Abstract
In this paper, the systematic evolution process of self-assembled Au droplets is successfully demonstrated on GaAs (111)A, (110), (100), and (111)B. On various GaAs substrates, self-assembled Au clusters begin to nucleate at around 300°C, and then, they develop into wiggly Au nanostructures at 350°C. Between 400°C and 550°C, the self-assembled dome-shaped Au droplets with fine uniformity are fabricated with various sizes and densities based on the Volmer-Weber growth mode. Depending on the annealing temperature, the size including the average height and lateral diameter and the density of Au droplets show the opposite trend of increased size with correspondingly decreased density as a function of the annealing temperature due to the difference in the diffusion length of adatoms at varied activation energy. Under an identical growth condition, depending on the surface index, the size and density of Au droplets show a clear distinction, observed throughout the temperature range. The results are systematically analyzed and discussed in terms of atomic force microscopy (AFM) images, cross-sectional line profiles, and Fourier filter transform (FFT) power spectra as well as the summary plots of the size and density.
Avoid common mistakes on your manuscript.
Background
Due to their increased cross-section and surface area as well as the size-dependent quantum confinement, semiconductor nanowires (NWs) have been successfully utilized in numerous device applications such as solar cells, LEDs, and FETs [1–8]. Until now, various semiconductor NWs have been successfully demonstrated through diverse epitaxial growth approaches including chemical vapor deposition [9, 10], molecular beam epitaxy [11, 12], and pulsed laser deposition [13, 14]. Vapor–liquid-solid (VLS) [15–18] method has been widely adapted as a common growth mechanism in the forth-mentioned epitaxial approaches. The first successful fabrication of Si whisker on Si (111) was reported by Wagner et al., and they introduced a novel concept of growth approach called the ‘VLS’ growth [15]. Later, Morales et al. successfully demonstrated the fabrication of crystalline Si NWs by utilizing the VLS approach [16]. In the VLS growth, Au droplets serve as catalysts, and regardless of the materials and substrates utilized, the vapor-phase atoms could diffuse into the liquid-phase Au droplets [17, 18]; from the supersaturated Au alloy droplets, the crystallization of NWs can occur at the liquid–solid interface due to the higher sticking probability at the interface [19–23]. In addition, the metallic nanoparticles were utilized in plasmonic applications such as solar cells and light emission enhancement [24–29]. The diameter, size, configuration, and even the density of NWs can innately be determined by those of the Au catalysts, and thus, the control of Au droplets is an essential step for the successful fabrication of the desired NWs. However, to date, the systematic studies on the evolution of Au droplets on various GaAs substrates are deficient, and therefore, in this paper, the detailed study on the evolution of the self-assembled Au droplets on GaAs (111)A, (110), (100), and (111)B is investigated. In order to investigate the detailed evolution process, feasible annealing temperatures were systematically tested ranging from 100°C to 550°C as briefly illustrated in Figure 1. Depending on the annealing temperature, the nucleation of self-assembled tiny Au clusters and wiggly Au nanostructures as shown in Figure 1c was clearly observed on various GaAs substrates. At increased annealing temperatures, the self-assembled Au droplets with fine uniformity were successfully fabricated on each GaAs index. The self-assembled Au droplets showed an opposite evolution trend of increased size including average height and lateral diameter with correspondingly decreased density as a function of annealing temperature, and the size and density evolution are systematically analyzed with the atomic force microscopy (AFM) images and cross-sectional line profiles as well as the summary plots. Under an identical growth condition, depending on the substrates utilized, the size and density of Au droplets show a clear disparity among various indices throughout the temperature range.
Methods
In this study, the self-assembled Au droplets were fabricated on GaAs (111)A, (111)B, (110), and (100) representing the general zinc blende lattice indices in a pulsed laser deposition (PLD) system. To start with, various index samples were indium-bonded together on an Inconel holder side by side for uniformity per batch and then treated with a degassing process at 350°C for 30 min under 1 × 10−4 Torr. Subsequently, a total amount of 2.5 nm of Au was equally deposited on the samples at a rate of 0.5 Å/s and at an ionization current of 3 mA under 1 × 10−1 Torr in an ion coater chamber. With the aim of investigating the detailed evolution process of the self-assembled Au droplets, each growth was systematically carried out by varying the annealing temperatures (Ta) at 100°C, 250°C, 300°C, 350°C, 400°C, 450°C, 500, and 550°C, respectively. For the systematic growths, the substrate temperature (Ts) was ramped up to the target temperature at a ramp rate of 1.83°C/s under 1 × 10−4 Torr by a computer-operated recipe, and after reaching each target, a dwell time of 450 s was equally given to the samples. After the termination of each growth, the Ts was immediately quenched down to diminish the Ostwald ripening [30, 31]. Following the fabrication, AFM was used for the characterization of surface morphologies, and XEI software was used for the data preparation and analysis of AFM top-view and side-view images and line profiles as well as the Fourier filter transform (FFT) power spectra. The FFT power spectrum represents the height information converted from the real spatial domain to the frequency domain, and thus, the horizontal (x) and vertical (y) information is converted by taking the reciprocal of the corresponding units of x and y from the AFM images; hence, the distribution of color patterns can present the distribution of frequent height with directionality.
