Abstract
Chip scale packages (CSP) have essential solder joint quality problems, and a board level reliability is a key issue in design and development of the CSP type packages. There has been an effort to eliminate Pb from solder due to its toxicology. To evaluate the various solder balls in CSP package applications, Pb-free Sn-Ag-X (X=In, Cu, Bi) and Sn-9Zn-1Bi-5In solder balls were characterized by melting behavior, phases, interfacial reaction, and solder joint reliability. For studying joint strength between solders and under bump metallurgy (UBM) systems, various UBMs were prepared by electroplating and electroless plating. After T/C (temperature cycle) test, Sn3.5Ag8.5In solder was partially corroded and its shape was distorted. This phenomenon was observed in a Sn3Ag10In 1Cu solder system, too. Their fractured surface, microstructure of solder joint interface, and of bulk solder ball were examined and analyzed by optical microscopy, SEM and EDX. To simulate the real surface mounting condition and evaluate the solder joint reliability on board level, Daisy chain test samples using LF-CSP packages were prepared with various Pb-free solders, then a temperature cycle test (−65∼ 150°C) was performed. All tested Pb-free solders showed better board level solder joint reliability than Sn-36Pb-2Ag. Sn-3.5Ag-0.7Cu and Sn-9Zn-1Bi-5In solders showed 35%, 100% superior solder joint reliability than Sn-36Pb-2Ag solder ball, respectively.
Similar content being viewed by others
References
W. Yang, R.W. Messler, Jr., and L.E. Felton, J. Electron. Mater. 23, 765 (1994).
S. Jin, JOM 45, 13 (1993).
S.W. Yoon, J.-R. Soh, B.-J. Lee, and H.M. Lee, Acta Mater. 45, 951 (1997).
S.W. Yoon, B.S. Rho, H.M. Lee, C-U. Kim, and B.-J. Lee, Metal. Trans. A 30A, 1503 (1999).
C. Melton, JOM 45, 33 (1993).
J. Glazer, J. Electron. Mater. 23, 693 (1994).
M.E. Loomans, S. Vaynman, G. Ghosh, and M.E. Fine, J. Electron. Mater. 23, 741 (1994).
S.K. Kang and A.K. Sarkhel, J. Electron. Mater. 23, 701 (1994).
IPC Roadmap for Lead-Free Electronics Assemblies (Northbrook, IL: IPC, 1999).
S.W. Yoon, W.K. Choi, and H.M. Lee, Scripta Metall. 40, 327 (1999).
S.W. Yoon, J.T. Moon, S.H. Hong, Y.H. Choi, and C.J. Park, Proc. SEMI Korea Tech. Symp. 99 (Seoul, Korea: SEMI, 1999).
J.T. Moon, S.W. Yoon, S.H. Hong, Y.H. Choi, C.J. Park, and Y.H. Koh, Proc. 49 IEEE Electron. Compon. and Technol. Conf. (Piscataway, NJ: IEEE, 1999).
T.-M. Korshonen and J.K. Kivilahti, J. Electron. Mater. 27, 149 (1998).
Y.C. Chan, P.L. Tu, A.C.K. So, and J.K.L. Lai, IEEE CPMT part B 20, 463 (1997).
S.W. Yoon, J.T. Moon, S.H. Hong, C.J. Park, and Y.H. Koh, J. Korean Phys. Soc. 35, s778 (1999).
H.D. Blair, T.-Y. Pan, and J.M. Nicholsol, Proc. 48 IEEE Electron. Compon. and Technol. Conf. (Piscataway, NJ: IEEE, 1998), p. 259.
D.R. Frear, S.N. Burchett, H.S. Morgen, and J.H. Lau, The Mechanics of Solder Alloy Interconnection (New York: Van Nostrand Reinhold, 1994), p. 369.
W.K. Choi and H.M. Lee, J. Electron. Mater. 28, 1251 (1999).
P.G. Harris and K.S. Chaggar, Soldering & Surface Mount Technol. 10, 38, 1998.
J. London and D.W. Ashall, Brazing and Soldering 11, 49 (1986).
S. Uegaki, S. Matsuzono, S. Sato, T. Kubota, S. Matsuda, and M. Fukui, Proc. 1999 Pan Pacific Microelectronic Symp. (Edina, MN: SMTA, 1999).
JCPDS #04-0673, #05-0390, #07-0396, ICDD PCPDFWIN (1996).
S.W. Yoon, S.H. Hong, C.J. Park, J.T. Moon, I.S. Park, and H.S. Chun, Proc. 50 IEEE Electron. Compon. and Technol. Conf. (Piscataway, NJ: IEEE, 2000).
J.W. Morris, Jr., D. Tribula, T.S.E. Summers, and D. Grivas, Solder Joint Reliability (New York: Van Nostrand Reinhold, 1991), pp. 225–265.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Yoon, S.W., Park, C.J., Hong, S.H. et al. Interfacial reaction and solder joint reliability of Pb-free solders in lead frame chip scale packages (LF-CSP). J. Electron. Mater. 29, 1233–1240 (2000). https://doi.org/10.1007/s11664-000-0018-3
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s11664-000-0018-3