Abstract
The Brazilian Microgravity Program is mainly based on experiments carried out on sounding rockets. A solidification furnace, capable of producing temperatures up to 900 °C, was developed to process metal and semiconductor alloys in microgravity environment. This paper describes a solidification experiment made in this furnace during a parabolic flight, with two eutectic alloys. The behavior of the eutectic alloys PbSn with 26.1 Pb at. % composition, and PbTe with 10.9 Pb at. % composition were presented and compared with laboratory solidifications carried out in the same furnace and thermal cycle. It was concluded that the formation of dendritic structures in PbSn alloy is related to the presence of sedimentation and convective flow during solidification, and the size of these structures is connected to the solidification time. Thus, in the microgravity alloy, there was no formation of dendritic structures and the profile of solute distribution remained constant throughout the sample. For the PbTe eutectic alloy the microgravity conditions have not caused significant changes compared to the earth solidified sample.
Similar content being viewed by others
References
An, C.Y., Bandeira, I.N., Rowe, D.M., Min, G.: An exact density formula for substitutional solid solution alloys. J. Mater. Sci. Lett. 13(14), 1051–1053 (1994)
An, C.Y., Silva, C.R.M., Rowe, D.M.: Density of cubic substitutional solid solution alloys. Mater. Lett. 28, 83–85 (1996)
An, C.Y., Boschetti, C., Ribeiro, F.M., Toledo, R.C., Freitas, F.E., Bandeira, I.N.: Perfomance of a solidification furnace developed for sounding rockets. Microgravity Sci. Technol. 23(4), 427–432 (2011). doi:10.1007/s12217-011-9263-8
An, C.Y., Boschetti, C., Ribeiro, F.M., Toledo, R.C., Freitas, F.E., Castilho, F.F., Bandeira, I.N.: Solidification furnace for microgravity experiments on sounding rockets. J. Aerosp. Technol. Manag. 2, 237–240 (2012). doi:10.5028/jatm.2012.04021412
Bandeira, I.N., An, C.Y., Boschetti, C., Ribeiro, M.F., Ferreira, F.A., Peixoto, J.C., Silva, S.A.: Forno Multiusuário para Solidificaċão (CUMÃ I). INPE, version 2013-05-14, LAS 07/2013 (2002). http://urlib.net/8JMKD3MGP7W/3E582SL. Accessed in 14 May 2013
Bandeira, I.N., An, C.Y., Boschetti, C., Ribeiro, M.F., Ferreira, F.A., Peixoto, J.C., Silva, S.A.: Forno Multiusuário para Solidificação (CUMÃ II). INPE, version 2013-05-14, LAS 06/2013, (2007). http://urlib.net/8JMKD3MGP7W/3E5836B. Accessed in 14 May 2013
European Space Agency (ESA): Sounding Rockets. In: European Users Guide to Low Gravity Platform, UIC-ESA-UM-0001, Issue 2, Revision 0. (2005) http://wsn.spaceflight.esa.int/docs/EuropeanUserGuide/-Cover.pdf. Accessed in 5 June 2013
Hunt, J.D., Jackson, K.A.: Binary eutectic solidification. Trans. AIME 236, 843 (1966)
Favier, J.J., Hunt, J.D., Sahm, P.R.: Metals and alloys. In: Walter, H.U. (ed.) Fluid Sciences And Materials Science In Space: A European Perspective, p 477. Springer XIV, Berlin (1987)
Flemings, M.: Solidification processing. McGraw-Hill series in Materials Science and Engineering. ISBN 9780070212831 (1974)
Franke, B.: Microgravity Research And Applications In Physical Sciences And Biotechnology. Proceedings Of The First International Symposium. Italy (2000)
SSC Group: TEXUS 50/51, Sweden (2013). http://www.sscspace.com/texus-5051. Accessed in 5 June 2013
Toledo, R.C.: Estudo da Solidificação de Ligas Metálicas Eutéticas em Ambiente de Microgravidade, Thesis (Part of PhD Thesis). INPE (2013)
Verhoeven, J.D., Gibson, E.D.: The dendrite-to-composite transition in off-eutectic Sn-Pb alloys. Metall. Mater. Trans. B 4(11), 2581–2590 (1973)
Verhoeven, J.D., Mason, J.T., Trivedi, R.: The effect of convection on the dendrite to eutectic transition. Metall. Trans. A 17A, 991–1000 (1986)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
An, C.Y., Toledo, R.C., Boschetti, C. et al. Solidification of Lead Tin and Lead Telluride Eutectic Alloys in Microgravity. Microgravity Sci. Technol. 25, 267–273 (2014). https://doi.org/10.1007/s12217-013-9348-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12217-013-9348-7