Results and discussion
Figure 2 presents the nucleation of the self-assembled Au clusters and the wiggling nanostructures induced by the variation of annealing temperature (Ta) between 250°C and 350°C on GaAs (111)A. The AFM top-view images of 1 × 1 μm2 are presented in Figure 2a,b,c,d along with the cross-sectional line profiles in Figure 2 (a-1) to (d-1), acquired from the white lines in Figure 2a,b,c,d. The insets in Figure 2 (a-2) to (d-2) show the FFT power spectra. In general, on GaAs (111)A from a relatively flat surface morphology in Figure 2a,b, with the increased Ta, the surface morphologies were drastically changed and gradually developed into Au clusters in Figure 3c and wiggly Au nanostructures in Figure 2d. In more detail, after the Au deposition before annealing, the surface showed a quite smooth topography as clearly observed by the AFM image in Figure 2a, and the line profile in Figure 2 (a-1) and the corresponding FFT spectrum in Figure 2 (a-2) showed a quite broad round pattern due to the narrow random surface modulation. At the Ta of 250°C, the diffusion of Au adatoms was induced as shown in Figure 2b, but the surface modulation was only slightly increased as evidenced by the line profile in Figure 2 (b-1). The FFT spectrum in Figure 2 (b-2) became smaller with a round pattern. With the increased thermal energy at 300°C, the diffusion of adatoms was further enhanced, and as a result, there was nucleation of tiny Au clusters with a slightly bumpy morphology as shown in Figure 2c and (c-1). Finally, at the Ta of 350°C, as clearly seen with the AFM image in Figure 2d and the line profile in Figure 2 (d-2), a sharp transition from the Au clusters to the wiggly nanostructures occurred with a height modulation of approximately ±10 nm as clearly evidenced by the line profiles of Figure 2 (c-1) and (d-1). The FFT pattern size was further reduced with the increased height modulation and became a symmetric circle as there was no apparent directionality of Au nanostructures. The Au clusters and wiggly nanostructures can be formed based on the Volmer-Weber growth mode [32, 33]. Given that the bonding energy among Au adatoms (Ea) is greater than that between Au adatoms and GaAs surface atoms (Ei), Au adatoms can be merged together to nucleate the Au clusters at a relatively lower Ta, and the wiggly Au nanostructures can result at an increased Ta. This transition of surface morphology associated with the nucleation of the Au clusters and wiggly nanostructures appears to be unique to GaAs. For example, on Si (111) neither this type of transition nor the Au clusters or the wiggly Au nanostructures were observed during the evolution of the self-assembled Au droplets while varying the Ta between 50°C and 850°C [34], but very high density dome-shaped Au droplets were observed throughout the temperature range. In short, with the increased Ta on GaAs (111)A, apparent transitions of surface morphologies at each Ta were clearly observed and the height modulation was gradually enlarged as a function of Ta; a sharp transition was observed at 350°C with a surface modulation of approximately ±10 nm due to the increased diffusion of Au adatoms induced by the enhanced thermal energy.
