Abstract
The morphologies and microstructures of kinked InP nanowires (NWs) prepared by solid-source chemical vapor deposition method were examined using scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM). Statistical analysis and structural characterization reveal that four different kinds of kinks are dominant in the grown InP NWs with a bending angle of approximately 70°, 90°, 110°, and 170°, respectively. The formation mechanisms of these kinks are discussed. Specifically, the existence of kinks with bending angles of approximately 70° and 110° are mainly attributed to the occurrence of stacking faults and nanotwins in the NWs, which could easily form by the glide of {111} planes, while approximately 90° kinks result from the local amorphorization of InP NWs. Also, approximately 170° kinks are mainly caused by small-angle boundaries, where the insertion of extra atomic planes could make the NWs slightly bent. In addition, multiple kinks with various angles are also observed. Importantly, all these results are beneficial to understand the formation mechanisms of kinks in compound semiconductor NWs, which could guide the design of nanostructured materials, morphologies, microstructures, and/or enhanced mechanical properties.
Avoid common mistakes on your manuscript.
Background
Recently, III-V compound semiconductor nanowires (NWs), especially InP NWs, have attracted enormous attention in next-generation electronics, sensors, photonics, and solar cells due to their superior carrier mobilities and as direct and suitable bandgaps for efficient photon coupling [1–6]. In the past decade, most studies have focused on understanding and controlling the morphology and structures of InP NWs, such as tapering, reversible switching of growth direction, twin-plane superlattices, and structural transition [2–4, 7–11]. However, to the best of our knowledge, few reports are relevant to the kinked InP NWs, particularly the detailed microstructures related to the bending configuration. Generally, it is believed that the kinks in the NWs would influence their transport properties, electron, and hole collection efficiencies for technological applications [12, 13]. In this regard, a detailed study on the formation of these kinks is extremely important, which could provide valuable information to further design NW materials with different shapes, morphologies, and microstructures, expanding their application domains [14].
In our experiment, kinked InP NWs frequently emerged in the growing process, which possess a crystal structure of face-centered cubic (zinc blende) [6]. In order to understand the growth mechanism of these bending InP NWs, the morphologies and microstructures of different InP NWs were studied utilizing scanning electron microscopy (SEM) and high-resolution transmission electronic microscopy (HRTEM), respectively. Through comprehensive statistical analysis and intensive structural characterization, it is revealed that the dominant bending angles of InP NWs are approximately 70°, 90°, 110°, and 170°. The formation of bending angles of approximately 70° and 110° is mainly attributed to the occurrence of nanotwins and stacking faults (SFs), which could easily form by the glide of {111} planes. However, for approximately 90° bending, local amorphorization is believed to be the main cause for this phenomenon while approximately 170° kinks are mostly induced by small-angle boundaries, where the insertion of extra atomic planes could make the NWs slightly bent. In addition, NWs with multiple curves composed of different bending angles are also observed.
Methods
Synthesis of InP NWs
InP NWs used in this study were prepared by a solid-source catalytic chemical vapor deposition method in a dual-zone horizontal tube furnace as previously reported [6]. Briefly, the solid source (1 g, InP powder, 99.9999% purity) was placed in a boron nitride crucible and evaporated at the center of the upstream zone, while the growth substrate (0.5 nm Au film deposited on SiO2/Si) was placed in the middle of the downstream zone with a tilt angle of approximately 20° and a distance of 10 cm away from the source. Au films with a thickness of 0.5 nm were thermally evaporated under a vacuum of approximately 1 × 10−6 Torr onto the substrates. During the growth of NWs, the substrate was thermally annealed at 800°C for 10 min in a hydrogen environment (99.999% pure H2, 100 sccm, 1 Torr) to obtain Au nanoclusters which acted as the catalysts. When the substrate temperature was cooled to the preset growth temperature (460°C), the source was heated to the required source temperature (770°C) for 60 min. After the growth, the source and substrate heater were stopped and cooled down to the room temperature under the flow of H2 gas.
