Abstract
CdS crystallites with rod- and flower-like architectures were synthesized using a facile hydrothermal growth method. The hexagonal crystal structure of CdS dominated the growth mechanisms of the rod- and flower-like crystallites under specific growth conditions, as indicated by structural analyses. The flower-like CdS crystallites had a higher crystal defect density and lower optical band gap value compared with the rod-like CdS crystallites. The substantial differences in microstructures and optical properties between the rod- and flower-like CdS crystallites revealed that the flower-like CdS crystallites exhibited superior photoactivity, and this performance could be further enhanced through appropriate thermal annealing in ambient air. A postannealing procedure conducted in ambient air oxidized the surfaces of the flower-like CdS crystallites and formed a CdO phase. The formation of heterointerfaces between the CdS and CdO phases mainly contributed to the improved photoactivity of the synthesized flower-like CdS crystallites.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Semiconductor photocatalysts have attracted considerable attention because of their successful utilization of solar energy for solving environmental remediation problems. However, because of their wide band gap, most photocatalysts are active only under ultraviolet light, which occupies several percentages of the received solar energy [1, 2]. The development of efficient photocatalysts for visible light irradiation has therefore become a critical scientific challenge for the photocatalyst community [3–5]. Compared with the abundant wide band gap semiconductor photocatalysts, photocatalysts with a visible-light band gap are relatively limited in number. Among the reported candidates of semiconductors with a visible-light band gap, CdS is a vital member of the II–VI semiconductor group with a direct band gap of approximately 2.4 eV, and it has high refraction index, excellent transport properties, and suitable energetics for harvesting solar light for photoactivated device applications. Several studies have fabricated CdS photocatalysts with various morphologies and scales for photoactivated device applications [5–8]. Among various synthesis methods, the hydrothermal synthesis route has been considered one of the most promising synthetic routes for fabricating binary semiconductor crystals because of its low process cost, easy process control, and high product reproducibility [9].
The photocatalytic activity of semiconductors is highly associated with their microstructures, which are substantially dominated by the crystal growth mechanisms under specific growth conditions. The crystal morphology, size, and composition are major factors influencing the efficiency of light absorption and photocatalytic performance [10–12]. Therefore, understanding the correlation between the crystal growth mechanism and the crystal feature is crucial in designing semiconductor photocatalysts with high photocatalytic performance. Recently, semiconductor heterostructures comprising two compounds have attracted research attention and have been used to improve photoactivated properties compared with the corresponding individual constituents [10, 13–15]. A suitable band alignment between the constituents is an effective method for separating photoinduced electron–hole pairs and enhancing photocatalytic performance [14, 16, 17]. Preparing two semiconductor compounds for heterostructures usually requires a complex and incompatible two-step process, and thus hinders the actual applications of such semiconductor heterostructures in photodegradation. Therefore, the selection of a simple synthesis process and constituent compound for a CdS-based heterostructure is crucial to realize its photocatalytic applications. CdO is an n-type semiconductor with a band gap in the visible-light region [18, 19]. Incorporating CdO into CdS to form a heterostructure might be favorable for improving the photoactivated properties of CdS-based materials because of the special band alignment structure between CdO and CdS [20]. The current study investigated the crystal growth, crystal features, and optical properties of rod- and flower-like CdS crystallites synthesized using a facile hydrothermal method. Moreover, a simple postannealing procedure was adopted to fabricate the CdS–CdO heterostructure. The photocatalytic performance levels of the CdS crystallites with various morphologies and CdO to form a heterostructure were compared and discussed on the basis of the differences in their microstructures.