Figure 3 shows the evolution of self-assembled Au droplets with further increased Ta between 400°C and 550°C on GaAs (111)A. AFM top-view images in Figure 3a,b,c,d show the large areas of 3 × 3 μm2, and the insets of Figure 3 (a-1) to (d-1) are the enlarged areas of 1 × 1 μm2. The surface line profiles in Figure 3 (a-2) to (d-2), the FFT power spectra in Figure 3 (a-3) to (d-3), and the height distribution histograms (HDHs) in Figure 3 (a-4) to (d-4) are respectively presented. Figure 4 shows the summary plots of the average height (AH) in Figure 4a, the lateral diameter (LD) in Figure 4b, and the average density (AD) in Figure 4c of the self-assembled Au droplets at each Ta on various GaAs substrates. Table 1 summarizes the corresponding values. In general, between 400°C and 550°C, the self-assembled dome-shaped Au droplets were successfully fabricated as shown in Figure 3. Due to the enhanced diffusion of Au adatoms at increased thermal energy, given Ea > Ei, the wiggly Au nanostructures preferentially evolve into the dome-shaped Au droplets to minimize the surface energy [35]. In terms of the size and density evolution, as clearly shown in Figure 4a,b,c, the size including the AH and LD of the Au droplets was gradually increased, while the density was correspondingly decreased as a function of the Ta on GaAs (111)A. In more detail, at an increased Ta of 400°C, finally, the self-assembled Au droplets were fabricated and we can clearly observe the apparent transition from the wiggly Au nanostructures at 350°C to the dome-shaped Au droplets at 400°C. The AH was 23.4 nm, the LD was 128.6 nm, and the AD was 1.39 × 1010 cm−2 as shown in Table 1. The HDH was approximately ±15 nm as shown in Figure 3 (a-4). At 450°C, the Au droplets grew larger in size and showed a lower density as shown in Figure 4. The AH was increased by × 1.09 and became 25.4 nm, and the LD was increased by × 1.04 and became 133.8 nm as shown in Table 1. The density was dropped by × 1.13 and became 1.23 × 1010 cm−2. Likewise, at 500°C, the size of the Au droplets was further increased, and the density was correspondingly decreased as shown in Figure 3c. The AH and LD were increased by × 1.14 and × 1.04 and became 28.9 and 138.5 nm, respectively, while the AD was decreased by × 1.04 and became 1.23 × 1010 cm−2. The HDH was now further extended with the increased size to over ±20 nm as shown in Figure 3 (c-4). Finally, with the 550°C annealing temperature, the Au droplets continually grew in size and the density was constantly decreased as shown in Figure 4. The AH and LD were increased by × 1.11 and × 1.04 and became 32.2 and 143.4 nm. Likewise, the AD was down by × 1.11 and became 9.9 × 109 cm−2 as shown in Table 1. The HDH in Figure 3 (d-4) now became clearly over ±20 nm wide along with the increased height of Au droplets. The self-assembled Au droplets on GaAs (111)A with the Ta variation between 400°C and 550°C showed quite excellent uniformity as witnessed in the symmetric round FFT power spectra of Figure 3 (a-3) to (d-3) and showed an overall increased size with decreased density as a function of the Ta. The size and density evolution induced by the variation of the Ta can be simply explained with the following equation [36]. The diffusion length (lD) can be expressed as where D is the surface diffusion coefficient and τ is the residence time of atoms. D can be written as D ∝ Tsub where Tsub is the substrate temperature, namely Ta in this case. With the increased Ta, the D proportionally increases and it results in an increased lD. With the increased lD, the density of the Au droplets can be decreased, given the stronger bonding energy between Au atoms (Ea > Ei). In this thermodynamic equilibrium system, in order to keep the energy of the whole system in the lowest state, bigger droplets tend to absorb nearby adatoms to lower the surface energy, and thus, the size can grow larger and the density can be reduced until reaching the equilibrium. Thus, this type of size and density evolution was witnessed in Ga and In metal droplets [35, 37, 38] and nanostructures [39–41] on various semiconductor substrates.
