to about 125.6 m2/g, and the mean pore size is about 3.43 nm. This CN exhibited an excellent adsorption-enhanced photocatalytic performance.
Graphical abstract
![](http://media.springernature.com/lw685/springer-static/image/art%3A10.1186%2Fs11671-018-2654-7/MediaObjects/11671_2018_2654_Figa_HTML.png)
Avoid common mistakes on your manuscript.
Background
Graphite carbon nitride (g-C3N4), possessing a two-dimensional (2D) nanosheet structure like graphene, has attracted much attention recently. The basic skeleton structure of g-C3N4 consists of tri-s-triazine units connected with tertiary amino groups, which owns regularly distributed triangular water-selective permeation nanopores throughout the entire laminar structure. Moreover, the spacers between the g-C3N4 nanosheets, which interact with each other through weak van der Waals forces, also provide nanochannels for water transport while bigger molecules are retained [1]. Due to this unique nanosheet structure, g-C3N4 exhibited many useful properties with applications in many fields, such as membrane separation materials [2, 3], photocatalysis [4,5,6], and electronic devices [7,8,9]. Up to now, the main method to prepare g-C3N4 was high-temperature calcination. However, the specific BET surfaces of these g-C3N4 materials were only 5–35 m2/g [2, 4, 10], which seriously limits the displaying of their unique properties in applications [4]. Then, the enhancement of specific BET surface for g-C3N4 was very important.
Inspired by the structures of covalent organic framework materials (COFs) [11,12,13,14,15,16] and their preparation methods [17], we try to combine the high calcination with the chemical condensation to prepare a new kind of porous TMC-incorporated carbon nitride (CN) linked by –CONH– bond and having periodic lattice defects as well [18]. This CN was synthesized by the condensation of melamine and 1,3,5-benzenetricarbonyl trichloride through the reaction of –NH2 and –COCl. Besides, due to the further calcination and thermal oxidation “etching” using melamine as a precursor, this CN could possess large numbers of –NH and –NH2 groups in the lattice structure, which could endow the CN with excellent performances.
Methods/Experimental
Materials
Melamine (99%), 1,3,5-benzenetricarbonyl trichloride (TMC, 98%), N-N-dimethylacetamide (DMAc, ≥ 99.8%), N,N-dimethylformamide (DMF, 99.5%), and triethyl phosphate (TEP, ≥ 99.5%) were purchased from Aladdin Chemistry Co., Ltd. (China). Ethanol (≥ 99.7 wt.%) and acetic acid (≥ 99.5 wt.%) were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Purified water was purchased from Hangzhou Wahaha Group Co., Ltd. (Hangzhou, China). All the materials and reagents were of analytical grade and used without further purification.
Synthesis of CN Material
The synthesis procedure of CN material is illustrated in Scheme 1. At first, a white suspension was obtained by dissolving melamine (5 g) and TMC (1.75 g) in DMAc (93.25 g) with the stirring at 80 °C for 3 h under oil bath reflow (Additional file 1: Table S1–S3 and Figure S1–S3). Then, the suspension was transferred into roller ball mill to mill 12 h, using zirconia porcelain balls as the ball milling media. After that, the suspension was followed by ultrasonic treatment for 3 h. Secondly, the suspension was filtrated and washed with ethanol and deionized water for three times, respectively. In the end, the resulted white precipitate was dried at 80 °C in vacuum drying oven for about 24 h.
The above white powder was heated in two steps at 550 °C and 500 °C, respectively. Specifically, the procedure consisted in an initial heating from room temperature (25 °C) to 500 °C, which required 150 min, holding for 120 min. Then, the temperature was increased to 550 °C in 10 min and holding for 240 min. After that, the temperature was allowed to drop back to 25 °C, which took 100 min. The obtained bulk CN was milled into powder. Finally, the bulk CN was transferred into an open ceramic boat and heated to 500 °C in air for 4 h with a ramp rate of 10 °C/min. The yield is about 25%.
