Abstract
A novel composite superionic system, [Cu2HgI4: 0·xAgI], (x = 0.2, 0.4, 0.6 mol wt.%), was prepared. A [Cu2HgI4] system was used as the host. Electrical conductivity was measured to study the transition behaviour at frequencies of 100 Hz, 120 Hz, 1 kHz and 10 kHz in the temperature range 90–170°C using a Gen Rad 1659 RLC Digibridge. Conductivity increased sharply during the β−α phase transition. Upon increasing the dopant-to-host ratio, the conductivity of the superionic system exhibited Arrhenius (thermally activated)-type behaviour. DTA, DTG, TGA and X-ray powder diffraction were performed to confirm doping effect and transition in the host. The phase transition temperature increased with an increase in the dopant concentration. Activation energies in eV for pre- and post-transition phase behaviour are also reported. Due to an interaction between [Cu2HgI4] and AgI, the addition of AgI to [Cu2HgI4] shifted the phase transition of the host [Cu2HgI4].
Similar content being viewed by others
References
Abenojar J, Velasco F and Martinez M A 2006 J. Solid State Chem. 179 2787
Adamski A, Sojka Z, Dyrek K and Che M 1999 Solid State Ionics 117 113
Agrawal R C and Kumar R 1994 J. Phys. D: Appl. Phys. 27 2431
Agrawal R C and Kumar R 1996 J. Phys. D: Appl. Phys. 29 156
Agrawal R C, Gupta R K, Kumar R and Kumar A 1994 J. Mater. Sci. 29 3673
Agrawal R C, Kumar R, Gupta R K and Saleem M 1995 J. Non-Cryst. Solids 181 110
Akopyan I Kh and Novikov B V 1996 Solid State Ionics 89 333
A.S.T.M. Powder Diffraction file No. 18-0450
Bates J B and Farington G C 1981 Proceedings of the international conference on fast ionic transport in solids (Amsterdam: North-Holland)
Burley G 1962 National Bureau of Standards, Washington DC
Fernandez V, Jaque F and Calleja J M 1986 Solid State Commun. 59 803
Hahn H, Frank G and Klinger W 1955 Z. Anorg. Chem. 271 279
Huang P -N and Secco E A 1993 J. Solid State Chem. 103 31
Hull S and Keen D A 2000 J. Phys: Condens. Matter 12 3751
Ingram M D 1987 Phys. Chem. Glasses 28 215
Ketelaar J A A 1931 Z. Kristallogr. 80 190
Ketelaar J A A 1934 Z. Phys. Chem. B26 327
Kumari M S and Secco E A 1985 Can. J. Chem. 63 324
LeDuc H G and Coleman L B 1985 Phys. Rev. B31 933
Mac R, Murrary L and Secco E A 1978 Can. J. Chem. 56 2616
Magistris A, Chiodelli G and Camari G V 1976 Z. Naturforsch. 31 974
Matsuura M 1979 Solid State Commun. 30 231
Mellander B E 1982 Phys. Rev. B26 5886
Mellander B -E and Friesel M 1987 Phys. Rev. B35 7902
Minami T and Tanaka M 1980 J. Solid State Chem. 32 51
Minami T 1986 in Materials for solid state batteries (eds) B V R Chowdhari and S Radhakrishna (Singapore: World Sci. Publ.) p. 181
Nair S M and Ahmad A 1997 J. Phys. Chem. Solids 58 331
Nair S M, Yahya A I and Ahmad A 1996a J. Solid State Chem. 122 349
Nair S M, Yahya A I, Rafiuddin and Ahmad A 1996b Solid State Ionics 86–88 137
Negoiu D and Tador R 1994 Rev. Chim. 45 201
Ono S, Kobayashi M, Kashida S and Ohachi T 2007 Solid State Ionics 178 1023
Secco E A and Usha M G 1994 Solid State Ionics 68 213
Secco E A and Sharma A 1995 J. Phys. Chem. Solids 56 251
Shibata S, Hoshino H and Shimoji M 1974 J. Chem. Soc. Faraday Trans. 1409
Suchow L and Pond G R 1953 J. Am. Chem. Soc. 75 5242
Swenson J, Greevy R L Mc, Boerjesson L, Wicks J D and Howells W S 1996 J. Phys. Condens. Matter 8 3542
Varshney P, Afaq S, Ahmad A and Beg S 2006 J. Phys. Chem. Solids 67 2305
Wagner C 1936 Phys. Z. Chem. B34 309
Wang Y and Rubner M F 1990 Synth. Metals 39 153
Wang Y and Rubner M F 1992 Synth. Metals 47 255
Wakamura K 2002 Solid State Ionics 149 73
Yanjiu L, Secco E A and Usha M G 1993 J. Phys. Chem. Solids 54 821
Ya S, Stomin I, Chernov S V, Antipov E V, Yu S and Dobrovolsky A 2007 J. Solid State Chem. 180 1882
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Noorussaba, Ahmad, A. Phase transition study in a [Cu2HgI4: 0·xAgI] mixed composite system. Bull Mater Sci 33, 419–425 (2010). https://doi.org/10.1007/s12034-010-0064-2
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-010-0064-2