Analysis of the Enameled AISI 316LVM Stainless Steel

  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

In this work, four different enamels were coated on AISI 316LVM stainless steel and the corrosion resistance of these samples was tested in 5 wt.% NaCl solution at room temperature. The preparation procedure of the enamels was optimized in terms of firing temperature, time and composition. First the thermal expansion was measured using dilatometry followed by electrochemical analysis using chronopotentiometry, electrochemical impedance spectroscopy and cyclic polarization. The topography of the most resistant sample was obtained by 3D-profilometry. All samples coated with enamel showed significantly higher corrosion and dilatation resistance compared with the uncoated stainless steel material.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

Similar content being viewed by others

References

  1. D. Talbot and J. Talbot, Corrosion Science and Technology, CRC Press LLC, Boca Raton, 1998

    Google Scholar 

  2. J.R. Davis, Corrosion: Understanding the Basics, ASM International, Materials Park, 2000

    Google Scholar 

  3. G. Horvat, K. Xhanari, M. Finšgar, L. Gradišnik, U. Maver, Ž. Knez, and Z. Novak, Novel Ethanol-Induced Pectin–Xanthan Aerogel Coatings for Orthopedic Applications, Carbohyd. Polym., 2017, 166, p 365–376

    Article  Google Scholar 

  4. M. Finšgar, A.P. Uzunalic, J. Stergar, L. Gradisnik, and U. Maver, Novel Chitosan/Diclofenac Coatings on Medical Grade Stainless Steel for Hip Replacement Applications, Sci Rep, 2016, 6, p 26653

    Article  Google Scholar 

  5. F.S. Shieu, M.J. Deng, K.C. Lin, and J.C. Wong, Effect of Surface Pretreatments on the Adherance of Porcelain Enamel to a Type 316L Stainless Steel, J. Mater. Sci., 1999, 34, p 5265–5272

    Article  Google Scholar 

  6. M. Aparicio, A. Jitianu, G. Rodriguez, K. Al-Marzoki, M. Jitianu, J. Mosa, and L.C. Klein, Thickness-Properties Synergy in Organic–Inorganic Consolidated Melting-Gel Coatings for Protection of 304 Stainless Steel in NaCl Solutions, Surf. Coat. Technol., 2017, 315, p 426–435

    Article  Google Scholar 

  7. M. Finšgar, S. Fassbender, S. Hirth, and I. Milošev, Electrochemical and XPS study of Polyethyleneimines of Different Molecular Sizes as Corrosion Inhibitors for AISI, 430 Stainless Steel in Near-Neutral Chloride Media, Mater. Chem. Phys., 2009, 116(1), p 198–206

    Article  Google Scholar 

  8. M. Zakeri, D. Nakhaie, M. Naghizadeh, and M.H. Moayed, The Effect of Dichromate Ion on the Pitting Corrosion of AISI, 316 Stainless Steel. Part I: Critical Pitting Temperature, Corros. Sci., 2015, 93, p 234–241

    Article  Google Scholar 

  9. E. Bardal, Corrosion and Protection, Springer, London, 2004

    Book  Google Scholar 

  10. P. Brügge, Pemco Enamel Manual, 2008

  11. X. Yang, A. Jha, R. Brydson, and R.C. Cochrane, An Analysis of the Microstructure and Interfacial Chemistry of Steel-Enamel Interface, Thin Solid Films, 2003, 443, p 33–45

    Article  Google Scholar 

  12. S. Rossi, N. Parziani, and C. Zanella, Abrasion Resistance of Vitreous Enamel Coatings in Function of Frit Composition and Particles Presence, Wear, 2015, 332–333, p 702–709

    Article  Google Scholar 

  13. S. Rossi, C. Zanella, and R. Sommerhuber, Influence of Mill Additives on Vitreous Enamel Properties, Mater. Des., 2014, 55, p 880–887

    Article  Google Scholar 

  14. Y. Son, C. Lee, J. Lee, and B. Kim, Deformation Prediction of Porcelain-Enameled Steels with Strain History by Press Forming and High-Temperature Behavior of Coating Layer, Trans. Nonferrous Metals Soc. China, 2012, 20, p 838–844

    Article  Google Scholar 

  15. X. Yang, A. Jha, R. Brydson, and R.C. Cochrane, The Effects of a Nickel Oxide Precoat on the Gas Bubble Structures and Fish-Scaling Resistance in Vitreous Enamels, Mater. Sci. Eng., 2004, 366, p 254–261

    Article  Google Scholar 

  16. O. Shalydina, L. Bragina, and M. Kuryakin, Powder Electrostatic Technology of Household Appliances Enamelling, Chem. Technol., 2012, 6, p 435–441

    Google Scholar 

  17. E. Scrinzi and S. Rossi, The Aesthetic and Functional Properties of Enamel Coatings on Steel, Mater. Des., 2010, 31(9), p 4138–4146

