Abstract
The structure of plate/shelf like disodium ditungstate (Na2W2O7) synthesized by new method in the process of ultrasonic spray pyrolysis using acidified aqueous solutions of tungsten (VI) oxide clusters as a precursor was refined down to the R-factor of 8.9 %. X-ray diffraction analysis undoubtedly confirmed formation of orthorhombic Na2W2O7 and refinement of the diffraction data showed that Na2W2O7 powder belongs to the base-centred orthorhombic type of structure with 64 space group, Cmca. The structure of Na2W2O7 can be described as infinite chains formed from tetrahedral (WO4) and octahedral (WO6) building units joined together. It was found that the basic units of the precursor complexes exist in the structure of Na2W2O7. Scanning electron microscopy confirmed formation of plate/shelf like Na2W2O7 particles with an average thickness of about 1.2 μm.
Similar content being viewed by others
References
Baes C F and Mesmer R E 1976 The hydrolysis of cations (New York: Wiley)
Chai F, Tan R, Cao F, Zhai F, Wang X, Shao C and Liu Y 2007 Mater. Lett. 61 3939
Chatterjee S 2004 Phys. Status Solidi A 201 588
Cheary R W and Coelho A A 1992 J. Appl. Crystallogr. 25 109
Choudhary S N and Choudhary R N P 1998 Mater. Lett. 34 411
Dahlborg M A et al 2002 J. Solid State Chem. 167 525
Dickens P G and Whittingham M S 1968 Q. Rev. Chem. Soc. 22 30
Hong K et al 2006 J. Cryst. Growth 295 75
Kim C Y, Huh S H and Riu D H 2009 Mater. Chem. Phys. 116 527
Lindqvist I 1950 Acta Chem. Scand. 4 1066
Okada K et al 1975 Acta Crystallogr. B31 1200
Pecharsky V K and Zavalij P Y 2005 Fundamentals of powder diffraction and structural characterization of materials (Berlin: Springer) Ch. 3
Pope M T 1983 Heteropoly and isopoly oxometalates (Berlin: Springer)
Redkin A F and Bondarenko G V 2010 J. Solution Chem. 39 1549
Rietveld H 1969 J. Appl. Crystallogr. 2 65
Sasaki Y 1961 Acta Chem. Scand. 15 175
Sharma S and Choudhary R N P 1999 Ferroelectrics 234 129
Tytko K H and Glemser O 1976 Adv. Inorg. Chem. Radiochem. 19 239
Wang L and Bian J J 2011 Mater. Lett. 65 726
Wei Q 2010 J. Cryst. Growth 312 1883
Wei Q H, Shi H S, Chai W X, Qin L S and Shu K Y 2011 Chin. Phys. Lett. 28 118104
Acknowledgements
Financial support for this study was granted by the Ministry of Science and Technological Development of the Republic of Serbia (Project III 45020).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
JOVANOVIĆ, D.J., VALIDŽIĆ, I.L., MITRIĆ, M. et al. Crystal structure studies on plate/shelf like disodium ditungstate. Bull Mater Sci 36, 149–152 (2013). https://doi.org/10.1007/s12034-013-0419-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-013-0419-6