Abstract
This study reports an analysis of the IR reflectance and Raman spectra of Cd x Zn(1 − x)P2 solid solutions. We have analyzed the effect of the doping of the CdP2 single crystal by the ZnP2 nanoclusters on the vibrational properties of studied samples: ε 0, ε inf, phonon frequencies, and strengths. These dependencies might be used as an alternative non-destructive way for the control of the Cd x Zn(1 − x)P2 composition. The obtained results show that variation of the concentration of ZnP2 nanoclusters opens a space to design the tailored material properties for the industrial applications.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Zinc and cadmium diphosphides ZnP2 and CdP2 are semiconductors which are characterized by a number of unique properties which make these materials promising for usage in different electronic devices, such as temperature detectors, deflectometers of laser beams, photoconducting cells, magnetic sensors, extenders and stabilizers of laser radiation, and photovoltaic applications [1, 2]. Vibrational properties of ZnP2 and CdP2 have been previously studied in [3–6] in the wide temperature range. However, vibrational properties of the solid solutions Cd x Zn(1 − x)P2 have not been studied yet. Doping CdP2 by the ZnP2 nanoclusters should modify the properties of the solid solutions Cd x Zn(1 − x)P2. This work is aimed to study the influence of concentration of ZnP2 nanoclusters on the vibrational properties of Cd x Zn(1 − x)P2 solid solutions. In order to achieve this aim, it is desired to understand the role of the ZnP2 nanoclusters in the vibrational properties of Cd x Zn(1 − x)P2 solid solutions to provide valuable information for understanding the electron-phonon interaction and transport properties in these solutions, which influence the electronic device performances.
This paper has the following structure: after the “Background” section which briefly summarizes the previous results and represents the motivation of the work, we describe the experimental procedures, such as preparing the samples, optical spectrum measurements, and their treatment. In the “Results and Discussion” section, we describe the influence of the doping of CdP2 by the ZnP2 nanoclusters on the vibrational properties of Cd x Zn(1 − x)P2 by the analysis of the systematic changes in the IR reflectance and Raman spectra. In the “Conclusions” section, we summarize the obtained results.
Methods
Tetragonal α-ZnP2 and β-CdP2 belong to the space symmetry group P41212 (\( {D}_4^4 \)) with the following lattice constants: α-ZnP2 a = b = 0.50586(7) nm and c = 1.8506(4) nm and β-CdP2 a = b = 0.52768(7) nm and c = 1.9753(4) nm [7]. As one can notice from Fig. 1, where the unit cell of tetragonal CdP2 and ZnP2 is displayed, each ion of metal M (Zn, Cd) is surrounded by four ions of anion A (P) and each ion A is surrounded by two ions M and two ions A. Ionic radius A is about 0.1 nm, and as A-A distance is 0.21 nm approximately, the chemical bond between anions is rather strong. The ions of anions in the structure of diphosphides form zigzag chains [1]. The ions of metal M are at the center of the deformed tetrahedron and link the chains of anions in a 3D structure. Diphosphides CdP2 and ZnP2 posses a complex character of chemical bonds: while phosphorus-phosphorus bonds exhibit a covalent character, in metal-anion bond, a proportion of ionic character (from 16 up to 54 % by different estimations) is present [1]. Figure 1 shows also that the elementary cell of CdP2 and ZnP2 consists of four layers revolved from each other on 90°. Very often, the sequence of packing of layers is broken, and instead of four, it is possible to observe the multiplets of six or five layers.
Polycrystalline CdP2 obtained from the initial elements by a two-temperature way were used to grow single crystals of CdP2. Ampoules with polycrystalline CdP2 were vacuumized till 10−3 Pa, soldered, and put into horizontal and vertical resistance furnace. Single crystals of CdP2 were grown in the conic side of the ampoule. Constancy of the temperature in the evaporation zone during all the process of growth was achieved by moving the ampoule sideways of the crystallization zone with a speed of 0.6–0.8 mm/h. XRD confirms that grown single crystals of CdP2 are single phase.
To obtain Cd x Zn(1 − x)P2 solid solutions, Zn was deposited on the CdP2 single crystal and annealed at the temperature of 650 °C for 600 h. The obtained Cd x Zn(1 − x)P2 represents a CdP2 single crystal with inclusions of crystalline ZnP2 with a size of up to 100 nm [1]. Variation of the concentration of ZnP2 nanoclusters in the solution was obtained by the variation of the annealing temperature and time. The concentration of ZnP2 nanoclusters has been controlled by X-ray fluorescence (XRF). In the present work, we studied two Cd x Zn(1 − x)P2 samples with x = 0.9991 and 0.9997.
In this study, we used a set of samples of single crystals in the shape of plates with a size of 2 mm × 3 mm × 1 mm.