Characterizations
The size and morphology were analyzed by scanning electron microscopy (SEM, QUANTA FEG450) and transmission electron microscopy (TEM, Tecnai G2 F30 S-TWIN). The crystalline structure was confirmed by X-ray diffraction (XRD, Switzerland ARL/X, TRA). Fourier transform infrared spectrometry (FT-IR, Nicolet is50) was used to study the chemical structure. Thermal stability was inspected using thermal gravimetric analysis and differential scanning calorimetry (TG-DSC, STA449F3). X-ray photoelectron spectroscopy (XPS, Thermo ESCALAB 250) signals were recorded with a monochromatic Al Ka source and a change neutralizer (hv = 1486.6 eV). Conventional method for measurement of the BET specific surface and average pore sizes were carried out by a B40-SA3100PLUS specific surface area and void meter (BECKMAN COULTER). The particle size distribution was analyzed by ZETSIZER NANO (ZSE, Malvern Instruments Ltd., UK).
Photodecomposition of 20 mg/L and 10 mg/L methyl orange (MO) were chosen as the model system to investigate the photoactivity of products using XPA photochemical reactor under visible-light irradiation of a 500-W Xe lamp with a 420-nm cutoff filter. A certain amount known concentration of H2O2 was then added into the reactor after 30 min dark adsorption, and the lamp was turned on to run 120 min continuously. Five milliliters of samples were withdrawn at regular intervals (20 min) with centrifugation to separate solids for measure. Furthermore, the CN suspension was filtered by a filter membrane and washing three times by deionized water and absolute ethanol, respectively. Then, the CN was dried in an oven at 80 °C for 3 h. The obtained CN was used to degrade MO again according to the above steps. The recycling experiments were carried out three times.
In order to prove the structure of the synthesized CN material, the XRD patterns of the CN molecular structure was simulated by Material Studio software (MS 2017, ver. 17.1.). The lattice models (e.g., cell parameters, orientation standard, atomic positions, and total energies) were then fully optimized using MS Forcite and Reflex modules method (Additional file 1: Figure S9).
Results and Discussion
Chemical Structure of CN Material
Figure 1a depicts the chemical structure of CN. The sharp peak at 810 cm−1 was assigned to the s-triazine ring mode. The characteristic peaks appearing at 1239 cm−1, 1324 cm−1, 1470 cm−1, 1569 cm−1, and 1645 cm−1 were related to the C–NH–C and N–(C)3 stretching vibration modes [19]. The peak at 1753 cm− 1 was belonged to –CONH– vibration, which was often called amide I band. A broad absorption around 3170 cm−1 was attributable to stretching modes of primary and secondary amines at the defect sites and their intermolecular hydrogen bonding interactions [2].
XPS was further employed to investigate the surface chemical composition and chemical states of the CN. As shown in Fig. 1b, the C/N ratio of CN was about 1:1, which was far beyond the traditional carbon-rich g-C3N4 [2, 20,21,22] (C/N ratio, about 3:1). Thus, this prepared material is the type of nitrogen-rich g-C3N4 [22] and we marked it as CN, the same phenomenon was obtained from the EDX element analysis in Additional file 1: Figure S5, 6, wherein only carbon, nitrogen, and oxygen species were detected (Fig. 1b). Besides, the O1s peak at 531.9 eV was likely due to the surface adsorbed H2O or hydroxyl group. As can be seen, the four same peaks in Fig. 1c at 288.59 eV, 288.20 eV, 285.42 eV, and 284.75 eV were ascribed to C–N–C, C–(N)3, O=C–N, and C–C groups, respectively. From the high-resolution scan of N1s (Fig. 1d), four typical peaks are ascribed to the nitrogen in C–N–C (398.81 eV), N–(C)3 (399.99 eV), N–H (400.80 eV), and pi-excitations groups (404.75 eV) [3], respectively. Furthermore, from the -resolution scan of O1s (Additional file 1: Figure S7), the two peaks at 533.12 eV and 531.82 eV were ascribed to C–O and C=O groups, respectively. The C=O was mainly ascribed to the C=O–N and C=O–C groups in the TMC and the generated –CONH–. The C–O peak may be due to the surface oxygen cavity or hydroxyl group. In all, from above analysis results, the possible detailed monomer structure is shown in Fig. 2a, and the CN material was prepared in a brief process successfully.
