Abstract
Ge/Si quantum dots fabricated by molecular-beam epitaxy at 500°C are overgrown with Si at different temperatures Tcap, and effect of boron delta doping of Si barriers on the mid-infrared photoresponse was investigated. The photocurrent maximum shifts from 2.3 to 3.9 μ m with increasing Tcapfrom 300°C to 750°C. Within the sample set, we examined devices with different positions of the δ-doping layer with respect to the dot plane, different distances between the δ-doping layer and the dot plane d, and different doping densities pB. All detectors show pronounced photovoltaic behavior implying the presence of an internal inversion asymmetry due to the placing dopants in the barriers. The best performance was achieved for the device with Tcap = 600°C, pB = 12 × 1011cm−2, and d = 5 nm in a photovoltaic regime. At a sample temperature of 90 K and no applied bias, a responsivity of 0.83 mA/W and detectivity of 8 × 1010 cm Hz1/2/W at λ = 3.4 μ m were measured under normal incidence infrared radiation.
Avoid common mistakes on your manuscript.
Background
In the past years, there has been a surge of interest in structures that exhibit quantum confinement in all three dimensions, commonly known as quantum dots (QDs). Intersubband optical transitions in QDs have attracted a great deal of attention due to their potential applications in infrared detectors operating at normal incidence and displaying low dark current[1, 2]. Most of the demonstrations of quantum dot infrared photodetectors (QDIPs) were achieved with III to V heterostuctures. Ge QDs enclosed in a silicon matrix represent another attractive type of the device due to its compatibility with standard Si readout circuitry. In particular, it has been demonstrated that p-type Ge/Si(001) QDs exhibit intraband photoresponse in the spectral range of 3 to 5 μ m[3–7], thus opening the route towards the fabrication of Si-based QDIPs for mid-infrared atmospheric window. Photovoltaic sensors operating without external bias voltage are preferrable for application in focal plane arrays as they have the advantage of reduced noise equivalent temperature difference[8]. In this paper, performance of ten-period Ge/Si quantum-dot mid-infrared photodetectors was investigated. By adjusting the capping temperature and Si delta-doping parameters, we demonstrated a responsivity of 0.83 mA/W and detectivity of 8 × 1010 cm Hz1/2/W at photon wavelength (λ) = 3.4 μ m for a Ge/Si device operating in a photovoltaic mode.
Methods
The samples were grown by solid source molecular beam epitaxy on a (001)-oriented boron-doped p+ -Si substrate with resistivity of 0.01 Ω cm. An active region was composed of ten stacks of Ge quantum dots separated by 50-nm Si barriers. Each Ge QD layer consisted of a nominal Ge thickness of about 6 monolayers (ML) and formed by self-assembling in the Stranski-Krastanov growth mode at 500°C and at a growth rate of 0.2 ML/s for all samples. From scanning tunneling microscopy experiments with uncapped samples, we observed the Ge dots to be approximately 10 to 15 nm in lateral size and about 1.0 to 1.5 nm in height. They have the form of hut clusters bounded by {105} facets. The density of the dots is about 3 to 4 × 1011 cm−2. Immediately after the deposition of Ge, the temperature was lowered to 400°C, and the structure was covered by a 1-nm Si layer. This procedure is necessary to preserve island shape from the effect of a further high temperature overgrowth. The Si barriers were deposited at Tcap ranging from 300°C to 750°C for different samples, with temperature ramps before and after QD growth. The increase of the overgrowth temperature is expected to result in a lowering of the hole binding energy in the dots due to enhanced Si-Ge alloying[9].
The active region was sandwiched in between the 200-nm-thick intrinsic Si buffer and cap layers. Finally, a 200-nm-thick p+ -Si top contact layer (5 × 1018cm−3) was deposited. For vertical photocurrent measurements, the samples were processed in the form of circular mesas with diameter of 3 mm by wet chemical etching and contacted by Al/Si metallization. The bottom contact is defined as the ground when applying voltage to all detectors.
