Scanning Kelvin Probe Force Microscopy and Density Functional Theory Studies on the Surface Potential of the Intermetallics in AA7075-T6 Alloys

  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

The surface potentials of Mg2Si and Al7Cu2Fe intermetallic particles in AA7075-T6 alloys were investigated by scanning Kelvin probe force microscopy (SKPFM) technique. The experimental surface potentials of Mg2Si and Al7Cu2Fe intermetallic particles relative to Al matrix were ranging from − 368 to − 265 mV and 480–500 mV, respectively. A theoretical method for assessing relative nobility of intermetallics in Al alloys was discussed through first principle calculation. The work functions and surface energies of Mg2Si and Al7Cu2Fe surfaces were calculated by using density functional theory (DFT) method. The results showed that work functions and surface energies of Mg2Si and Al7Cu2Fe intermetallics were influenced by the orientations of crystal face and terminal types. At the oxygen coverage of 1/4 ML and 1 ML, the theoretical surface potential differences between Mg2Si intermetallics and Al matrix were increased by 10–560 mV and 0–620 mV, while those between Al7Cu2Fe intermetallics and Al matrix were increased by 62–360 mV and 102–331 mV. For the adsorption of oxygen atom, theoretical surface potentials of Mg2Si and Al7Cu2Fe intermetallics relative to Al matrix had a close agreement with the experimental surface potentials. It was verified that DFT method was a valuable theoretical approach to assess the relative nobility of different phases in alloys.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12

Similar content being viewed by others

References

  1. X. Yuan, K. Gao, G.S. Rohrer, and X. Fang, Grain Boundary Plane Distributions in a Hot Rolled 5A06 Aluminum Alloy, Adv. Eng. Mater., 2014, 16(9), p 1105–1110

    Article  Google Scholar 

  2. R. Rana, R. Purohit, and S. Das, Reviews on the Influences of Alloying Elements on the Microstructure and Mechanical Properties of Aluminum Alloys and Aluminum Alloy Composites, Int. J. Sci. Res. Publ., 2012, 2(6), p 1–7

    Google Scholar 

  3. Y. Liu and Y. Cheng, Role of Second Phase Particles in Pitting Corrosion of 3003 Al Alloy in NaCl Solution, Mater. Corros., 2010, 61(3), p 211–217

    Article  Google Scholar 

  4. J. Li, N. Birbilis, and R.G. Buchheit, Electrochemical Assessment of Interfacial Characteristics of Intermetallic Phases Present in Aluminium Alloy 2024-T3, Corros. Sci., 2015, 101, p 155–164

    Article  Google Scholar 

  5. P. Leblanc and G. Frankel, A Study of Corrosion and Pitting Initiation of AA2024-T3 Using Atomic Force Microscopy, J. Electrochem. Soc., 2002, 149(6), p B239–B247

    Article  Google Scholar 

  6. S. Jain, J. Hudson, and J. Scully, Effects of Constituent Particles and Sensitization on Surface Spreading of Intergranular Corrosion on a Sensitized AA5083 Alloy, Electrochim. Acta, 2013, 108, p 253–264

    Article  Google Scholar 

  7. D. Najjar, T. Magnin, and T. Warner, Influence of Critical Surface Defects and Localized Competition Between Anodic Dissolution and Hydrogen Effects During Stress Corrosion Cracking of a 7050 Aluminium Alloy, Mater. Sci. Eng. A, 1997, 238(2), p 293–302

    Article  Google Scholar 

  8. M. Rohwerder and F. Turcu, High-Resolution Kelvin Probe Microscopy in Corrosion Science: Scanning Kelvin Probe Force microscopy (SKPFM) Versus Classical Scanning Kelvin Probe (SKP), Electrochim. Acta, 2007, 53(2), p 290–299

    Article  Google Scholar 

  9. P. Schmutz and G. Frankel, Corrosion Study of AA2024-T3 by Scanning Kelvin Probe Force Microscopy and In Situ Atomic Force Microscopy Scratching, J. Electrochem. Soc., 1998, 145(7), p 2295–2306

    Article  Google Scholar 

  10. V. Guillaumin, P. Schmutz, and G. Frankel, Characterization of Corrosion Interfaces by the Scanning Kelvin Probe Force Microscopy Technique, J. Electrochem. Soc., 2001, 148(5), p B163–B173

    Article  Google Scholar 

  11. M. Iannuzzi, K. Vasanth, and G. Frankel, Unusual Correlation Between SKPFM and Corrosion of Nickel Aluminum Bronzes, J. Electrochem. Soc., 2017, 164(9), p C488–C497

    Article  Google Scholar 

  12. N. Sathirachinda, R. Pettersson, S. Wessman, and J. Pan, Study of Nobility of Chromium Nitrides in Isothermally Aged Duplex Stainless Steels by Using SKPFM and SEM/EDS, Corros. Sci., 2010, 52(1), p 179–186

    Article  Google Scholar 

  13. K. Ralston, N. Birbilis, M. Cavanaugh, M. Weyland, B. Muddle, and R. Marceau, Role of Nanostructure in Pitting of Al-Cu-Mg Alloys, Electrochim. Acta, 2010, 55(27), p 7834–7842

    Article  Google Scholar 

  14. Y. Jin, M. Liu, C. Zhang, C. Leygraf, L. Wen, and J. Pan, First-Principle Calculation of Volta Potential of Intermetallic Particles in Aluminum Alloys and Practical Implications, J. Electrochem. Soc., 2017, 164(9), p C465–C473