Methods
In this study, CdS crystallites with various morphologies were synthesized using a hydrothermal method. Ethylenediamine solution was used as a surfactant to hydrothermally synthesize high-density rod-like CdS crystallites. Moreover, flower-like CdS crystallites were synthesized without ethylenediamine-assisted growth. The precursor solution for the hydrothermal synthesis comprised cadmium nitrate and thiourea with a molar ratio of 1:5 and was balanced with ethylenediamine solution or deionized water. The precursor solution was stirred for 10 min and then transferred into a Teflon autoclave to undergo a hydrothermal synthesis reaction. The temperature for the hydrothermal synthesis reactions was fixed at 170 °C and maintained for different durations. Finally, the reaction system was cooled to room temperature naturally, and the final precipitates were then washed in deionized water and dried in an oven. The CdO@CdS heterostructure was prepared by subjecting the flower-like CdS crystallites to thermal postannealing at 400 °C for 5 min in ambient air.
Sample crystal structures were investigated by X-ray diffraction (XRD; Bruker D2 PHASER) using Cu Kα radiation. The morphologies of the as-synthesized samples were characterized by scanning electron microscopy (SEM; Hitachi S-4800), and high-resolution transmission electron microscopy (HRTEM; Philips Tecnai F20 G2) was used to investigate the detailed microstructures of the samples. Room-temperature-dependent photoluminescence (PL; HORIBA HR800) spectra were obtained using the 325-nm line of a He–Cd laser. The diffuse reflectance spectra of the samples were recorded by using UV–Vis spectrophotometer (Jasco V750). Photocatalytic activity of as-prepared samples were performed by comparing the degradation of 10−6 M aqueous solution of methylene blue (MB) with various CdS samples as catalysts under visible light irradiation (λ > 420 nm). For each photodegradation test, 50 mg of CdS catalysts powdered sample was dispersed in 20 mL of MB solution. After the photodegradation reaction, the supernatant solution was measured by UV–Vis spectrophotometer in the wavelength range of 400–700 nm and analyzed the photodegradation ratio at the maximum absorption wavelength (~663 nm) of MB aqueous solution. The photodegradation size is defined as (C/C o), where C o is the concentration of aqueous MB without irradiation after dark adsorption equilibrium and C is the concentration of aqueous MB corresponding to a given visible light irradiation duration.
Results and Discussion
Figure 1a–c depicts the SEM images of different growth stages of the rod-like CdS crystallites for various hydrothermal growth durations. Figure 1a shows that the hydrothermal precursor solution colloids have begun to form aggregates to provide nucleation sites in the initial stage of the hydrothermal growth. The surface of the aggregates turned thorny with increased hydrothermal growth duration, demonstrating that the CdS crystals have a tendency to grow along particular orientations from the surfaces of the initially formed aggregates (Fig. 1b). As the hydrothermal growth duration continued increasing, the as-formed tiny thorny crystals further grew because of the continuous supply of many CdS molecules from the precursor solution. These molecules were absorbed into the tiny thorny crystals and mainly grew along a specific crystal direction; finally, large CdS clusters with clear rod-like CdS extrusions were successfully formed on the substrate with a sufficient hydrothermal growth duration (Fig. 1c) [21]. As indicated in the high-magnification SEM image in Fig. 1d, the length of the CdS nanorods was approximately 100–250 nm, and the diameter of the CdS nanorods was approximately 10 nm. Figure 2a–d depicts the SEM images of the different growth stages of the flower-like CdS crystallites for various hydrothermal growth durations (1, 1.5, 2, and 5 h, respectively). Figure 2a shows CdS pellets with a size of approximately 150–200 nm dispersed on the substrate during the initial growth stage of the hydrothermal crystal growth process. When the hydrothermal growth duration was further increased to 1.5 h, the size of the CdS pellets increased to approximately 400–650 nm (Fig. 2b). Pellet-like crystals with a clear rugged surface were formed during this stage. The CdS crystals were coarsened by their aggregation with neighboring CdS pellets as the growth duration increased (Fig. 2c); many CdS crystal branches with lengths of several micrometers were formed because the CdS crystals continued to grow along specific orientations from various facets of the aggregated pellets for the prolonged growth duration. Finally, CdS crystals with a flower-like architecture were formed for sufficient hydrothermal growth duration (Fig. 2d). The flower-like CdS crystals comprised small secondary twigs on the main CdS branches, which were preformed from the crystal growth of coarse CdS pellets, as exhibited in Fig. 2c. The image of a single flower-like CdS and its high-magnification version obtained from the top region of the image (Fig. 2e, f) demonstrated that these secondary twigs had an angle interval of approximately 60° between each CdS twig, showing a clear extended secondary crystal growth from the hexagonal phase of main CdS branches. The lengths of the CdS branches were approximately 2.5–4 μm, and the sizes of the CdS twigs reached several hundred nanometers.
