Abstract
Graphene-enhanced Raman scattering (GERS) spectra and coherent anti-Stokes Raman scattering (CARS) of thymine molecules adsorbed on a single-layer graphene were studied. The enhancement factor was shown to depend on the molecular groups of thymine. In the GERS spectra of thymine, the main bands are shifted with respect to those for molecules adsorbed on a glass surface, indicating charge transfer for thymine on graphene. The probable mechanism of the GERS enhancement is discussed. CARS spectra are in accord with the GERS results, which indicates similar benefit from the chemical enhancement.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Surface-enhanced Raman spectroscopy (SERS) has become an efficient technique that enables detection and study of an extremely small amount of biochemical materials and single-molecule detection [1-4]. SERS is based on the enhancement of the local optical field by several orders of magnitude in the vicinity of a rough metal surface or metal island film due to excitation of the collective oscillations of conduction electrons at the metal surface (surface plasmons). However, investigation of the biological and biochemical species often requires substrates of higher chemical inertness. Such substrates can be based in particular on carbon allotropes, e.g., on graphene or carbon nanotubes. But in graphitic materials, the surface plasmon resonance is found in the THz range [5,6], i.e., plasmon-based local field enhancement can hardly be employed in optical spectroscopy with such carbon-based substrates. Nevertheless, it has been recently demonstrated [7-10] that the Raman signal of molecules deposited on graphene and graphene oxides is enhanced by several orders of magnitude, which is likely to be caused by the so-called chemical mechanism [11], i.e., chemical interaction of deposited molecules and carbon atoms of the substrate. This phenomenon is called graphene-enhanced Raman scattering (GERS) [12] and may become important for spectroscopy of certain biological and biochemical species. In particular, we have recently reported the enhancement for Raman and coherent anti-Stokes Raman scattering of thymine adsorbed on graphene oxide [10].
In the present paper, we report on a comparative study of the surface-enhanced Raman scattering and surface-enhanced coherent anti-Stokes Raman scattering for thymine (Thy) adsorbed on graphene layers.
Samples
In the Raman and coherent anti-Stokes Raman scattering (CARS) measurements, we use aqueous 1 mg/ml and 10 μg/ml solutions of commercially available thymine (Sigma-Aldrich, St. Louis, MO, USA). The samples for optical experiments were prepared by depositing a drop of Thy solution on graphene-on-silica or glass substrates, respectively. The average surface density of Thy after water evaporation was either 200 ng/cm2 or 20 μg/cm2.
The graphene-on-silica substrates were fabricated by depositing a graphene sheet on fused silica. Single-layer graphene was prepared by using chemical vapor deposition (CVD) of graphene on a copper foil described elsewhere [13,14]. Before the start of the graphitization process, the copper substrate was annealed for 1 h at a temperature of 1,000°C in 15-mbar hydrogen atmosphere. After the annealing, the CVD chamber was pumped down and filled with 1:1 H2:CH4 gas mixture for 10 min (15 mbar). Because of the self-limiting graphene growth on a copper substrate, almost single-layer graphene [15] was deposited on both surfaces of the copper foil. The templated graphene growth was suppressed by short hydrogen etching at a temperature of 1,000°C and pressure of 50 mbar [16]. After the etching, the CVD chamber was cooled down to room temperature in hydrogen atmosphere (15 mbar). The graphene deposited on the backside of the copper was etched away in harsh oxygen plasma (100 W/20 sccm/2 min).
The graphene sheet was spin coated by a 1-μm-thick polymethyl methacrylate (PMMA) layer, and then the copper foil was removed by wet etching in FeCl3. The remaining PMMA/graphene stack was rinsed in deionized water for 30 min and then placed on a silica substrate in such a way that the graphene was facing the silica. In order to relax internal stress in the stack, another PMMA layer was deposited on top of the existing PMMA [17]. After removal of both the PMMA layers by acetone, the obtained graphene-on-silica substrate was rinsed in isopropanol and water. The procedure described above is scalable, i.e., one can add one or more graphene sheets on the top of the first one using the same technique.