Each Si barrier contains a boron delta-doping layer located near the QD plane to provide holes to the dots. To study the effects of doping on the detector characteristics, we varied (a) the relative position of the δ-doping layer with respect to the QD plane, (b) the distance between the δ-doping layer and the QD plane, and (c) the doping level. In a first type of devices, referred to as devices with bottom doping, the delta-doping layer with a sheet hole density of pB = 8 × 1011cm−2 was inserted 5 nm below the Ge QD layer to yield about two holes per dot. In a second type of detectors, the delta-doping layer was placed above the Ge dots with boron concentration pB = 4 × 1011cm−2 (about one hole per QD), 8 × 1011cm−2 (approximately two holes per QD), and 12 × 1011cm−2(three to four holes per QD). The distance between the dots and the doping plane was d = 2, 5, and 10 nm.
The normal-incidence photoresponse was obtained using a Bruker Vertex 70 Fourier transform infrared spectrometer (Bruker Optik Gmbh, Ettlingen, Germany) with a spectral resolution of 5 cm−1 along with a SR570 low-noise current preamplifier (Stanford Research Systems, Inc., Sunnyvale, CA, USA). The photocurrent (PC) spectra were calibrated with a DLaTGS detector (SELEX Galileo Inc., Arlington, VA, USA). The noise characteristics were measured with an SR770 fast Fourier transform analyzer (Stanford Research Systems, Inc.), and the white noise region of the spectra was used to determine the detectivity. The sample noise was obtained by subtracting the preamplifier-limited noise level from the experimental data. The dark current was tested as a function of bias (U b ) by a Keithley 6430 Sub-Femtoamp Remote SourceMeter (Keithley Instruments Inc., Cleveland, OH, USA). The devices were mounted in a cold finger inside a Specac cryostat with ZnSe windows. For dark current and noise measurements, the samples were surrounded with a cold shield.
Results and discussion
Figure1a depicts the photovoltaic spectral response at T = 90 K from six detectors with bottom doping (pB = 8 × 1011 cm−2, d = 5 nm) in which the overgrowth temperature was varied from 300°C to 750°C. In all samples, a broad peak is observed with no applied voltage. As expected, the peak wavelength of the device shows a redshift from 2.3 to 3.9 μ m with increasing T cap. This is significant since it provides a recipe to control the operating wavelength of a Ge/Si QD detector. The specific detectivity is given by, where A is the device area; R s , the responsivity; i n , the noise current; and Δf, the bandwidth. The detectivity obtained from the devices at 90 K is shown in Figure1b. Despite the responsivity value is approximately the same for all samples, the detectivity is ultimate for Tcap = 600°C. The physical mechanism of such a behavior is still under investigation. We suspect that at low cap temperature, a large number of point defects are generated in Si layers producing high noise level[10]. At the same time, at Tcap > 700°C, the structure resembles a two-dimensional SiGe layer with significant composition and thickness variations[9], thus, again giving rise to a large dark current.
In fact, capping of Ge islands under a Si layer at elevated Tcap results both in a reduction of Ge content in the dots and growth of dot size. The former implies a lowering of the hole binding energy due to the decrease of the valence band offset, while the latter leads to a deepening of the hole level due to the weakening of the size quantization effect. The competition of these two processes is a possible reason of why the peak wavelength shows a nonmonotonic shift with Tcap around 600°C as observed in Figure1a.
Figures2 and3 show bias-dependent PC spectra of the devices with bottom and top positions of the delta-doping plane, respectively. In both samples, the distance between the QD layer and the doping plane is 5 nm, the sheet hole density pB = 8 × 1011cm−2. A broad mid-infrared peak is observed with no applied bias implying the presence of a built-in electric field near the dots. An applied external bias (positive in Figure2 and negative in Figure3) compensates the internal electric field, thus leading to a drastic drop of responsivity at 0.4 to 0.8 V in Figure2 and around -0.8 V in Figure3. This is a characteristic feature of a photovoltaic mode operation[11]. At large U b , the photoexcited holes can easily overcome the built-in potential barrier, and responsivity starts to increase.