Figure 5 summarizes the evolution process of the self-assembled Au droplets on GaAs (110) induced by the variation of the Ta between 250°C and 550°C, and similarly, Figures 6 and 7 show that on GaAs (100) and (111)B. In general, the evolution process of the Au droplets on GaAs (110), (100), and (111)B showed quite a similar behavior to that on GaAs (111)A in terms of the nucleation of Au clusters and wiggly nanostructures as shown in Figure 2 and the evolution of size and density as a function of the T a as summarized with the plots in Figure 4. For example, on GaAs (110) between 250°C and 350°C, the nucleation of Au clusters and wiggly Au nanostructures was clearly observed as shown in Figure 5b,c,d, and between 400°C and 550°C, the self-assembled dome-shaped Au droplets were successfully fabricated as shown in Figure 5e,f,g,h. The size of droplets on GaAs (110) was also constantly increased as a function the Ta, while the density was correspondingly decreased as clearly shown in Figure 4. However, the size of Au droplets on GaAs (110) was slightly smaller than that on GaAa (111)A, putting the (110) line below the (111)A in Figure 4a,b, and as a result, based on the thermodynamic description, the density was slightly higher throughout the whole temperature range, marking the (110) line above the (111)A in Figure 4c. For example, at 400°C, the AH, LD, and AD were 22.6 nm, 122.5 nm, and 1.48 × 1010 cm−2, which are 3.42% and 4.47% smaller in size and 6.47% higher in density as compared to those on GaAs (111)A. Similarly, at 550°C, the size and density of droplets on (110) were 31.2 nm (AH), 141 nm (LD), and 1.07 × 1010 cm−2 (AD), which are 3.11% smaller in AH and 1.67% smaller in LD and 8.08% higher in AD. In short, the self-assembled Au droplets on GaAs (110) clearly showed smaller size and correspondingly higher density as compared to those on GaAs (111)A throughout the Ta range. In the meantime, on GaAs (100) and (111)B, the nucleation of Au clusters and wiggly nanostructures was also clearly observed between 250°C and 350°C as shown in Figures 6b,c,d and 7b,c,d, and the self-assembled Au droplets were also successfully fabricated between 400°C and 550°C as shown in Figure 6e,f,g,h and 7e,f,g,h. In the same way, on both GaAs (100) and (111)B, the size of the Au droplets was constantly increased as a function of Ta and the density was correspondingly decreased. Depending on the surface index, there appeared a clear difference in size and density between the indices, and this trend constantly appeared throughout the Ta range as clearly shown in Figure 4. For instance, GaAs (111)B showed the smallest Au droplets at each point of the Ta, putting the (111)B line at the bottom of the plots (a) and (b), and the (100) was the second. Then, the (110) showed further increased size, and finally, the biggest droplets were fabricated on GaAs (111)A. In terms of the density, GaAs (111)B showed the highest at each point of the Ta, followed by (100), (110), and (111)A. The Miller index [110] of zinc blende lattice is located at 45° toward [010] from the [100], and these two indices with [111] can represent the general zinc blende indices except for the high index. As discussed, the diffusion length (lD) can be directly related to the Ta and thus can affect the size and density of Au droplets. The lD can also be related to the root mean squared (RMS) surface roughness (Rq) caused by several factors such as the dangling bond density, atomic step density, and surface reconstruction [42–46]. If the Rq value of one surface is relatively lower, the surface would possess longer lD, and it can result in a larger size and a lower density of Au droplets. The measurements of Rq values on the GaAs indices are as follows: (111)A, 0.289 nm; (110), 0.305 nm; (100), 0.322 nm; and (111)B, 0.291 nm. GaAs (111)A showed the lowest Rq, and (110) had a slightly increased value; thus, this can explain the larger size and the lower density of droplets on GaAs (111)A as shown in Figure 4. Similarly, we can relate the decreased size and the increased density of Au droplets on GaAs (100) as compared to those on (110) with the increased Rq. However, the (111)B surface showed similar Rq to the (111)A, and the results nevertheless showed the smallest size with the highest density. The type-A GaAs surface is characterized to be Ga-rich, while the type-B surface is As-rich [42]. The Ga-rich surface can possess a higher interface energy than the As-rich surface based on the atomistic modeling of the Au droplet-GaAs interface [47], and thus, the reduced diffusion of Au atoms on type-B surface can lead to a lower lD; hence, the smaller size of droplets with a higher density can result. In short, on various GaAs surfaces, the evolution process of the self-assembled Au droplets was clearly demonstrated, and they showed quite similar behaviors in terms of the size and density evolution while keeping the difference between indices throughout the whole Ta range.
Conclusions
The evolution of the self-assembled Au droplets has been successfully demonstrated on GaAs (111)A, (110), (100), and (111)B through the variation of annealing temperature throughout the feasible annealing temperature (Ta) range between 250°C to 550°C. The resulting Au nanostructures were systematically analyzed in terms of AFM images, cross-sectional line profiles, height distribution histograms, and FFT power spectra. The unique nucleation stages of the Au clusters and wiggly nanostructures were observed on various GaAs surfaces at the Ta range between 250°C and 350°C, and the self-assembled dome-shaped Au droplets with excellent uniformity were successfully fabricated between 400°C and 550°C. The average height and lateral diameter of the Au droplets were gradually increased with the increased Ta, and the average density was correspondingly decreased at each Ta point. The nucleation and the formation of Au droplets were described based on the Volmer-Weber growth mode, namely Ea > Ei. The evolution of the size and density of Au droplets was described in terms of the lD of Au adatoms in relation with the thermal dynamic equilibrium along with the Ta. In addition, an apparent distinction in the size and density of Au droplets between various GaAs indices was clearly observed, and it was maintained throughout the Ta range GaAs (111)A > (110) > (100) > (111)B in size and vice versa in diameter, and the trend was described in relation between the Rq and lD. This study can find applications in the nanowire fabrications on various GaAs surfaces.