Reflectance spectra of the samples were measured in the range from 100 to 500 cm−1 at room temperature, using a Bruker IFS 88 spectrometer with a globar as the radiation source and employing a resolution of 1 cm−1 and polarized radiation. We have collected 256 scans in each experiment. Spectra were taken for the E ⊥ c orientation of the electrical vector E of the IR radiation with respect to the crystal. Raman spectra were measured in the spectral range from 60 to 3600 cm−1 at room temperature using a FRA-106 Raman attachment applying the diode pump Nd:YAG laser of ca. 200-mW power and liquid nitrogen-cooled Ge detector for y(zz)y backscattering configuration with the resolution set to 1 cm−1 with 256 scans collected in each experiment.
To analyze the reflectance spectra, we used the model of the dielectric function which includes the following summands: ε inf, which describes the polarizability of bounded electrons and plays the major role in the higher energy range (i.e., core electrons) [8]; phonon contributions were described by Lorentz oscillators with three parameters: the frequency ν j , the damping coefficient γ j , and the oscillator strength S j [9]. Measured Raman spectra were analyzed in CoRa [10], by modeling the Raman bands with Gauss and Lorentz profiles.
Results and Discussion
The vibrational modes of CdP2 and ZnP2 have the following symmetry types: 9A 1 + 9A 2 + 9B 1 + 9B 2 + 18E according to the results of [11]. Modes of the symmetry A 2(z) and E(x,y) modes are IR active, whereas A 1, B 1, B 2, and E are first-order Raman active. Reflectance and Raman spectra of CdP2, two Cd x Zn(1 − x)P2 (with different x values) samples, and ZnP2 samples are presented in Fig. 2. In the studied spectral range, we observe eight reflectance and ten Raman peaks. The first visual inspection of the experimental data shows that the obtained reflectance and Raman spectra of the studied samples exhibit a generic pattern. However, one can notice a presence of several differences, such as peaks’ intensities and positions and background values of the reflectance. In the following, we analyze the systematic character of these differences and their correlations with the value of (1 − x) which describes the relative amount of zinc in the studied sample.
We start our analysis with the most noticeable feature noticed in the spectra. As mentioned above, the crystal structures of ZnP2 and CdP2 are similar; therefore, spectra display a generic profile. Qualitative analysis based on the visual inspection of the data convinces that reflectance and Raman peaks shift to the higher wave numbers with increasing the concentration of ZnP2 nanoclusters. This can be explained by the difference in masses of Cd and Zn ions: different energies are needed for the excitement of the light Zn and heavy Cd ions. Peaks observed in the reflectance and Raman spectra of the samples of solid solutions originate from the contributions of the corresponding vibrations of Cd and Zn ions. Therefore, to fit these spectra, the frequencies of the corresponding oscillators have been slightly changed with respect to the concentration of ZnP2 nanoclusters. In order to perform the quantitative analysis of the phonon frequency changes, we have calculated the relative phonon peaks’ frequency shift \( \left({\nu}_j-{\nu}_{j\;{\mathrm{CdP}}_2}\right)/{\nu}_{j\;{\mathrm{CdP}}_2} \) for the studied samples and plotted versus the corresponding CdP2 phonon frequencies \( {\nu}_{j\;{\mathrm{CdP}}_2} \), as shown in Fig. 3 with linear trend lines for better data visualization. Interestingly enough is that Fig. 3 illustrates also the sensitivity of the low-frequency modes to the change of ZnP2 concentration. In diphosphides CdP2, ZnP2 anion atoms form zigzag chains which penetrate through the crystal [7]. In [12], the low-frequency lattice vibrations have been attributed to the Zn(Cd)-P and Zn(Cd)-Zn(Cd) modes, whereas the high-frequency peaks were assigned to the internal vibrations of the phosphorus chain. Therefore, upon the decrease of the x, most changes occur with the low-frequency cation vibrations, whereas the high-frequency vibrations of the phosphorus chain remain mostly unchanged.
Next, a noticeable feature of the reflectance spectra is the change in the size of reflectance peaks. According to the Lorentz model which was applied to fit these peaks, the parameter S j called the oscillator strength is responsible for the width of reflectance peaks. Figure 4 represents the systematic change in the summarized oscillator strength on x. It is obvious that the summarized oscillator strength steadily increases upon moving towards CdP2. As a next step in this analysis, we have looked at the distribution of the oscillator change on the corresponding oscillator frequencies. In Fig. 5, where the ΔS j is plotted versus the corresponding CdP2 phonon frequency, one can see again that low frequency is prone to the main changes of the oscillator strength. We believe that the observed evolution of the oscillators’ strengths could be explained in terms of the electronic polarizability of the vibrating ions. As reported in [13], Cd ions exhibit significantly higher polarizability, and therefore, the replacement of the Cd ions by Zn ones, upon forming the ZnP2 nanoclusters, reduces the corresponding dipole moment, which we detected in the reduced oscillator strength. This parameter links the static- and high-frequency dielectric permittivity of the material via a well-known relation:
Interestingly enough is to analyze the impact of the parameter x on the dielectric permittivity of Cd x Zn(1 − x)P2 beyond the phonon range. Whereas in the range of optical phonons the dielectric function is mainly governed by the phonons’ frequency, strength, and damping, above this phonon range and below the optical absorption, the parameter ε inf plays a crucial role in the dielectric permittivity of the sample. The ε inf is directly linked to the polarizabilites of the material’s components via the Clausius-Mossotti equation [9]. The electronic polarizabilities of the component cations of Cd x Zn(1 − x)P2 were reported in [13] as 0.46 Å3 for Zn and 0.7 Å3 for Cd. This explains the higher value of the ε inf in CdP2 in comparison with the lower value of the ε inf in ZnP2, as reported in [3, 5, 6, 14]. Thus, as shown in Fig. 6, doping the CdP2 by the ZnP2 nanoclusters enables one to vary the ε 0 and ε inf in the range between the corresponding values of CdP2 and ZnP2.
