Abstract
Background
The use of silica coated magnetic nanoparticles as contrast agents has resulted in the production of highly stable, non-toxic solutions that can be manipulated via an external magnetic field. As a result, the interaction of these nanocomposites with cells is of vital importance in understanding their behaviour and biocompatibility. Here we report the preparation, characterisation and potential application of new "two-in-one" magnetic fluorescent nanocomposites composed of silica-coated magnetite nanoparticles covalently linked to a porphyrin moiety.
Method
The experiments were performed by administering porphyrin functionalised silica-coated magnetite nanoparticles to THP-1 cells, a human acute monocytic leukaemia cell line. Cells were cultured in RPMI 1640 medium with 25 mM HEPES supplemented with heat-inactivated foetal bovine serum (FBS).
Results
We have synthesised, characterised and analysed in vitro, a new multimodal (magnetic and fluorescent) porphyrin magnetic nanoparticle composite (PMNC). Initial co-incubation experiments performed with THP-1 macrophage cells were promising; however the PMNC photobleached under confocal microscopy study. β-mercaptoethanol (β-ME) was employed to counteract this problem and resulted not only in enhanced fluorescence emission, but also allowed for elongated imaging and increased exposure times of the PMNC in a cellular environment.
Conclusion
Our experiments have demonstrated that β-ME visibly enhances the emission intensity. No deleterious effects to the cells were witnessed upon co-incubation with β-ME alone and no increases in background fluorescence were recorded. These results should present an interest for further development of in vitro biological imaging techniques.
Similar content being viewed by others
Background
Magnetic nanoparticles have been the focus of much research due to their potential biomedical applications as both diagnostic tools and therapeutic agents [1, 2]. Suspensions of superparamagnetic nanoparticles of iron oxide are promising magnetic resonance imaging contrast agents, improving the image quality of anatomical structures by altering the relaxation time of the protons present [3–6]. Magnetic nanoparticles may also induce heat once subjected to an external magnetic AC field, opening up the possibility of hyperthermic cancer treatment [7, 8]. Site-specific drug delivery is an enticing possibility, which may be realised by loading nano-magnetic carriers with therapeutic agents and directing them to the site of interest using external magnetic fields [9, 10]. The assembly of a number of building blocks with different functionalities could provide a multimodal platform allowing for the combination of diagnostic imaging and therapeutic capabilities [11–13]. In particular, nanoscale entities combining magnetic and fluorescent properties have attracted much attention. Their potential uses in medicine are far-reaching including in imaging, bio- and chemo- sensing, drug delivery and therapy systems. Challenges remain in their fabrication, which frequently involve multi-step reactions to prevent the quenching of the fluorophore. Several synthetic routes have been reported, including core-shell composites, bilipid layers between the particle surface and the fluorescent moiety composites, and use of electrostatic interactions between stabilizers, magnetic particles and fluorophores [14–18]. The surface chemistry of these composite materials plays a crucial role in cellular uptake. For example magnetic nanoparticles, functionalised with a chitosan-labelled fluorescein isothiocyanate derivative, have shown uptake by human hepatoma cells via charged interactions [19]. Interesting multifunctional nanocomposites comprising of silver and iron oxide nanoparticles embedded in a silica shell, together with a Raman reporter molecule have been published by Murphy et. al. [20]. The introduction of a rhodamine moiety to the silica surface gives the composite a broad range of potential applications due to its magnetic, light scattering, SERS and fluorescent properties. Trapping a rhodamine dye within a silica matrix during the formation of a shell surrounding the magnetite nanoparticles has also led to the formation of magnetic-fluorescent nanocomposites [21, 22]. In addition superparamagnetic iron oxide nanoparticles (SPION) are of particular interest for targeted cancer therapy. Tumour-targeted hyperthermia using super-paramagnetic, biocompatible, and nanosized delivery vehicles would allow patients to receive increased treatment dosages while minimizing side effects. Some recent research investigating SPION was also dedicated to the early detection of cancer, diabetes, and atherosclerosis [23–25].
Here we report the preparation, characterisation and application of new "two-in-one" magnetic-fluorescent nanocomposites composed of silica-coated magnetite nanoparticles, which are covalently linked to a porphyrin moiety.