Figure 3a, b shows the XRD patterns of the rod- and flower-like CdS crystallites, respectively. Bragg reflections were observed for the rod-like CdS crystals and were ascribed to the hexagonal phase of CdS (JCPDS no. 00-041-1049); moreover, no other impurity phases were detected. The flower-like CdS crystals also exhibited Bragg reflections originating from the hexagonal phase of CdS. Notably, the peak intensity of hexagonal CdS (002) was considerably stronger than other peaks, indicating that the flower-like CdS crystals were preferentially grown along the c-axis orientation of the hexagonal phase.
Figure 4a depicts a low-magnification TEM image of the rod-like CdS crystallites, and Fig. 4b shows the selected area electron diffraction (SAED) pattern obtained from the rod-like CdS crystallites in Fig. 4a. The rod-like CdS crystallites had a homogeneous diameter of approximately 10 nm. Moreover, the hexagonal CdS (100), (002), and (101) were indexed on the SAED pattern, and these crystallographic planes are in close agreement with the XRD results. Figure 4c shows the energy-dispersive X-ray spectroscopy (EDS) spectra obtained from the rod-like CdS crystallites, confirming that Cd and S formed the major elemental composition of the sample. Figure 4d, e shows the high-resolution TEM images taken from the local regions (marked with red circles in Fig. 4a) of various rod-like CdS crystallites. Clear and ordered lattice fringes in the CdS crystallites revealed that the as-synthesized rod-like CdS crystallites exhibited a high degree of crystallinity. The atomic lattice fringes had an interval of approximately 0.334 nm, which corresponds to the interatomic distance of hexagonal CdS (002). The corresponding fast Fourier transform (FFT) patterns of the CdS crystallites are shown in the insets of Fig. 4d, e. The FFT patterns show the crystal orientation of the single crystalline CdS herein. These results indicate that each rod-like CdS crystallite is in a single crystalline, and the crystal growth of the rod-like CdS crystallite is along the c-axis of the hexagonal phase. Figure 5a–c shows a series of low-magnification TEM images of single and grouped flower-like CdS crystallites. The EDS spectrum showed that the pure flower-like CdS crystallites were formed without any impurities (Fig. 5d). Figure 5e, f shows the HRTEM images obtained from the local regions of various CdS twigs. The lattice fringes with an interval of approximately 0.334 nm corresponded to the lattice constant of hexagonal CdS (002). The clear FFT patterns in the insets of Fig. 5e, f exhibit a high atomic order of the CdS phase in the selected regions. The formation of CdO@CdS heterostructures through the annealing of the flower-like CdS crystallites in ambient air was difficult to identify using the XRD pattern and SEM image because of the trace content of the CdO phase in the heterostructures. The successful synthesis of the CdO@CdS heterostructures was further confirmed by TEM analyses (Fig. 6). As shown in the low-magnification TEM image (Fig. 6a), the morphology of the flower-like CdO@CdS heterostructure had no marked change compared with that of the flower-like CdS crystallite without postthermal annealing. Figure 6b, c shows the HRTEM images obtained from the edges of the heterostructure. Clear and ordered lattice fringes with intervals of approximately 0.237 and 0.271 nm, corresponding to cubic CdO (200) and CdO (111), respectively, were observed (JCPDS no. 005–0640), and the lattice fringes with an interval of approximately 0.334 nm in the internal region matched the spacing distance of hexagonal CdS (002). Moreover, the FFT patterns in the insets of Fig. 6b, c confirm the formation of a crystalline CdO phase in the outer region of the heterostructure when the CdS crystallites underwent postthermal annealing.