References
Steffen B, Carsten P€u, Timur F, Oliver B, Grahn HT, Lutz G, Henning R: Suitability of Au- and self-assisted GaAs nanowires for optoelectronic applications. Nano Lett 2011, 11: 1276–1279. 10.1021/nl104316t
Wen C-Y, Reuter MC, Bruley J, Tersoff J, Kodambaka S, Stach EA, Ross FM: Formation of compositionally abrupt axial heterojunctions in silicon-germanium nanowires. Science 2009, 326: 1247–1250. 10.1126/science.1178606
Mahpeykar SM, Koohsorkhi J, Ghafoori-fard H: Ultra-fast microwave-assisted hydrothermal synthesis of long vertically aligned ZnO nanowires for dye-sensitized solar cell application. Nanotechnology 2012, 23: 165602(1)-165602(7).
Haofeng L, Rui J, Chen C, Zhao X, Wuchang D, Yanlong M, Deqi W, Xinyu L, Tianchun Y: Influence of nanowires length on performance of crystalline silicon solar cell. Appl Phys Lett 2011, 98: 151116(1)-151116(3).
Tae Hoon S, Bo Kyoung K, GangU S, Changhyup L, Myung Jong K, Hyunsoo K, Eun-Kyung S: Graphene-silver nanowire hybrid structure as a transparent and current spreading electrode in ultraviolet light emitting diodes. Appl Phys Lett 2013, 103: 051105(1)-051105(5).
Shirak O, Shtempluck O, Kotchtakov V, Bahir G, Yaish YE: High performance horizontal gate-all-around silicon nanowire field-effect transistors. Nanotechnology 2012, 23: 395202(1)-395202(8).
Jae-Hyuk A, Sung-Jin C, Jin-Woo H, Tae Jung P, Sang Yup L, Yang-Kyu C: Double-gate nanowire field effect transistor for a biosensor. Nano Lett 2010, 10: 2934–2938. 10.1021/nl1010965
Frajtag P, Hosalli AM, Bradshaw GK, Nepal N, El-Masry NA, Bedair SM: Improved light-emitting diode performance by conformal overgrowth of multiple quantum wells and fully coalesced p-type GaN on GaN nanowires. Appl Phys Lett 2011, 98: 143104(1)-143104(3).
Ying X, Linyou C, Sonia C-B, Sonia E, Jordi A, Francesca Peiro MH, Zardo I, Morante JR, Brongersma ML, Morral AF: single crystalline and core–shell indium-catalyzed germanium nanowires—a systematic thermal CVD growth study. Nanotechnology 2009, 20: 245608(1)-245608(9).
Jorg KNL, DjamilaBahloul H, Daniel K, Michael W, Thierry M, Bernd S: TEM characterization of Si nanowires grown by CVD on Si pre-structured by nanosphere lithography. Mater Sci Semicond Process 2008, 11: 169–174. 10.1016/j.mssp.2008.09.016
Cai Y, Wong TL, Chan SK, Sou IK, Su DS, Wang N: Growth behaviors of ultrathin ZnSe nanowires by Au-catalyzed molecular-beam. epitaxyAppl Phys Lett 2008, 93: 233107(1)-233107(3).
Tchernycheva M, Harmand JC, Patriarche G, Travers L, Cirlin GE: Temperature conditions for GaAs nanowire formation by Au-assisted molecular beam epitaxy. Nanotechnology 2006, 17: 4025–4030. 10.1088/0957-4484/17/16/005
Kazuki N, Takeshi Y, Hidekazu T, Tomoji K: Epitaxial growth of MgO nanowires by pulsed laser deposition. Appl Phys Lett 2007, 101: 124304(1)-124304(4).
Bjorn E, Vladimir S, Andreas B, Silke C: Growth of axial SiGe heterostructures in nanowires using pulsed laser deposition. Nanotechnology 2011, 22: 305604(1)-305604(8).
