Enhancement of the nickel converter slag-cleaning operation with the addition of spent potlining

  • Published:
International Journal of Minerals, Metallurgy, and Materials Aims and scope Submit manuscript

Abstract

The slag cleaning (or matte settling) process was experimentally investigated at 1573 K using a fayalitic nickel converter slag containing spinel and matte/alloy particles. The addition of various amounts of spent potlining (SPL) was studied in terms of its influence on matte settling and the overall metal recoveries. The slags produced were characterized by scanning electron microscopy, energy-dispersive spectroscopy, and wet chemical analysis using inductively coupled plasma optical emission spectrometry. The presence of solid spinel particles in the molten slag hindered coalescence and settling of matte/alloy droplets. Matte settling was effectively promoted with the addition of as little as 2wt% SPL because of the reduction of spinel by the carbonaceous component of the SPL. The reduced viscosity of the molten slag in the presence of SPL also contributed to the accelerated matte settling. Greater metal recoveries were achieved with larger amounts of added SPL. Fast reduction of the molten slag at 1573 K promoted the formation of highly dispersed metal particles/clusters via accelerated nucleation in the molten slag, which increased the overall slag viscosity. This increase in viscosity, when combined with rapid gas evolution from accelerated reduction reactions, led to slag foaming.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. A.E.M. Warner, C.M. Díaz, A.D. Dalvi, P.J. Mackey, A.V. Tarasov, and R.T. Jones, JOM world nonferrous smelter survey Part IV: Nickel: Sulfide, JOM, 59(2007), No. 4, p. 58.

    Article  Google Scholar 

  2. P. Toscano and T.A. Utigard, Nickel, copper, and cobalt slag losses during converting, Metall. Mater. Trans. B, 34(2003), p. 121.

    Article  Google Scholar 

  3. F.K. Crundwell, M.S. Moats, V. Ramachandran, T.G. Robinson, and W.G. Davenport, Extractive Metallurgy of Nickel, Cobalt and Platinum Group Metals, Elsevier, New York, 2011, p. 233.

    Book  Google Scholar 

  4. R.T. Jones, D.A. Hayman, and G.M. Denton, Recovery of cobalt, nickel and copper from slags, using DC-arc furnace technology, [in] 35th Annual Conference of Metallurgists, Montreal, 1996, p. 451.

    Google Scholar 

  5. D. Yu and K. Chattopadhyay, Numerical simulation of copper recovery from converter slags by the utilisation of spent potlining (SPL) from alumimium electroytic cells, Can. Metall. Q., 55(2016), No. 2, p. 251.

    Article  Google Scholar 

  6. P. Toscano and T.A. Utigard, Slag loss control with Bessemer mattes, CIM Bull., 97(2004), No. 1076, p. 71.

    Google Scholar 

  7. G. Holywell and R. Breault, An overview of useful methods to treat, recover, or recycle spelt potlining, JOM, 65(2013), No. 11, p. 1441.

    Article  Google Scholar 

  8. J.B. Cashman, Detoxifying Spent Aluminum Potliners, US Patent, No. 6190626 B1, 2001.

    Google Scholar 

  9. R.P. Pawlek, Spent potlining: an update, [in] Light Metals 2012, Springer, Cham, 2012, p. 1313.

    Book  Google Scholar 

  10. D. Mikša, M. Homšak, and N. Samec, Spent potlining utilisation possibilities, Waste Manage. Res., 21(2003), No. 5, p. 467.

    Article  Google Scholar 

  11. B.I. Silveira, A.E. Dantas, J.E. Blasquez, and R.K.P. Santos, Characterization of inorganic fraction of spent potliners: evaluation of the cyanides and fluorides content, J. Hazard. Mater., 89(2002), No. 2–3, p. 177.

    Article  Google Scholar 

  12. W.K. O’Connor, P.C. Turner, and G.W. Addison, Method for Processing Aluminum Spent Potliner in Graphite Electrode Arc Furnace, US Patent, No. 6498282 B1, 2002.

    Google Scholar 

  13. T.K. Pong, R.J. Adrien, J. Besida, T.A. O’Donnell, and D.G. Wood, Spent potlining ― a hazardous waste made safe, Process Saf. Environ. Prot., 78(2000), No. 3, p. 204.

    Article  Google Scholar 

  14. I. Rustad, K.H. Karstensen, and K.E. Ødegrd, Disposal options for spent potlining, Waste Manage. Ser., 1(2000), p. 617.

    Article  Google Scholar 

  15. B. Meirelles and H. Santos, Economic and environmental alternative for destination of spent pot lining from primary aluminum production, [in] Light Metals 2014, Springer, Cham, 2014, p. 565.

    Google Scholar 

  16. K.W. Grieshaber, C.T. Philipp, and G.F. Bennett, Process for recycling spent potliner and electric arc furnace dust into commercial products using oxygen enrichment, Waste Manage., 14(1994), No. 3–4, p. 267.

    Article  Google Scholar 

  17. D.W. Yu, V. Mambakkam, D.H. Li, K. Chattopadhyay, and L. Gao, Alternative applications of SPL: Testing ideas through experiments and mathematical modeling, [in] Light Metals 2017, Springer International Publishing, Cham, 2017, p. 579.