The crystal growth mechanism for the rod-like CdS crystallites is schematically shown in Fig. 7. According to the aforementioned structural information, the possible crystal growth mechanism of the rod-like CdS architecture could be divided into four stages. At the hydrothermal reaction stage, alkaline medium S2− ions were generated by the hydrolysis of thiourea, whereas Cd2+ ions were generated by the hydrolysis of cadmium nitrate [22]. Upon heating the reaction solution during the initial hydrothermal reaction stage, the complex precursors were decomposed, and S2− ions were gradually increased with the reaction time and then reacted with Cd2+ ions to nucleate tiny and dispersed CdS crystals in the reaction solution (the first stage). The as-formed tiny CdS crystals further underwent bonding interaction among the adjacent tiny CdS crystals because of a drop in surface energy. The tiny crystals then began to assemble to form CdS crystals with a sufficient size to be stable exist in the reaction solution in the second stage. When the reaction duration was further increased, these CdS crystals formed large and irregular aggregates. Notably, because of its strong coordination interaction with metal ions, ethylenediamine has been shown to play a crucial role in promoting the growth of hexagonal ZnS crystals along its c-axis orientation to form one-dimensional rod-like nanostructures through an aqueous chemical method [23]. It was therefore suggested in the current study that the ethylenediamine surfactant acted as a template-directing agent, continuously inducing the Cd2+ and S2− ions in the reaction solution to adsorb with favorable directions onto the as-formed CdS aggregates. The addition of ethylenediamine in the reaction solution might promote the continuous growth of the newly formed CdS crystals along the c-axis crystal facet on the CdS aggregates; CdS aggregates with a needle-like surface structure were consequently formed (third stage). At the final stage, because of a relatively fast growth rate of hexagonal CdS along the c-axis crystal orientation [24], the rod-like CdS crystals were finally formed on the basis of the continuous growth of the needle-like CdS crystals along the c-axis until the reactants were almost depleted during the hydrothermal reaction. Figure 8 shows the growth mechanism of the flower-like CdS crystallites. The first and second stages herein are similar to those of rod-like CdS crystallites. Faceted CdS crystals with a definite size were formed and dispersed on the substrate. These small CdS crystals aggregated to form large CdS clusters with irregular architectures when the hydrothermal reaction duration was further increased (third stage). The distinct extrusion of the CdS crystals grew from the faceted CdS of the clusters and favorably extended along the c-axis direction to form large CdS branches (fourth stage). Moreover, the relatively small secondary CdS crystals extended from the side of the initially grown CdS branches and toward specific directions to form CdS twigs. Every twig grew at an angle interval of approximately 60° owing to the six-side facets of the hexagonal structure of CdS. Finally, CdS crystallites with a suitable flower-like architecture were formed on the substrate (fifth stage). A similar flower-like architecture was observed in electrochemically grown ZnO crystals because the crystal growth rate of (001) is faster than that of the crystallographic planes of the six-side facets in the hexagonal wurtzite ZnO [25].
