Abstract
Mullite whiskers were prepared from Si powders in molten Al2(SO4)3-Na2SO4 mixture salts with different Al/Si molar ratio (R) of raw materials. The resulting mullite whiskers, had been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) and infrared spectroscopy analysis (FT-IR). Mullite phase was obtained in molten salts when the temperature reached at 850 °C. SEM and EDS results revealed that two kinds of microstructures were formed in the final product, Al-rich mullite pellets and clusters of tiny mullite crystals, and the content of Al-rich mullite pellets increased with the higher Al/Si molar ratio (R) adopted in raw materials. A new oxidation-dissolution mechanism was proposed to explain mullite whiskers growth. According to thermodynamic analysis, mullite phase might be spontaneously formed as the temperature reached the decomposition temperature of aluminum sulfate (1023 K).
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Zhang YB, Ding YP, Gao JQ, et al. Mullite fibres prepared by sol-gel method using polyvinyl butyral. J Eur Ceram Soc 2009, 29: 1101–1107.
Bagchi B, Das S, Bhattacharya A, et al. Nanocrystalline mullite synthesis at a low temperature: Effect of copper ions. J Am Ceram Soc 2009, 92: 748–751.
Kong LB, Zhang TS, Ma J, et al. Mullitization behavior and microstructural development of B2O3-Al2O3-SiO2 mixtures activated by high-energy ball milling. Solid Sate Sci 2009, 11: 1333–1342.
Zhang TS, Kong LB, Du ZH, et al. In situ interlocking structure in gel-derived mullite matrix induced by mechanoactivated commercial mullite powders. Scripta Mater 2010, 63: 1132–1135.
Zhang TS, Kong LB, Du ZH, et al. Tailoring the microstructure of mechanoactivated Al2O3 and SiO2 mixtures with TiO2 addition. J Alloys Compd 2010, 506: 777–783.
Roy B, Fuierer PA. Molten salt synthesis of Bi-4(V0.85Co0.15)(2)O11-delta (BICOVOX) ceramic powders. J Am Ceram Soc 2009, 92: 520–523.
Li JF, Lin H, Li JB, et al. Effects of different potassium salts on the formation of mullite as the only crystal phase in kaolinite. J Eur Ceram Soc 2009, 29: 2929–2936.
Park YM, Yang TY, Yoon SY, et al. Mullite whiskers derived from coal fly ash. Mater Sci Eng A 2007, 454–455: 518–522.
Zhang PY, Liu JC, Du HY, et al. Molten salt synthesis of mullite whiskers from various alumina precursors. J Alloys Compd 2010, 491: 447–451.
Ouatib RE, Guillemet S, Durand B, et al. Reactivity of aluminum sulfate and silica in molten alkali-metal sulfates in order to prepare mullite. J Eur Ceram Soc 2005, 25: 73–80.
Kong LB, Gan YB, Ma J, et al. Mullite phase fromation and reaction sequences with the presence of pentoxides. J Alloys Compd 2003, 351: 264–272.
Kim BM, Cho YK, Yoon SY, et al. Mullite whiskers derived from kaokin. Ceram Int 2009, 35: 579–583.
Zhang PY, Liu JC, Du HY, et al. Influence of silica sources on morphology of mullite whiskers in Na2SO4 flux. J Alloys Compd 2009, 484: 580–584.
Levin EM, Mcmurdie HF. Phase diagrams for ceramists 1975 supplement. Am Ceram Soc OH, Westerville, 1975: 1318–1318.
Liu K, Feng Q, Yang YX, et al. Preparation and characterization of amorphous silica nanowires from natural chrysotile. J Non-Cryst Solids 2007, 353: 1534–1539.
Lavat AE, Grasselli MC, Tasca JE. Phase changes of ceramic whiteware slip-casting bodies studied by XRD and FTIR. Ceram Int 2007, 33: 1111–1117.
Barin I. Thermochemical Data of Pure Substances. Weinheim: VCH Verlagsgesellschaft, 1989.
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is published with open access at Springerlink.com
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Wang, W., Li, H., Guo, Y. et al. Mullite whiskers prepared by molten salt method using Si powders. J Adv Ceram 1, 283–289 (2012). https://doi.org/10.1007/s40145-012-0028-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40145-012-0028-7