Methods
Raman measurements
The Raman spectra of the bare and Thy-adsorbed graphene layers were obtained using a Renishaw inVia Raman microscope (Renishaw plc, Wotton-under-Edge, UK) at an excitation wavelength of 633 nm and spot size of 1 μm. All Raman measurements were performed at room temperature. The WiRE 3.4 software (Renishaw) was used for Raman data acquisition and data analysis. The Si Raman band centered at 520 cm−1 was used as the reference.
CARS measurements
The experimental setup was based on a homemade CARS microscope equipped with a compact laser source (EKSPLA Ltd., Vilnius, Lithuania) capable of providing pump and Stokes pulses with energies up to 10 nJ (see [10,18] for more details). The excitation beams were focused on the sample with an oil immersion objective (Plan Apochromat, ×60, NA 1.42, Olympus Corporation, Tokyo, Japan). The CARS mapping of the Thy-adsorbed graphene-on-silica substrate and glass was performed with a spatial resolution of approximately 0.5 and 1.0 μm in the lateral and normal (z) directions, respectively. The CARS images of the sample surface were composed of 250 × 250 pixels obtained with a 2-ms pixel dwell time using a piezo scanning system (Physik Instrumente GmbH & Co., Karlsruhe, Germany). CARS spectra were recorded with a scanning rate of 5 cm−1 s−1 in the frequency ranges of 1,200 to 1,700 cm−1 and 2,500 to 3,400 cm−1 with a resolution of about 8 cm−1.
Results and discussion
Raman spectra of the stacked graphene sheets
Raman spectra of the fabricated graphene samples (see Figure 1) dominate G and 2D bands. The shape and position of the 2D peak indicate that the samples consist of one graphene layer (Figure 2). A relatively weak D peak situated in the vicinity of 1,325 cm−1 indicates the presence of defects in the graphene [19-22]. The ratio of the D and G peaks can be employed for quantitative characterization of the crystallinity. Specifically, if we assume that there is no amorphous and/or carbon and sp3-bonded carbon in the samples, the size of the graphene crystallites L a can be estimated according to Tuinstra-Koening (TK) [22], which yields L a ~ I (D)/I (G) where I (D) and I (G) are intensities of the G and D peaks in the Raman spectrum. In our case, the ratio L a does not exceed 0.1 for single-layer graphene, indicating a good crystallinity of the fabricated graphene.
The position ω G of the G peak can be employed to estimate the number of graphene layers n on the silica substrate by using the following equation [23]: ω G = 1,581.6 + 11/(1 + n 1.6).
The obtained experimental value of ω G = 1,589 cm−1 corresponds to n ~ 1. It should be mentioned that this layer had defects that is proved by the presence of the weak D peak situated in the vicinity of 1,325 cm−1. The ratio I (G)/I (2D), which also can be used to estimate the number of graphene layers, does not exceed 0.4, indicating the presence of one to two layers of graphene. These results correspond well to SEM images of graphene-on-silica substrates that show gaps and defects in the graphene sheets.
The Raman spectrum of the bare graphene-on-silica substrate includes a pronounced band at 450 cm−1 which originated from symmetric stretching vibrations of neighboring Si-O bonds [24,25]. The band near 800 cm−1 is also associated with symmetric stretching vibrations of oxygen atoms, which involve also a substantial amount of surrounding Si atoms. The peaks at 485 and 600 cm−1 are attributed to the formation of four-membered (four oxygen atoms in the ring) and three-membered (three oxygen atoms in the ring) defects, respectively [26]. Very weak bands at 1,056 and 1,205 cm−1 (Figure 1) are similar to those associated with Si-O transverse and longitudinal optical modes [25,27].
In the graphene layers, the position, width, and intensity of the 2D peak depend on the number of graphene sheets in the sample [28]. In our case, the 2D band for the graphene monolayer (Figure 2) exhibits a single Lorentzian feature with a full width at half maximum (FWHM) of approximately 30 cm−1.
Surface-enhanced scattering of Thy adsorbed on graphene-on-silica substrate
The Raman spectrum of Thy adsorbed on the graphene-on-silica substrate is shown in Figure 3a. One can observe that when Thy is adsorbed on single-layer graphene, the major intensive peaks in the Raman spectrum of Thy were blueshifted from 1,366 and 1,669 cm−1 (on glass, Figure 3b) to 1,367 and 1,671 cm−1 (on graphene, Figure 3a), respectively. By comparing Figure 3a,b, one can observe that the Thy Raman peak at 3,062 cm−1 shifts to 3,066 cm−1 and is strongly enhanced when Thy is adsorbed on graphene. It is worth noting also the change of the intensity of the Thy Raman peak at 2,932 cm−1.