Wagner RS, Ellis WC: Vapor liquid solid mechanism of single crystal growth. Appl Phys Lett 1964, 4: 89–90. 10.1063/1.1753975
Morales AM, Lieber CM: Laser ablation method for the synthesis of crystalline semiconductor nanowires. Science 1998, 279: 208–208. 10.1126/science.279.5348.208
Volker S, Ulrich G: How nanowires grow. Science 2007, 316: 698–698. 10.1126/science.1142951
Khac An D, Khang Dao D, Dai Nguyen T, Tuan Phan A, Hung Manh D: The effects of Au surface diffusion to formation of Au droplets/clusters and nanowire growth on GaAs substrate using VLS method. Mater Electron 2012, 23: 2065–2074. 10.1007/s10854-012-0704-y
Borgstrom M, Deppert K, Samuelson L, Seifert W: Size- and shape-controlled GaAs nano-whiskers grown by MOVPE: a growth study. J Cryst Growth 2004, 260: 18–22. 10.1016/j.jcrysgro.2003.08.009
Yi C, Lauhon LJ, Gudiksen MS, Jianfang W, Lieber CM: Diameter-controlled synthesis of single-crystal silicon nanowires. Appl Phys Lett 2001, 78: 2214–2216. 10.1063/1.1363692
Pin Ann L, Dong L, Samantha R, Xuan P, Gao A, Mohan Sankaran R: Shape-controlled Au particles for InAs nanowire growth. Nano Lett 2012, 12: 315–320. 10.1021/nl2036035
Hannon JB, Kodambaka S, Ross FM, Tromp RM: The influence of the surface migration of gold on the growth of silicon nanowires. Nature 2006, 440: 69–71. 10.1038/nature04574
Jianwei Z, Lirong Q, Yong Z, Yonghao H, Qing G, Lide Z: Catalytic growth of cubic phase ZnO nanowires with jagged surface. Micro Nano Lett 2010, 5: 336–339. 10.1049/mnl.2010.0126
Jiang W, Seungyong L, Reddy VR, Manasreh MO, Weaver BD, Yakes MK, Furrow CS, Kunets VP, Benamara M, Salamo GJ: Photoluminescence plasmonic enhancement in InAs quantum dots coupled to gold nanoparticle. Mater Lett 2011, 65: 3605–3608. 10.1016/j.matlet.2011.08.019
Guang Z, Fengfang S, Tian L, Likun P, Zhuo S: Au nanoparticles as interfacial layer for CdS quantum dot-sensitized solar cells. Nanoscale Res Lett 2010, 5: 1749–1754. 10.1007/s11671-010-9705-z
Catchpole KR, Polman A: Design principles for particle plasmon enhanced solar cells. Appl Phys Lett 2008, 93: 191113(1)-191113(3).
Jiang W, Mangham SC, Reddy VR, Manasreh MO, Weaver BD: Surface plasmon enhanced intermediate band based quantum dots solar cell. Sol Energy Mater Sol Cells 2012, 102: 44–49.
Zhang YF, Wang YF, Chen N, Wang YY, Zhang YZ, Zhou ZH, Wei LM: Photovoltaic enhancement of Si solar cells by assembled carbon nanotubes. Nano-Micro Lett 2010, 2: 22–25.
Jiunn-Woei L, Huang-Chih C, Mao-Kuen K: Plasmonic Fano resonance and dip of Au-SiO2-Au nanomatryoshka. Nanoscale Res Lett 2013, 8: 468(1)-486(8).
Jian Hua Y, Elder KR, Hong G, Martin G: Theory and simulation of Ostwald ripening. Phys Rev B 1993, 47: 14110–14125. 10.1103/PhysRevB.47.14110
Alloyeau D, Oikawa T, Nelayah J, Wang G, Ricolleau C: Following Ostwald ripening in nanoalloys by high-resolution imaging with single-atom chemical sensitivity. Appl Phys Lett 2012, 101: 121920(1)-121920(3).
Zhenyu Z, Lagally MG: Atomistic processes in the early stages of thin-film growth. Science 1997, 276: 377–383. 10.1126/science.276.5311.377
Abraham DB, Newman CM: Equilibrium Stranski-Krastanow and Volmer-Weber models. Europhysics Lett 2009, 86: 16002(p1)-16002(p4).