Characterization of InP NWs
Philips XL30 SEM (Philips, Amsterdam, Netherlands) was employed to view surface morphologies of the grown InP NWs. Selected-area electron diffraction (SAED), bright field (BF) transmission electron microscopy (TEM), and HRTEM were carried out to determine crystal structure and to examine microstructures of the grown InP NWs using a JEOL JEM2100F TEM (JEOL Ltd., Tokyo, Japan) operating at 200 kV. The incident electron beam was along the direction. Specimens for HRTEM examinations were prepared by peeling off the InP NWs from the surface of the substrate, ultrasonicating them into anhydrous ethanol for several seconds, and dispersing the finished solution onto a holey-carbon-film-coated copper grid.
Results and discussion
Figure 1a shows a low-magnification SEM image of InP NWs prepared by 0.5-nm-thick Au catalyst film. It is observed that different kinds of kinks exist in the grown InP NWs. Interestingly, in most cases the bending angles are close to approximately 110° as indicated by white arrows. Magnified SEM image (Figure 1b) exhibits a clear morphology of InP NWs. It is shown that despite there exists some kinks, the overall morphology of grown InP NWs is relatively straight and smooth. As observed from TEM images, InP NWs with kinks can be clearly seen and the diameter of InP NWs is uniform and ranges from 20 to 40 nm. In order to systematically understand the characteristics of the different kinks, initially, a comprehensive statistical analysis was carried out using typical BF TEM images (Figure 1c), which are mainly concentrated in the range of 20 to 30 nm. In this work, the bending angles of more than 180 kinks in different NWs were measured and the statistical result is presented in Figure 1d. It is noted that the angles and frequency of kinks are found independent of the nanowire diameter and four dominant groups of kinks with the bending angles of approximately 70°, 90°, 110°, and 170° are clearly displayed, with the relative percentage of them observed being 17%, 11%, 35%, and 6%, respectively. Except the four dominant groups, the kinked InP NWs with other angles are scarce. Furthermore, the bending angles less than 30° are not observed.
To shed light in exploring the formation mechanism of these kinks with different angles, HRTEM technique was exploited to examine the microstructures of these grown InP NWs. Figure 2 shows the typical BF and HRTEM images of approximately 110° kinks observed in different NWs. It is clear that alternating bright/dark contrast appears in a periodic manner along the axial direction of the wire in BF TEM images (Figure 2a,c,e), which indicates the existence of planar defect structure. The phenomenon is consistent with the previous report that high density of SFs in <111> -oriented nanowires commonly form perpendicularly to the growth direction [15]. HRTEM images (Figure 2b,d,f) and corresponding SAED patterns were acquired from the bending areas, which present explicit illustrations of the microstructures in these kink areas. The SAED patterns (Figure 2a,c insets) show the crystal structure of InP NWs here being face-centered cubic (zinc blende). In Figure 2b, it is obvious that the NWs grows along <111> directions and the bending angle is consistent with that between (111) and planes, namely, approximately 110°. Since the {111} planes are the faces with lower energy in the face-centered cubic structure, the growth of NWs through {111} planes is energetically favorable. Figure 2b also reveals a stacking fault, almost transecting the entire nanowire in the kink area. We suppose that the transecting SFs in the kinked area would be beneficial to the change of growth direction. In addition, nanotwins and SFs were also observed in the region close to approximately 110° kink as depicted in Figure 2d, which corresponds to the selected area in Figure 2c. As mentioned in the previous report [16], the bending of nanowires typically associated with a significantly large local strain in which SFs are induced and resulted to releasing the stress. It is as well noted that an approximately 110° kink consisted of successive curves is observed in Figure 2e. Noticeable contrast variations indicated by white arrows in Figure 2e are supposed to be imaging effects which occur when twin boundary relaxations are present, although it should be pointed out that images with similar appearances could result from astigmatism or misalignment [17]. HRTEM image corresponding to the selected area in Figure 2e is presented in Figure 2f. It is obvious that there is large amount of SFs in the region of approximately 110° kink. In this case, we believe that the larger local strain could be introduced by two successive curves in such narrow space. It is noted that most SFs in the kinked area run nearly parallel to the growth direction. We suppose that in the kinked area, a large amount of stress is introduced such that the {111} planes nearly parallel to the growth direction can easily glide and could facilitate the formation of SFs, which plays an important role in releasing the stress. In addition, nanotwins marked by TB are observed in the bending area. According to the literature, twin-plane formation in zinc blende crystals requires very little energy [18]. The twins are as expected for bulk zinc blende crystals, which can twin on {111} planes by rotating through 60° about the <111> axis [19]. Consequently, in theory, nanotwins could facilitate the NWs to switch from one favorable growth direction to another.