In the Raman spectra of Thy adsorbed on single-layer graphene, one may clearly observe the characteristic G, 2D, and D peaks of graphene (Figure 3a). The adsorption of the Thy molecules onto the single-layer graphene results in the blueshift of the G peak and redshift of the 2D peak (see Table 1).
The observed shifts of the G and 2D peaks indicate that deposition of Thy results in doping of graphene [29,30]. Specifically, the blueshift of the G band and redshift of 2D indicate n-doping of graphene by Thy molecules. FWHMs of the G band and the intensity ratio I (2D)/I (G) for bare and Thy-adsorbed graphene-on-silica substrates are presented in Table 2. One can see from Table 1 that adsorption of Thy decreases the FWHM of the G band for single-layer graphene. This experimental finding corresponds well to [30,31] where it has been shown that decrease of FWHM will saturate with the shift of the Fermi level. The ratio I (2D)/I (G) is also sensitive to the doping effects [32,33].
The GERS enhancement factor can be found by comparing the Raman signal obtained for Thy molecules deposited on glass (I glass) and graphene-on-silica (I Gr) substrates (see Figure 3) using the following equation:
where m Gr(Thy) and m glass(Thy) are the Thy surface densities on relevant substrates. Under our experimental conditions, we can well register already 200 ng/cm2 of Thy adsorbed on a single-layer graphene (Figure 3a, blue curve). However, when Thy surface density on the glass substrate is 200 ng/cm2, no Raman signal was observed at the same excitation intensity. For the registration of Raman spectra of Thy on glass, we increase surface densities of Thy up to 20 μg/cm2 (Figure 3b) to get a similar signal size to that on graphene. One can observe from Figure 3a that the GERS enhancement factor depends on the Thy molecular group and its interaction with the graphene surface. The maximum enhancement factor (g exp) of about 5 × 102 was observed for the C(6)-H group and about 3 × 102 for NH and C = O vibrations of Thy molecules adsorbed on single-layer graphene.
The assignments of Raman shift for thymine adsorbed on graphene and glass substrate are listed in Table 2.
The band observed for Thy adsorbed on single-layer graphene in Figure 3a (blue curve) at 617 cm−1 is attributed to the wag of N-H in the structure of Thy, 741 cm−1 is attributed to ring breathing and coupled to the out-plane wag of N-H, 804 cm−1 is attributed to the wag of C-H on C = C, 985 cm−1 is attributed to ring breathing coupled to in-plane -CH3 asymmetric stretching, 1,367 cm−1 is attributed to N-H and C-H in-plane bending, and 1,671 cm−1 is attributed to C = O stretching and coupled to N-H and C-H asymmetric bending. The bands of 1,410 and 1,491 cm−1 were also the characteristic peaks of GERS for ring modes of Thy, not visible on glass. The bands centered at 116 and 152 cm−1 in the Raman spectra deposited on the glass substrate indicate the presence of three-dimensional micro-crystallites of Thy due to the lower sticking probability on glass compared to graphene. These bands do not appear in the Raman spectra of Thy on the graphene-on-silica substrate. The microscopy images also show that Thy adsorbed on graphene seems to form flat flakes - the same observation we had in our previous work [10] for Thy adsorbed on graphene oxide. Due to the presence of big three-dimensional micro-crystallites of Thy on glass, the broad band at 250 to 600 cm−1 which is associated with the molecular vibrations in the substrate is absent in Figure 3b, while in the case of Thy on the graphene-on-silica substrate (Figure 3a), the band at 250 to 600 cm−1 is available due to the very small thickness of flakes of Thy.
The band at 3,066 cm−1 in GERS spectra of Thy, which is attributed to the aromatic C(6)-H stretching vibration, is strongly enhanced, while the band at 2,932 cm−1, which is assigned to the symmetric CH3 stretching vibration, is decreased (Figure 3). The possible orientation of Thy with respect to the graphene surface and binding sites between adsorbed molecules and graphene needs additional investigations and discussions.