    Article  Google Scholar 

  18. A. Zucchelli, M. Dignatici, M. Montorsi, R. Carlotti, and C. Siligardi, Characterization of Vitreous Enamel-Steel Interface by Using Hot Stage ESEM and Nano-indentation Techniques, J. Eur. Ceram. Soc., 2012, 32, p 2243–2251

    Article  Google Scholar 

  19. L.G. Protasova, V.G. Kosenko, and E.P. Farafontova, Corrosion of Steel Under Enamel Coating, Glass Ceram., 2003, 60(7–8), p 229–230

    Article  Google Scholar 

  20. Y.M. Xiong, S.L. Zhu, F.H. Wang, and C.H. Lee, Effect of Vitreous Enamel Coating on the Oxidation Behavior of Ti6Al4V and TiAl Alloys at High Temperatures, J. Coat. Technol. Res., 2008, 5(1), p 93–98

    Article  Google Scholar 

  21. Y.M. Xiong, C.H. Guan, S.L. Zhu, and F.H. Wang, Effect of Enamel Coating on Oxidation and Hot Corrosion Behaviors of Ti-24Al-14Nb-3V Alloy, J. Mater. Eng. Perform., 2006, 15(5), p 564–569

    Article  Google Scholar 

  22. J. Tao, X.Z. Guo, Z.D. Huang, H.B. Liu, and T. Wang, Preparation and Characterization of Enamel Coating on Pure Titanium as a Hydrogen Penetration Barrier, Nucl. Eng. Des., 2013, 259, p 65–70

    Article  Google Scholar 

  23. E.A. Yatsenko, A.P. Zubekhin, and A.A. Nepomnyashchev, Protection of Copper Against High-Temperature Corrosion, Glass Ceram., 1999, 56(9–10), p 295–297

    Article  Google Scholar 

  24. Y. Bao, D.T. Gawne, J. Gao, T. Zhang, B.D. Cuenca, and A. Alberdi, Thermal-Spray Deposition of Enamel on Aluminium Alloys, Surf. Coat. Technol., 2013, 232, p 150–158

    Article  Google Scholar 

  25. J. Lawrence and L. Li, A Laser-Based Technique for the Coating of Mild Steel with a Vitreous Enamel, Surf. Coat. Technol., 2001, 140(3), p 238–243

    Article  Google Scholar 

  26. J. Lawrence and L. Li, The Characteristics of a High-Power Diode Laser Fired Enamel Coating on a Carbon Steel, Proc. Inst. Mech. Eng. Part B J. Eng. Manuf., 2001, 215(4), p 509–519

    Article  Google Scholar 

  27. H.J. Brown-Shaklee, W. Carty, and D.D. Edwards, Spectral Selectivity of Composite Enamel Coatings on 321 Stainless Steel, Sol. Energy Mater. Sol. Cells, 2009, 93(8), p 1404–1410

    Article  Google Scholar 

  28. S. Rossi and E. Scrinzi, Evaluation of the Abrasion Resistance of Enamel Coatings, Chem. Eng. Process., 2013, 68, p 74–80

    Article  Google Scholar 

  29. L.G. Protasova and I.G. Kosnyreva, Influence of Enamel Composition and Calcination Conditions on the Corrosion of Steel Under a Layer of Enamel Melt, Russ. J. Appl. Chem., 2004, 77(4), p 666–669

    Article  Google Scholar 

  30. F. Tang, X. Cheng, G. Chen, R.K. Brow, J.S. Volz, and M.L. Koenigstein, Electrochemical Behavior of Enamel-Coated Carbon Steel in Simulated Concrete Pore Water Solution with Various Chloride Concentrations, Electrochim. Acta, 2013, 92, p 36–46

    Article  Google Scholar 

  31. F. Tang, G. Chen, R.K. Brow, J.S. Volz, and M.L. Koenigstein, Corrosion Resistance and Mechanism of Steel Rebar Coated with Three Types of Enamel, Corros. Sci., 2012, 59, p 157–168

    Article  Google Scholar 

  32. A. Conde and J.J. de Damborenea, Electrochemical Impedance Spectroscopy for Studying the Degradation of Enamel Coatings, Corros. Sci., 2002, 44(7), p 1555–1567

    Article  Google Scholar 

  33. K. Xhanari, N. Grah, M. Finšgar, R. Fuchs-Godec, and U. Maver, Corrosion Inhibition and Surface Analysis of Amines on Mild Steel in Chloride Medium, Chem. Pap., 2017, 71(1), p 81–89

    Article  Google Scholar 

  34. M. Finšgar, B. Petovar, K. Xhanari, and U. Maver, The Corrosion Inhibition of Certain Azoles on Steel in Chloride Media: Electrochemistry and Surface Analysis, Corros. Sci., 2016, 111, p 370–381

    Article  Google Scholar 

  35. M. Finšgar and J. Jackson, Electrochemical Study of AISI, C1018 Steel in Methanesulfonic Acid Containing an Acetylenic Alcohol-Based Corrosion Inhibitor Formulation, J. Lab. Autom., 2015, 21(5), p 632–641