Conclusions
Thus, we performed an analysis of the doping of the CdP2 by the ZnP2 nanoclusters on the vibrational properties of Cd x Zn(1 − x)P2 solid solutions. We have shown that ZnP2 nanoclusters impact ε 0, ε inf, phonon frequencies, and strengths. Analysis of these dependences enables one to design the tailored material properties and might be used as an alternative non-destructive way for the control of the Zn concentration in Cd x Zn(1 − x)P2 solid solutions.
References
Marenkin SF, Trukhan VM (2010) Phosphides and arsenides of Zn and Cd. IP, A.N. Varaksin, Minsk
Stepanchikov D, Shutov S (2006) Cadmium phosphide as a new material for infrared converters. Semicond Phys Quantum Electron Optoelectron 9:40–44
Shportko KV, Izotov AD, Trukhan VM et al (2014) Effect of temperature on the region of residual rays of CdP2 and ZnP2 single crystals. Russ J Inorg Chem 59:986–991. doi:10.1134/S0036023614090204
Baran J, Pasechnik YA, Shportko KV, Trzebiatowska-Gusowska M, Venger EF (2006) Raman and FIR reflection spectroscopy of ZnP2 and CdP2 single crystals. J Mol Struct 792–793:239–242. doi:10.1016/j.molstruc.2006.01.068
Shportko KV, Rückamp R, Trukhan VM, Shoukavaya TV (2014) Reststrahlen of CdP2 single crystals at low temperatures. Vib Spectrosc 73:111–115. doi:10.1016/j.vibspec.2014.05.001
Shportko KV, Pasechnik YA, Wuttig M, Rueckamp R, Trukhan VM, Haliakevich TV (2009) Plasmon–phonon contribution in the permittivity of ZnP2 single crystals in FIR at low temperatures. Vib Spectrosc 50:209–213. doi:10.1016/j.vibspec.2008.11.006
Aleinikova KB, Kozlov AI, Kozlova SG, Sobolev VV (2002) Electronic and crystal structures of isomorphic ZnP2 and CdP2. Phys Solid State 44:1257–1262. doi:10.1134/1.1494619
Reul J, Fels L, Qureshi N et al (2013) Temperature-dependent optical conductivity of layered LaSrFeO4. Phys Rev B Condens Matter Mater Phys 87:205142
Fox M (2006) Optical properties of solids. Oxford University Pres, Oxford
Shportko K, Ruekamp R, Klym H (2015) CoRa: an innovative software for Raman spectroscopy. J NANO Electron Phys 7:1–4
Gorban IS, Gorinya VA, Dashkovskaya RA, Lugovoi VI, Makovetskaya AP, Tychina II (1978) One and two-phonon states in tetragonal ZnP2 and CdP2 crystals. Phys Stat Sol (b) 86:419–424
Jayaraman A, Maines RG, Chattopadhyay T (1986) Effect of high pressure on the vibrational modes and the energy gap of ZnP2. Pramana J Phys 27:291–297
Shanker J, Agrawal SC, Lashkari AKG (1978) Electronic polarizabilities of ions in the chalcogenides of Zn and Cd. Solid State Commun 26:675–677. doi:10.1016/0038-1098(78)90717-2
Venger EF, Pasechnik YA, Shportko KV (2005) Reflection spectra of phosphides in the residual beams region. J Mol Struct 744–747:947–950
Acknowledgements
One of the authors (KS) gratefully acknowledges the support from the Polish Academy of Sciences.
Authors’ Contributions
TS and VT prepared the samples. KS, SS, and JB performed the measurements. KS, JB, TS, VT, SS, and EV discussed the results. KS analyzed the experimental data and drafted the manuscript. VT and JB helped draft the manuscript. All authors read and approved the final manuscript.
Competing Interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Shportko, K., Shoukavaya, T., Trukhan, V. et al. The Role of ZnP2 Nanoclusters in the Vibrational Properties of Cd x Zn(1 − x)P2 Solid Solutions. Nanoscale Res Lett 11, 423 (2016). https://doi.org/10.1186/s11671-016-1635-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1635-y