Abstract
The surface tensions of melts in the system CaO-FeO-SiO2 have been measured in the temperature range 1573 to 1708 K using the hollow cylinder technique. The iron oxide content was maintained constant at 30 wt pct and the CaO/SiO2 wt pct ratio was varied in the range 0.43 to 1.5. Surface tension increases with increasing basicity and with decreasing temperature. The data were used to test published correlations of slag foaming indexes with surface tension and viscosity. Foam life increases with increasing viscosity and with decreasing surface tension.
Similar content being viewed by others
References
P. Kozakevitch: J. Met., 1969, pp. 57–68.
J.W. Gibbs: The Collected Works of J.W. Gibbs, vol. I, Thermodynamics, Yale University Press, New Haven, CT, 1948, p. 300.
W. Harkins and F. Jordan: J. Am. Chem. Soc., 1930, vol. 52, pp. 1751–72.
Y. Kawai, K. Mori, H. Shiraishi, and N. Yamada: Tetsu-to-Hagané, 1976, vol. 62, pp 53–61.
P. Kozakevitch and A. Konoenko: J. Phys. Chem., 1940, vol. 14, p. 1118.
J. Swisher and C. McCabe: Trans. AIME, 1964, vol. 230, pp. 1669–75.
C. Cooper and J.A. Kitchener: J. Iron Steel Inst., 1959, vol. 193, pp. 48–51.
J.F. Elliott: W.O. Philbrook Memorial Symp. Conf. Proc., Iron and Steel Society, Warrendale, PA, 1988, pp. 3–5.
P. Bhattacharyya and D.R. Gaskell: Metall. Mater. Trans. B, 1996, vol. 27B, pp. 139–41.
C. Cooper and J.A. Kitchener: J. Iron Steel Inst., 1959, vol. 193, pp. 48–59.
J. Swisher and C. McCabe: Trans. AIME, 1964, vol. 230, pp. 1669–75.
S. Hara and O. Ogino: The Reinhardt Schuhmann Int. Symp. on Innovative Technology and Reactor Design in Extraction Metallurgy, TMS-AIME, Warrendale, PA, 1986, pp. 639–47.
K. Ito and R.J. Fruehan: Metall. Trans. B, 1989, vol. 20B, pp. 509–14.
K. Ito and R.J. Fruehan: Metall. Trans. B, 1989, vol. 20B, pp. 515–21.
R. Jiang and R.J. Fruehan: Metall. Trans. B, 1991, vol. 22B, pp. 481–89.
G. Urbain, Y. Bottinga, and P. Richet: Geochim. Cosmochim. Acta, 1982, vol. 46, pp. 1061–72.
P. Rontgen: Z. Erz. Metallhuttenwes., 1960, vol. 13, pp. 363–73.
Y.E. Lee and D.R. Gaskell: Metall. Trans., 1974, vol. 5, pp. 853–60.
Author information
Authors and Affiliations
Additional information
This article is based on a presentation made in the “Geoffrey Belton Memorial Symposium,” held in January 2000, in Sydney, Australia, under the joint sponsorship of ISS and TMS.
Rights and permissions
About this article
Cite this article
Skupien, D., Gaskell, D.R. The surface tensions and foaming behavior of melts in the system CaO-FeO-SiO2 . Metall Mater Trans B 31, 921–925 (2000). https://doi.org/10.1007/s11663-000-0068-1
Issue Date:
DOI: https://doi.org/10.1007/s11663-000-0068-1