The XRD characterization in Additional file 1: Figure S4a-c was indicated that the crystal structure of CNs were not destroyed by different solvents, temperature, and addition amount of TMC. From Fig. 2b–d, we know that the strong peak located at 26.96° corresponded to the stacking of conjugated aromatic planes (002 planes) and the relatively weak peak at 12.45° was assigned to in-plane structural packing motif of tri-s-triazine units (100 planes), respectively. When different space groups were used to build CN to obtain XRD patterns, typical characteristic peaks of CN were perfectly displayed in the simulated XRD patterns. Thus, the CN structure predicted in this work is reasonable.
Physical Structure of CN Material
The permanent porosity of CN was demonstrated by N2 adsorption-desorption analysis at − 195.671 °C (Fig. 3a). The isotherm shows a sharp uptake below P/P0 = 1.0, and the Brunauer-Emmett-Teller (BET) surface area was calculated to be 125.6 m2/g. Compared with traditional g-C3N4 materials (5–35 m2/g [2, 20, 21], Fig. 3b and Additional file 1: Table S4), the BET surface of this new CN was enhanced greatly. From Scheme 1, through the reactions between –NH2 and –COCl in melamine and TMC, melamine could graft to TMC strongly and regularly, thereby dispersing uniformly in DMAc solution. Then, this process may provide more grafting sites for the subsequent calcination of melamine and improved the BET specific surface area greatly. As shown in Fig. 3c, d, the average particle size of CN was 467.1 nm, which was smaller than the 955.5 nm of g-C3N4. It is also proved that the CN material owned a large BET surface.
It was seen that the CN showed a uniformly distributed and loose block morphology from Fig. 4a. From the Additional file 1: Figure S8, the different CN layer structures were arranged orderly, and there was no obvious agglomeration. Besides, there were many pores in this CN due to the introduction of TMC. Moreover, as clearly observed in TEM (Fig. 4b), the CN owned many wrinkles and grooves. These are just the main reasons for that the CN has a high BET surface.
The results of TGA curves are shown in Fig. 5. From Fig. 5, as the most stable allotrope of carbon nitride, the prepared CN material and g-C3N4 showed a unique temperature resistance up to 721 °C and 710 °C, respectively. From the result, it can be concluded that the CN is thermally stable in oxygen condition under 530 °C.
Adsorption-Enhanced Photoactivity of CN Material
The photoactivity of 20 mg/L and 10 mg/L methyl orange (MO) was investigated by XPA photochemical reactor, which is shown in Fig. 6 (the C0 is the absorbance of MO in initial concentration (20 mg/L and 10 mg/L), the C is the absorbance of MO at different time) [20].
From Fig. 6a, this new CN had a high MO adsorption performance due to the large BET surface. After 120 min, the photoactivity was reached 60% far beyond the photoactivity of g-C3N4 [2], which was about 20%. The CN exhibited an excellent adsorption-enhanced photoactivity, even after 4 cycles under identical conditions (Fig. 6b). As we know, photo induced electron-hole pairs were generated on the surface of CN after absorption visible-light photons which were equal or higher than its band gap. During the photocatalytic process, while the photoelectron of CN reacted with oxygen to generate ⋅O2− and ⋅OH. Subsequently, ⋅O2− and ⋅OH combined with MO to further decompose into CO2 and H2O. However, the periodic lattice defects in the CN and g-C3N4 would capture photo-generated electrons, thereby reducing the photocatalytic efficiency [20]. Thus, the photoactivities of single CN and g-C3N4 materials were not high, which should be combined with other materials.
Conclusions
A new –CONH– bond linked CN material with hexagonal and quadrangle honeycomb-like structure was constructed by combining the high calcination with the chemical condensation of melamine and 1,3,5-benzenetricarbonyl trichloride. This material has a tri-s-triazine ring and benzene ring skeleton structure. The BET specific surface area of CN was about 125.6 m2/g, and the mean pore size is about 3.43 nm. This CN exhibited an excellent adsorption-enhanced photocatalytic performance.