Figure 9a, b shows the PL spectra of the rod- and flower-like CdS crystallites. Notably, two emission bands were observed for the rod- and flower-like CdS crystallites. The peaks of emission bands centered at approximately 500 and 527 nm corresponded to the near band-edge emission of the CdS crystallites [26]. Crystal defect-related emission bands of CdS were reported; the emission bands centered at approximately 540–650 nm were attributed to the shallow trap engendered by surface states or the recombination of holes in valence band electrons with deeply trapped S2− vacancies in CdS (V+ S) [27]. On the basis of the aforementioned information, it is reasonable to determine that the peaks of emission bands centered at approximately 665 nm herein originated from the recombination of trapped electrons–holes in some surface states or bulk defects [27]. The flower-like CdS crystallites had a higher intensity ratio of the emission band at 665 nm to the near band-edge emission than did the rod-like CdS crystallites, revealing that the flower-like CdS crystallites are more crystal defective compared with the rod-like CdS crystallites. To understand the optical band gap value of the CdS crystallites with various morphologies, the current study further measured diffuse reflectance spectra of the samples and converted them into absorption coefficient spectra by applying the Kubelka–Munk function [28]. For comparison, the data of the CdS crystallites annealed in the ambient atmosphere are presented in Fig. 9c. As shown in the Kubelka–Munk conversion spectra, the rod-like CdS crystallites, flower-like CdS crystallites, and CdO@CdS heterostructure displayed excellent optical absorption capabilities and spectral intensity variation in the 400–800-nm light wavelength range. The optical band gap values of the samples were estimated according to the theory of Tauc’s formula for direct band gap semiconductors and are presented in Fig. 9d [29]. The optical band gap values of the rod- and flower-like CdS crystallites were approximately 2.4 and 2.3 eV, respectively. The optical band gap value of the CdO@CdS heterostructure was approximately 2.32 eV. No marked change in the optical absorption edge occurred when the flower-like CdS crystallites were thermally annealed; the formation of a trace content of the CdO phase on the CdS surfaces after thermal annealing might explain this observation.
Figure 10a–c shows the variations in the intensity of the absorbance spectra of the MB solution containing different CdS samples as catalysts upon exposure to visible light irradiation at various durations. The intensity of the absorbance spectra of the MB solution decreased with the duration of visible light irradiation. This is because during photodegradation, photoexcited electrons or holes in the semiconductor were transferred to the active surface and join in the redox reactions, in which the electrons reduced the dissolved molecular oxygen to produce superoxide radical anions (•O2 −). The unstable •O2 − further reacted with water rapidly, producing hydroxyl radicals (•OH). Moreover, the holes oxidized H2O molecules to yield hydroxyl radicals, and these radicals were strong oxidizing agents and effectively decomposed the MB herein (Fig. 10d) [30]. Figure 10e shows the summarized photodegradation efficiencies of the CdS crystallites with various morphologies and postthermal annealing. Comparatively, the degradation activities followed the following order: CdO@CdS > flower-like CdS > rod-like CdS crystallites. Figure 11a–c illustrates the photodegradation performance of these CdS samples. The sizes of red and blue arrows represent the degree of reaction between the radicals and MB. The photocatalytic activity of the flower-like CdS crystallites was greater than that of the rod-like CdS crystallites; this finding can be attributed to the lower optical band edge of the flower-like CdS crystallites, which broadened the optical absorption range