Compared with approximately 110° kinks, the approximately 70° kink bends sharply as shown in Figure 3a. Its corresponding SAED pattern (inset) matches well with cubic zinc blende structure, and the lattice planes are {111} planes. As shown in Figure 3b, the nanotwin appears in the bending area, which is similar to that occurs in approximately 110° kinks. As mentioned above, the formation of nanotwin could be beneficial to the change of growth direction. In addition, it is worth noting that highly dense SFs are also observed in the approximately 70° kink area and nearly parallel to the growth direction. In such a sharp bending, the strain is so severe, which could produce the internal stress larger than that in approximately 110° kink.
On the basis of the above observed results, approximately 70° and 110° kinks are believed to form by the glide of {111} planes, which produces nanotwins and SFs to facilitate the formation of such kinks. It is known that {111} planes are the closest packed planes with the lower interfacial energy in cubic zinc blende structure and the angles between two different {111} planes are 70.5° or 109.5°. Therefore, the change of growth direction is inclined to be <111> and the bending angle is mostly close to 70.5° or 109.5°. However, due to their difference in the bending degree, the densities of SFs in local areas for approximately 70° and 110° kinks are different. When the bending angle is approximately 70°, the curvature is so sharp and supposed to cost larger energy. As a result, the internal stress would be larger than that of approximately 110° kinks, which needs massive and dense SFs to release. In addition, the sharp curvature makes the formation of approximately 70° kinks more difficult, which can be interpreted by presence of a smaller percentage with approximately 70° kink than that of approximately 110° kink as illustrated in Figure 1d.
In the previous studies, SFs and nanotwins are frequently observed in III-V semiconductor NWs [7, 9, 20]. Here, the intensive study of microstructures reveals some novel characteristics in the remaining two groups of kinks in InP NWs, i.e., approximately 90° kinks and 170° kinks. As presented in Figure 4a, an approximately 90° kink can be clearly observed. The inset gives its corresponding SAED pattern, in which each diffraction spot indicated by white arrows was split into adjacent irregular spots. It indicates that the crystal orientation makes slight changes in this area. It is evidenced in Figure 4b that the amorphous regions pointed by arrows are firstly observed in the approximately 90° kink, where the crystal orientation is disordered. This result could guide us presenting reasonable explanations for the formation of approximately 90° kinks. In crystallography, it is not easier to form an approximately 90° angle by the glide of {111} planes. Therefore, in order to produce such shape, the change of crystal lattice becomes reasonable. It is known that amorphorization could distort the crystal lattice and break the barrier for the transition of morphology in the growing process. As a result, the growth of NWs would become more flexible, which is beneficial to the formation of approximately 90° kinks.
As for the slight bendings, i.e., approximately 170° kinks, careful examinations show that the small-angle boundary exists in the bending area, being rarely observed in III-V semiconductor NWs [16]. As depicted in Figure 5a, the InP NWs are slightly bent in which planar defects could be easily observed. Furthermore, as given in Figure 5b, a small-angle boundary was clearly seen in the selected area of Figure 5a. The extra atomic planes are inserted as indicated by arrows. This result is similar to that observed in Au NWs [21]. In the growing process, the NWs are likely to be affected by the disturbance of growth conditions, such as the gas flow fluctuation. As a result, the atomic arrangement is likely to collapse and tend to reconstruct in order to accommodate the disturbance effect, which causes the formation of small-angle boundary. The inserted extra atomic planes could generate unbalanced internal stress for the growth of the upper side and lower side of InP NWs shown in Figure 5b. Consequently, the InP NWs show slight bending. In addition, depending on the simulation of Cao et al. [22], the motion of dislocations along the well-defined slip systems can be restricted by twin boundaries (TBs). As observed, there are plenty of TBs in the left and right sides of the small-angle boundary, which would restrict the occurrence and the motion of dislocations. Therefore, the number of kinks with approximately 170° is relatively small.
