Abstract
In this study, the assimilation behaviors between calcium ferrite (CF), calcium diferrite (CF2) and sintered Al2O3, and MgO were explored by an improved sessile drop technique, and the interfacial microstructure was discussed. The results indicated that the apparent contact angles of CF slag on Al2O3 and MgO substrate were 15.7 and 5.5 deg, and the apparent contact angles of CF2 slag on Al2O3 and MgO substrate were 17.9 and 7.2 deg, respectively. Namely, CF and CF2 slag were wetting well with Al2O3 and MgO substrate. The dissolution of Al2O3 substrate into the CF and CF2 slag was found to be the driving force of the wetting process. For the CF-MgO and CF2-MgO substrate systems, CaO contrarily distributed with MgO after wetting. For the CF-MgO system, after wetting, the slag was composed of CF and C2F, and most of the Fe2O3 permeated into substrate and formed two permeating layers.
Similar content being viewed by others
Reference
C.K. Du, Q.M. Luo, J.C. Mai, X.L. Yuan, X. Wan, H. Liu: Iron Steel Vanadium Titanium, 2012, vol. 1, pp. 50-55.
Y. Wu: Research On Iron and Steel, 2005, vol. 6, pp.5-9.
Q. Gan, Q. He, J.M. Li, T.Y. Yuan, Z.D. Wang: IRON AND STEEL, 2003, vol. 38, pp.1-5.
S.C. Panigrahy, P. Verstraeten, J. Dilewijns: Metall. Mater. Trans. B, 1984, vol. 15, pp. 23-28.
U.S. Yadav, B.D. Pandey, B.K. Das, D.N. Jena: Ironmaking Steelmaking, 2002, vol. 29, pp. 91-96.
L.H. Hsieh, J.A. Whiteman: ISIJ Int., 1993, vol. 33, pp. 462-467.
E. Kasai, Y. Sakano, T. Kawaguchi, T. Nakamura: ISIJ Int., 2000, vol. 40, pp. 857-862.
L.H. Hsieh: ISIJ Int., 2005, vol. 45, pp. 551-555.
F.M. Shen, X. Jiang, G. Wu, G. Wei, X. Li, Y. Shen: ISIJ Int., 2006, vol. 46, pp. 65-69.
A. Cores, A. Babich, M. Muñiz, S. Ferreira, J. Mochon: ISIJ Int., 2010, vol. 50, 1089-1095.
Y.Z. Zhang, Z.W. Lu, Z.S. Rao, H. Wang: Sintering and Pelletizing, 2001, vol. 26, pp.47-52.
M. Matsumura, K. Snahara, M. Hoshi: CAMP-ISIJ, 2004, vol. 17, pp. 812-816.
D.J. Jiang, Q.G. Lin, M.G. He, Q. Gan, W.G. Fu: China Metallurgy, 2010, vol. 1, pp. 10-14.
T. Umadevi, A.K. Roy, P.C. Mahapatra, M. Prabhu, M. Ranjan: Steel Res. Int., 2009, vol. 80, pp. 800-805.
M. Matsumura, M. Hoshi, T. Kawaguchi: ISIJ Int., 2005, vol. 45, pp. 594-600.
B. Nandy, S. Chandra, D. Bhattacharjee, D. Ghosh: Ironmaking Steelmaking, 2006, vol. 33, pp.111-115.
B. Yu, X.W. Lv, S.L. Xiang, C.G. Bai and J.Q. Yin: ISIJ Int., 2015, vol. 55, pp.483-487.
P. R. Dawson, J. Ostwald and K. M. Hayes: Trans. Inst. Min. Metall., Sect. C, 1985, vol. 94, pp.71-75
S. J. Zhang and S. T. Wang: IRON AND STEEL, 1992, vol. 27, pp. 7-13.
F. Matsuno and T. Harada: Sumitomo Metals, 1979, vol. 1, pp. 1-5.
F. Matsuno and T. Harada: Sumitomo Metals, 1979, vol. 1, pp. 1-5.
Bergman B.: J. Am. Ceram. Soc., 1986, vol. 69, pp. 608-613.
H. Sakamoto, M. Iwata, et al.: Tetsu-to-Hagane(J. Iron Steel Inst. Jpn.), 1985 vol. 71, pp.45-50
T.J. Chun, D.Q. Zhu, Metall. Mater. Trans. B, 2015, vol.46, pp. 1-4.
B. Yu, X.W. Lv and S.L. Xiang et al.: ISIJ Int., 2015, vol. 55, pp. 483-488.
B. Yu, X.W. Lv and S.L. Xiang et al.: ISIJ Int., 2015, vol. 55, pp.1558-1563.
Y.F. Ren, L.Y. Jiang: Sintering and Pelletizing, 1984, vol. 1, pp. 1-5.
M.F. Jin, G.S. Li, M.S. Chu, F.M. Shen: Iron and Steel, 2008, vol. 43, pp.10-14.
G.C. Yu: The theoretical basis of basic refractory, Shanghai Scientific and Technical Publishers, Shanghai, 1982, pp. 99-105.
Acknowledgments
The authors are thankful to the Projects of National Natural Science Foundation (51504003) and Science and Technology Development of Anhui Province (1501041126) and Natural Science Research of universities of Anhui Province (KJ2015A028) for sponsoring the study.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted March 14, 2016.
Rights and permissions
About this article
Cite this article
Long, H., Wu, X., Chun, T. et al. Assimilation Behavior of Calcium Ferrite and Calcium Diferrite with Sintered Al2O3 and MgO. Metall Mater Trans B 47, 2830–2836 (2016). https://doi.org/10.1007/s11663-016-0723-9
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-016-0723-9