compared with that of the rod-like CdS crystallites. The absorption band edge of the semiconductor photocatalysts shifted to the red region, indicating that the photocatalysts can utilize more solar light, thus enhancing their photocatalytic performance. Several studies have proposed that a similar optical absorption edge shift to a lower energy region improved the photocatalytic ability of semiconductors [31, 32]. Moreover, a study posited that more active sites on the surfaces of catalyst materials are favorable to promote their photoactivated degradation reaction with organic pollutants [33]. Surface defects may serve as charge carrier traps as well as adsorption sites, where the charge transfers to the adsorbed species and prevents electron–hole recombination [34]. In the current study, compared with the rod-like CdS crystallites, a relatively high crystal defect density in the flower-like CdS crystallites, as demonstrated by the PL analysis, was beneficial for improving the efficiency of photodegradation. Notably, the optical band gap of the CdO@CdS heterostructure was not smaller than that of the flower-like CdS crystallites; however, its photodegradation activity was superior to that of the pure CdS crystallites with various morphologies. This observation might be explained by the favorable separation of photogenerated charge carriers engendered by the existence of heterointerfaces in CdO@CdS (Fig. 11c). The ZnO–TiO2 heterostructure is proved to manifest superior photocatalytic activity to that of the single constituent compound of ZnO or TiO2; the enhanced photocatalytic activity of the heterostructure is primarily attributed to the formation of a heterojunction structure in the interface between ZnO and TiO2, which greatly promotes efficient separation of photogenerated electron–hole charge carriers [30]. In the current study, the band alignment at the CdS–CdO interface facilitated the effective transfer of the photogenerated electrons from the conduction band of CdS to the conduction band of CdO. A similar band alignment at the interface of the ZnO–ZnSe heterostructure was reported to play a crucial role in enhancing the photocatalytic activity of the ZnO–ZnSe heterostructure [35]. The band alignment between CdS and CdO might contribute to the spatial separation of electrons and holes, engendering an increase in minority carrier lifetime [36]. Therefore, compared with those of the single CdS, the higher number of charge carriers of the heterostructure could serve the redox reaction during photodegradation. An increased yield of superoxide radical anions and hydroxyl radicals from the photoactivated CdO@CdS heterostructure in the MB solution improved the photodegradation efficiency of MB. Therefore, the photodegradation performance of the flower-like CdS crystallites was enhanced herein by partially oxidizing their surfaces with moderate postthermal annealing.
Conclusions
In this study, rod- and flower-like CdS crystallites were synthesized using a facile hydrothermal growth method. XRD analyses showed that the rod- and flower-like CdS crystallites have mainly hexagonal phases. The faster crystal growth rate on the c-axis than on the other crystallographic planes in the hexagonal CdS phase under the given growth condition might account for the anisotropic growth behavior observed in the rod- and flower-like architectures of the CdS crystallites. The flower-like CdS crystallites exhibited more defective crystal features than did the rod-like CdS crystallites. Moreover, the flower-like CdS crystallites exhibited a broader visible light absorption range than that of the rod-like CdS crystallites. Therefore, the photoactivity of the flower-like CdS crystallites is higher than that of the rod-like CdS crystallites. The postannealing of the flower-like CdS crystallites in ambient air also resulted in the formation of a CdO phase on the surfaces of these crystallites. In this study, the existence of heterointerfaces in the CdO@CdS heterostructure was beneficial for the separation of photogenerated charge carriers, and therefore, the photoactivity of the flower-like CdS crystallites was further improved.
