Atomic level simulations are used to study crack propagation mechanisms in nanocrystalline Ni. Digital samples with a mean grain size of 5 and 8 nm containing 125 grains were used. For both grain sizes, the mechanism of crack propagation involves the formation of nanocracks along grain boundaries in the vicinity of the main crack. Crack resistance curves for the two grain sizes indicate that the smaller grain sizes are more ductile, requiring higher stress intensities for crack propagation. This result is consistent with softer behavior for smaller grain sizes in the inverse Hall–Petch regime, where deformation is accommodated by grain boundary mechanisms. The present simulations specifically show that grain boundary sliding also plays an important role in crack blunting observed in these materials. In many cases, the crack is arrested as it encounters grain boundaries in its path, showing increased resistance to propagation. Increased ductility for smaller grain sizes in this regime indicates that there is a minimum in ductility as a function of grain size in these materials, located around the 10- to 12-nm grain size.
Similar content being viewed by others
References
Van Swygenhoven H., Spazer M., Caro A., Farkas D. (1999) Phys. Rev. B: Condens. Matter Mater. Phys. 60: 22-25
Kumar K.S., Van Swygenhoven H., Suresh S. (2003) Acta Mater. 51: 5743-74
Schiotz J., Jacobsen K.W. (2003) Science, 301: 1357-59
Yamakov V., Wolf D., Phillpot S.R., Mukherjee A.K., Gleiter H. (2002) Nat. Mater. 1: 45-48
Farkas D., Van Swygenhoven H., Derlet P.M. (2002) Phys. Rev. B: Condens. Matter Mater. Phys. 66, 60101
Farkas D., Van Petegem S., Derlet P.M., Van Swygenhoven H. (2005) Acta Mater. 53: 3115-23
Latapie A., Farkas D. (2004) Phys. Rev. B: Condens. Matter Mater. Phys. 69(13): 134110
Van Swygenhoven H., Farkas D., Caro A. (2000) Phys. Rev. B: Condens. Matter Mater. Phys. 62: 831-38
Mishin Y., Mehl M., Farkas D., Papaconstantopoulos D. (1999) Phys. Rev. B: Condens. Matter Mater. Phys. 59: 3393-407
S.J. Plimpton: J. Comp. Phys., 1995, vol. 117, p. 1-19, www.cs.san dia.gov/~sjplimp/lammps.html
Latapie A., Farkas D. (2003) Scripta Mater. 48: 611-15
Frederiksen S.L., Jacobsen K.W., Schiotz J. (2004) Acta Mater. 52: 5019-29
Farkas D. (2000) Phil. Mag. Lett. 80: 229-37
Li H.Q., Ebrahimi F. (2005) Adv. Mater. 17(16): 1969-72
Li H.Q., Ebrahimi F. (2004) Appl. Phys. Lett. 84: 4307-09
Farkas D., Hyde B. (2005) Nano Lett. 5: 2403-07
Bonetti E., Campari E.G., Del Bianco L., Scipione G. (1995) Nanostruct. Mater. 6: 639-42
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is based on a presentation given in the symposium entitled “Deformation and Fracture from Nano to Macro: A Symposium Honoring W.W. Gerberich’s 70th Birthday,” which occurred during the TMS Annual Meeting, March 12–16, 2006, in San Antonio, Texas, and was sponsored by the Mechanical Behavior of Materials and Nanomechanical Behavior Committees of TMS.
Rights and permissions
About this article
Cite this article
Farkas, D. Fracture Resistance of Nanocrystalline Ni. Metall Mater Trans A 38, 2168–2173 (2007). https://doi.org/10.1007/s11661-007-9180-z
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-007-9180-z