    Article  Google Scholar 

  15. G. Kresse and J. Furthmüller, Efficient Iterative Schemes for Ab Initio Total-Energy Calculations Using a Plane-Wave Basis Set, Phys. Rev. B, 1996, 54(16), p 11169

    Article  Google Scholar 

  16. X. Wei, C. Dong, Z. Chen, K. Xiao, and X. Li, A DFT Study of the Adsorption of O2 and H2O on Al (111) Surfaces, RSC Adv., 2016, 6(61), p 56303–56312

    Article  Google Scholar 

  17. J. Wang and S.-Q. Wang, Surface Energy and Work Function of fcc and bcc Crystals: Density Functional Study, Surf. Sci., 2014, 630, p 216–224

    Article  Google Scholar 

  18. W. Tyson and W. Miller, Surface Free Energies of Solid Metals: Estimation from Liquid Surface Tension Measurements, Surf. Sci., 1977, 62(1), p 267–276

    Article  Google Scholar 

  19. X. Tian, T. Wang, L. Fan, Y. Wang, H. Lu, and Y. Mu, A DFT Based Method for Calculating the Surface Energies of Asymmetric MoP Facets, Appl. Surf. Sci., 2018, 427, p 357–362

    Article  Google Scholar 

  20. W. Li and D. Li, Effect of Surface Geometrical Configurations Induced by Microcracks on the Electron Work Function, Acta Mater., 2005, 53(14), p 3871–3878

    Article  Google Scholar 

  21. K.A. Yasakau, M.L. Zheludkevich, S.V. Lamaka, and M.G. Ferreira, Role of Intermetallic Phases in Localized Corrosion of AA5083, Electrochim. Acta, 2007, 52(27), p 7651–7659

    Article  Google Scholar 

  22. L. Li, B. Zhang, B. Tian, Y. Zhou, J. Wang, E. Han, and W. Ke, SVET Study of Galvanic Corrosion of Al/Mg2Si Couple in Aqueous Solutions at Different pH, J. Electrochem. Soc., 2017, 164(6), p C240–C249

    Article  Google Scholar 

  23. D.-P. Ji, Q. Zhu, and S.-Q. Wang, Detailed First-Principles Studies on Surface Energy and Work Function of Hexagonal Metals, Surf. Sci., 2016, 651, p 137–146

    Article  Google Scholar 

  24. Z.-J. Zhao, A. Genest, and N. Rösch, Identification of Surface Species by Vibrational Normal Mode Analysis. A DFT Study, Surf. Sci., 2017, 664, p 233–240

    Article  Google Scholar 

  25. H. Kobayashi and S. Kato, Observations on the Photoelectric Work Function and Leed Pattern from the (111) Surface of an Iron Single Crystal, Surf. Sci., 1969, 18(2), p 341–349

    Article  Google Scholar 

  26. H.L. Skriver and N. Rosengaard, Surface Energy and Work Function of Elemental Metals, Phys. Rev. B, 1992, 46(11), p 7157

    Article  Google Scholar 

  27. R. Eastment and C. Mee, Work Function Measurements on (100) (110) and (111) Surfaces of Aluminium, J. Phys. F Metals Phys., 1973, 3(9), p 1738

    Article  Google Scholar 

  28. C. Nakhowong, T. Sumpao, and T. Seetawan, Synthesis and Characterization of Mg2Si Thermoelectric Material, Advanced Materials Research, J. Nukeaw and W. Pecharapa, Eds., Trans Tech Publications, 2013, p 213–217

  29. J. Proveti, C. Larica, and E. Passamani, Structural Properties and Phase Transformation in Mechanically Alloyed Al/Cu/Fe System, J. Phys. D Appl. Phys., 2003, 36(7), p 798

    Article  Google Scholar 

  30. J. Ryl, J. Wysocka, M. Jarzynka, A. Zielinski, J. Orlikowski, and K. Darowicki, Effect of Native Air-Formed Oxidation on the Corrosion Behavior of AA 7075 Aluminum Alloys, Corros. Sci., 2014, 87, p 150–155

    Article  Google Scholar 

  31. F. Andreatta, H. Terryn, and J. De Wit, Effect of Solution Heat Treatment on Galvanic Coupling Between Intermetallics and Matrix in AA7075-T6, Corros. Sci., 2003, 45(8), p 1733–1746

    Article  Google Scholar 

  32. J. De Wit, Local Potential Measurements with the SKPFM on Aluminium Alloys, Electrochim. Acta, 2004, 49(17–18), p 2841–2850

    Article  Google Scholar 

Download references

Acknowledgment

This work is supported by the National Key Research and Development Program of China (No. 2017YFB0702300) and the National Natural Science Foundation of China (No. 51671029). Supported by 111 Project (No. B170003).

Author information

Authors and Affiliations

  1. Corrosion and Protection Center, Key Laboratory for Corrosion and Protection (MOE), University of Science and Technology Beijing, Beijing, 100083, People’s Republic of China

    Ni Li, Chaofang Dong, Xin Wei, Chen Man, Jizheng Yao, Jiangli Cao & Xiaogang Li

Authors
  1. Ni Li
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Chaofang Dong
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Xin Wei
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Chen Man
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Jizheng Yao
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Jiangli Cao
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Xiaogang Li
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Chaofang Dong.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Li, N., Dong, C., Wei, X. et al. Scanning Kelvin Probe Force Microscopy and Density Functional Theory Studies on the Surface Potential of the Intermetallics in AA7075-T6 Alloys. J. of Materi Eng and Perform 28, 4289–4301 (2019). https://doi.org/10.1007/s11665-019-04160-6

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-019-04160-6

Keywords

Search

Navigation