References
Reddy LS, Ko YH, Yu JS (2015) Hydrothermal synthesis and photocatalytic property of β-Ga2O3 nanorods. Nanoscale Res Lett 10(1):364
Chen W, Ruan H, Hu Y, Li D, Chen Z, Xian J, Chen J, Fu X, Shao Y, Zheng Y (2012) One-step preparation of hollow ZnO core/ZnS shell structures with enhanced photocatalytic properties. CrystEngComm 14(19):6295–6305
Lü W, Chen J, Wu Y, Duan L, Yang Y, Ge X (2014) Graphene-enhanced visible-light photocatalysis of large-sized CdS particles for wastewater treatment. Nanoscale Res Lett 9(1):148
Asif SA, Khan SB, Asiri AM (2015) Visible light functioning photocatalyst based on Al2O3 doped Mn3O4 nanomaterial for the degradation of organic toxin. Nanoscale Res Lett 10(1):355
Li Y, Tang L, Peng S, Li Z, Lu G (2012) Phosphate-assisted hydrothermal synthesis of hexagonal CdS for efficient photocatalytic hydrogen evolution. CrystEngComm 14(20):6974–6982
Xu D, Xu Y, Chen D, Guo G, Gui L, Tang Y (2000) Preparation of CdS single-crystal nanowires by electrochemically induced deposition. Adv Mater 12(7):520–522
Shen G, Cho JH, Yoo JK, Yi GC, Lee CJ (2005) Synthesis of single-crystal CdS microbelts using a modified thermal evaporation method and their photoluminescence. J Phys Chem B 109(19):9294–9298
Shanmugapriya T, Vinayakan R, Thomas KG, Ramamurthy P (2011) Synthesis of CdS nanorods and nanospheres: shape tuning by the controlled addition of a sulfide precursor at room temperature. CrystEngComm 13(7):2340–2345
Nicholas NJ, Franks GV, Ducker WA (2012) The mechanism for hydrothermal growth of zinc oxide. CrystEngComm 14(4):1232–1240
Liang YC, Lin TY, Lee CM (2015) Crystal growth and shell layer crystal feature-dependent sensing and photoactivity performance of zinc oxide–indium oxide core–shell nanorod heterostructures. CrystEngComm 17(41):7948–7955
Liu T, Li Y, Zhang H, Wang M, Fei X, Duo S, Chen Y, Pan J, Wang W (2015) Tartaric acid assisted hydrothermal synthesis of different flower-like ZnO hierarchical architectures with tunable optical and oxygen vacancy-induced photocatalytic properties. Appl Surf Sci 357:516–529
Shanmugam N, Sathya T, Viruthagiri G, Kalyanasundaram C, Gobi R, Ragupathy S (2016) Photocatalytic degradation of brilliant green using undoped and Zn doped SnO2 nanoparticles under sunlight irradiation. Appl Surf Sci 360:283–290
Zhu L, Li C, Li Y, Feng C, Li F, Zhang D, Chen Z, Wen S, Ruan S (2015) Visible-light photodetector with enhanced performance based on a ZnO@CdS heterostructure. J Mater Chem C 3(10):2231–2236
Liang YC, Liu SL, Hsia HY (2015) Physical synthesis methodology and enhanced gas sensing and photoelectrochemical performance of 1D serrated zinc oxide-zinc ferrite nanocomposites. Nanoscale Res Lett 10(1):350–356
Wu Y, Xu F, Guo D, Gao Z, Wu D, Jiang K (2013) Synthesis of ZnO/CdSe hierarchical heterostructure with improved visible photocatalytic efficiency. Appl Surf Sci 274:39–44
Xia W, Wang H, Zeng X, Han J, Zhu J, Zhou M, Wu S (2014) High-efficiency photocatalytic activity of type II SnO/Sn3O4heterostructures via interfacial charge transfer. CrystEngComm 16(30):6841–6847
Zou X, Dong Y, Zhang X, Cui Y (2016) Synthesize and characterize of Ag3VO4/TiO2 nanorods photocatalysts and its photocatalytic activity under visible light irradiation. Appl Surf Sci 366:173–180
Yakuphanoglu F (2010) Nanocluster n-CdO thin film by sol–gel for solar cell applications. Appl Surf Sci 257(5):1413–1419
Danţuş C, Rusu GG, Dobromir M, Rusu M (2008) Preparation and characterization of CdO thin films obtained by thermal oxidation of evaporated Cd thin films. Appl Surf Sci 255(5):2665–2670
Li W, Li M, Xie S, Zhai T, Yu M, Liang C, Ouyang X, Lu X, Li H, Tong Y (2013) Improving the photoelectrochemical and photocatalytic performance of CdO nanorods with CdS decoration. CrystEngComm 15(21):4212