The interesting feature is the observation of two distinct peaks at a positive bias for the sample with bottom doping and at a negative bias for the sample with top doping. An additional photoresponse at a longer wavelength appears when the applied bias polarity is such that holes escape from the QDs towards the nearest δ-doping plane. The origin of photovoltaic signal and dual-peak response is illustrated in Figure4. This is caused by asymmetry of the samples due to selected position of the doping planes within the spacer layers between the dots. At zero bias, the resulting potential profile leads to a preferential hole flow in the direction opposite to the nearest δ-doping layer side (Figure4a). The corresponding PC peak arises from the transition of holes from the ground state to the continuum states. When the polarity of applied bias U b is that holes move toward the doping layer, holes can be transferred into the extended state by excitation to a shallow level confined near the valence band edge with subsequent tunneling through the triangle barrier (Figure4b). As a result, an additional PC peak on the low energy side of the spectra appears.
The measured responsivity and detectivity of the two QDIPs with bottom and top positions of the doping planes are depicted in Figure5. For both samples we find that at U b = 0 V, the measured noise current is closed to the calculated thermal noise. This leads to a better performance when detectors are operating in the photovoltaic regime, where specific detectivity reaches the value of D⋆ = 6.2 × 1010 cm Hz1/2/W at T = 90 K, with a corresponding responsivity of 0.5 to 0.6 mA/W. The important observation is a reversal of the voltage dependence of responsivity with respect to zero bias when the δ-doping plane is moved from the bottom to the top of the dot layer. This result undoubtedly points out that the main reason for the asymmetric photoresponse is the existence of a built-in electric field due to the charged δ-doping plane and is not caused by the asymmetry of the strain distribution, dot shape, and wetting layer as proposed in[12, 13].
Figure6 displays the bias dependent responsivity and detectivity from three detectors in which the distance between the δ-doping layer and the QD plane was varied from 2 to 10 nm. The most symmetrical R(U b ) and D⋆(U b ) characteristics and the less pronounced photovoltaic effect are realized in a device with d = 2 nm (the peak wavelength is 3.5 μ m). For this sample, the highest detectivity of 6.0 × 1010 cm Hz1/2/W is observed at U b = 0.2 V, i.e., in a photoconductive mode. A possible reason responsible for the suppression of the photovoltaic effect at small d is the penetration of boron atoms into the QD layer, which results in a more symmetric electric-field distribution around the dots.
Figure7 shows the responsivity and detectivity for three detectors in which the sheet boron density in the δ-doping layers was varied from 4 × 1011 to 12 × 1011 cm−2. The distance between the dots and the doping plane was d = 5 nm. An increase of doping density leads to a higher responsivity at U b < 0.4 V. This is likely in agreement with the theoretical prediction[14]. The best performance is achieved for pB = 12 × 1011cm−2 in the photovoltaic mode, where R = 0.83 mA/W and D⋆ = 8.1 × 1010 cm Hz1/2/W at λ = 3.4 μ m. The highest peak detectivity of the sample with a lower doping density is observed in the photoconductive mode at U b = 0.2 V.
Conclusions
We have presented the performance characteristics of Ge/Si(001) quantum dot mid-infrared detectors in which the capping temperature Tcap and parameters of doping were systematically varied. With increasing Tcap from 300°C to 750°C, the photocurrent peak wavelength shifts from 2.3 to 3.9 μ m, reflecting enhanced Si-Ge intermixing at higher overgrowth temperatures. The devices with lower doping density or shorter QD-dopant separation have better performance in a photoconductive mode while other detectors display the highest specific detectivity at zero bias. We demonstrated that the main reason for the photovoltaic response is the existence of a built-in electric field due to the charge redistribution between QDs and δ-doping layers. The highest photovoltaic detectivity and responsivity at 90 K are D⋆ = 8.1 × 1010 cm Hz1/2/W and R = 0.83 mA/W, respectively, for Tcap = 600°C and the 3.4-μ m photoresponse peak. The possibility of the device to operate in a photovoltaic mode makes it compatible with existing Si-readout circuits in focal plane array applications.
Authors’ information
AY is a leading researcher in the Institute of Semiconductor Physics. His research interests are in the area of electronic processes in low-dimensional systems. VT is a postgraduate student working on nanotechnology. AB is a researcher specializing in computational simulation physics. AN is the head of the Laboratory of Molecular Beam Epitaxy. Current research topics in his group include growth process studies of Ge quantum dots on Si, delta-doped Si layers, and low-temperature growth. AD is a professor and a member of the scientific boards on the problems of Semiconductor Physics and Radiation Physics of Solid State in Russian Academy of Science.
