Abstract
The microstructural evolution and mechanical properties of a hypereutectic Al-Si alloy processed by liquid die forging were investigated. It is found that the grain size of the primary Si was significantly reduced by liquid die forging with increased pressure. The volume fraction of eutectic silicon was decreased with increased pressure. By liquid die forging with pressure up to 180 MPa, the average size of the primary Si was reduced to about 18 μm, which results in the remarkable increase in the fracture strength and hardness of the hypereutectic Al-Si alloy.
Similar content being viewed by others
References
Begg J 1992 Process optimization in the squeeze casting of zinc-aluminum alloys and composites (UK: Loughborough University of Technology)
Brazhkina V V, Popov S V, Voloshina R N, Stanev L M and Spirov I G 1991 High Press. Res. 6 333
Chang J Y, Moon I and Choi C S 1998 J. Mater. Sci. 33 5015
Chen Z W, Jie W Q and Zhang R J 2005 Mater. Lett. 599 2183
Choi H S, Konishi H and Li X C 2012 Mater. Sci. Eng. A541 159
Choi H S and Li X C 2012 J. Mater. Sci. 47 3096
Dahle A K, Nogita K, McDonald S D, Dinnis C and Lu L 2005 Mater. Sci. Eng. A413–414 243
Hekmat-Ardakan A and Ajersch F 2010 Acta Mater. 58 3422
Hekmat-Ardakan A, Liu X C, Ajersch F and Chen X G 2010 Wear 269 684
Hong S Z and Zeng Z P 2002 Spec. Cast. Nonferr. Alloys 22 26
Jung H K, Seo P K and Kang C G 2001 J. Mater. Process. Technol. 113 568
Kilicaslana M F, Lee W R, Lee T H, Sohn Y H and Hong S J 2012 Mater. Lett. 71 164
Li B, Wang H W, Jie J C and Wei Z J 2011a Mater. Des. 32 1617
Li B, Wang H W, Jie J C and Wei Z J 2011b J. Alloys Compd. 509 3387
Li L X, Zong H T, Li M, Wang H X and Cai H X 2012 High Temp.-High Pres. 41 69
Liu G, Li G D, Cai A H and Chen Z K 2011 Mater. Des. 32 121
Lu D H, Jiang Y H, Guan G S, Zhou R F, Li Z H and Zhou R 2007 J. Mater. Process. Technol. 189 13
Lu L, Nogita K and Dahle A K 2005 Mater. Sci. Eng. A399 244
Mayers M A and Chawla K K 1999 Mechanical behaviour of materials (Upper Saddle River, New Jersey: Prentice Hall)
McDonald S D, Nogita K and Dahle A K 2004 Acta Mater. 52 4273
Mohamed A M A, Samuel A M, Samuel F H and Doty H W 2009 Mater. Des. 30 3943
Murali S and Yong M S 2010 J. Mater. Process. Technol. 210 1276
Nogita K, Yasuda H, Yoshida M, McDonald S D, Uesugi K, Takeuchi A and Suzuki Y 2010 J. Alloys Compd. 489 415
Prukkanona W, Srisukhumbowornchai N and Limmaneevichitr C 2009 J. Alloys Compd. 477 454
Sha M, Wu S S, Wang X T, Wan L and Ping A 2012 Mater. Sci. Eng. A535 258
Song K K, Bian X F, Guo J, Wang S H, Sun B A, Li X L and Wang C D 2007 J. Alloys Compd. 440 L8
Srirangam P, Kramer M J and Shankar S 2011 Acta Mater. 59 503
Tsai Y C, Chou C Y, Lee S L, Lin C K, Lin J C and Lim S W 2009 J. Alloys Compd. 487 157
Uzun O, Karaaslan T, Gogebakan M and Keskin M 2004 J. Alloys Compd. 376 149
Voncina M, Kores S, Mrvar P and Medved J 2011 J. Alloys Compd. 509 7349
Wang E D, Hui X D, Wang S S, Zhao Y F and Chen G L 2011 Mater. Sci. Eng. A528 5764
Wang Y P, Wang S J, Li H and Liu X F 2009 J. Alloys Compd. 477 139
Wu H and Chin B A 1991 J. Mater. Sci. 26 993
Xing P F, Gao B, Zhuang Y X, Liu K H and Tu G F 2010a J. Rare Earths 28 927
Xing P F, Gao B, Zhuang Y X, Liu K H and Tu G F 2010b Acta Metall. Sin. 23 327
Xu C L, Wang H Y, Yang Y F and Jiang Q C 2007 Mater. Sci. Eng. A452–453 341
Yi H K and Zhang D 2003 Mater. Lett. 57 2523
Yu X F, Zhang G Z, Wang X Y, Gao Y Y, Jia G L and Hao Z Y 1999 J. Mater. Sci. 34 4149
Yu X F, Zhang G Z, Xiao H J, Pan A S, Jia G L, Gao Y Y, Hao Z Y and Guo X B 2000 Chin. J. Mater. Res. 14 141
Zhang H H, Duan H L, Shao G J, Xu L P, Yin J L and Yan B 2006 Rare Metals 25 11
Zhou J and Duszczyk J 1990 J. Mater. Sci. 25 4541
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wu, F.F., Li, S.T., Zhang, G.A. et al. Microstructural evolution and mechanical properties of hypereutectic Al-Si alloy processed by liquid die forging. Bull Mater Sci 37, 1153–1157 (2014). https://doi.org/10.1007/s12034-014-0056-8
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-014-0056-8