References
Wang Y, Li L, Wei Y, Xue J, Chen H, Ding L, Caro J, Wang H (2017) Water transport with ultralow friction through partially exfoliated g-C3N4 nanosheet membranes with self-supporting spacers. Angew Chem Int Ed 56:8974–8980
Wang J, Li M, Zhou S, Xue A, Zhang Y, Zhao Y, Zhong J, Zhang Q (2017) Graphitic carbon nitride nanosheets embedded in poly (vinyl alcohol) nanocomposite membranes for ethanol dehydration via pervaporation. Sep Purif Technol 188:24–37
Cao K, Jiang Z, Zhang X, Zhang Y, Zhao J, Xing R, Yang S, Gao C, Pan F (2015) Highly water-selective hybrid membrane by incorporating g-C3N4 nanosheets into polymer matrix. J Membr Sci 490:72–83
Fang LJ, Li YH, Liu PF, Wang DP, Zeng H, Wang X, Yang HG (2017) Facile fabrication of large-aspect-ratio g-C3N4 nanosheets for enhanced photocatalytic hydrogen evolution. ACS Sustain Chem Eng 5:2039–2043
Ma XG, Lv YH, Xu J, Liu YF, Zhang RQ, Zhu YF (2012) A strategy of enhancing the photoactivity of g-C3N4 via doping of nonmetal elements: a first-principles study. J Phys Chem C 116:23485–23493
Zhang X, Xie X, Wang H, Zhang J, Pan B, Xie Y (2013) Enhanced photoresponsive ultrathin graphitic-phase C3N4 nanosheets for bioimaging. J Am Chem Soc 135:18–21
Ding X, Guo J, Feng X, Honsho Y, Guo J, Seki S, Maitarad P, Saeki A, Nagase S, Jiang D (2011) Synthesis of metallophthalocyanine covalent organic frameworks that exhibit high carrier mobility and photoconductivity. Angew Chem Int Ed 50:1289–1293
Wan S, Gándara F, Asano A, Furukawa H, Saeki A, Dey SK, Liao L, Ambrogio MW, Botros YY, Duan X (2011) Covalent organic frameworks with high charge carrier mobility. Chem Mater 23:4094–4097
Wang P, Zong L, Guan Z, Li Q, Yang J (2018) PtNi alloy cocatalyst modification of eosin Y-sensitized g-C3N4/GO hybrid for efficient visible-light photocatalytic hydrogen evolution. Nanoscale Res Lett 13:33–41
Zhang XS, Hu JY, Jiang H (2014) Facile modification of a graphitic carbon nitride catalyst to improve its photoreactivity under visible light irradiation. Chem Eng J 256:230–237
Côté AP, Benin AI, Ockwig NW, O'Keeffe M, Matzger AJ, Yaghi OM (2005) Porous, crystalline, covalent organic frameworks. Science 310:1166–1170
Ding SY, Wang W (2013) ChemInform abstract: covalent organic frameworks (COFs): from design to applications. Chem Soc Rev 42:548–568
Xue R, Guo H, Wang T, Wang X, Ai JB, Yue LG, Wei YL, Yang W (2017) Synthesis and characterization of a new covalent organic framework linked by -NH- linkage. Mater Lett 209:171–174
Graetz J (2009) New approaches to hydrogen storage. Chem Soc Rev 38:73–82
Fang QR, Wang JH, Gu S, Kaspar RB, Zhuang ZB, Zheng J, Guo HX, Qiu SL, Yan YS (2015) 3D porous crystalline polyimide covalent organic frameworks for drug delivery. J Am Chem Soc 137:8352–8355
Zhuang X, Mai Y, Wu D, Zhang F, Feng X (2015) Two-dimensional soft nanomaterials: a fascinating world of materials. Adv Mater 27:403–427
Chen Y, Xie B, Ren Y, Yu M, Qu Y, Xie T, Zhang Y, Wu Y (2014) Designed nitrogen doping of few-layer graphene functionalized by selective oxygenic groups. Nanoscale Res Lett 9:646–654
Hu M, Mi B (2013) Enabling graphene oxide nanosheets as water separation membranes. Environ Sci Technol 47:3715–3723
Wang C, Li Z, Chen J, Li Z, Yin Y, Cao L, Zhong Y, Wu H (2017) Covalent organic framework modified polyamide nanofiltration membrane with enhanced performance for desalination. J Membr Sci 523:273–281