    Google Scholar 

  18. H.J. Hittner and Q.C. Nguyen, Stabilization of Fluorides of Spent Potlining by Chemical Dispersion, US Patent, No. 5024822, 1991.

    Google Scholar 

  19. D.W. Yu and K. Chattopadhyay, Fluxing molten converter slags with spent potlining (SPL) for metal recovery, [in] 54th Annual Conference of Metallurgists, Toronto, 2015, p. 1.

    Google Scholar 

  20. L. Blaney, Magnetite (Fe3O4): properties, synthesis, and applications, Lehigh Rev., 15(2007), p. 33.

    Google Scholar 

  21. X.F. Cheng, Z.X. Cui, L. Contreras, M. Chen, A. Nguyen, and B.J. Zhao, Introduction of matte droplets in copper smelting slag, [in] 8th International Symposium on High-Temperature Metallurgical Processing, Springer International Publishing, Cham, 2017, p. 385.

    Google Scholar 

  22. S.W. IP and J.M. Toguri, Entrainment behaviour of copper and copper matte in copper smelting operations, Metall. Mater. Trans. B, 23(1992), No. 3, p. 303.

    Article  Google Scholar 

  23. H. Sato, Viscosity measurement of subliquidus magmas: 1707 basalt of Fuji volcano, J. Mineral. Petrol. Sci., 100(2005), No. 4, p. 133.

    Article  Google Scholar 

  24. R. Roscoe, The viscosity of suspensions of rigid spheres, Br. J. Appl. Phys., 3(1952), No. 8, p. 267.

    Article  Google Scholar 

  25. A. Warczok, G. Riveros, R. Degel, J. Kunze, and H. Oterdoom, Computer simulation of slag cleaning in an electric furnace, [in] The Carlos Diaz Symposium on Pyrometallurgy, Toronto, 2007, p. 367.

    Google Scholar 

  26. K.L. Chang, C.T. Huang, W.J. Huang, and Y.C. Liu, Investigation of microstructure and phosphorus distribution in BOF slag, China Steel Tech. Rep., 2008, No. 21, p. 1.

    Google Scholar 

  27. W.N. Afolabi, Mineral phase crystallization sequence of Delta Steel company (DSC), Ovwian-Aladja, Western Niger Delta Steelmaking slag for use as material in industry, Int. J. Mater. Sci. Appl., 6(2017), No. 2, p. 99.

    Google Scholar 

  28. H.J. Greenfield and D. Miller, Spatial petterning of Early Iron Age metal production at Ndondondwane, South Africa: the question of cultural continuity between the Early and Late Iron Ages, J. Archaeol. Sci., 31(2004), No. 11, p. 1511.

    Article  Google Scholar 

  29. A. Selskienė, Examination of smelting and smithing slags formed in bloomery iron-making process, Chemija, 18(2007), No. 2, p. 22.

    Google Scholar 

  30. C.W. Bale, E. Bélisle, P. Chartrand, S.A. Decterov, G. Eriksson, A.E. Gheribi, K. Hack, I.-H. Jung, Y.-B. Kang, J. Melançon, A.D. Pelton, S. Petersen, C. Bobelin, J. Sangster, and M-A. Van Ende, FactSage thermochemical software and databases, 2010–2016, Calphad, 54(2016), p. 35.

    Article  Google Scholar 

  31. L. Andrews, Base Metal Losses to Furnace Slag During Processing of Platinum-Bearing Concentrates [Dissertation], University of Pretoria, Pretoria, 2009, p. 1.

    Google Scholar 

  32. H. Shahrokhi and J.M. Shaw, Fine drop recovery in batch gas-agitated liquid-liquid system, Chem. Eng. Sci., 55(2000), No. 20, p. 4719.

    Article  Google Scholar 

  33. L.R. Nelson, F. Stober, J. Ndlovu, L.P.S de Villiers, and D. Wanblad, Role of technical innovation on production delivery at the Polokwane Smelter, [in] 44th Annual Conference of Metallurgists of CIM. Nickel and Cobalt 2005-Challenges in Extraction and Production, Calgary, 2005, p. 91.

    Google Scholar 

  34. R. Minto and W.G. Davenport, Entrapment and flotation of matte in molten slags, Trans. Inst. Min. Metall., 81(1972), p. C59.

    Google Scholar 

  35. V. Raghavan, Fe–Ni–S (iron-nickel-sufur), J. Phase Equilib. Diffus., 25(2004), No. 4, p. 373.

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. School of Metallurgy and Environment, Central South University, Changsha, 410083, China

    Dawei Yu

  2. CanmetMINING, Natural Resources Canada, Ottawa, Ontario, K1A 0G1, Canada

    Dawei Yu

  3. Process Metallurgy & Modelling Group, Department of Materials Science and Engineering, University of Toronto, Toronto, Ontario, M5S 3E4, Canada

    Kinnor Chattopadhyay

Authors
  1. Dawei Yu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Kinnor Chattopadhyay
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Dawei Yu.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Yu, D., Chattopadhyay, K. Enhancement of the nickel converter slag-cleaning operation with the addition of spent potlining. Int J Miner Metall Mater 25, 881–891 (2018). https://doi.org/10.1007/s12613-018-1637-0

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12613-018-1637-0

Keywords

Search

Navigation