Results and discussion
Synthesis and characterisation of the porphyrin-magnetite nanocomposite (PMNC)
Magnetite nanoparticles have been produced by a previously reported co-precipitation method (see Materials and Methods) [26, 27]. Application of a silica layer was achieved by following a method reported by Philips and co-workers [28]. Briefly, a colloidal solution of magnetite nanoparticles in tetramethylammonium hydroxide (TMAH) was treated with sodium silicate in order to deposit a thin layer of silica on the surface of the oxide particles (Figure 1). In a separate step, a carboxylic acid protoporphyrin (protoporphyrin IX) was reacted with 3-aminopropyltriethoxysilane (3-APTES) under inert conditions in the presence of the carbodiimide coupling agent (EDCI) to form an amide bond. This modified porphyrin was then reacted with the silica coated particles, to form a stable colloidal suspension. In this case the silica shell was necessary to provide an effective barrier between the particle core and the fluorescent porphyrin, preventing the risk of quenching.
Elemental analysis of the PMNC shows a content of C - 9.31, H - 1.21 and N - 1.51%. This clearly confirms the presence of conjugated porphyrin molecules at the surface of nanoparticles.
The presence of the porphyrin on the surface of the silica-coated magnetite nanoparticles was also confirmed by Fourier Transform Infrared Infra-red (FTIR) spectroscopy (Figure 2). FTIR spectra of the silica coated magnetite nanoparticles before and after reaction with the protoporphyrin were recorded in KBr. The silica coated particles (shown in heavy black circles above) have stretches at 579, 1087, 1625 and 3286 cm-1 corresponding to the Fe-O, Si-O-Si, and water stretches respectively. The stretch found at 947 cm-1 is due to the presence of Fe-O-Si bonds in the sample. For the nanocomposite material, again Fe-O and water stretches are found at 579, 1621 and 3286 cm-1 respectively. The Fe-O-Si stretch is this time masked by the NH wagging from the porphyrin centred at 901 cm-1. NH stretches are found at 1473 cm-1. Aromatic and aliphatic stretches associated with the porphyrin are found at 2500 and 2945 cm-1 respectively. FTIR spectra (Figure 2) of the porphyrin nanocomposite material showed stretches for NH due to the presence of the porphyrin at 901 and 1473 cm-1. Aromatic and aliphatic stretches associated with the porphyrin are found at 2500 and 2945 cm-1 respectively. A core-shell-like morphology is apparent from TEM images taken of the silica coated nanoparticles. The average primary particle size is calculated to be 9.3 ± 1 nm. The silica coating on the particles has an average thickness of 3 nm, however upon reaction with the 3-APTES modified protoporphyrin IX, the coating thickness is found to slightly increase to 4 nm.
Absorbance spectra of the original porphyrin and the PMNC were taken in tetrahydrofuran, THF (Figure 3). Peaks at 406, 505, 538, 577 and 632 nm were observed for a solution of porphyrin. Emission (λex, 406 nm) and excitation spectra (λem was 633 nm) have also been recorded, with significant broadening witnessed for the PMNC when compared to the original porphyrin. This can be attributed to the scattering of the incoming light by the PMNC suspension, but gives further indication of the binding of the porphyrin to the nanoparticle surface.
Dynamic Light Scattering (DLS) studies of silica coated magnetite nanoparticles have shown a very broad size distribution with an average hydrodynamic diameter of 131 nm, due to aggregation of nanoparticles. However, silica coated porphyrin functionalised magnetic nanoparticles have demonstrated relatively narrow distribution with an average hydrodynamic diameter of 818 nm (Figure 4).
TEM images taken of the silica coated nanoparticles reveal the presence of a core-shell structure (Figure 5). The silane coating on the particles has an average thickness of 3 nm and the particles are found to aggregate in group of approximately ten particles. Upon reaction with the 3-aminopropyltriethoxysilane modified protoporphyrin, the coating thickness is found to slightly increase to 4 nm.
Magnetisation measurements of original non-coated magnetite nanoparticles, silica coated magnetite nanoparticles and silica-coated porphyrin functionalised magnetite nanoparticles as expected, have shown a gradual reduction in saturation magnetisation values (58.4 Am2/kg for pristine magnetite nanoparticles, 35.2 Am2/kg for silica coated magnetite nanoparticles and 27.5 Am2/kg for the corresponding porphyrin conjugates) with an increasing amount of non-magnetic material, i.e. silica and porphyrin conjugates (Figure 6).
