Abstract
Calcium montmorillonite from Liao-ning was organically intercalated by using cety1 trimethy1 ammonium bromide after it was treated with sodium carbonate. The optimal dosage of intercalating agent was tested. The organically intercalated montmorillonite composites were characterized by the methods of XRD, FTIR and DTA/TG. The results show that the intercalating effect of the organically intercalated montmorillonite composite is the best when the amount of intercalating agent reached 120% cation exchange capacity (CEC)
Similar content being viewed by others
References
George R Alther, Blomin Inc, Ferndale MI. Organically Modified Clay Removes Oil From Water[J]. Waste Manage, 1995, 15(8): 623–627
Smith J A, Galan A. Sorption of Nonionic Organic Contaminants to Single and Dual Organic Cation Bentonites from Water[J]. Environ. Sci. Technol., 1995, 29(3): 685–692
Chen Zhiyong, Li Yuling, Zhang Zhiyang. Preparation and Performance Analysis of the Organic Bentonite[J]. Non-metallic Minerals, 2002, 25(5): 45–47
Wu Pingxiao, Zhang Huifen, Xiao Wending. Synthesis and Characterization of Pillared Montmorillonite[J]. Mineral Journal, 1997, 17(2): 200–207
Wu Pingxiao, Zhang Huifen, Guo Jiugao. The Microstructure of Montmorillonite and It’s Thermal Treatment Products[J]. Geoscience, 2000, 35(2): 185–196
ISIL ISIK, ULKU Yilmazer. Impacked Modified Epoxy/Montmorillonite Nanocomposite[J]. Polyer, 2003, 44: 6371–6372
Bors J, Dultz St. Retention of Radionuclides by Organophilic Bentonite[J]. Journal of Contaminant Hydrology, 1999, (54): 195–206
Dultz St, Bors J. Organophilic Bentonites as Adsorbents for Radionuclides II: Chemical and Mineralogical Properties of HDPY-montmorillonite[J]. Applied Clay Science, 2000, (16): 15–29
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the 11th Five National Science and Technology Supporting Key Project “Engineering Research for Nonmetallic Resources Comprehensive Utilization” (2006BAB12B00) and Educational Ministry Scientific and Technological Research Key Project (No. 02052)
Rights and permissions
About this article
Cite this article
Fu, G., Gong, W. & Liu, G. Preparation and structural analysis of montmorillonite composites. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 24, 931–934 (2009). https://doi.org/10.1007/s11595-009-6931-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-009-6931-2