Graphene-enhanced coherent anti-Stokes Raman scattering of thymine
The CARS measurements for the Thy adsorbed on different substrates were carried out in spectral ranges of 1,200 to 1,700 cm−1 and 2,500 to 3,400 cm−1. CARS and Raman spectra of Thy are quite similar: main bands are about 10 cm−1 shifted to the short wavenumber region (Figures 4 and 5). The low-energy shift of the band in CARS spectra is an intrinsic feature of this technique caused by mixing of resonance (vibrational) response with non-resonance contribution.
Another relevant feature of the CARS method is the quadratic CARS signal dependence on concentration of matter. For this reason, the CARS spectra contain strong bands of Thy and the vanished G band of graphene (Figure 4a). Additionally, the coherence origin of CARS may have an effect on the signal weakening from graphene.
One can observe from Figure 5 that the Thy adsorption on graphene results in the redistribution of the intensity of the Thy Raman bands in the 2,700- to 3,100-cm−1 range and enhancement of the ν(C6-H) mode at 3,055 cm−1 in the CARS spectrum. The aromatic C(6)-H stretching band of Thy in Raman spectra is observed at 3,062 cm−1, and in CARS spectra, this band shifts to 3,055 cm−1. In addition, we have to indicate that this band is indistinguishable for samples prepared on glass substrates (Figure 5) in both Raman and CARS spectra.
The important difference between the CARS spectrum of Thy adsorbed on glass and that on graphene-on-silica substrates (yellow and blue curves in Figure 5b) must be noted: in the CARS spectrum of Thy adsorbed on the graphene-on-silica substrate, the band near 2,965 cm−1 is stronger than that of Thy adsorbed on glass. We have recently observed enhancement for the CARS signal of Thy adsorbed on graphene oxide [10] where the broadening of the CARS band at 2,700 to 3,100 cm−1 originated from the electron-phonon and phonon-phonon coupling.
Figure 6 shows CARS microscopy images in a 50 × 50-μm area of Thy adsorbed on glass and graphene-on-silica substrates. One can observe from Figure 6a,b that at 2,925 cm−1, both substrates provide high-contrast images of adsorbed Thy molecules. In contrast, at 3,055 cm−1, the Thy molecules adsorbed on graphene provide a strong CARS signal over the sample surface (Figure 6c), while Thy molecules adsorbed on glass give no CARS signal (not shown). The Thy molecules on glass form crystals with an average size of several tens of micrometers. We can see that adsorbed Thy molecules deposited on the graphene sheet form complex Thy/graphene as flat flakes with a lateral size up to 30 μm. The image at 3,055 cm−1 illustrates enhancement of the CARS signal from Thy molecules on the graphene monolayer. The CARS signal intensity of both 2,925 and 3,055 cm−1 bands of the Thy adsorbed on graphene dramatically reduced with the distance from the graphene surface.
The performed Raman and CARS measurements reveal that signal enhancement manifests itself similarly in both linear and nonlinear experiments. This enhancement may originate from charge transfer between the Thy molecules and the graphene surface that results in increase of the molecular polarizability. The experimentally observed doping-related shift of the G and 2D Raman peaks of graphene (see Table 1) supports the importance of the charge transfer. However, the resonant interaction of exciting light with electronic states of the graphene sheets and the increase of the local field at the defects [34] and edges of the graphene layers can also contribute to the observed enhancement. Since the plasmon resonance for graphene is usually situated in the THz range [5,6], we believe that the observed GERS is due to the formation of the charge transfer between the Thy molecules and the graphene sheet.
Conclusions
GERS was studied for the Thy adsorbed on single-layer graphene. The observed enhancement of the Raman signal of more than 100 times was observed for C(6)-H, NH, and C = O vibrations of Thy molecules adsorbed on single-layer graphene and was accompanied with a minor shift of these Thy bands. The highest enhancement in GERS effect was observed for ring modes of thymine. The CARS spectra of Thy adsorbed on single-layer graphene are in accord with GERS of Thy and demonstrated redistribution of the intensity of the Thy Raman bands in the 2,800- to 3,100-cm−1 range and enhancement of the ν(C6-H) mode at 3,055 cm−1 in the CARS and at 3,066 cm−1 in Raman, respectively. The change in GERS compared to ordinary Raman strongly depends on the vibrational mode of adsorbed molecules and thus can provide an insight into the chemical mechanism.
