Abstract
In this communication, we report on the electro-optical characterization of planar back-side-illuminated HgCdTe electron initiated avalanche photodiode (e-APD) test arrays with cut-off wavelengths λ c = 2.4 μm, λ c = 4.8 μm, and λ c = 9.2 μm. The e-APDs were manufactured at LETI using absorption layers grown by molecular beam epitaxy (MBE). We present measurements of the distributions in gain, noise, and equivalent input dark current. The mid-wave (MW) diodes yielded a very low dispersion (2%) and high operability (98%) for gains up to M = 200. The excess noise factor and equivalent input current (I eq_in) operability were slightly lower, due to defects in the depletion region. The lowest measured value of I eq_in = 1 fA corresponds to the lowest level measured so far in HgCdTe e-APDs and opens the way to new applications. The gain in the long-wave (LW) diodes was limited by tunnelling currents to a value of M = 2.4, associated with an average noise factor F = 1.2. A gain of M = 20 at a bias of −22.5 V was demonstrated in the short-wave (SW) e-APDs.
Similar content being viewed by others
References
J.D. Beck, C.-F. Wan, M.A. Kinch, J.E. Robinson, Proc. SPIE. 4454, 188 (2001)
J.D. Beck, C.-F. Wan, M.A. Kinch, J.E. Robinson, P. Mitra, R. Scrithfield, F. Ma, J. Campbell, J. Electron. Mater. 35, 1166 (2006)
J.D. Beck, C.-F. Wan, M.A. Kinch, J.E. Robinson, P. Mitra, R. Scritchfield, F. Ma, J. Campbell, Proc. SPIE. 5564, 44 (2004)
M.A. Kinch, J.D. Beck, C.-F. Wan, F. Ma, J. Campbell, J. Electron. Mater. 33, 630 (2004)
M. Vaidyanathan et al., 2004 IEEE Aerospace Conference Proc. 3, 1776 (2004)
R.S. Hall et al., Proc. SPIE. 5783, 412 (2005)
G. Perrais, J. Rothman, G. Destefanis, J. Baylet, P. Castelein, J.-P. Chamonal etP. Tribolet, Proc. SPIE. 6935, 69350H (2006)
M.B. Reine, J.W. Marciniec, K.K. Wong, T. Parodos, J.D. Mullarkey, P.A. Lamarre, S.P. Tobin, K.A. Gustavsen, Proc. SPIE. 6294, 629401 (2006)
M.B. Reine, J.W. Marciniec, K.K. Wong, T. Parodos, J.D. Mullarkey, P.A. Lamarre, S.P. Tobin, K.A. Gustavsen, J. Electron. Mater. 36, 1059 (2007)
G. Perrais, J. Baylet, G. Destefanis, J. Rothman, J. Electron. Mater. 36, 963 (2007)
J. Beck, M. Woodall, R. Scritchfield, M. Ohlson, L. Wood, P. Mitra, and J. Robinson, to be published in J. Electron. Mater. 37 (2008). doi:10.1007/s11664-008-0420-9
M.B. Reine, J.W. Marciniec, K.K. Wong, T. Parodos, J.D. Mullarkey, P.A. Lamarre, S.P. Tobin, R.W. Minich, and K.A. Gustavsen, to be published in J. Electron. Mater. 37, (2008)
J. Rothman, G. Perrais, G. Destefanis, J. Baylet, P. Castelein, J.-P. Chamonal. SPIE Proc. SPIE. 6542, 654219 (2007)
M.A. Kinch, to be published in J. Electron. Mater. 37 (2008). doi:10.1007/s11664-008-0439-y
Acknowledgements
The authors wish to thank the DGA and J.-C. Peyrard for supporting this study.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rothman, J., Perrais, G., Ballet, P. et al. Latest Developments of HgCdTe e-APDs at CEA LETI-Minatec. J. Electron. Mater. 37, 1303–1310 (2008). https://doi.org/10.1007/s11664-008-0449-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-008-0449-9