In addition to individual kinks, multiple kinks are also frequently observed in InP NWs. As shown in Figure 6, different shapes, such as zig-zag and rectangle, are composed of kinks with different angles mentioned above. They are likely to be formed by the change of growth conditions. At the same time, it is observed that the formation of kinks is not related to the substrate tilting during the growth. For the growth substrate without any tilt angle, the InP NWs with kinks were also frequently observed. The occurrence of continuous kinks means that there is a possibility to produce NWs with different shapes in large scale, such as the nanospring produced in ZnO NWs [16]. Our results also call into question how to control the shape and microstructures of NWs by tuning the NW growth conditions in order to satisfy the needs of practical applications.
Conclusions
In conclusion, four dominant kinds of kinks with an angle of approximately 70°, 90°, 110°, and 170° have been observed in InP NWs. The dominant InP crystal structure in this work is zinc blende and the kinks with bending angles of approximately 70° and 110° are mainly attributed to the SFs and nanotwins, which could easily form by the glide of {111} planes. However, the approximately 90° kinks result from the local amorphorization of InP NWs while the approximately 170° kinks are mainly caused by small-angle boundaries, where the insertion of extra atomic planes could make the NWs slightly bend. In addition, NWs with multiple kinks in various angles are also observed.
Abbreviations
- BF:
-
Bright field
- HRTEM:
-
high-resolution transmission electronic microscopy
- NWs:
-
nanowires
- SAED:
-
selected-area electron diffraction
- SEM:
-
scanning electron microscopy
- SFs:
-
stacking faults
- TBs:
-
twin boundaries.
References
Duan X, Huang Y, Cui Y, Wang J, Lieber CM: Indium phosphide nanowires as building blocks for nanoscale electronic and optoelectronic devices. Nature 2001, 409: 66–69. 10.1038/35051047
Han N, Wang F, Hou JJ, Yip SP, Lin H, Xiu F, Fang M, Yang Z, Shi X, Dong G, Hung TF, Ho JC: Tunable electronic transport properties of metal-cluster-decorated III-V nanowire transistors. Adv Mater 2013, 25: 4445–4451. 10.1002/adma.201301362
Johansson J, Karlsson LS, Svensson CP, Martensson T, Wacaser BA, Deppert K, Samuelson L, Seifert W: Structural properties of <111> B-oriented III-V nanowires. Nat Mater 2006, 5: 574–580. 10.1038/nmat1677
Caroff P, Dick KA, Johansson J, Messing ME, Deppert K, Samuelson L: Controlled polytypic and twin-plane superlattices in III-V nanowires. Nat Nanotechnol 2009, 4: 50–55. 10.1038/nnano.2008.359
Han N, Hou JJ, Wang F, Yip S, Yen YT, Yang ZX, Dong G, Hung T, Chueh YL, Ho JC: GaAs nanowires: from manipulation of defect formation to controllable electronic transport properties. ACS Nano 2013, 7: 9138–9146. 10.1021/nn403767j
Hui AT, Wang F, Han N, Yip S, Xiu F, Hou JJ, Yen YT, Hung T, Chueh YL, Ho JC: High-performance indium phosphide nanowires synthesized on amorphous substrates: from formation mechanism to optical and electrical transport measurements. J Mater Chem 2012, 22: 10704. 10.1039/c2jm31232h
Ikejiri K, Kitauchi Y, Tomioka K, Motohisa J, Fukui T: Zinc blende and wurtzite crystal phase mixing and transition in indium phosphide nanowires. Nano Lett 2011, 11: 4314–4318. 10.1021/nl202365q
Wang J, Plissard SR, Verheijen MA, Feiner LF, Cavalli A, Bakkers EP: Reversible switching of InP nanowire growth direction by catalyst engineering. Nano Lett 2013, 13: 3802–3806. 10.1021/nl401767b
Dick KA, Caroff P, Bolinsson J, Messing ME, Johansson J, Deppert K, Wallenberg LR, Samuelson L: Control of III–V nanowire crystal structure by growth parameter tuning. Semicond Sci Tech 2010, 25: 024009. 10.1088/0268-1242/25/2/024009
Glas F, Harmand JC, Patriarche G: Why does wurtzite form in nanowires of III-V zinc blende semiconductors? Phys Rev Lett 2007, 99: 146101.
