Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water

  • Published:
Acta Metallurgica Sinica (English Letters) Aims and scope

Abstract

In pressurized water reactor, fretting corrosion has become the main reason for the failure of 690TT heat exchanger tubes. The effect of temperature on the fretting corrosion behavior between 690TT tube and 405 stainless steel (SS) bar has been studied during 106 fretting cycles. The overall average coefficient of friction (COF) values descends with an increase in test temperature, while the width of worn scar becomes wider. The severest fretting corrosion happens when the test temperature is at 100 °C. The wear mechanism differs at different test temperatures, from adhesive wear at room temperature to abrasive wear and delamination at 100 °C, to abrasive wear at 200 °C. Deformation slips, high residual strain concentration, and micro-cracks are found which are disadvantageous for the further service performance of the tubes.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

Similar content being viewed by others

References

  1. R.S. Dutta, R. Tewari, P.K. De, Corros. Sci. 49, 303 (2007)

    Article  CAS  Google Scholar 

  2. J. Benson, Overview of steam generator operating experience. Paper presented at the 4th international symposium on materials and reliability in nuclear power plants, Shenyang, China, 21 September 2015

  3. P. Sherburne, Stress Corrosion cracking of alloy 600 &690 steam generator tubing. Paper presented at international seminar on welding and non-destructive examination in nuclear power plants, Suzhou, China, 27 June 2009