The combination of both magnetic and fluorescent properties in one nanocomposite can provide additional benefits. For example, these nanocomposites could serve as multimodal assays for in vitro- and vivo- bioimaging applications such as MRI and fluorescence microscopy. They can also be used as bimodal agents for anticancer therapy, encompassing photodynamic and hyperthermic capabilities. Fluorescent-magnetic nanocomposites may also be utilised as a multimodal diagnostic and therapeutic tool, which could be used, for example, to identify, diagnose and simultaneously treat various diseases. Other potential exciting applications of these nanocomposites include cell tracking, cytometry and magnetic separation, which could be easily controlled and monitored using fluorescent microscopy and MRI.
Cell culture experiments
Previously, the cytotoxic effects of poly(ethylene glycol)-co-fumarate (PEGF)-coated magnetite nanoparticles and their capability for changing cell culture medium compositions have been investigated. The primary mouse connective tissue cells (L929) were used for this purpose. Toxicity levels and changes in the cell culture medium compositions were determined using the MTT assay and a UV/vis spectroscopy method, respectively. As compared to the conventional method, a more reliable method for determining the cytotoxicity of nanoparticles for in vitro applications is found [29]. It also has been demonstrated that the incorporation of anticancer drugs such paclitaxel into PLGA nanoparticles in nanoparticles strongly enhances the cytotoxic effect of the drug as compared to Taxol, this effect being more relevant for prolonged incubation times [30, 31].
In our studies THP-1 (human acute monocytic leukaemia) cells were cultured in the presence of phorbol 12-myristate 13-acetate (PMA) for 3 days to initiate monocyte to macrophage differentiation. Half the volume of complete culture media was then replaced with serum free media to "starve" the cells, allowing for an enhanced up-take of the PMNC. Figure 7 shows a confocal image of a THP-1 cell after incubation with the PMNC for 3 hours. The particles are localised in the cytoplasm, as detected by confocal imaging, and the image is representative of the broader cell population.
During the experiments we have found that following an exposure time of only 482 ms, the PMNC begins to photobleach, and after only 4 seconds, the fluorescence intensity has greatly decreased (Figure 8). This process is highly undesirable as it makes the generation, capture and interpretation of the image extremely difficult and does not allow for a full examination of the cells to determine precisely the nature of the nanocomposite localisation.
In an effort to alleviate the photobleaching, β-mercaptoethanol (β-ME) was employed to counteract this problem, and was added once the cells were fixed. Control experiments performed with THP-1 cells in the presence of β-ME show that no deleterious effects are witnessed and the cells retain their size, shape and membrane integrity (Figure 9). Addition of β-ME to cells cultured with the PMNC prevented this photobleaching effect and resulted in a stronger fluorescence signal compared to those without β-ME (see Figures 9 and 10). Following the same cell preparation and co-incubation times, we can clearly see not only an increased resistance to photobleaching, but the addition of β-ME also resulted in an enhanced and extended fluorescence emission. This improved photostability is due to the β-ME acting as a scavenger for singlet oxygen, which is traditionally attributed to the photobleaching of porphyrin based dyes.
To further exemplify the enhancement in fluorescent emission intensity due to the presence of the β-ME, pseudocoloured images of the cells were generated (Figure 10). The pseudocoloured images reflect the integrated fluorescence intensity levels across the cytoplasmic and nuclear compartments of the THP-1 cells. Background fluorescence appears blue and predominates for those cells without any nanocomposite added (panels 10 c and d) but also for cells cultured with the PMNC alone (panel 10 a). A dramatic change is witnessed upon addition of the β-ME (panel 10 b). The PMNC is no longer quenched so dramatically and readily emits with substantial emission increases recorded after 4 seconds.
To verify that the increased emission is due to the PMNC and not as a result of increased cellular autofluorescence, control experiments were also conducted. Panels 10 c and d show untreated and β-ME treated THP-1 cells respectively and clearly illustrate that the level of background fluorescence remains constant throughout the experiment. This proves that autofluorescence does not contribute to the enhanced levels of emission witnessed for those cells cultured with the PMNC in the presence of β-ME.
