Strain-Induced Phase Transformation and Nanocrystallization of 301 Metastable Stainless Steel Upon Ultrasonic Shot Peening

Abstract

The following study investigated the strain-induced phase transformation in metastable austenitic 301 stainless steels via an ultrasonic shot peening treatment (USP) for 5 to 30 minutes. Following the USP, the microhardness increased to a depth of 400 μm and from 200 to 400 HV. The deformed grains and the phase transformation were monitored via X-ray diffraction and electron backscattered diffraction analysis. The grain evolution was studied via transmission electron microscopy. Approximately 500 nm α′-martensite grains formed in the top-most region after 5 minutes of the USP treatment. The grains were then further refined to ~ 100 nm when the peening time increased to 10 and 15 minutes. The grains refined down to tens of nanometers after the specimen was treated for 30 minutes, where the phases were composed of α′-martensite (~ 50 nm). There was a mixture of austenite with α′-martensite (~ 25 nm). The grain refinement and the phase transformation of austenite to α′-martensite during ultrasonic shot peening were systematically investigated.