Abstract
The strength and elongation to fracture of spray deposited Al-Si-Pb alloys were studied as a function of lead content, silicon content, and distance from the centre to periphery of the deposit. It is found that the ultimate tensile strength, proof stress and elongation to fracture decrease, linearly and exponentially, with the increase in lead content and porosity of the deposit, respectively. Both the strengths and elongation to fracture linearly increase with increasing distance from the centre to periphery of the deposit. The ultimate tensile strength and proof stress are higher at a higher silicon content and they have a linear relationship with the hardness of the deposit.
Similar content being viewed by others
References
S. Mohan, J.P. Pathak, N. Chander, and S. Sarkar, Surface studies of centrifugally cast aluminum-based lead bearing composites, J. Reinf. Plast. Compos., 27(2008), No. 13, p. 1461.
G. Ran, J.E. Zhou, S.Q. Xi, and P.L. Li, Microstructure and morphology of Al-Pb bearing alloy synthesized by mechanical alloying and hot extrusion, J. Alloys Compd., 419(2006), No. 1–2, p. 66.
J. An, Y.B. Liu, Y. Lu, and Q.Y. Zhang, The formation of reacted film and its influence on tribological properties of extruded Al-Si-Cu-20-25Pb alloy under dry sliding, J. Mater. Sci., 38(2003), No. 9, p. 1975.
F.X. Yu, D.S. Dwarakadasa, and S. Ranganathan, Microstructure and mechanical properties of spray-formed Al-Si-Pb alloys, J. Mater. Process. Technol., 137(2003), No. 1–3, p. 164.
J. An, C. Dong, and Q.Y. Zhang, Improvement of the wear behavior of stircast Al-Si-Pb alloys by hot extrusion, Tribol. Int., 36(2003), p. 25.
J. An, Y.B. Liu, and Y. Lu, The influence of Pb on the friction and wear behavior of Al-Si-Pb alloys, Mater. Sci. Eng. A, 373(2004), No. 1–2, p. 294.
X. Fang and Z. Fan, Rheo-diecasting of Al-Si-Pb immiscible alloys, Scripta Mater., 54(2006), p. 789.
P. Padhi, S.K. Anand, D. Kar, S. Ghosh, and S.K. Panigrahi, Modeling structure of Al-Sn alloy, Mater. Sci. Forum, 519–521(2006), p. 1519.
G.B. Rudrakshi, V.C. Srivastava, J.P. Pathak, and S.N. Ojha, Spray forming of Al-Si-Pb alloys and their wear characteristics, Mater. Sci. Eng. A, 383(2004), No. 1, p. 30.
E.M. Mazzer, C.R.M. Afonso, C. Bolfarini, and C.S. Kiminami, Microstructure study of Al 7050 alloy reprocessed by spray forming and hot-extrusion and aged at 121°C, Intermetallics, 43(2013), p. 182.
E.M. Mazzer, C.R.M. Afonso, M. Galano, C.S. Kiminami, and C. Bolfarini, Microstructure evolution and mechanical properties of Al-Zn-Mg-Cu alloy reprocessed by spray-forming and heat treated at peak aged condition, J. Alloys Compd., 579(2013), p. 169.
Y.C. Suh and Z.H. Lee, Nucleation of liquid Pb-phase in hypermonotectic Al-Pb melt and the segregation of Pb-droplets in melt-spun ribbon, Scripta Metall. Mater., 33(1995), No. 8, p. 1231.
C.S. Cui, U. Fritsching, and A. Schulz, Three-dimensional mathematical modeling and numerical simulation of billet shape in spray forming using a scanning gas atomizer, Metall. Mater. Trans. B, 38(2007), No. 2, p. 333.
K.V. Ojha, A. Tomar, D. Singh, and G.C. Kaushal, Shape, microstructure and wear of spray formed hypoeutectic Al-Si alloys, Mater. Sci. Eng. A, 487(2008), p. 591.
J. Mi and P.S. Grant, Modelling the shape and thermal dynamics of Ni superalloy rings during spray forming: Part 1. Shape modelling — Droplet deposition, splashing and redeposition. Acta Mater., 56(2008), No. 7, p. 1588.
D.M. Liu, J.Z. Zhao, and M.S. Li, Modeling and experimental verification of tubular product formation during spray forming, Trans. Nonferrous Met. Soc. China, 19(2009), No. 3, p. 661.
R. Mittal and D. Singh, Dry sliding wear behaviour of spray formed ZrSiO4 reinforced Al-Si-Sn alloy, Adv. Mater. Lett, 3(2012), No. 1, p. 38.
G.B. Rudrakshi, V.C. Srivastava, and S.N. Ojha, Microstructural development in spray formed Al-3.5Cu-10Si-20Pb alloy and its comparative wear behaviour in different environmental conditions, Mater. Sci. Eng. A, 457(2007), No. 1, p. 100.
D. Singh and S. Dangwal, Effects of process parameters on surface morphology of metal powders produced by free fall gas atomization, J. Mater. Sci., 41(2006), No. 12, p. 3853.
S. Hagege, Lead inclusions in silicon: structure, morphology and thermal behavior, Interface Sci., 7(1999), p. 85.
A. Tomar and D. Singh, Porosity in disk shape spray formed Al-Si-Pb alloy preform, Powder Metall. Min., (2012), No. 1, p.4.
A.K. Prasada Rao, K. Das, B.S. Murty, and M. Chakraborty, Effect of grain refinement on wear properties of Al and Al-7Si alloy, Wear, 257(2004), No. 1–2, p. 148.
G.F. Bocchini, The influences of porosity on the characteristics of sintered materials, Int. J. Powder Metall., 22(1986), No. 3, p. 185.
R.D. Payne, A.L. Moran, and R.C. Cammarata, Relating porosity and mechanical properties in spray formed tubulars, Scripta Metal. Mater., 29(1993), No. 7, p. 907.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Tomar, A., Mittal, R. & Singh, D. Strength and elongation of spray formed Al-Si-Pb alloys. Int J Miner Metall Mater 21, 1222–1227 (2014). https://doi.org/10.1007/s12613-014-1030-6
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-014-1030-6