  4. H.J. Connors, Nucl. Technol. 55, 311 (2017)

    Article  Google Scholar 

  5. M.H. Attia, Tribol. Int. 39, 1294 (2006)

    Article  Google Scholar 

  6. S.H. Jeong, C.W. Cho, Y.Z. Lee, Tribol. Int. 38, 283 (2005)

    Article  CAS  Google Scholar 

  7. J. Li, B.B. Yang, Y.H. Lu, L. Xin, Z.H. Wang, T. Shoji, Tribol. Int. 116, 147 (2017)

    Article  CAS  Google Scholar 

  8. J.K. Hong, I.S. Kim, C.Y. Park, E.S. Kim, Wear 259, 349 (2005)

    Article  CAS  Google Scholar 

  9. X. Mi, Z.B. Cai, X.M. Xiong, H. Qian, L.C. Tang, Y.C. Xie, J.F. Peng, M.H. Zhu, Tribol. Int. 100, 400 (2016)

    Article  CAS  Google Scholar 

  10. Z.H. Wang, Y.H. Lu, J. Li, T. Shoji, Tribol. Int. 95, 162 (2016)

    Article  CAS  Google Scholar 

  11. J. Li, B. Yang, Y. Lu, L. Xin, Z. Wang, T. Shoji, Mater. Charact. 131, 224 (2017)

    Article  CAS  Google Scholar 

  12. J. Li, Y.H. Lu, Wear 304, 223 (2013)

    Article  CAS  Google Scholar 

  13. L. Xin, B.B. Yang, Z.H. Wang, J. Li, Y. Lu, T. Shoji, Wear 368, 210 (2016)

    Article  Google Scholar 

  14. X. Guo, P. Lai, L. Tang, J. Wang, L. Zhang, Tribol. Int. 116, 155 (2017)

    Article  CAS  Google Scholar 

  15. L. Xin, Y.H. Lu, Y. Otsuka, Y. Mutoh, Z.H. Wang, T. Shoji, Mater. Charact. 134, 260 (2017)

    Article  CAS  Google Scholar 

  16. J.Y. Yun, M.C. Park, G.S. Shin, J.H. Heo, D.I. Kim, S.J. Kim, Wear 313, 83 (2014)

    Article  CAS  Google Scholar 

  17. L. Xin, Y. Lu, T. Shoji, Mater. Charact. 131, 157 (2017)

    Article  CAS  Google Scholar 

  18. H. Sun, X. Wu, E.H. Han, Corros. Sci. 51, 2840 (2012)

    Article  Google Scholar 

  19. I. Betova, M. Bojinov, V. Karastoyanov, P. Kinnunen, T. Saario, Corros. Sci. 58, 20 (2012)

    Article  CAS  Google Scholar 

  20. Z.M. Zhang, J.Q. Wang, E.H. Han, W. Ke, Corros. Sci. 53, 3623 (2011)

    Article  CAS  Google Scholar 

  21. J.B. Huang, X.H. Liu, E.H. Han, X.Q. Wu, Corros. Sci. 53, 3254 (2011)

    Article  CAS  Google Scholar 

  22. W.J. Kuang, X.Q. Wu, E.H. Han, Corros. Sci. 63, 259 (2012)

    Article  CAS  Google Scholar 

  23. J.Y. Yun, H.S. Lee, D.H. Hur, W.S. Kang, C.H. Bae, S.J. Kim, Wear 368, 344 (2016)

    Article  Google Scholar 

  24. X. Guo, P. Lai, L. Tang, J. Lu, J. Wang, L. Zhang, Wear 400–401, 119 (2018)

    Article  Google Scholar 

  25. S.M. Hong, I.S. Kim, Wear 259, 356 (2005)

    Article  CAS  Google Scholar 

  26. H.L. Ming, X.C. Liu, Z.M. Zhang, J.Q. Wang, E.H. Han, Tribol. Int. 126, 133 (2018)

    Article  CAS  Google Scholar 

  27. Z.R. Zhou, L. Vincent (eds.), Fretting Wear (Science Press, Beijing, 2002)

    Google Scholar 

  28. Q. Luo, Q.S. Wu, Q. Xu, J. Li, Phys. Exam. Test 32, 3 (2014)

    CAS  Google Scholar 

  29. J.Z. Wang, J.Q. Wang, H.L. Ming, Z.M. Zhang, E.H. Han, J. Mater. Sci. Technol. 34, 1419 (2018)

    Article  CAS  Google Scholar 

  30. P. Lai, X. Gao, L. Tang, X. Guo, L. Zhang, Nucl. Eng. Des. 327, 51 (2018)

    Article  CAS  Google Scholar 

  31. W.J. Kuang, X.Q. Wu, E.H. Han, J.C. Rao, Corros. Sci. 53, 3853 (2011)

    Article  CAS  Google Scholar 

  32. L. Xin, Z. Wang, J. Li, Y. Lu, T. Shoji, Mater. Charact. 115, 32 (2016)

    Article  CAS  Google Scholar 

  33. F. Huang, J.Q. Wang, E.H. Han, W. Ke, J. Mater. Sci. Technol. 28, 562 (2012)

    Article  CAS  Google Scholar 

  34. D. Chen, E.H. Han, X. Wu, Corros. Sci. 111, 518 (2016)

    Article  CAS  Google Scholar 

  35. L. Xin, B. Yang, J. Li, Y. Lu, T. Shoji, Corros. Sci. 123, 116 (2017)

    Article  CAS  Google Scholar 

  36. H.L. Ming, Z.M. Zhang, P.Y. Xiu, J.Q. Wang, E.H. Han, W. Ke, Acta Metall. Sin. (Engl. Lett.) 29, 848 (2016)

    Article  Google Scholar 

  37. X.Q. Wu, S. Xu, E.H. Han, W. Ke, Acta Metall. Sin. (Engl. Lett.) 47, 790 (2011)

    CAS  Google Scholar 

Download references

Acknowledgements

This work is supported by the National Natural Science Foundation of China (No. 51771211), the Large-scale advanced PWR major projects (No. 2017ZX06002006), the Liaoning Provincial Natural Science Foundation of China (No. 20180540076), and the open-ended fund of the CAS Key laboratory of Nuclear Materials and Safety Assessment (Institute of Metal Research, Chinese Academy of Sciences, China) (Nos. 2019NMSAKF02 and 2017NMSAKF04). The authors are grateful for the help of 3D surface morphology analysis from Dr. Hui Feng at IMR, CAS.

Author information

Authors and Affiliations

  1. CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China

    Xing-Chen Liu, Hong-Liang Ming, Zhi-Ming Zhang, Jian-Qiu Wang & En-Hou Han

  2. School of Materials Science and Engineering, University of Science and Technology of China, Shenyang, 110016, China

    Xing-Chen Liu

  3. Shanghai Nuclear Engineering Research and Design Institute Ltd. Co., Shanghai, 200233, China

    Li-Chen Tang, Hao Qian & Yong-Cheng Xie

Authors
  1. Xing-Chen Liu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hong-Liang Ming
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Zhi-Ming Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Jian-Qiu Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Li-Chen Tang
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Hao Qian
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Yong-Cheng Xie
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. En-Hou Han
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Hong-Liang Ming.

Additional information

Available online at http://link.springer.com/journal/40195

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Liu, XC., Ming, HL., Zhang, ZM. et al. Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water. Acta Metall. Sin. (Engl. Lett.) 32, 1437–1448 (2019). https://doi.org/10.1007/s40195-019-00929-9

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40195-019-00929-9

Keywords

Search

Navigation