Kitauchi Y, Kobayashi Y, Tomioka K, Hara S, Hiruma K, Fukui T, Motohisa J: Structural transition in indium phosphide nanowires. Nano Lett 2010, 10: 1699–1703. 10.1021/nl1000407
Hou JJ, Han N, Wang F, Xiu F, Yip S, Hui AT, Hung T, Ho JC: Synthesis and characterizations of ternary InGaAs nanowires by a two-step growth method for high-performance electronic devices. ACS Nano 2012, 6: 3624–3630. 10.1021/nn300966j
Han N, Wang F, Hui AT, Hou JJ, Shan GC, Fei X, Hung TF, Ho JC: Facile synthesis and growth mechanism of Ni-catalyzed GaAs nanowires on non-crystalline substrates. Nanotechnology 2011, 22: 285607. 10.1088/0957-4484/22/28/285607
Tian B, Xie P, Kempa TJ, Bell DC, Lieber CM: Single-crystalline kinked semiconductor nanowire superstructures. Nat Nanotechnol 2009, 4: 824–829. 10.1038/nnano.2009.304
Krishnamachari U, Borgstrom M, Ohlsson BJ, Panev N, Samuelson L, Seifert W, Larsson MW, Wallenberg LR: Defect-free InP nanowires grown in [001] direction on InP (001). Appl Phys Lett 2004, 85: 2077. 10.1063/1.1784548
Wang X, Ding Y, Summers CJ, Wang ZL: Large-scale synthesis of six-nanometer-wide ZnO nanobelts. J Phys Chem B 2004, 108: 8773–8777. 10.1021/jp048482e
Marks L, Smith DJ: HREM and STEM of defects in multiply-twinned particles. J Microsc 1983, 130: 249–261. 10.1111/j.1365-2818.1983.tb04222.x
Hurle D, Rudolph P: A brief history of defect formation, segregation, faceting, and twinning in melt-grown semiconductors. J Cryst Growth 2004, 264: 550–564. 10.1016/j.jcrysgro.2003.12.035
Korgel BA: Semiconductor nanowires: twins cause kinks. Nat Mater 2006, 5: 521–522. 10.1038/nmat1688
Algra RE, Verheijen MA, Borgstrom MT, Feiner LF, Immink G, Van Enckevort WJ, Vlieg E, Bakkers EP: Twinning superlattices in indium phosphide nanowires. Nature 2008, 456: 369–372. 10.1038/nature07570
Wang C, Wei Y, Jiang H, Sun S: Bending nanowire growth in solution by mechanical disturbance. Nano Lett 2010, 10: 2121–2125. 10.1021/nl100661v
Cao AJ, Wei YG, Mao SX: Deformation mechanisms of face-centered-cubic metal nanowires with twin boundaries. Appl Phys Lett 2007, 90: 151909. 10.1063/1.2721367
Acknowledgements
The work is financially supported by National Key Basic Research Development Program of China (grant no. 2012CB722705), the Natural Science Foundation for Outstanding Young Scientists in Shandong Province, China (grant no. JQ201002), the Program for Foreign Cultural and Educational Experts (grant nos. W20123702084, W20133702021), and the Early Career Scheme of the Research Grants Council of Hong Kong SAR, China (grant no. CityU139413). YQW would like to thank the financial support from the Top-notch Innovative Talents Program of Qingdao City and the Taishan Scholar Program of Shandong Province, China.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
MHZ analyzed the experimental results and drafted the manuscript. FYW performed the SEM observations and revised the manuscript. CW performed the HRTEM observations. YQW proposed the formation mechanism of the kinks in InP NWs and revised the manuscript. SPY and FYW fabricated InP NWs. JCH directed the experiment of fabricating InP NWs. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, M., Wang, F., Wang, C. et al. Formation mechanisms for the dominant kinks with different angles in InP nanowires. Nanoscale Res Lett 9, 211 (2014). https://doi.org/10.1186/1556-276X-9-211