Abstract
In this study, AISI P20, H13 and D2 steels were pack borided at 900 and 950 °C for retention times of 2, 4 and 6 h. The boride layer thickness values changed depending on the chemical composition of the steels. The hardness of borides that formed on the surface of AISI P20, AISI H13 and AISI D2 steels were 1897 HV(50 g), 1989 HV(50 g) and 1916 HV(50 g), respectively. On the other hand, the Vickers hardness values of the untreated steels were 532 HV(50 g), 485 HV(50 g) and 408 HV(50 g), respectively. The adhesion properties of the boride layer were analyzed by performing the Daimler–Benz Rockwell-C adhesion method. According to the adhesion and wear test results, the adhesion and wear resistance of the boride layer decreased with the increase in the boriding temperature and time.
Similar content being viewed by others
References
Maragoudakis N, Stergioudis G, Omar H, Paulidou H, and Tsipas D N Mater Lett 57 (2002) 949.
Ozbek I, and Bindal C, Surf Coat Technol 154 (2002) 14.
Ozdemir O, Omar M A, Usta M, Zeytin S, Bindal C, and Ucisik A H, Vacuum 83 (2009) 175.
Ozbek I, Akbulut H, Zeytin S, Bindal C, and Ucisik A H, Surf Coat Technol 126 (2000) 166.
Sinha A K, Heat Treat ASM Handbook 4 (1997) 437.
Taktak S, Mater Des 28 (2007) 1836.
Uslu I, Comert H, Ipek M, Ozdemir O, and Bindal C, Mater Des 28 (2007) 55.
Oliveira C K N, Casteletti L C, Lombardi Neto A, Totten G E, and Heck S C, Vacuum 84 (2010) 792.
Vidakis N, Antoniadis A, and Bilalis N, J Mater Process Technol 481 (2003) 143.
Verein Deutscher Ingenieure Normen, VDI 3198 (1991) Dusseldorf, VDI-Verlag.
Daimler Benz Adhesion Test, Verein Deutscher Ingenieure (VDI) Richlinie 3198 (1992) 7.
Kayali Y, and Taktak S, J Adhes Sci Technol 29 (2015) 2065.
Meric C, Sahin S, and Yilmaz S S, Mater Res Bull 35 (2000) 2165.
Melendez E, Campos I, Rocha E, et al, Mater Sci Eng A 234 (1997) 900.
Carbucicchio M, and Palombarini G, J Mater Sci Lett 6 (1987) 1147.
Genel K, Vacuum 80 (2006) 451.
Efe G C, Ipek M, Ozbek I, Zeytin S, Bindal C, Mater Charact 59 (2008) 23.
Kayali Y, Phys Metals Metallogr 114 (2013) 1061.
Taktak S, and Tasgetiren S, J Mater Eng Perform 15 (2006) 570.
Kayali Y, Yalcin Y, and Taktak S, Mater Des 32 (2011) 4295.
Tabur M, Izciler M, Gulb F, and Karacan I, Wear 266 (2009) 1106.
Celikyurek I, Baksan B, Torun O, and Gurler R, Intermetallics 14 (2006) 136.
Hunger H J, and Trute G, Heat Treat 2 (1994) 31.
Tsipas D N, and Rus J, J Mater Sci Lett 6 (1987) 118.
Kayali Y, J Balkan Tribol Assoc 19 (2013) 340.
Fichtl W, Trausner N, and Matuschka AG, in Boronizing with Ekabor. Elektroschmelzwerk Kempten GmbH, Wolfson Heat Treatment Centre, Univ Aston Birmingham, Gosta Green, Birmingham (1987).
Subrahmanyam J, and Gopinath K, Wear 95 (1984) 287.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kara, R., Çolak, F. & Kayali, Y. Investigation of Wear and Adhesion Behaviors of Borided Steels. Trans Indian Inst Met 69, 1169–1177 (2016). https://doi.org/10.1007/s12666-015-0698-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-015-0698-2