Zhang B, Yao W, Huang C, Xu Q, Wu Q (2013) Shape effects of CdS photocatalysts on hydrogen production. Int J Hydrogen Energy 38(18):7224–7231
Pandey G, Dixit S (2011) Growth mechanism and optical properties determination of CdS nanostructures. J Phys Chem C 115(36):17633–17642
Zhao Q, Hou L, Huang R (2003) Synthesis of ZnS nanorods by a surfactant-assisted soft chemistry method. Inorg Chem Commun 6(7):971–973
Thongtem T, Phuruangrat A, Thongtem S (2009) Solvothermal synthesis of CdS nanowires templated by polyethylene glycol. Ceram Int 35(7):2817–2822
Liang YC (2012) Growth and physical properties of three-dimensional flower-like zinc oxide microcrystals. Ceram Int 38(2):1697–1702
Kumar S, Mehtab SK (2015) Varying photoluminescence emission of CdS nanoparticles in aqueous medium: a comparative study on effect of surfactant structure. Nano-Structures Nano-Objects 2:1–10
Huang L, Yang J, Wang X, Han J, Han H, Li C (2013) Effects of surface modification on photocatalytic activity of CdS nanocrystals studied by photoluminescence spectroscopy. Phys Chem Chem Phys 15(2):553–560
Zhang YC, Du ZN, Li KW, Zhang M, Dionysiou DD (2011) High-performance visible-light-driven SnS2/SnO2 nanocomposite photocatalyst prepared via in situ hydrothermal oxidation of SnS2 nanoparticles. ACS Appl Mater Interfaces 3(5):1528–1537
Zhang LJ, Li S, Liu BK, Wang DJ, Xie TF (2014) Highly efficient CdS/WO3 photocatalysts: Z-scheme photocatalytic mechanism for their enhanced photocatalytic H2 evolution under visible light. ACS Catal 4(10):3724–3729
Xiao FX (2012) Construction of highly ordered ZnO-TiO2 nanotube arrays (ZnO/TNTs) heterostructure for photocatalytic application. ACS Appl Mater Interfaces 4(12):7055–7063
Huang Y, Li H, Balogun MS, Liu W, Tong Y, Lu X, Ji H (2014) Oxygen vacancy induced bismuth oxyiodide with remarkably increased visible-light absorption and superior photocatalytic performance. ACS Appl Mater Interfaces 6(24):22920–22927
Li J, Liu Y, Li H, Chen C (2016) Fabrication of g-C3N4/TiO2 composite photocatalyst with extended absorption wavelength range and enhanced photocatalytic performance. J Photochem Photobiol A 317:151–160
Zhou L, Shao Y, Liu J, Ye Z, Zhang H, Ma J, Jia Y, Gao W, Li Y (2014) Preparation and characterization of magnetic porous carbon microspheres for removal of methylene blue by a heterogeneous Fenton reaction. ACS Appl Mater Interfaces 6(10):7275–7285
Bai X, Wang L, Zong R, Lv Y, Sun Y, Zhu Y (2013) Performance enhancement of ZnO photocatalyst via synergic effect of surface oxygen defect and graphene hybridization. Langmuir 29(9):3097–3105
Cho S, Jang JW, Kim J, Lee JS, Choi W, Lee KH (2011) Three-dimensional type II ZnO/ZnSe heterostructures and their visible light photocatalytic activities. Langmuir 27(16):10243–10250
Cheng B, Wu G, Ouyang Z, Su X, Xiao Y, Lei S (2014) Effects of interface states on photoexcited carriers in ZnO/Zn(2)SnO(4) type-II radial heterostructure nanowires. ACS Appl Mater Interfaces 2014(6):4057–4062
Acknowledgements
This work is supported by the Ministry of Science and Technology of Taiwan (Grant Nos. MOST 104-2221-E-019-041 and MOST 102-2221-E-019-006-MY3).
Authors’ contributions
YCL designed the experiments and drafted the manuscript. TWL carried out the sample preparations, material analyses, and characterization tests. Both authors read and approved the final manuscript.
Authors’ information
YCL is a professor of the Institute of Materials Engineering at National Taiwan Ocean University (Taiwan). TWL is a graduate student of the Institute of Materials Engineering at National Taiwan Ocean University (Taiwan).
Competing interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Liang, YC., Lung, TW. Growth of Hydrothermally Derived CdS-Based Nanostructures with Various Crystal Features and Photoactivated Properties. Nanoscale Res Lett 11, 264 (2016). https://doi.org/10.1186/s11671-016-1490-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1490-x