In order to probe the maximum fluorescence intensity of the PMNC as a function of excitation wavelength and also to monitor the fluorescence intensity across the cell compartments, a series of fluorescence images were recorded over varying wavelengths together with emission spectral mapping of the cell. Cells were cultured with the PMNC with and without the presence of β-ME. Lambda scans recorded of cells cultured without β-ME show a noted decrease in brightness and the combined image is noticeably lower in fluorescence intensity. This is shown quantitatively in the fluorescence emission spectra, which show an almost 20% decrease in fluorescence intensity (Figures 11 and 12).
Finally, to compare the results a series of similar control experiments have been performed on "non-starved" THP-1 cells, which were incubated with serum free media. Confocal and composite images of the cells incubated with fluorescent magnetic nanoparticles have been taken at different periods of time 24 hrs, 48 hrs and 5 days (Figures 13, 14, 15 and 16). The results have demonstrated that there was no cellular uptake of the fluorescent nanocomposites but only binding of the PMNC to the outer cell membranes.
Conclusion
In summary, we have successfully synthesised a new two-in-one magnetic-fluorescent nanocomposite. Initial co-incubation experiments performed with THP-1 macrophage cells in the presence of the PMNC showed a distinct photobleaching of the porphyrin upon exposure to light under a fluorescent microscope. This bleaching was counteracted by the addition of β-ME which resulted not only in increased fluorescence intensity levels, but also allowed for enhanced imaging and increased exposure times of the PMNC in a cellular environment. This was further corroborated by pseudofluorescent images which show how β-ME visibly enhances the emission intensity. Furthermore, no deleterious effects to the cells were witnessed upon co-incubation with β-ME alone and no increases in background fluorescence were recorded. We believe that this research should present an interest for further development of and new multimodal nanoparticulate agents for in vitro biological imaging.
Materials and methods
Synthesis
Synthesis of nanoparticles and coating with silica
Magnetite nanoparticles were prepared according to the previously reported coprecipitation method. Stock solutions of 25 mL of each of 1 M FeCl3.6H2O (6.56 g, 0.024 mol), 0.5 M FeCl2.4H2O (2.48 g, 0.012 mol), and 0.4 M HCl were made up with Millipore water. NaOH solution (0.5 M, 250 mL) was heated to 80°C and the iron solution was added dropwise. After one hour of stirring (at 1200 rpm) with heat, the black magnetic nanoparticles were washed with Millipore water (5 × 20 mL) until neutral. A sample of the nanoparticles (1 g) was dispersed in tetramethylammonium hydroxide (30 mL) and made up to 570 mL with Millipore water. 0.58% activated sodium silicate (430 mL) was added to the nanoparticle suspension. The sodium silicate was activated by passing through a regenerated cation exchange resin. After two hours stirring, the magnetic fluid was transferred into dialysis tubing and dialysed against Millipore water brought to pH 10 by the addition of tetramethylammonium hydroxide. The dialysis tubing was prepared by boiling tubing of the required length in 2% (w/v) sodium bicarbonate (100 mL) and 1 mM EDTA (100 mL) at pH 8.0 for ten minutes. The tubing was rinsed with Millipore water then boiled for ten minutes in 1 mM EDTA followed by Millipore water rinsing. After 24 hour dialysis, the solution was brought to pH 8.0 by the addition of dilute HCl. The particles were washed and finally dried under vacuum.
Modification of protoporphyrin and attachment to magnetic nanoparticles
Protoporphyrin IX (0.1 g; 0.177 mmol) was dissolved in dry THF (20 mL). N-(3-Dimethylaminopropyl)-N'-ethylcarbodiimide (0.17 g; 0.887 mmol) was added to' the stirring deep red solution and the reaction mixture was stirred (at 1200 rpm) for 3 hours at 0°C. The reaction was carried out in the dark to prevent any possible photobleaching of the porphryin. 3-Aminopropyltriethoxysilane (83 μL; 0.355 mmol) in 2 mL dry THF was added to the porphyrin solution at 0°C. The reaction mixture was brought to room temperature and allowed to react overnight. Silica coated magnetite nanoparticles (0.1 g) were added to the reaction vessel with triethylamine (300 μL) and allowed to react for 24 hours. The mixture was centrifuged and the particles were washed with bench THF (5 × 40 mL) to remove any un-reacted porphyrin or unwanted side-products. The particles of PMNC were finally washed with water. Elemental analysis, found: C - 9.31, H - 1.21, N - 1.51.
