Abstract
The tensile deformation behavior and the associated mechanism of extruded Ni50Al50 polycrystals were systemically investigated. The superplastic deformation behavior was observed at certain conditions. The deformation microstructures consisted of subgrains, low-angle grains, and high-angle grains, meaning that a continuous dynamic recrystallization (CDRX) process was operating. This finding suggests that the relative balance between comparable work hardening (dislocation glide) and dynamic work softening (CDRX) results in the occurrence of superplastic deformation process.
Similar content being viewed by others
References
D.R. Miracle: Acta Metall. Mater., 1993, vol. 41 (3), pp. 649–84.
R.D. Noebe, R.R. Bowman, and M.V. Nathal: Int. Mater. Rev., 1993, vol. 38 (4), pp. 193–232.
A.G. Rozner and R.J. Wasilewski: J. Inst. Met., 1966, vol. 34, pp. 169–75.
R.D. Noebe, C.L. Cullers, and R.R. Bowman: J. Mater. Res., 1992, vol. 7 (3), pp. 605–11.
T. Takasugi, J. Kishino, and S. Hanada: Acta Metall. Mater., 1993, vol. 41 (4), pp. 1009–20.
M.H. Loretto and R.J. Wasilewski: Phil. Mag., 1971, vol. 23 (186), pp. 1311–28.
R.J. Wasilewski, S.R. Butler, and J.E. Hanlon: Trans. TMS-AIME, 1967, vol. 239, pp. 1357–64.
R.R. Bowman, R.D. Noebe, S.V. Rai, and I.E. Locci: Metall. Trans. A, 1992, vol. 23A, pp. 1493–1507.
R.D. Noebe and R. Gibala: Scripta Metall., 1986, vol. 20 (11), pp. 1635–39.
A. Ball and R.E. Smallman: Acta Metall., 1966, vol. 14 (7), pp. 1349–61.
X.H. Du, J.T. Guo, and B.D. Zhou: Scripta Mater., 2001, vol. 45 (1), pp. 69–74.
J. Hu and D. Lin: Mater. Lett., 2004, vol. 58, pp. 1297–1301.
D. Jiang and D. Lin: Mater. Lett., 2004, vol. 57, pp. 747–52.
Dongliang Lin, Jing Hu, and Dongmei Jiang: Intermetallics, 2005, vol. 13, pp. 343–49.
Olegy D. Sherby and Jeffrey Wadsworth: Progr. Mater. Sci., 1989, vol. 33 (3), pp 169–221.
T.G. Nieh and J. Wadsworth: Int. Mater. Rev., 1999, vol. 44 (2), pp. 59–75.
M.R. Barnett and F. Montheillet: Acta Mater., 2002, vol. 50 (9), pp. 2285–96.
J.P. Chu, J.H. Wu, H.Y. Yasuda, Y. Umakoshi, and K. Inoue: Intermetallics, 2000, vol. 8 (1), pp. 39–46.
S.J. Hales and T.R. McNelly: Acta Metall., 1988, vol. 36 (5), pp. 1229–39.
A. Belyakov and R. Kaibyshev: Phys. Met. Metallogr., 1994, vol. 78 (10), pp. 91–99.
J.C. Tan and M.J. Tan: Mater. Sci. Eng., 2003, vol. 339 A (1–2), pp. 124–32.
S. Gourdet and F. Montheillet: Mater. Sci. Eng., 2000, vol. 283 A (1–2), pp. 274–88.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Du, X., Wu, B. Continuous dynamic recrystallization of extruded NiAl polycrystals during the superplastic deformation process. Metall Mater Trans A 36, 3343–3351 (2005). https://doi.org/10.1007/s11661-005-0009-3
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-005-0009-3