Sui M, Li MY, Kim ES, Lee JH: Annealing temperature effect on self-assembled Au droplets on Si (111). Nanoscale Res Lett 2013, 8: 525. 10.1186/1556-276X-8-525
Lei G, Yusuke H, Ming-Yu L, Jiang W, Sangmin S, Sang-Mo K, Eun-Soo K, Wang ZM, Jihoon L, Salamo GJ: Observation of Ga metal droplet formation on photolithographically patterned GaAs (100) surface by droplet epitaxy. IEEE Trans Nanotechnol 2012, 11: 985–991.
Rijnders G, Blank DHA: Pulsed Laser Deposition of Thin Films: Applications-Led Growth of Functional Materials, Chapter 8. USA: Wiley-Interscience, USA; 2007:179–180.
Jihoon L, Zhiming W, Yusuke H, Eun-Soo K, Namyoung K, Seunghyun P, Cong W, Salamo GJ: Various configurations of In nanostructures on GaAs (100) by droplet epitaxy. Cryst Eng Comm 2010, 12: 3404–3408. 10.1039/c0ce00057d
Ziad Y, Abu W, Wang ZM, Lee JH, Salamo GJ: Optical behavior of GaAs/AlGaAs ring-like nanostructures. Nanotechnology 2006, 17: 4037–4040. 10.1088/0957-4484/17/16/007
Lee JH, Wang ZM, Black WT, Kunets VP, Mazur YI, Salamo GJ: Spatially localized formation of InAs quantum dots on shallow mesa- and trench patterns regardless of crystallographic directions. Adv Funct Mater 2007, 17: 3187. 10.1002/adfm.200700066
Lee JH, Wang ZM, Kim ES, Kim NY, Park SH, Salamo GJ: Self-assembled InGaAs tandem nanostructures consisting a hole and pyramid on GaAs (311)A by droplet epitaxy. Phys Status Solidi (a) 2010, 207: 348. 10.1002/pssa.200925406
Lee JH, Sablon K, Wang ZM, Salamo GJ: Evolution of InGaAs quantum dot molecules. J Appl Phys 2008, 103: 054301. 10.1063/1.2890149
Wang ZM, Seydmohamadi S, Lee JH, Salamo GJ: Surface ordering of (In, Ga)As quantum dots controlled by GaAs substrate indexes. Appl Phys Lett 2004, 85: 5031. 10.1063/1.1823590
Biegelsen DK, Bringans RD, Northrup JE, L E : Surface reconstructions of GaAs(100) observed by scanning tunneling microscopy. Phys ReV B 1990, 41: 5701–5711. 10.1103/PhysRevB.41.5701
Laukkanen P, Kuzmin M, Perälä RE, Ahola M, Mattila S, Väyrynen I: Electronic and structural properties of GaAs(100) (2 × 4) and InAs(100) (2 × 4) surfaces studied by core-level photoemission and scanning tunneling microscopy. J Phys ReV B 2005, 72: 045321.
Jiang W, Wang ZM, Li AZ, Shibin L, Salamo GJ: Surface mediated control of droplet density and morphology on GaAs and AlAs surfaces. Phys Status Solidi (RRL)-Rapid Res Lett 2010, 4: 371–373. 10.1002/pssr.201004402
Duke CB, Mailhiot C, Paton A, Kahn A, Stiles K: Shape and growth of InAs quantum dots on high-index GaAs(113)A, B and GaAs(2 5 11)A, B substrates. J Vac Sci Technol A 1986, 4: 947–952. 10.1116/1.573762
Sakong S, Du YA, Kratzer P: Atomistic modeling of the Au droplet–GaAs interface for size-selective nanowire growth. Phys ReV B 2013, 88: 155309.
Acknowledgements
This work was supported by the National Research Foundation (NRF) of Korea (no. 2011–0030821 and 2013R1A1A1007118). This research was in part supported by the research grant of Kwangwoon University in 2014.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
ML, MS, and JL participated in the experiment design and carried out the experiments. ML, MS, EK, and JL participated in the analysis of data. ML, MS, and JL designed the experiments and testing methods. ML and JL carried out the writing. All authors helped in drafting and read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, MY., Sui, M., Kim, ES. et al. From the nucleation of wiggling Au nanostructures to the dome-shaped Au droplets on GaAs (111)A, (110), (100), and (111)B. Nanoscale Res Lett 9, 113 (2014). https://doi.org/10.1186/1556-276X-9-113
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-113