Tissue culture
THP-1 cells, a human acute monocytic leukaemia cell line, were obtained from the American Type Culture Collection (ATCC, LGC Promochem, U.K.). Cells were cultured in RPMI 1640 medium with 25 mM HEPES (Gibco, Invitrogen Ltd., Ireland), supplemented with heat-inactivated foetal bovine serum (FBS) (9%), 200 mM/ml L-glutamine (0.9%, 1.8 mM/ml), 10,000 U/ml penicillin (0.9%, 90 U/ml), and 10 mg/ml streptomycin (0.9%, 0.09 mg/ml) at 37°C and 5% CO2 content.
Cell assays
THP-1 cells were seeded into an 8-well chamber slide, with a final concentration of 2 × 104 cells per well. To induce monocyte to macrophage differentiation, THP-1 cells were cultured in 100 ng/ml phorbol 12-myristate 13-acetate (PMA) for 3 days at 37°C in 5% CO2. Half the volume of media was then replaced by serum free media (RPMI 1640 with 25 mM HEPES) and the cells were incubated for 2 hours at 37°C in 5% CO2. The PMNC was then added at a final concentration of 0.25 mg/ml. To another well, β-mercaptoethanol β-ME was added. A control experiment with the Protoporphyrin IX dissolved in mixture of water and tetrahydrofuran (THF) was carried out in parallel using the same conditions, with a final porphyrin concentration of 0.119 mg/ml. Fluorescence images were recorded using a Nikon TE3000 inverted microscope. Confocal imges were collected using a 63× oil immersion objective, laser excitation 561 nm and LP 575 nm filter on a Zeiss LSM Meta-510 confocal microscope.
Spectroscopy
UV-Vis absorption spectra were recorded using a Cary 50 UV-Vis spectrophotometer. Fluorescence measurements were performed on a Cary Eclipse spectrophotometer. FT-IR spectra were recorded KBr using a Perkin Elmer Spectrum One FT-IR spectrophotometer. TEM images were taken on a Hitachi H-7000 at a beam voltage of 100 kV.
Abbreviations
- AC:
-
alternating current
- 3-APTES:
-
3-aminopropyltriethoxysilane
- β-ME:
-
β-mercaptoethanol
- DLS:
-
Dynamic Light Scattering
- EDTA:
-
ethylenediamine tetraacetic acid
- EDCI:
-
1-ethyl-3-(3-dimethylaminopropyl carbodiimide)
- HEPES:
-
4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid
- THP-1 cells:
-
human acute monocytic leukaemia cells
- PMA:
-
phorbol 12-myristate 13-acetate
- PMNC:
-
porphyrin-magnetite nanocomposite
- RPMI:
-
Roswell Park Memorial Institute Medium
- TEM:
-
Transmission electron microscopy
- THF:
-
tetrahydrofuran
- TMAH:
-
tetramethylammonium hydroxide
- UV-vis:
-
Ultra-violet visible.
References
Pankhurst QA, Connolly J, Jones SK, Dobson J: Applications of magnetic nanoparticles in biomedicine. Journal of Physics D: Applied Physics. 2003, R167-10.1088/0022-3727/36/13/201.
Bergemann C, Muller-Schulte D, Oster J, a Brassard L, Lubbe AS: Magnetic ion-exchange nano- and microparticles for medical, biochemical and molecular biological applications. J Magn Magn Mater. 1999, 194: 45-52. 10.1016/S0304-8853(98)00554-X.
Byrne SJ, Corr SA, Gun'ko YK, Kelly JM, Brougham DF, Ghosh S: Magnetic nanoparticle assemblies on denatured DNA show unusual magnetic relaxivity and potential applications for MRI. Chemical Communications. 2004, 2560-2561. 10.1039/b409603g.
Wan J, Cai W, Meng X, Liu E: Monodisperse water-soluble magnetite nanoparticles prepared by polyol process for high-performance magnetic resonance imaging. Chemical Communications. 2007, 5004-5006. 10.1039/b712795b.
Corr SA, Byrne SJ, Tekoriute R, Meledandri CJ, Brougham DF, Lynch M, Kerskens C, O'Dwyer L, Gun'ko YK: Linear Assemblies of Magnetic Nanoparticles as MRI Contrast Agents. Journal of the American Chemical Society. 2008, 130: 4214-4215. 10.1021/ja710172z.