Abbreviations
- λ:
-
photon wavelength
- ML:
-
monolayer
- PC:
-
photocurrent
- QD:
-
quantum dot
- QDIP:
-
quantum dot infrared photodetector.
References
Ryzhii V: Physical model and analysis of quantum dot infrared photodetectors with blocking layer. J Appl Phys 2001, 89(9):5117–5124. 10.1063/1.1359759
Phillips J: Evaluation of the fundamental properties of quantum dot infrared detectors. J Appl Phys 2002, 91(7):4590–4594. 10.1063/1.1455130
Yakimov AI, Dvurechenskii AV, Proskuryakov YY, Nikiforov AI, Pchelyakov OP, Teys SA, Gutakovskii AK: Normal-incidence infrared photoconductivity in Si p-i-n diode with embedded Ge self-assembled quantum dots. Appl Phys Lett 1999, 75(10):1413–1415. 10.1063/1.124710
Miesner C, Röthig O, Brunner K, Abstreiter G: Intra-valence band photocurrent spectroscopy of self-assembled Ge dots in Si. Appl Phys Lett 2000, 76(8):1027–1029. 10.1063/1.125927
Bougeard D, Brunner K, Abstreiter G: Intraband photoresponse of SiGe quantum dot/quantum well multilayers. Physica E 2003, 16: 609–613. 10.1016/S1386-9477(02)00640-9
Finkman E, Shuall N, Vardi A, Thanh VL, Schacham SE: Interlevel transitions and two-photon processes in Ge/Si quantum dot photocurrent. J Appl Phys 2008, 103: 093114. 10.1063/1.2919151
Singha RK, Manna S, Das S, Dhar A, Ray SK: Room temperature infrared photoresponse of self assembled Ge/Si (001) quantum dots grown by molecular beam epitaxy. Appl Phys Lett 2010, 96: 233113. 10.1063/1.3446848
Schneider H, Walther M, Schönbein C, Rehm R, Fleissner J, Pletschen W, Braunstein J, Koidl P, Weimann G: QWIP FPAS for high-performance thermal imaging. Physica E 2000, 7: 101–107. 10.1016/S1386-9477(99)00287-8
Denker U, Stoffel M, Schmidt OG, Sigg H: Ge hut cluster luminescence below bulk Ge band gap. Appl Phys Lett 2003, 82(3):454–456. 10.1063/1.1537437
Hastas NA, Dimitriadis CA, Dozsa L, Gombia E, Mosca R: Investigation of single electron traps induced by InAs quantum dots embedded in GaAs layer using the low-frequency noise technique. J Appl Phys 2004, 96: 5735–5739. 10.1063/1.1801163
Tang SF, Lin SY, Lee SC: Near-room-temperature operation of an Inas/GaAs quantum-dot infrared photodetector. Appl Phys Lett 2001, 78(17):2428–2430. 10.1063/1.1362201
Pan D, Towe E, Kennerly S: Photovoltaic quantum-dot infrared detectors. Appl Phys Lett 2000, 76(22):3301–3303. 10.1063/1.126613
Ma WQ, Yang XJ, Chong M, Yang T, Chen LH, Shao J, Lu W, Song CY, Liu HC, Lü X: Voltage tunable two-color InAs/GaAs quantum dot photodetector. Appl Phys Lett 2008, 93: 013502. 10.1063/1.2956672
Ryzhii V: Negative differential photoconductivity in quantum-dot infrared photodetectors. Appl Phys Lett 2001, 78(21):3346–3348. 10.1063/1.1373414
Acknowledgements
The work was supported by RFBR (grant no. 11-02-12007).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
AY conceived and designed the experiment, carried out the photocurrent measurements, participated in the discussions, and drafted the manuscript. VT and AN prepared the samples using molecular beam epitaxy technique. AB performed the noise measurements. AD supervised the project. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Yakimov, A., Timofeev, V., Bloshkin, A. et al. Photovoltaic Ge/Si quantum dot detectors operating in the mid-wave atmospheric window (3 to 5 μ m). Nanoscale Res Lett 7, 494 (2012). https://doi.org/10.1186/1556-276X-7-494
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-494