Abbreviations
- CARS:
-
coherent anti-Stokes Raman scattering
- GECARS:
-
graphene-enhanced coherent anti-Stokes Raman scattering
- GERS:
-
graphene-enhanced Raman scattering
- SERS:
-
surface-enhanced Raman scattering
- Thy:
-
thymine
References
Otto C, Tweel T, Mul F, Greve J. Surface-enhanced Raman spectroscopy of DNA bases. J Raman Spectroscopy. 1986;17:289–98.
Rivas L, Saґnchez-Corteґs S, Garcıґa-Ramos J. Raman structural study of thymine and its 2-deoxy-ribosyl derivatives in solid state, aqueous solution and when adsorbed on silver nanoparticles. Phys Chem Chem Phys. 2002;4:1943–8.
Sharma B, Frontiera R, Henry A, Ringe E, Van Duyne R. SERS: materials, applications, and the future. MaterToday. 2012;15:16–25.
Le R, Etchegoin PG. Single-molecule surface-enhanced Raman spectroscopy. Annu Rev Phys Chem. 2012;63:65–87.
Rana F. Graphene terahertz plasmon oscillators. IEEE Trans Nanotechnol. 2008;7:91–9.
Zhang Q, Háros E, Jin Z, Ren L, Wang X, Arvidson R, Lüttge A, Kono J. et. al. Plasmonic Nature of the Terahertz Conductivity Peak in Single-Wall Carbon Nanotubes. Nano Lett. 2013;13(12):5991–5996.
Ling X, Zhang J. First-layer effect in graphene-enhanced Raman scattering. Small. 2010;6:2020–5.
Huang C, Kim M, Wong B, Safron N, Arnold M, Gopalan P. Raman enhancement of a dipolar molecule on graphene. J Phys Chem. 2014;118:2077–84.
Xu W, Mao N, Zhang J. Graphene: a platform for surface-enhanced Raman spectroscopy. Nano Micro Small. 2013;8(9):1206–24.
Dovbeshko G, Fesenko O, Dementjev A, Karpicz R, Fedorov V, Posudievsky Y. Coherent anti-Stokes Raman scattering enhancement of thymine adsorbed on graphene oxide. J Nanoscale Res Letters. 2014;9:263. doi:10.1186/1556-276X-9-263.
Ling X, Moura L, Pimenta M, Zhang J. Charge-transfer mechanism in graphene-enhanced Raman scattering. J Phys Chem C. 2012;116(47):25112–8.
Ling X, Xie L, Fang Y, Xu H, Zhang H, Kong J, et al. Can graphene be used as substrate for Raman enhancement? Nano Lett. 2010;10:553–61.
Mattevi C, Kim H, Chhowalla M. A review of chemical vapour deposition of graphene on copper. J Mater Chem. 2011;21:3324–34.
Kaplas T, Zolotukhin A, Svirko Y. Thickness determination of graphene on metal substrate by reflection spectroscopy. Opt Express. 2011;19:17226–31.
Li X, Cai W, Colombo L, Ruoff R. Evolution of graphene growth on Ni and Cu by carbon isotope labeling. Nano Lett. 2009;9(12):4268–72.
Yao Y, Wong C. Monolayer graphene growth using additional etching process in atmospheric pressure chemical vapor deposition. Carbon. 2012;50:5203–9.
Li X, Chen D, Zhu Y, Cai W, Piner R, Borysiak M, et al. Transfer of large-area graphene films for high-performance transparent conductive electrodes. Nano Lett. 2009;9(12):4359–63.
Dementjev A, Gulbinas V, Serbenta A, Kaucikas M, Niaura G. Coherent anti-Stokes Raman scattering spectroscope/microscope based on a widely tunable laser source. J Modern Optics. 2010;57(6):503–9.
Vidano R, Fishbach D. Observation of Raman band shifting with excitation wavelength for carbons and graphites. Solid State Comm. 1981;39(2):341–4.
Ferrari A, Basko D. Raman spectroscopy as a versatile tool for studying the properties of graphene. Nat Nanotechnol. 2013;8:235–46.