Corr SA, Gun’ko YK, Tekoriute R, Meledandri CJ, Brougham DF: Poly(sodium-4-styrene)sulfonate-Iron Oxide Nanocomposite Dispersions with Controlled Magnetic Resonance Properties. The Journal of Physical Chemistry C. 2008, 112: 13324-13327. 10.1021/jp805519n.
Samanta B, Yan H, Fischer NO, Shi J, Jerry DJ, Rotello VM: Proteinpassivated Fe3O4 nanoparticles: low toxicity and rapid heating for thermal therapy. Journal of Materials Chemistry. 2008, 18: 1204-1208. 10.1039/b718745a.
Babincová M, Leszczynska D, Sourivong P, Babinec P: Selective treatment of neoplastic cells using ferritin-mediated electromagnetic hyperthermia. Medical hypotheses. 2000, 54: 177-179.
Guo M, Yan Y, Zhang H, Yan H, Cao Y, Liu K, Wan S, Huang J, Yue W: Magnetic and pH-responsive nanocarriers with multilayer core-shell architecture for anticancer drug delivery. Journal of Materials Chemistry. 2008, 18: 5104-5112. 10.1039/b810061f.
Landmark KJ, DiMaggio S, Ward J, Kelly C, Vogt S, Hong S, Kotlyar A, Myc A, Thomas TP, Penner-Hahn JE: Synthesis, Characterization, and in Vitro Testing of Superparamagnetic Iron Oxide Nanoparticles Targeted Using Folic Acid-Conjugated Dendrimers. ACS Nano. 2008, 2: 773-783. 10.1021/nn800034w.
Ji-Ho P, Geoffrey von M, Lianglin Z, Michael PS, Erkki R, Sangeeta NB, Michael JS: Magnetic Iron Oxide Nanoworms for Tumor Targeting and Imaging. Advanced Materials. 2008, 20: 1630-1635. 10.1002/adma.200800004.
Quarta A, Di Corato R, Manna L, Argentiere S, Cingolani R, Barbarella G, Pellegrino T: Multifunctional Nanostructures Based on Inorganic Nanoparticles and Oligothiophenes and Their Exploitation for Cellular Studies. Journal of the American Chemical Society. 2008, 130: 10545-10555. 10.1021/ja800102v.
Teodor E, Litescu SC, Petcu C, Mihalache M, Somoghi R: Nanostructured Biomaterials with Controlled Properties Synthesis and Characterization. Nanoscale Research Letters. 2009, 4: 544-549. 10.1007/s11671-009-9278-x.
Corr S, Rakovich Y, Gun'ko Y: Multifunctional Magnetic-fluorescent Nanocomposites for Biomedical Applications. Nanoscale Research Letters. 2008, 3: 87-104. 10.1007/s11671-008-9122-8.
Salgueiriño-Maceira V, Correa-Duarte MA: Increasing the Complexity of Magnetic Core/Shell Structured Nanocomposites for Biological Applications. Advanced Materials. 2007, 19: 4131-4144.
Xiao Q, Xiao C: Preparation and Characterization of Silica-Coated Magnetic-Fluorescent Bifunctional Microspheres. Nanoscale Research Letters. 2009, 4: 1078-1084. 10.1007/s11671-009-9356-0.
Gallagher JJ, Tekoriute R, O'Reilly JA, Kerskens C, Gun'ko YK, Lynch M: Bimodal magnetic-fluorescent nanostructures for biomedical applications. Journal of Materials Chemistry. 2009, 19: 4081-4084. 10.1039/b906023p.
Prina-Mello A, Whelan AM, Atzberger A, McCarthy JE, Byrne F, Davies GL, Coey JMD, Volkov Y, Gun'ko YK: Comparative Flow Cytometric Analysis of Immunofunctionalized Nanowire and Nanoparticle Signatures. Small. 6: 247-255. 10.1002/smll.200901014.
Ge Y, Zhang Y, He S, Nie F, Teng G, Gu N: Fluorescence Modified Chitosan-Coated Magnetic Nanoparticles for High-Efficient Cellular Imaging. Nanoscale Research Letters. 2009, 4: 287-295. 10.1007/s11671-008-9239-9.