Xu YS, Zhang LL, Yin MH, Xie DY, Chen JQ, Yin JZ, Fu YS, Zhao PS, Zhong H, Zhao YJ, Wang X (2018) Ultrathin g-C3N4 films supported on attapulgite nanofibers with enhanced photocatalytic performance. Appl Surf Sci 440:170–176
Wang J, Li MS, Zhou SY, Xue AL, Zhang Y, Zhao YJ, Zhong J (2018) Controllable construction of polymer/inorganic interface for poly (vinyl alcohol)/graphitic carbon nitride hybrid pervaporation membranes. Chem Eng Sci 181:237–250
Zhang JS, Wang B, Wang XC (2013) Chemical synthesis and applications of graphitic carbon nitride. Acta Phys -Chim Sin 29:1865–1876
Acknowledgements
The authors are grateful for the financial support of Jiangsu Province Natural Science Foundation (BK20171268), the National Natural Science Foundation of China (21878118, 21476094), the Major Projects of Natural Science Foundation of Jiangsu Higher Education Institutions of China (18KJA530003),the Program for Science and Technology Development of Huaian (HAG201609), and Jiangsu Province Qing Lan Project and the Opening Program for Jiangsu Key Lab for Chemistry of Low-Dimensional Materials (JSKC15142).
Availability of Data and Materials
The datasets supporting the conclusions of this article are included within the article and in Additional file 1.
Author information
Authors and Affiliations
Contributions
JW, Prof. ML, and Prof. YZ gave the idea and designed and performed the experiment, data processing, and manuscript drafting. Prof. ML modified the manuscript writing. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
Table S1. BET surface areas and average pore sizes of CNs prepared at 80 °C with the addition amount of 1.0 g TMC under different solvents. Table S2. BET surface areas and average pore sizes of CNs prepared at different temperature with the addition amount of 1.0 g TMC under the solvent of DMAc. Table S3. BET surface areas and average pore sizes of CNs prepared with different addition amount of TMC under the solvent of DMAc at 80 °C. Figure S1. Pore size distribution of CNs at 80 °C with the addition amount of 1.0 g TMC under different solvents. (a) H2O, (b) CH3COOH, (c) DMAc, (d) TEP, (e) DMF. Inset: N2 adsorption and desorption isotherm for CNs measured at − 195.671 °C. Figure S2. Pore size distribution of CNs at different temperature with the addition amount of 1.0 g TMC under the solvent of DMAc. (a) 50 °C, (b) 60 °C, (c) 70 °C, (d) 90 °C, (e) 100 °C. Inset: N2 adsorption and desorption isotherm for CNs measured at − 195.671 °C. Figure S3. Pore size distribution of CNs with different addition amount of TMC under the solvent of DMAc at 80 °C. (a) 1.5 g, (b) 2.0 g, (c) 2.5 g. Inset: N2 adsorption and desorption isotherm for CNs measured at − 195.671 °C. Table S4. The comparison of BET surface areas of CNs. Figure S4. XRD of different CNs (a) different solvents, (b) different temperature and (c) different addition amount of TMC. Figure S5. EDX spectra of (a) H2O, (b) CH3COOH, (c) DMAc, (d) TEP, (e) DMF. Figure S6. The element analysis of EDX. Figure S7. The high resolution scan of O1s of CN material. Figure S8. SEM images of CNs under different solvents. (a) H2O, (b) CH3COOH, (c) TEP, (d) DMF. Figure S9. Flow chart of simulation calculation of CN material. (DOC 8323 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Wang, J., Li, M., Qian, M. et al. Simple Synthesis of High Specific Surface Carbon Nitride for Adsorption-Enhanced Photocatalytic Performance. Nanoscale Res Lett 13, 248 (2018). https://doi.org/10.1186/s11671-018-2654-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2654-7