Nemanich R, Solin S. First- and second-order Raman scattering from finite-size crystals of graphite. Phys Rev B. 1979;20:392.
Tuinstra F, Koenig L. Raman spectrum of graphite. J Phys Chem. 1970;53:1126–30.
Wang H, Wang Y, Cao X, Feng M, Lan G. Vibrational properties of graphene and graphene layers. J Raman Spectroscopy. 2009;40(12):1791–6.
Skuja L. Optically active oxygen-deficiency-related centers in amorphous silicon dioxide. J Non-Crystalline Solids. 1998;239:16–48.
Galeener F. Band limits and the vibrational spectra of tetrahedral glasses. Phys Rev B. 1979;19(8):4292–7.
Dovbeshko G, Fesenko O, Boyko V, Romanyuk V, Moiseyenko V, Gorelik V, et al. Vibrational spectra of opal-based photonic crystals. IOP Conf Series: Materials Science and Engineering. 2012;38:012008. 1–6. doi:10.1088/1757-899X/38/1/012008.
Galeener F, Lucovsky G. Longitudinal optical vibrations in glasses: GeO2 and SiO2. Phys Rev Lett. 1976;37:1474.
Malard L, Nilsson J, Elias D, Brant J, Plentz F, Alves E, et al. Probing the electronic structure of bilayer graphene by Raman scattering. Phys Rev B. 2007;76:201401.
Das A, Pisana S, Chakraborty B, Piscanec S, Saha SK, Waghmare UV, et al. Monitoring dopants by Raman scattering in an electrochemically top-gated graphene transistor. Nat Nanotechnol. 2008;3:205–10.
Pisana S, Lazzeri M, Casiraghi C, Novoselov K, Geim A, Ferrari A, et al. Breakdown of the adiabatic Born-Oppenheimer approximation in graphene. Nat Mater. 2007;6:198–201.
Yan J, Zhang Y, Kim P, Pinczuk A. Electric field effect tuning of electron–phonon coupling in graphene. Phys Rev Lett. 2007;98(16):166802.
Casiraghi C, Hartschuh A, Qian H, Piscanec S, Georgi C, Fasoli A, et al. Raman spectroscopy of graphene edges. Nano Lett. 2009;9(4):1433–41.
Basko D, Piscanec S, Ferrari A. Electron–electron interactions and doping dependence of the two-phonon Raman intensity in graphene. Phys Rev B. 2009;80(16):165413.
Lopes M, Candini A, Urdampilleta M, Reserbat-Plantey A, Bellini V, Klyatskaya S, et al. Surface-enhanced Raman signal for terbium single-molecule magnets grafted on graphene. ACS Nano. 2010;4(12):127531–7.
Singh J. FTIR and Raman spectra and fundamental frequencies of biomolecule: 5-methyluracil (thymine). J Mol Struct. 2008;876:127–33.
Colarusso P, Zhang K, Guo B, Bernath P. The infrared spectra of uracil, thymine, and adenine in the gas phase. Chem Phys Lett. 1997;269:39–48.
Aroca R, Bujalski R. Surface enhanced vibrational spectra of thymine. Vib Spectrosc. 1999;19:11–21.
Acknowledgements
The work has been supported by the European Commission (FP7 projects FAEMCAR, Nanotwinning and Graphene Flagship) and by the Finnish Innovation and Technology TEKES (NP-nano FiDi Project). We thank Prof. Philippe Lambin (University of Namur) for helpful discussions.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
OF gave final approval of the version to be published and measured and analyzed the Raman spectra. GD was involved in the discussion of the manuscript. AD was involved in the drafting of the manuscript and in the measuring of the CARS spectra. RK was involved in the drafting of the manuscript and analysis of CARS images. TK carried out the synthesis of the graphene layers. YS contributed to the design of the manuscript and to the analysis and interpretation of data. All authors read and approved the final manuscript.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (https://creativecommons.org/licenses/by/4.0), which permits use, duplication, adaptation, distribution, and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Fesenko, O., Dovbeshko, G., Dementjev, A. et al. Graphene-enhanced Raman spectroscopy of thymine adsorbed on single-layer graphene. Nanoscale Res Lett 10, 163 (2015). https://doi.org/10.1186/s11671-015-0869-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-015-0869-4