Gole A, Agarwal N, Nagaria P, Wyatt MD, Murphy CJ: One-pot synthesis of silica-coated magnetic plasmonic tracer nanoparticles. Chemical Communications. 2008, 6140-6142. 10.1039/b814915a.
Ren C, Li J, Liu Q, Ren J, Chen X, Hu Z, Xue D: Synthesis of Organic Dye-Impregnated Silica Shell-Coated Iron Oxide Nanoparticles by a New Method. Nanoscale Research Letters. 2008, 3: 496-501. 10.1007/s11671-008-9186-5.
Corr SA, Byrne AO, Gun'ko YK, Ghosh S, Brougham DF, Mitchell S, Volkov Y, Prina-Mello A: Magnetic-fluorescent nanocomposites for biomedical multitasking. Chemical Communications. 2006, 43: 4474-4476. 10.1039/b610746j.
Mahmoudi M, Shokrgozar MA, Simchi A, Imani M, Milani AS, Stroeve P, Vali H, Hafeli UO, Bonakdar S: Multiphysics Flow Modeling and in Vitro Toxicity of Iron Oxide Nanoparticles Coated with Poly(vinyl alcohol) (vol 113C, pg 2323, 2009). Journal of Physical Chemistry C. 2009, 113: 17274-17274. 10.1021/jp904884y.
Moroz P, Jones SK, Gray BN: Magnetically mediated hyperthermia: current status and future directions. International Journal of Hyperthermia. 2002, 18: 267-284. 10.1080/02656730110108785.
Petri-Fink A, Chastellain M, Juillerat-Jeanneret L, Ferrari A, Hofmann H: Development of functionalized superparamagnetic iron oxide nanoparticles for interaction with human cancer cells. Biomaterials. 2005, 26: 2685-2694. 10.1016/j.biomaterials.2004.07.023.
Massart R: Preparation of aqueous magnetic liquids in alkaline and acidic media. IEEE Trans Magn. 1981, 17: 1247-1248. 10.1109/TMAG.1981.1061188.
Mahmoudi M, Simchi A, Imani M, Milani AS, Stroeve P: Optimal Design and Characterization of Superparamagnetic Iron Oxide Nanoparticles Coated with Polyvinyl Alcohol for Targeted Delivery and Imaging. Journal of Physical Chemistry B. 2008, 112: 14470-14481. 10.1021/jp803016n.
Philipse AP, van Bruggen MPB, Pathmamanoharan C: Magnetic silica dispersions: preparation and stability of surface-modified silica particles with a magnetic core. Langmuir. 1994, 10: 92-99. 10.1021/la00013a014.
Mahmoudi M, Simchi A, Imani M, Milani AS, Stroeve P: An in vitro study of bare and poly(ethylene glycol)-co-fumarate-coated superparamagnetic iron oxide nanoparticles: a new toxicity identification procedure. Nanotechnology. 2009, 20: 10.1088/0957-4484/20/22/225104.
Fonseca C, Simoes S, Gaspar R: Paclitaxel-loaded PLGA nanoparticles: preparation, physicochemical characterization and in vitro anti-tumoral activity. Journal of Controlled Release. 2002, 83: 273-286. 10.1016/S0168-3659(02)00212-2.
Hosseinkhani H, Aoyama T, Ogawa O, Tabata Y: Ultrasound enhancement of in vitro transfection of plasmid DNA by a cationized gelatin. Journal of Drug Targeting. 2002, 10: 193-204. 10.1080/10611860290022624.
Acknowledgements
We would like to thank Science Foundation Ireland (SFI) and the Health Research Board of Ireland for financial support.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
MN and JC performed all cellular experiments. MN and SAC performed all nanoparticle synthesis and characterisation, and wrote the manuscript with SB and YKG. MN and JC conducted confocal imaging. YKG and YV designed the overall project and helped with data and manuscript revision. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is published under license to BioMed Central Ltd. This is an Open Access article is distributed under the terms of the Creative Commons Attribution License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Nowostawska, M., Corr, S.A., Byrne, S.J. et al. Porphyrin-magnetite nanoconjugates for biological imaging. J Nanobiotechnol 9, 13 (2011). https://doi.org/10.1186/1477-3155-9-13
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1477-3155-9-13