    Article  Google Scholar 

  36. A.I. Andrews, S. Pagliuca, W.D. Faust, Porcelain (Vitreous) Enamels and Industrial Enamelling Processes: The Preparation, Application and Properties of Enamels, 3rd ed., Tipografia commerciale, Mantova, Italy, 2011

  37. M. Finšgar, 2-mercaptobenzimidazole as a Copper Corrosion Inhibitor: Part I. Long-Term Immersion, 3D-Profilometry, and Electrochemistry, Corros. Sci., 2013, 72, p 82–89

    Article  Google Scholar 

  38. M. Finšgar and D. Kek Merl, 2-Mercaptobenzoxazole as a Copper Corrosion Inhibitor in Chloride Solution: Electrochemistry, 3D-Profilometry, and XPS Surface Analysis, Corros. Sci., 2014, 80, p 82–95

    Article  Google Scholar 

  39. I.D. Raistrick, D.R. Franceschetti, and J.R. Macdonald, Impedance Spectroscopy Theory, Experiment and Application, 2nd ed., Wiley, Hoboken, 2005

    Google Scholar 

  40. F. Lampert, A.B. Christiansen, R.U. Din, Y. Gonzalez-Garcia, and P. Møller, Corrosion Resistance of AISI, 316L Coated with an Air-Cured Hydrogen Silsesquioxane Based Spin-on-Glass Enamel in Chloride Environment, Corros. Sci., 2017, 127(Supplement C), p 110–119

    Article  Google Scholar 

  41. F. Lampert, A.H. Jensen, R.U. Din, and P. Møller, Hydrogen Silsesquioxane Based Silica Glass Coatings for the Corrosion Protection of Austenitic Stainless Steel, Surf. Coat, Technol., 2016, 307(Part A), p 879–885

    Article  Google Scholar 

  42. M.-G. Olivier and M. Poelman, Use of electrochemical impedance spectroscopy (EIS) for the evaluation of electrocoatings performances, Recent Researches in Corrosion Evaluation and Protectioned, R.S. Razavi, Ed., InTech, Rijeka, 2012

    Google Scholar 

  43. D.K. Merl, P. Panjan, M. Čekada, and M. Maček, The Corrosion Behavior of Cr-(C, N) PVD Hard Coatings Deposited on Various Substrates, Electrochim. Acta, 2004, 49(9–10), p 1527–1533

    Article  Google Scholar 

  44. D. Kek-Merl, J. Lappalainen, and H.L. Tuller, Electrical Properties of Nanocrystalline CeO2 Thin Films Deposited by In Situ Pulsed Laser Deposition, J. Electrochem. Soc., 2006, 153(3), p J15–J20

    Article  Google Scholar 

  45. ASTM F2129-17, Standard Test Method for Conducting Cyclic Potentiodynamic Polarization Measurements to Determine the Corrosion Susceptibility of Small Implant Devices. ASTM International 2017

  46. M. Finšgar, S. Fassbender, F. Nicolini, and I. Milošev, Polyethyleneimine as a Corrosion Inhibitor for ASTM 420 Stainless Steel in Near-Neutral Saline Media, Corros. Sci., 2009, 51(3), p 525–533

    Article  Google Scholar 

  47. M. Finšgar and I. Milošev, Corrosion Behaviour of Stainless Steels in Aqueous Solutions of Methanesulfonic Acid, Corros. Sci., 2010, 52(7), p 2430–2438

    Article  Google Scholar 

  48. L. Samiee, H. Sarpoolaky, and A. Mirhabibi, Microstructure and Adherence of Cobalt Containing and Cobalt Free Enamels to Low Carbon Steel, Mater. Sci. Eng. A, 2007, 458(1), p 88–95

    Article  Google Scholar 

  49. D.A. Jones, Principles and Prevention of Corrosion, 2nd ed., Prentice-Hall, Upper Saddle River, 1996

    Google Scholar 

Download references

Acknowledgment

The authors would like to acknowledge the financial support for this project received from the Slovenian Research Agency (Grant Number P2-0032).

Author information

Authors and Affiliations

  1. Faculty of Chemistry and Chemical Engineering, University of Maribor, Smetanova ulica 17, 2000, Maribor, Slovenia

    Mitja Bukovec, Klodian Xhanari, Barbara Petovar & Matjaž Finšgar

  2. Faculty of Natural Sciences, University of Tirana, Boulevard “Zogu I”, 1001, Tirana, Albania

    Klodian Xhanari

  3. EMO Frite, Mariborska cesta 86, 3000, Celje, Slovenia

    Tadej Lešer

Authors
  1. Mitja Bukovec
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Klodian Xhanari
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Tadej Lešer
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Barbara Petovar
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Matjaž Finšgar
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Matjaž Finšgar.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Bukovec, M., Xhanari, K., Lešer, T. et al. Analysis of the Enameled AISI 316LVM Stainless Steel. J. of Materi Eng and Perform 27, 1122–1129 (2018). https://doi.org/10.1007/s11665-018-3186-0

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-018-3186-0

Keywords

Search

Navigation